CN106192600A - Composite kraft paper and preparation method thereof - Google Patents
Composite kraft paper and preparation method thereof Download PDFInfo
- Publication number
- CN106192600A CN106192600A CN201610520532.7A CN201610520532A CN106192600A CN 106192600 A CN106192600 A CN 106192600A CN 201610520532 A CN201610520532 A CN 201610520532A CN 106192600 A CN106192600 A CN 106192600A
- Authority
- CN
- China
- Prior art keywords
- kraft paper
- composite kraft
- sizing agent
- layer
- consumption
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of composite kraft paper, it is formed by bottom, sandwich layer, surface layer and decorative layer are compound successively, and wherein, described bottom, it is made up of secondary stock, bamboo wood pulp and softwood pulp；Described sandwich layer, it is made up of the first sizing agent and essence；Described surface layer, it is made up of secondary stock, softwood pulp and hardwood pulp；Described decorative layer, it is made up of the second sizing agent and dry flower；The preparation method of a kind of composite kraft paper, prepares including bottom, prepared by surface layer, prepared by sandwich layer, and bottom, sandwich layer and surface layer are compound, dry, and decorative layer is combined and drying and other steps.The outer surface of the composite kraft paper of the present invention uses dry flower to decorate, and outward appearance is unique, attractive in appearance, and with the pleasant fragrance consistent with dry flower odor type, natural to people, healthy experience, it is adaptable to make all kinds of high-grade gift bag and packaging bag；The preparation method of the composite kraft paper of the present invention is simple, and available tradition kraft paper production line produces, and secondary stock consumption is big, environmental protection.
Description
Technical field
The present invention relates to kraft paper preparation field.It is more particularly related to a kind of composite kraft paper and preparation thereof
Method.
Background technology
Kraft paper is used as packaging material, and intensity is the highest, and generally in yellowish-brown, the kraft pulp of half drift or full drift is light brown
Color, cream-colored or white, quantitative 80-120g/m2, tearing toughness, rupture merit and resistance to vibration is the highest, mostly be roll web, also
Having sheet paper, general employing kp softwood pulp is raw material, through making beating, manufactures paper with pulp and forms, can be used as water on fourdrinier machine
Mud bag paper, M.G. pure sulphite paper, glue envelope paper dress, bituminized paper, cable protective paper, insulating paper etc..
Along with proposition and the reinforcement of people's environmental consciousness of plastic limit, NK natural kraft is strong due to environmental protection, bearing capacity, often quilt
For making kraft paper bag, and consumption rises year by year, but the decoration of existing kraft paper bag is all to use ink print on its surface
Map brushing case or mark, the most novel, unique, and during use, easily cause ink and come off or permeate, pollute packing content
Thing, additionally, ink printing also can make the abnormal smells from the patient of residual ink on kraft paper bag, to the sensory experience that people is the most joyful.
Summary of the invention
It is an object of the invention to solve at least the above, and the advantage that at least will be described later is provided.
It is a still further object of the present invention to provide a kind of composite kraft paper and preparation method thereof, the appearance of this composite kraft paper
Face uses dry flower to decorate, and outward appearance is unique, attractive in appearance, and with the pleasant fragrance consistent with dry flower odor type, natural to people, strong
The experience of health, it is adaptable to making all kinds of high-grade gift bag and packaging bag, the preparation method of this composite kraft paper is simple, available biography
System kraft paper production line produces, and secondary stock consumption is big, environmental protection.
In order to realize according to object of the present invention and further advantage, it is provided that a kind of composite kraft paper, by bottom, core
Layer, surface layer and decorative layer compound composition successively, wherein,
Described bottom, it is mixed by weight 5:2:1 by secondary stock, bamboo wood pulp and softwood pulp；
Described sandwich layer, it is made up of the first sizing agent and essence, described first sizing agent by polyvinyl alcohol and dextrin by weight
Amount is made than 2:3, and the consumption of described first sizing agent is 0.5-2g/m2, described essence, it is microscapsule powder essence, and it is used
Amount is 0.01-0.05g/m2；
Described surface layer, it is mixed by weight 2:1:1 by secondary stock, softwood pulp and hardwood pulp；
Described decorative layer, it is made up of the second sizing agent and dry flower, and described second sizing agent is Styrene And Chloroalkyl Acrylates gluing
Agent, its consumption is 2-3g/m2, described dry flower, it is to be prepared through microwave drying and hot air drying by flower, and its consumption is 10-50
Piece/m2。
The odor type of heretofore described essence is consistent with the odor type of described dry flower, and described dry flower can be Flos Rosae Rugosae, Kang Nai
One or more of the flower kind apoplexy due to endogenous wind such as fragrant, Caulis et folium pavettae hongkongensis, Bellis perennis, Flos Mume and lavandula angustifolia, described dry flower can only have flower, it is possible to
To be flower and the stem of flower lower end and leaf, it is also possible to be stem or the leaf of plant.
Preferably, described composite kraft paper, described essence is rose essence, and it is by fresh Flos Rosae Rugosae and distillation
Water adds in vacuum back-flow extraction equipment in the ratio of 2:1, and reflux, extract, 4-6h at 50-55 DEG C filters, and to gained filtrate
Middle addition cyclodextrin, carrageenan and sodium carboxymethyl cellulose, after being sufficiently mixed, then carry out gained mixed liquor being spray-dried system
, wherein, the addition of described cyclodextrin is 5g/kg, and the addition of described carrageenan is 3g/kg, described carboxymethyl cellulose
The addition of sodium is 3g/kg.
Preferably, described composite kraft paper, described dry flower is dry Flos Rosae Rugosae, and it is by after new fresh-rose shaping,
Under 800-900w after microwave drying 20-25min, then by gained Flos Rosae Rugosae hot air drying at 25-30 DEG C, until its water content
Less than 12%, prepare.
The preparation method of a kind of composite kraft paper, comprises the steps:
Step one, secondary stock, bamboo wood pulp and softwood pulp are put in the pulping pond of base pastes by weight 5:2:1,
By size degradation, screen, purify, flotation, dissipation of heat and defibrination process, and obtain base pastes；
Step 2, secondary stock, softwood pulp and hardwood pulp are put into the pulping pond of surface layer slurry by weight 2:1:1
In, by size degradation, screen, purify, flotation, dissipation of heat and defibrination process, and obtain surface layer slurry；
Step 3, carry out manufacturing paper with pulp respectively molding by base pastes and surface layer slurry, prepares separate bottom dough-making powder
Layer；
Step 4, the essence of above-mentioned consumption is mixed homogeneously with the first sizing agent of above-mentioned consumption after, spray to the described end
The upper surface of layer, forms sandwich layer；
Step 5, bottom, sandwich layer and surface layer are sequentially placed, carry out the compound composite kraft paper body paper that to obtain of press dewatering, and
It is dried process, until its water content is 25-30% at described composite kraft paper body paper is placed in 190-210 DEG C；
Step 6, by the outer surface of the second sizing agent even application of 1/2 above-mentioned consumption to described composite kraft paper body paper,
Form the first glue surface, then the dry flower of above-mentioned consumption is uniformly placed in described first glue surface, the most again by the of remaining consumption
Two sizing agent even application, in described first glue surface and dry flower, form the second glue surface, the first glue surface, dry flower and the second glue surface group
Become decorative layer, obtain composite kraft paper；
Step 7, described composite kraft paper is dried process at 40-45 DEG C, until its water content is 10-12%,
Obtain qualified composite kraft paper.
Preferably, the preparation method of described composite kraft paper, in described step 4, the spraying of described first sizing agent
Pressure is 0.12-0.15Mpa, spraying rate is 180-200m/min.
Preferably, the preparation method of described composite kraft paper, in described step 5, press dewatering Combined Mining is with up and down
Double rod fashion of extrusion are carried out, and to control extruding force be 105-110kN/m.
Preferably, the preparation method of described composite kraft paper, in described step 6, the spraying of described second sizing agent
Pressure is 0.2-0.25Mpa, spraying rate is 150-160m/min.
Preferably, the preparation method of described composite kraft paper, described base pastes is added with oven dry stock meter
The sodium carboxymethyl cellulose of 0.3-0.5% and 2-3% dextrin.
The present invention at least includes following beneficial effect:
The first, the composite kraft paper of the present invention, outer surface decorated by natural dry flower, and outward appearance is unique, attractive in appearance, and sandwich layer contains micro-
Capsule powders essence, fragrance is lasting, pleasant, natural to people, healthy sensory experience, meets popular, ring healthy to wrapping paper
Guarantor, attractive in appearance, applicable demand, be particularly well-suited to make high-grade gift bag and packaging bag；
The second, in the present invention, secondary stock consumption accounting is big, Original Pulp (bamboo wood pulp, softwood pulp and hardwood pulp) consumption
Accounting is little, beneficially the recycling of waste paper resources and environmental conservation, reduces production cost；
3rd, the method for the present invention can use tradition kraft paper production line to produce, production cost and tradition kraft paper
Quite, and can be according to client's needs, the dry flower moulding of customized composite kraft paper outer surface, to improve its identification so that it is rear
The phase course of processing can not carry out ink printing, directly carry out packaging bag and gift bag makes, save operation, environmental protection；
4th, aobvious by arranging the secondary stock consumption in different base pastes and surface layer formula of size, and base pastes
Writing higher than surface layer slurry, make bottom compared with surface layer, loosely, the beneficially release of sandwich layer fragrance, the structure of surface layer causes structure
Close, the mechanical strength of kraft paper bag can be improved so that it is anti tear, resistance to broken；By adding carboxymethyl cellulose in base pastes
Sodium and dextrin, can the appropriate mechanical strength improving bottom；
5th, by adding a certain proportion of cyclodextrin, carrageenan and sodium carboxymethyl cellulose in rose extract,
The odourant molecules that can make Flos Rosae Rugosae is wrapped in the cavity that cyclodextrin, carrageenan and sodium carboxymethyl cellulose are formed, and reduces the later stage
It is spray-dried the destruction to odourant molecules, controls the fragrance rate of release of gained rose essence, make fragrance more longlasting；
6th, by microwave drying hot air drying more first after Flos Rosae Rugosae shaping, compared with omnidistance microwave drying, the method can be kept away
Exempting from dry Flos Rosae Rugosae edge overdrying, coking, affect the sight of dry Flos Rosae Rugosae, compared with omnidistance hot air drying, the method can shorten
Drying time, it is to avoid Flos Rosae Rugosae holder is partially dried not exclusively, making Flos Rosae Rugosae be dried evenly, flower-shape keeps.
Part is embodied by the further advantage of the present invention, target and feature by description below, and part also will be by this
Invention research and practice and be understood by the person skilled in the art.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described in further detail, to make those skilled in the art with reference to description
Word can be implemented according to this.
It should be noted that experimental technique described in following embodiment, if no special instructions, it is conventional method, described
Reagent and material, if no special instructions, the most commercially obtain.
Embodiment 1:
A kind of composite kraft paper, is formed by bottom, sandwich layer, surface layer and decorative layer are compound successively, wherein,
Described bottom, it is mixed by weight 5:2:1 by secondary stock, bamboo wood pulp and softwood pulp；
Described sandwich layer, it is made up of the first sizing agent and essence, described first sizing agent by polyvinyl alcohol and dextrin by weight
Amount is made than 2:3, and the consumption of described first sizing agent is 0.5g/m2, described essence, it is microscapsule powder essence, its consumption
For 0.01g/m2；
Described surface layer, it is mixed by weight 2:1:1 by secondary stock, softwood pulp and hardwood pulp；
Described decorative layer, it is made up of the second sizing agent and dry flower, and described second sizing agent is Styrene And Chloroalkyl Acrylates gluing
Agent, its consumption is 2g/m2, described dry flower, it is to be prepared through microwave drying and hot air drying by flower, and its consumption is 30/m2。
The preparation method of a kind of composite kraft paper, comprises the steps:
Step one, secondary stock, bamboo wood pulp and softwood pulp are put in the pulping pond of base pastes by weight 5:2:1,
By size degradation, screen, purify, flotation, dissipation of heat and defibrination process, and obtain base pastes；
Step 2, secondary stock, softwood pulp and hardwood pulp are put into the pulping pond of surface layer slurry by weight 2:1:1
In, by size degradation, screen, purify, flotation, dissipation of heat and defibrination process, and obtain surface layer slurry；
Step 3, carry out manufacturing paper with pulp respectively molding by base pastes and surface layer slurry, prepares separate bottom dough-making powder
Layer；
Step 4, the essence of above-mentioned consumption is mixed homogeneously with the first sizing agent of above-mentioned consumption after, spray to the described end
The upper surface of layer, forms sandwich layer；
Step 5, bottom, sandwich layer and surface layer are sequentially placed, carry out the compound composite kraft paper body paper that to obtain of press dewatering, and
Described composite kraft paper body paper is placed at 190 DEG C and is dried process, until its water content is 25%；
Step 6, by the outer surface of the second sizing agent even application of 1/2 above-mentioned consumption to described composite kraft paper body paper,
Form the first glue surface, then the dry flower of above-mentioned consumption is uniformly placed in described first glue surface, the most again by the of remaining consumption
Two sizing agent even application, in described first glue surface and dry flower, form the second glue surface, the first glue surface, dry flower and the second glue surface group
Become decorative layer, obtain composite kraft paper；
Step 7, at 40 DEG C, described composite kraft paper being dried process, until its water content is 10%, it is qualified to obtain
Composite kraft paper.
The preparation method of described composite kraft paper, in described step 4, the spray pressure of described first sizing agent is
0.12Mpa, spraying rate are 180m/min.
The preparation method of described composite kraft paper, in described step 5, press dewatering Combined Mining extrudes with the most double rods
Mode is carried out, and to control extruding force be 105kN/m.
The preparation method of described composite kraft paper, in described step 6, the spray pressure of described second sizing agent is
0.2Mpa, spraying rate are 150m/min.
The preparation method of described composite kraft paper, is added with the carboxylic first to oven dry stock meter 0.3% in described base pastes
Base sodium cellulosate and 2% dextrin.
Embodiment 2:
A kind of composite kraft paper, is formed by bottom, sandwich layer, surface layer and decorative layer are compound successively, wherein,
Described bottom, it is mixed by weight 5:2:1 by secondary stock, bamboo wood pulp and softwood pulp；
Described sandwich layer, it is made up of the first sizing agent and essence, described first sizing agent by polyvinyl alcohol and dextrin by weight
Amount is made than 2:3, and the consumption of described first sizing agent is 0.5g/m2, described essence, it is microscapsule powder essence, its consumption
For 0.02g/m2；
Described surface layer, it is mixed by weight 2:1:1 by secondary stock, softwood pulp and hardwood pulp；
Described decorative layer, it is made up of the second sizing agent and dry flower, and described second sizing agent is Styrene And Chloroalkyl Acrylates gluing
Agent, its consumption is 2g/m2, described dry flower, it is to be prepared through microwave drying and hot air drying by flower, and its consumption is 10/m2。
Described composite kraft paper, described essence is rose essence, and it is by 2:1's by fresh Flos Rosae Rugosae and distilled water
Ratio adds in vacuum back-flow extraction equipment, reflux, extract, 6h at 50 DEG C, filters, and add in gained filtrate cyclodextrin,
Carrageenan and sodium carboxymethyl cellulose, after being sufficiently mixed, then gained mixed liquor is carried out be spray-dried prepare, wherein, described ring
The addition of dextrin is 5g/kg, and the addition of described carrageenan is 3g/kg, and the addition of described sodium carboxymethyl cellulose is 3g/
kg。
Described composite kraft paper, described dry flower is dry Flos Rosae Rugosae, and it is by after new fresh-rose shaping, micro-under 800w
After ripple is dried 25min, then by gained Flos Rosae Rugosae hot air drying at 25 DEG C, until its water content is less than 12%, prepare.
The preparation method of a kind of composite kraft paper, comprises the steps:
Step one, secondary stock, bamboo wood pulp and softwood pulp are put in the pulping pond of base pastes by weight 5:2:1,
By size degradation, screen, purify, flotation, dissipation of heat and defibrination process, and obtain base pastes；
Step 2, secondary stock, softwood pulp and hardwood pulp are put into the pulping pond of surface layer slurry by weight 2:1:1
In, by size degradation, screen, purify, flotation, dissipation of heat and defibrination process, and obtain surface layer slurry；
Step 3, carry out manufacturing paper with pulp respectively molding by base pastes and surface layer slurry, prepares separate bottom dough-making powder
Layer；
Step 4, the essence of above-mentioned consumption is mixed homogeneously with the first sizing agent of above-mentioned consumption after, spray to the described end
The upper surface of layer, forms sandwich layer；
Step 5, bottom, sandwich layer and surface layer are sequentially placed, carry out the compound composite kraft paper body paper that to obtain of press dewatering, and
Described composite kraft paper body paper is placed at 190 DEG C and is dried process, until its water content is 25%；
Step 6, by the outer surface of the second sizing agent even application of 1/2 above-mentioned consumption to described composite kraft paper body paper,
Form the first glue surface, then the dry flower of above-mentioned consumption is uniformly placed in described first glue surface, the most again by the of remaining consumption
Two sizing agent even application, in described first glue surface and dry flower, form the second glue surface, the first glue surface, dry flower and the second glue surface group
Become decorative layer, obtain composite kraft paper；
Step 7, at 40 DEG C, described composite kraft paper being dried process, until its water content is 10%, it is qualified to obtain
Composite kraft paper.
The preparation method of described composite kraft paper, in described step 4, the spray pressure of described first sizing agent is
0.12Mpa, spraying rate are 180m/min.
The preparation method of described composite kraft paper, in described step 5, press dewatering Combined Mining extrudes with the most double rods
Mode is carried out, and to control extruding force be 105kN/m.
The preparation method of described composite kraft paper, in described step 6, the spray pressure of described second sizing agent is
0.2Mpa, spraying rate are 150m/min.
The preparation method of described composite kraft paper, is added with the carboxylic first to oven dry stock meter 0.3% in described base pastes
Base sodium cellulosate and 2% dextrin.
Embodiment 3:
A kind of composite kraft paper, is formed by bottom, sandwich layer, surface layer and decorative layer are compound successively, wherein,
Described bottom, it is mixed by weight 5:2:1 by secondary stock, bamboo wood pulp and softwood pulp；
Described sandwich layer, it is made up of the first sizing agent and essence, described first sizing agent by polyvinyl alcohol and dextrin by weight
Amount is made than 2:3, and the consumption of described first sizing agent is 1g/m2, described essence, it is microscapsule powder essence, and its consumption is
0.3g/m2；
Described surface layer, it is mixed by weight 2:1:1 by secondary stock, softwood pulp and hardwood pulp；
Described decorative layer, it is made up of the second sizing agent and dry flower, and described second sizing agent is Styrene And Chloroalkyl Acrylates gluing
Agent, its consumption is 2.5g/m2, described dry flower, it is to be prepared through microwave drying and hot air drying by flower, its consumption is 30/
m2。
Described composite kraft paper, described essence is rose essence, and it is by 2:1's by fresh Flos Rosae Rugosae and distilled water
Ratio adds in vacuum back-flow extraction equipment, reflux, extract, 5h at 52 DEG C, filters, and add in gained filtrate cyclodextrin,
Carrageenan and sodium carboxymethyl cellulose, after being sufficiently mixed, then gained mixed liquor is carried out be spray-dried prepare, wherein, described ring
The addition of dextrin is 5g/kg, and the addition of described carrageenan is 3g/kg, and the addition of described sodium carboxymethyl cellulose is 3g/
kg。
Described composite kraft paper, described dry flower is dry Flos Rosae Rugosae, and it is by after new fresh-rose shaping, micro-under 850w
After ripple is dried 22min, then by gained Flos Rosae Rugosae hot air drying at 27 DEG C, until its water content is less than 12%, prepare.
The preparation method of a kind of composite kraft paper, comprises the steps:
Step one, secondary stock, bamboo wood pulp and softwood pulp are put in the pulping pond of base pastes by weight 5:2:1,
By size degradation, screen, purify, flotation, dissipation of heat and defibrination process, and obtain base pastes；
Step 2, secondary stock, softwood pulp and hardwood pulp are put into the pulping pond of surface layer slurry by weight 2:1:1
In, by size degradation, screen, purify, flotation, dissipation of heat and defibrination process, and obtain surface layer slurry；
Step 3, carry out manufacturing paper with pulp respectively molding by base pastes and surface layer slurry, prepares separate bottom dough-making powder
Layer；
Step 4, the essence of above-mentioned consumption is mixed homogeneously with the first sizing agent of above-mentioned consumption after, spray to the described end
The upper surface of layer, forms sandwich layer；
Step 5, bottom, sandwich layer and surface layer are sequentially placed, carry out the compound composite kraft paper body paper that to obtain of press dewatering, and
Described composite kraft paper body paper is placed at 200 DEG C and is dried process, until its water content is 28%；
Step 6, by the outer surface of the second sizing agent even application of 1/2 above-mentioned consumption to described composite kraft paper body paper,
Form the first glue surface, then the dry flower of above-mentioned consumption is uniformly placed in described first glue surface, the most again by the of remaining consumption
Two sizing agent even application, in described first glue surface and dry flower, form the second glue surface, the first glue surface, dry flower and the second glue surface group
Become decorative layer, obtain composite kraft paper；
Step 7, at 43 DEG C, described composite kraft paper being dried process, until its water content is 11%, it is qualified to obtain
Composite kraft paper.
The preparation method of described composite kraft paper, in described step 4, the spray pressure of described first sizing agent is
0.13Mpa, spraying rate are 190m/min.
The preparation method of described composite kraft paper, in described step 5, press dewatering Combined Mining extrudes with the most double rods
Mode is carried out, and to control extruding force be 108kN/m.
The preparation method of described composite kraft paper, in described step 6, the spray pressure of described second sizing agent is
0.22Mpa, spraying rate are 155m/min.
The preparation method of described composite kraft paper, is added with the carboxylic first to oven dry stock meter 0.4% in described base pastes
Base sodium cellulosate and 2.5% dextrin.
Embodiment 4:
A kind of composite kraft paper, is formed by bottom, sandwich layer, surface layer and decorative layer are compound successively, wherein,
Described bottom, it is mixed by weight 5:2:1 by secondary stock, bamboo wood pulp and softwood pulp；
Described sandwich layer, it is made up of the first sizing agent and essence, described first sizing agent by polyvinyl alcohol and dextrin by weight
Amount is made than 2:3, and the consumption of described first sizing agent is 2g/m2, described essence, it is microscapsule powder essence, and its consumption is
0.05g/m2；
Described surface layer, it is mixed by weight 2:1:1 by secondary stock, softwood pulp and hardwood pulp；
Described decorative layer, it is made up of the second sizing agent and dry flower, and described second sizing agent is Styrene And Chloroalkyl Acrylates gluing
Agent, its consumption is 3g/m2, described dry flower, it is to be prepared through microwave drying and hot air drying by flower, and its consumption is 50/m2。
Described composite kraft paper, described essence is rose essence, and it is by 2:1's by fresh Flos Rosae Rugosae and distilled water
Ratio adds in vacuum back-flow extraction equipment, reflux, extract, 4h at 55 DEG C, filters, and add in gained filtrate cyclodextrin,
Carrageenan and sodium carboxymethyl cellulose, after being sufficiently mixed, then gained mixed liquor is carried out be spray-dried prepare, wherein, described ring
The addition of dextrin is 5g/kg, and the addition of described carrageenan is 3g/kg, and the addition of described sodium carboxymethyl cellulose is 3g/
kg。
Described composite kraft paper, described dry flower is dry Flos Rosae Rugosae, and it is by after new fresh-rose shaping, micro-under 900w
After ripple is dried 20min, then by gained Flos Rosae Rugosae hot air drying at 30 DEG C, until its water content is less than 12%, prepare.
The preparation method of a kind of composite kraft paper, comprises the steps:
Step one, secondary stock, bamboo wood pulp and softwood pulp are put in the pulping pond of base pastes by weight 5:2:1,
By size degradation, screen, purify, flotation, dissipation of heat and defibrination process, and obtain base pastes；
Step 2, secondary stock, softwood pulp and hardwood pulp are put into the pulping pond of surface layer slurry by weight 2:1:1
In, by size degradation, screen, purify, flotation, dissipation of heat and defibrination process, and obtain surface layer slurry；
Step 3, carry out manufacturing paper with pulp respectively molding by base pastes and surface layer slurry, prepares separate bottom dough-making powder
Layer；
Step 4, the essence of above-mentioned consumption is mixed homogeneously with the first sizing agent of above-mentioned consumption after, spray to the described end
The upper surface of layer, forms sandwich layer；
Step 5, bottom, sandwich layer and surface layer are sequentially placed, carry out the compound composite kraft paper body paper that to obtain of press dewatering, and
Described composite kraft paper body paper is placed at 210 DEG C and is dried process, until its water content is 30%；
Step 6, by the outer surface of the second sizing agent even application of 1/2 above-mentioned consumption to described composite kraft paper body paper,
Form the first glue surface, then the dry flower of above-mentioned consumption is uniformly placed in described first glue surface, the most again by the of remaining consumption
Two sizing agent even application, in described first glue surface and dry flower, form the second glue surface, the first glue surface, dry flower and the second glue surface group
Become decorative layer, obtain composite kraft paper；
Step 7, at 45 DEG C, described composite kraft paper being dried process, until its water content is 12%, it is qualified to obtain
Composite kraft paper.
The preparation method of described composite kraft paper, in described step 4, the spray pressure of described first sizing agent is
0.15Mpa, spraying rate are 200m/min.
The preparation method of described composite kraft paper, in described step 5, press dewatering Combined Mining extrudes with the most double rods
Mode is carried out, and to control extruding force be 110kN/m.
The preparation method of described composite kraft paper, in described step 6, the spray pressure of described second sizing agent is
0.25Mpa, spraying rate are 160m/min.
The preparation method of described composite kraft paper, is added with the carboxylic first to oven dry stock meter 0.5% in described base pastes
Base sodium cellulosate and 3% dextrin.
Although embodiment of the present invention are disclosed as above, but it is not restricted in description and embodiment listed
Using, it can be applied to various applicable the field of the invention completely, for those skilled in the art, and can be easily
Realizing other amendment, therefore under the general concept limited without departing substantially from claim and equivalency range, the present invention does not limit
In specific details.
Claims (8)
1. a composite kraft paper, it is characterised in that formed by bottom, sandwich layer, surface layer and decorative layer are compound successively, wherein,
Described bottom, it is mixed by weight 5:2:1 by secondary stock, bamboo wood pulp and softwood pulp；
Described sandwich layer, it is made up of the first sizing agent and essence, and described first sizing agent is by polyvinyl alcohol and dextrin by weight
2:3 makes, and the consumption of described first sizing agent is 0.5-2g/m2, described essence, it is microscapsule powder essence, and its consumption is
0.01-0.05g/m2；
Described surface layer, it is mixed by weight 2:1:1 by secondary stock, softwood pulp and hardwood pulp；
Described decorative layer, it is made up of the second sizing agent and dry flower, and described second sizing agent is Styrene And Chloroalkyl Acrylates adhesive,
Its consumption is 2-3g/m2, described dry flower, it is to be prepared through microwave drying and hot air drying by flower, its consumption is 10-50/
m2。
2. composite kraft paper as claimed in claim 1, it is characterised in that described essence is rose essence, and it is by fresh
Flos Rosae Rugosae and distilled water add in vacuum back-flow extraction equipment in the ratio of 2:1, and reflux, extract, 4-6h at 50-55 DEG C filters,
And in gained filtrate, add cyclodextrin, carrageenan and sodium carboxymethyl cellulose, after being sufficiently mixed, then gained mixed liquor is carried out
Being spray-dried and prepare, wherein, the addition of described cyclodextrin is 5g/kg, and the addition of described carrageenan is 3g/kg, described carboxylic
The addition of sodium carboxymethylcellulose pyce is 3g/kg.
3. composite kraft paper as claimed in claim 1, it is characterised in that described dry flower is dry Flos Rosae Rugosae, and it is by fresh rose
After rare colored shaping, under 800-900w after microwave drying 20-25min, then by gained Flos Rosae Rugosae hot air drying at 25-30 DEG C,
Until its water content is less than 12%, prepare.
4. the preparation method of the composite kraft paper as described in claim 1-3 is arbitrary, it is characterised in that include walking as follows
Rapid:
Step one, secondary stock, bamboo wood pulp and softwood pulp are put in the pulping pond of base pastes by weight 5:2:1, pass through
Size degradation, screen, purify, flotation, dissipation of heat and defibrination process, and obtain base pastes；
Step 2, secondary stock, softwood pulp and hardwood pulp are put in the pulping pond of surface layer slurry by weight 2:1:1, logical
Cross size degradation, screen, purify, flotation, dissipation of heat and defibrination process, and obtain surface layer slurry；
Step 3, carry out manufacturing paper with pulp respectively molding by base pastes and surface layer slurry, prepares separate bottom and surface layer；
Step 4, the essence of above-mentioned consumption is mixed homogeneously with the first sizing agent of above-mentioned consumption after, spray to described bottom
Upper surface, forms sandwich layer；
Step 5, bottom, sandwich layer and surface layer are sequentially placed, carry out that press dewatering is compound to obtain composite kraft paper body paper, and by institute
State at composite kraft paper body paper is placed in 190-210 DEG C and be dried process, until its water content is 25-30%；
Step 6, by the outer surface of the second sizing agent even application of 1/2 above-mentioned consumption to described composite kraft paper body paper, formed
First glue surface, then the dry flower of above-mentioned consumption is uniformly placed in described first glue surface, execute the second of remaining consumption the most again
Colloid even application, in described first glue surface and dry flower, forms the second glue surface, the first glue surface, dry flower and the second glue surface composition dress
Decorations layer, obtains composite kraft paper；
Step 7, described composite kraft paper is dried process at 40-45 DEG C, until its water content is 10-12%, obtains conjunction
The composite kraft paper of lattice.
5. the preparation method of composite kraft paper as claimed in claim 4, it is characterised in that in described step 4, described first
The spray pressure of sizing agent is 0.12-0.15Mpa, spraying rate is 180-200m/min.
6. the preparation method of composite kraft paper as claimed in claim 4, it is characterised in that in described step 5, press dewatering
Combined Mining up and down double rod fashion of extrusion are carried out, and to control extruding force be 105-110kN/m.
7. the preparation method of composite kraft paper as claimed in claim 4, it is characterised in that in described step 6, described second
The spray pressure of sizing agent is 0.2-0.25Mpa, spraying rate is 150-160m/min.
8. the preparation method of composite kraft paper as claimed in claim 4, it is characterised in that it is right to be added with in described base pastes
The sodium carboxymethyl cellulose of oven dry stock meter 0.3-0.5% and 2-3% dextrin.