CN106189786A - 一种力学性能好建筑墙体用耐磨保温墙 - Google Patents
一种力学性能好建筑墙体用耐磨保温墙 Download PDFInfo
- Publication number
- CN106189786A CN106189786A CN201610739984.4A CN201610739984A CN106189786A CN 106189786 A CN106189786 A CN 106189786A CN 201610739984 A CN201610739984 A CN 201610739984A CN 106189786 A CN106189786 A CN 106189786A
- Authority
- CN
- China
- Prior art keywords
- parts
- stirring
- mechanical property
- wear resistant
- heat preserving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种力学性能好建筑墙体用耐磨保温墙，其原料按重量份包括：醇酸树脂20～40份，酚醛树脂10～20份，聚氨酯50～70份，苯乙烯1～2份，N，N‑二甲基乙醇胺3～7份，聚二甲基硅氧烷1.5～2.5份，硅烷偶联剂KH‑550 1～3份，改性石蜡3～7份，壳聚糖2～6份，2‑氨基‑2‑甲基‑1‑丙醇3～7份，表面活性剂3～5份，醋酸纤维4～10份，纳米二氧化硅20～30份，凹凸棒土10～20份，蚕丝纤维15～25份，石棉10～20份，滑石粉3～7份，稳泡剂2～4份，发泡剂2～4份。本发明耐磨性好，耐热性能优异，还具有优异的力学性能。
Description
技术领域
本发明涉及涂料技术领域，尤其涉及一种力学性能好建筑墙体用耐磨保温墙。
背景技术
目前市面上使用的保温墙起到保温隔热，维持室内温度稳定的作用，但其耐磨、力学性能较差，由于长时间暴晒，导致保温墙开裂，雨水、烟尘便渗入保温墙内部，迅速腐蚀保温墙体，既影响保温墙的保温隔热作用，又降低保温墙的整体防护效果，随着人们对居住环境进行改善，如何制备一种耐磨性好，耐热性能优异，且具有优异力学性能的保温墙成为目前需要解决的技术问题。
发明内容
基于背景技术存在的技术问题，本发明提出了一种力学性能好建筑墙体用耐磨保温墙，耐磨性好，耐热性能优异，而且具有优异的力学性能。
本发明提出的一种力学性能好建筑墙体用耐磨保温墙，其原料按重量份包括：醇酸树脂20～40份，酚醛树脂10～20份，聚氨酯50～70份，苯乙烯1～2份，N，N-二甲基乙醇胺3～7份，聚二甲基硅氧烷1.5～2.5份，硅烷偶联剂KH-5501～3份，改性石蜡3～7份，壳聚糖2～6份，2-氨基-2-甲基-1-丙醇3～7份，表面活性剂3～5份，醋酸纤维4～10份，纳米二氧化硅20～30份，凹凸棒土10～20份，蚕丝纤维15～25份，石棉10～20份，滑石粉3～7份，稳泡剂2～4份，发泡剂2～4份。
优选地，醇酸树脂、酚醛树脂、聚氨酯、苯乙烯、N,N～二甲基乙醇胺的重量比为25～35：12～18：55～65：1.3～1.7：4～6。
优选地，2-氨基-2-甲基-1-丙醇、表面活性剂、醋酸纤维、纳米二氧化硅、凹凸棒土、蚕丝纤维、石棉、滑石粉的重量比为4～6：3.5～4.5：6～8：23～27：12～18：18～22：14～18：4～6。
优选地，其原料按重量份包括：醇酸树脂25～35份，酚醛树脂12～18份，聚氨酯55～65份，苯乙烯1.3～1.7份，N，N-二甲基乙醇胺4～6份，聚二甲基硅氧烷1.8～2.2份，硅烷偶联剂KH-550 1.5～2.5份，改性石蜡4～6份，壳聚糖3～5份，2-氨基-2-甲基-1-丙醇4～6份，表面活性剂3.5～4.5份，醋酸纤维6～8份，纳米二氧化硅23～27份，凹凸棒土12～18份，蚕丝纤维18～22份，石棉14～18份，滑石粉4～6份，稳泡剂2.5～3.5份，发泡剂2.5～3.5份。
优选地，改性石蜡采用如下工艺制备：将四氧化三铁、水混合搅拌得到预制料；将羧甲基微晶纤维素、无水乙醇混合搅拌均匀，在搅拌过程中向其中加入预制料，加入完全后继续搅拌，冷却，洗涤，干燥，研磨得到改性四氧化三铁；将微晶石蜡、天然蜂蜡、聚乙烯蜡、十二羟基硬脂酸密闭加热至融化，在通入空气的状态下，加入高锰酸钾混合搅拌，降至室温，加入改性四氧化三铁搅拌得到改性石蜡。
优选地，改性石蜡采用如下工艺制备：将四氧化三铁、水混合搅拌10～20min，得到预制料；将羧甲基微晶纤维素、无水乙醇混合搅拌均匀，搅拌温度为60～70℃，在搅拌过程中向其中加入预制料，加入完全后继续搅拌8～12min，冷却，洗涤，干燥，研磨得到改性四氧化三铁；将微晶石蜡、天然蜂蜡、聚乙烯蜡、十二羟基硬脂酸密闭加热至融化，在通入空气的状态下，加入高锰酸钾混合搅拌70～130min，降温至室温，加入改性四氧化三铁搅拌80～120min，得到改性石蜡。
优选地，改性石蜡采用如下工艺制备：按重量份将12～16份四氧化三铁、40～60份水混合搅拌10～20min，得到预制料；将4～8份羧甲基微晶纤维素、16～22份无水乙醇混合搅拌均匀，搅拌温度为60～70℃，在搅拌过程中向其中加入预制料，加入完全后继续搅拌8～12min，冷却，洗涤，干燥，研磨得到改性四氧化三铁；将15～25份微晶石蜡、8～12份天然蜂蜡、25～45份聚乙烯蜡、2～4份十二羟基硬脂酸密闭加热至融化，在通入空气的状态下，加入0.3～0.9份高锰酸钾混合搅拌70～130min，降温至室温，加入改性四氧化三铁搅拌80～120min，得到改性石蜡。
本发明采用常规制备工艺制得。
本发明的改性石蜡制备过程中，微晶石蜡、天然蜂蜡、聚乙烯蜡配合，在十二羟基硬脂酸配合作用下，与高锰酸钾混合程度极高，通过氧化反应引入含氧基团，使改性石蜡极性高，乳化性能极好，而且具有强的亲和力和表面活性，通过加入吸附性、耐磨、耐热性能优异的改性四氧化三铁，使改性石蜡具有一定耐磨耐热性的基础上，同时与聚氨酯、酚醛树脂、醇酸树脂的混溶性极好，而且可与聚氨酯、酚醛树脂、醇酸树脂上的活性基团在N，N-二甲基乙醇胺、苯乙烯的配合作用下交联，不仅耐磨性能极好，同时耐热、耐温变环境的性能极好，在壳聚糖、硅烷偶联剂KH-550、聚二甲基硅氧烷配合作用，与凹凸棒土、纳米二氧化硅、石棉、蚕丝纤维、滑石粉的结合力强，力学性能好，耐磨及耐热性能进一步增强。
具体实施方式
下面，通过具体实施例对本发明的技术方案进行详细说明。
实施例1
本发明提出的一种力学性能好建筑墙体用耐磨保温墙，其原料按重量份包括：醇酸树脂20份，酚醛树脂20份，聚氨酯50份，苯乙烯2份，N，N-二甲基乙醇胺3份，聚二甲基硅氧烷2.5份，硅烷偶联剂KH-550 1份，改性石蜡7份，壳聚糖2份，2-氨基-2-甲基-1-丙醇7份，表面活性剂3份，醋酸纤维10份，纳米二氧化硅20份，凹凸棒土20份，蚕丝纤维15份，石棉20份，滑石粉3份，稳泡剂4份，发泡剂2份。
实施例2
本发明提出的一种力学性能好建筑墙体用耐磨保温墙，其原料按重量份包括：醇酸树脂40份，酚醛树脂10份，聚氨酯70份，苯乙烯1份，N，N-二甲基乙醇胺7份，聚二甲基硅氧烷1.5份，硅烷偶联剂KH-550 3份，改性石蜡3份，壳聚糖6份，2-氨基-2-甲基-1-丙醇3份，表面活性剂5份，醋酸纤维4份，纳米二氧化硅30份，凹凸棒土10份，蚕丝纤维25份，石棉10份，滑石粉7份，稳泡剂2份，发泡剂4份。
改性石蜡采用如下工艺制备：将四氧化三铁、水混合搅拌得到预制料；将羧甲基微晶纤维素、无水乙醇混合搅拌均匀，在搅拌过程中向其中加入预制料，加入完全后继续搅拌，冷却，洗涤，干燥，研磨得到改性四氧化三铁；将微晶石蜡、天然蜂蜡、聚乙烯蜡、十二羟基硬脂酸密闭加热至融化，在通入空气的状态下，加入高锰酸钾混合搅拌，降至室温，加入改性四氧化三铁搅拌得到改性石蜡。
实施例3
本发明提出的一种力学性能好建筑墙体用耐磨保温墙，其原料按重量份包括：醇酸树脂25份，酚醛树脂18份，聚氨酯55份，苯乙烯1.7份，N，N-二甲基乙醇胺4份，聚二甲基硅氧烷2.2份，硅烷偶联剂KH-550 1.5份，改性石蜡6份，壳聚糖3份，2-氨基-2-甲基-1-丙醇6份，表面活性剂3.5份，醋酸纤维8份，纳米二氧化硅23份，凹凸棒土18份，蚕丝纤维18份，石棉18份，滑石粉4份，稳泡剂3.5份，发泡剂2.5份。
改性石蜡采用如下工艺制备：按重量份将16份四氧化三铁、40份水混合搅拌20min，得到预制料；将4份羧甲基微晶纤维素、22份无水乙醇混合搅拌均匀，搅拌温度为60℃，在搅拌过程中向其中加入预制料，加入完全后继续搅拌12min，冷却，洗涤，干燥，研磨得到改性四氧化三铁；将15份微晶石蜡、12份天然蜂蜡、25份聚乙烯蜡、4份十二羟基硬脂酸密闭加热至融化，在通入空气的状态下，加入0.3份高锰酸钾混合搅拌130min，降温至室温，加入改性四氧化三铁搅拌80min，得到改性石蜡。
实施例4
本发明提出的一种力学性能好建筑墙体用耐磨保温墙，其原料按重量份包括：醇酸树脂35份，酚醛树脂12份，聚氨酯65份，苯乙烯1.3份，N，N-二甲基乙醇胺6份，聚二甲基硅氧烷1.8份，硅烷偶联剂KH-550 2.5份，改性石蜡4份，壳聚糖5份，2-氨基-2-甲基-1-丙醇4份，表面活性剂4.5份，醋酸纤维6份，纳米二氧化硅27份，凹凸棒土12份，蚕丝纤维22份，石棉14份，滑石粉6份，稳泡剂2.5份，发泡剂3.5份。
改性石蜡采用如下工艺制备：按重量份将12份四氧化三铁、60份水混合搅拌10min，得到预制料；将8份羧甲基微晶纤维素、16份无水乙醇混合搅拌均匀，搅拌温度为70℃，在搅拌过程中向其中加入预制料，加入完全后继续搅拌8min，冷却，洗涤，干燥，研磨得到改性四氧化三铁；将25份微晶石蜡、8份天然蜂蜡、45份聚乙烯蜡、2份十二羟基硬脂酸密闭加热至融化，在通入空气的状态下，加入0.9份高锰酸钾混合搅拌70min，降温至室温，加入改性四氧化三铁搅拌120min，得到改性石蜡。
实施例5
本发明提出的一种力学性能好建筑墙体用耐磨保温墙，其原料按重量份包括：醇酸树脂30份，酚醛树脂15份，聚氨酯60份，苯乙烯1.5份，N，N-二甲基乙醇胺5份，聚二甲基硅氧烷2份，硅烷偶联剂KH-550 2份，改性石蜡5份，壳聚糖4份，2-氨基-2-甲基-1-丙醇5份，表面活性剂4份，醋酸纤维7份，纳米二氧化硅25份，凹凸棒土15份，蚕丝纤维20份，石棉16份，滑石粉5份，稳泡剂3份，发泡剂3份。
改性石蜡采用如下工艺制备：将四氧化三铁、水混合搅拌15min，得到预制料；将羧甲基微晶纤维素、无水乙醇混合搅拌均匀，搅拌温度为65℃，在搅拌过程中向其中加入预制料，加入完全后继续搅拌10min，冷却，洗涤，干燥，研磨得到改性四氧化三铁；将微晶石蜡、天然蜂蜡、聚乙烯蜡、十二羟基硬脂酸密闭加热至融化，在通入空气的状态下，加入高锰酸钾混合搅拌100min，降温至室温，加入改性四氧化三铁搅拌100min，得到改性石蜡。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (7)
1.一种力学性能好建筑墙体用耐磨保温墙，其特征在于，其原料按重量份包括：醇酸树脂20～40份，酚醛树脂10～20份，聚氨酯50～70份，苯乙烯1～2份，N，N-二甲基乙醇胺3～7份，聚二甲基硅氧烷1.5～2.5份，硅烷偶联剂KH-550 1～3份，改性石蜡3～7份，壳聚糖2～6份，2-氨基-2-甲基-1-丙醇3～7份，表面活性剂3～5份，醋酸纤维4～10份，纳米二氧化硅20～30份，凹凸棒土10～20份，蚕丝纤维15～25份，石棉10～20份，滑石粉3～7份，稳泡剂2～4份，发泡剂2～4份。
2.根据权利要求1所述力学性能好建筑墙体用耐磨保温墙，其特征在于，醇酸树脂、酚醛树脂、聚氨酯、苯乙烯、N,N～二甲基乙醇胺的重量比为25～35：12～18：55～65：1.3～1.7：4～6。
3.根据权利要求1或2所述力学性能好建筑墙体用耐磨保温墙，其特征在于，2-氨基-2-甲基-1-丙醇、表面活性剂、醋酸纤维、纳米二氧化硅、凹凸棒土、蚕丝纤维、石棉、滑石粉的重量比为4～6：3.5～4.5：6～8：23～27：12～18：18～22：14～18：4～6。
4.根据权利要求1-3任一项所述力学性能好建筑墙体用耐磨保温墙，其特征在于，其原料按重量份包括：醇酸树脂25～35份，酚醛树脂12～18份，聚氨酯55～65份，苯乙烯1.3～1.7份，N，N-二甲基乙醇胺4～6份，聚二甲基硅氧烷1.8～2.2份，硅烷偶联剂KH-550 1.5～2.5份，改性石蜡4～6份，壳聚糖3～5份，2-氨基-2-甲基-1-丙醇4～6份，表面活性剂3.5～4.5份，醋酸纤维6～8份，纳米二氧化硅23～27份，凹凸棒土12～18份，蚕丝纤维18～22份，石棉14～18份，滑石粉4～6份，稳泡剂2.5～3.5份，发泡剂2.5～3.5份。
5.根据权利要求1-4任一项所述力学性能好建筑墙体用耐磨保温墙，其特征在于，改性石蜡采用如下工艺制备：将四氧化三铁、水混合搅拌得到预制料；将羧甲基微晶纤维素、无水乙醇混合搅拌均匀，在搅拌过程中向其中加入预制料，加入完全后继续搅拌，冷却，洗涤，干燥，研磨得到改性四氧化三铁；将微晶石蜡、天然蜂蜡、聚乙烯蜡、十二羟基硬脂酸密闭加热至融化，在通入空气的状态下，加入高锰酸钾混合搅拌，降至室温，加入改性四氧化三铁搅拌得到改性石蜡。
6.根据权利要求1-5任一项所述力学性能好建筑墙体用耐磨保温墙，其特征在于，改性石蜡采用如下工艺制备：将四氧化三铁、水混合搅拌10～20min，得到预制料；将羧甲基微晶纤维素、无水乙醇混合搅拌均匀，搅拌温度为60～70℃，在搅拌过程中向其中加入预制料，加入完全后继续搅拌8～12min，冷却，洗涤，干燥，研磨得到改性四氧化三铁；将微晶石蜡、天然蜂蜡、聚乙烯蜡、十二羟基硬脂酸密闭加热至融化，在通入空气的状态下，加入高锰酸钾混合搅拌70～130min，降温至室温，加入改性四氧化三铁搅拌80～120min，得到改性石蜡。
7.根据权利要求1-6任一项所述力学性能好建筑墙体用耐磨保温墙，其特征在于，改性石蜡采用如下工艺制备：按重量份将12～16份四氧化三铁、40～60份水混合搅拌10～20min，得到预制料；将4～8份羧甲基微晶纤维素、16～22份无水乙醇混合搅拌均匀，搅拌温度为60～70℃，在搅拌过程中向其中加入预制料，加入完全后继续搅拌8～12min，冷却，洗涤，干燥，研磨得到改性四氧化三铁；将15～25份微晶石蜡、8～12份天然蜂蜡、25～45份聚乙烯蜡、2～4份十二羟基硬脂酸密闭加热至融化，在通入空气的状态下，加入0.3～0.9份高锰酸钾混合搅拌70～130min，降温至室温，加入改性四氧化三铁搅拌80～120min，得到改性石蜡。