CN106189300A - A kind of wood-plastic window frame - Google Patents
A kind of wood-plastic window frame Download PDFInfo
- Publication number
- CN106189300A CN106189300A CN201610533014.9A CN201610533014A CN106189300A CN 106189300 A CN106189300 A CN 106189300A CN 201610533014 A CN201610533014 A CN 201610533014A CN 106189300 A CN106189300 A CN 106189300A
- Authority
- CN
- China
- Prior art keywords
- wood
- window frame
- profile
- sandwich layer
- longitudinal profile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of wood-plastic window frame, it is characterized in that, including orthogonal transverse profile (1) and longitudinal profile (2), described transverse profile (1) and longitudinal profile (2) all include double-layer structure, clad (12,22) moulded by timber sandwich layer (11,21) and wood, the end of described transverse profile (1) and longitudinal profile (2) is provided with mortise-tenon joint structure, and described mortise-tenon joint structure is one-body molded by timber sandwich layer.The wood-plastic window mount structure that the present invention provides connects simple, it is not necessary to additionally coordinating handware, sound construction, convenient disassembly, and low cost, service life is long；Additionally, by being possible not only to protect solid wood core to be difficult to moisture absorption with wood plastic composite cladding solid wood core, prevent deformation; and solid wood core easily processes joinery and its construction, connecting easy to be firm, window frame entirety bond strength is higher; it is unlikely to deform, also improves the service life of window frame.
Description
Technical field
The present invention relates to sheet material, specifically a kind of wood-plastic window frame.
Background technology
Commercially available window frame mostly is Al-alloy products, and its attachment structure also more uses handware to connect, on the one hand, whether window frame
Itself or the cost of handware are the most higher；Second aspect, aluminum alloy window frame is yielding, is easily caused window and opens inconvenience；3rd
Aspect, handware attachment structure, operating process are complicated, wasting manpower and material resources.
The tubing such as wood plastic composite is a kind of Novel ring material, common-use words interior/exterior decoration wallboard, floor, drain pipe with
And the profile shapes such as sash, with plastics as base material, fill the materials such as timber, bamboo wood and agricultural crop straw and be made, have
Waterproof and dampproof, agent of low hygroscopicity, low morphotropism, and the advantage such as mechanical strength is good.Wood-plastic window frame not only has above good property
Can, and its easy extrusion molding in the course of processing, can process abnormally-structured, connect in its structure and easily realize without five metals
Part connects.
Summary of the invention
In view of this, the wood that the invention provides a kind of simple in construction, low cost, length in service life and safety good is moulded
Window frame.
The present invention solves technical problem and adopts the following technical scheme that
A kind of wood-plastic window frame, it is characterised in that include orthogonal transverse profile and longitudinal profile, described transverse profile
All include double-layer structure with longitudinal profile, clad moulded by timber sandwich layer and wood, and the end of described transverse profile and longitudinal profile sets
Having mortise-tenon joint structure, described mortise-tenon joint structure is one-body molded by timber sandwich layer.
Further, the end face of described transverse profile and longitudinal profile is an inclined-plane, described transverse profile or longitudinal profile
One of them inclined-plane is provided with the falcon head protruded out by timber sandwich layer, and another inclined-plane is provided with the falcon groove being positioned at timber sandwich layer；Institute
Stating falcon head is right angled triangle, and wherein flushing with the side of section bar of described right angled triangle, described tenon is provided with one
To parallel sub-tongue-and-groove, the oral area of described sub-tongue-and-groove is towards section bar side；Protrude out pair of parallel it is additionally provided with in described falcon groove
Sub-tenon, described sub-tenon is right angled triangle, wherein flushes with the side of section bar.
The material of clad moulded by described wood is a kind of wear-resistant wood plastic composite materials.
Compared with the prior art, beneficial effects of the present invention is embodied in:
The wood-plastic window mount structure that the present invention provides connects simple, it is not necessary to additionally coordinate handware, sound construction, dismounting side
Just, and low cost, service life is long；Additionally, by being possible not only to protect solid wood with wood plastic composite cladding solid wood core
Core is difficult to moisture absorption, prevents deformation, and solid wood core easily processes joinery and its construction, connects easy to be firm, and window frame entirety combines strong
Spend higher, be unlikely to deform, also improve the service life of window frame.
Accompanying drawing explanation
Fig. 1 is the wood-plastic window mount structure figure of the present invention
Fig. 2 is longitudinal window frame profile and the joinery and its construction of the present invention
Fig. 3 is horizontal window frame profile and the joinery and its construction of the present invention
Below by way of detailed description of the invention, technical solution of the present invention is described further.
Detailed description of the invention
As it is shown in figure 1, a kind of wood-plastic window frame of the present invention, longitudinal including orthogonal window frame transverse profile 1 and window frame
Section bar 2, window frame profile all includes that double-layer structure, timber sandwich layer 11,21 and wood mould clad 12,22.
Wherein joinery and its construction is directly in the direct machine-shaping in timber sandwich layer end, and as Figure 2-3, transverse profile 1 is with vertical
Being an inclined-plane to the end face of section bar 2, one of them inclined-plane of transverse profile or longitudinal profile is provided with and is protruded out by timber sandwich layer
Falcon 11, another inclined-plane is provided with the falcon groove 21 being positioned at timber sandwich layer；Described falcon 11 is right angled triangle, described right angle three
Dihedral wherein while flushing with the side of section bar, described tenon is provided with pair of parallel sub-tongue-and-groove 112, described sub-tongue-and-groove
Oral area is towards section bar side；Being additionally provided with the pair of parallel sub-tenon 211 protruded out in described falcon groove 21, described sub-tenon is right angle
Triangle, wherein flushes with the side of section bar.
The material of clad moulded by described wood is a kind of wear-resistant wood plastic composite materials；Raw material including following weight portion:
Modified wood powder 50-80 part, polrvinyl chloride (PVC) 40-100 part, coupling agent 2-5 part, compatilizer 2-10 part, calcium carbonate
(particle diameter is at 200-300 mesh) 4-6, lubricant 4-6 part, antioxidant 2-4 part.
Further, described modified wood powder is by wood powder 15% soaking with sodium hydroxide 1.5h, and pretreatment temperature is 110 DEG C,
Put into dewatered drying at 60 DEG C, place into and flour mill is worn into fiber, after screening processes, obtain 20-60 mesh granule, then
Under 110 DEG C of temperature conditionss of baking oven, carry out 24 hours dried, make the average moisture content of wood powder be maintained at less than 1%.Will
50-80 part wood powder fiber, hard calcium acetate 3-5 part and nano aluminium oxide 3-5 part add ball mill, stir under rotating speed is 110r/min
Mix 15min, obtain modified fibre.
Further, described coupling agent is that Silane coupling agent KH550 forms according to 1:2 configuration with aqueous isopropanol.
Further, described compatilizer is maleic acid liquor-saturated grafting compatilizer (PP-g-MAH).
Further, described lubricant is paraffin oil.
Preparation method is as follows:
Method one:
1) wood powder is obtained, by wood powder with 15% after, solid wood sandwich layer being processed remaining sides corner material, and size-reduced, ball milling, screening
Soaking with sodium hydroxide 1.5h, pretreatment temperature is 110 DEG C, puts into dewatered drying at 60 DEG C, places into and wears into fiber in flour mill,
After screening processes, obtain 40 mesh granules, then under 110 DEG C of temperature conditionss of baking oven, carry out 24 hours dried, make wood
The average moisture content of powder is maintained at less than 1%.50 parts of wood powder fibers, hard calcium acetate 6 parts and nano aluminium oxide 3 parts are added ball milling
Machine, stirs 15min under rotating speed is 110r/min, screens 100 mesh granules, obtain modified fibre.
2), by the ethanol solution of above-mentioned modified wood powder even spraying silane coupler, then dry for standby at 60 DEG C.
3) weigh modified fibre according to above-mentioned formula and remain each component raw material, it is all added in high-speed mixer,
Under rotating speed is 400r/min, stirs 5min, obtains mixed material.
Composition of raw materials is: modified wood powder 50 parts, polrvinyl chloride (PVC) 40 parts, coupling agent 5 parts, compatilizer 4 parts, calcium carbonate
(particle diameter is at 200-300 mesh) 4, lubricant 4 parts, antioxidant 2 parts.
4) mixed material is obtained molding Wood-plastic composite section bar by extruder is crowded.
The physical property that the present invention prepares wood plastic composite is as follows:
Hot strength: 15.7Mpa, bending modulus: 2380Mpa, impact strength: 12.3KJ/m2, wear rate: 2.1 ×
105mm3/m。
Method 2
1) wood powder is obtained, by wood powder with 15% after, solid wood sandwich layer being processed remaining sides corner material, and size-reduced, ball milling, screening
Soaking with sodium hydroxide 1.5h, pretreatment temperature is 110 DEG C, puts into dewatered drying at 60 DEG C, places into and wears into fiber in flour mill,
After screening processes, obtain 60 mesh granules, then under 110 DEG C of temperature conditionss of baking oven, carry out 24 hours dried, make wood
The average moisture content of powder is maintained at less than 1%.80 parts of wood powder fibers, hard calcium acetate 10 parts and nano aluminium oxide 6 parts are added goal
Grinding machine, stirs 15min under rotating speed is 110r/min, screens 110 mesh granules, obtain modified fibre.
2), by the ethanol solution of above-mentioned modified wood powder even spraying silane coupler, then dry for standby at 60 DEG C.
3) weigh modified fibre according to above-mentioned formula and remain each component raw material, it is all added in high-speed mixer,
Under rotating speed is 400r/min, stirs 10min, obtains mixed material.
Composition of raw materials is: modified wood powder 70 parts, polrvinyl chloride (PVC) 50 parts, coupling agent 2 parts, compatilizer 10 parts, calcium carbonate
(particle diameter is at 200-300 mesh) 6, lubricant 6 parts, antioxidant 4 parts.
4) mixed material is obtained molding Wood-plastic composite section bar by extruder is crowded.
The physical property that the present invention prepares wood plastic composite is as follows:
Hot strength: 18.9Mpa, bending modulus: 2501Mpa, impact strength: 17.3KJ/m2, wear rate: 3.6 ×
105mm3/m。
Below by being embodied as step, the present invention is described in detail:
Step 1: process orthogonal solid wood board, the solid wood sandwich layer 11 of horizontal window frame profile, and longitudinal window frame profile
Solid wood sandwich layer 21, process tenon 111 at the both ends of horizontal solid wood sandwich layer 11, longitudinal solid wood sandwich layer 21 process tenon
Groove 211.
Step 2: the wood-plastic window frame section processed is coated on outside solid wood sandwich layer, and utilize the joinery and its construction at its two ends to incite somebody to action
It combines, and is assembled into wood-plastic window mount structure.
In above example, unless otherwise noted, its component is commercial prior art products.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of the spirit or essential attributes of the present invention, it is possible to realize the present invention in other specific forms.Therefore, no matter
From the point of view of which point, all should regard embodiment as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit requires rather than described above limits, it is intended that all by fall in the implication of equivalency and scope of claim
Change is included in the present invention.Should not be considered as limiting involved claim by any reference in claim.
Although moreover, it will be appreciated that this specification is been described by according to embodiment, but the most each embodiment only wraps
Containing an independent technical scheme, this narrating mode of description is only that for clarity sake those skilled in the art should
Description can also be formed those skilled in the art through appropriately combined as an entirety, the technical scheme in each embodiment
May be appreciated other embodiments.
Claims (3)
1. a wood-plastic window frame, it is characterised in that include orthogonal transverse profile (1) and longitudinal profile (2), described laterally
Section bar (1) and longitudinal profile (2) all include that double-layer structure, timber sandwich layer (11,21) and wood mould clad (12,22), described horizontal stroke
Be provided with mortise-tenon joint structure to the end of section bar (1) and longitudinal profile (2), described mortise-tenon joint structure is become by timber sandwich layer one
Type.
A kind of wood-plastic window frame the most according to claim 1, it is characterised in that described transverse profile (1) and longitudinal profile (2)
End face be an inclined-plane, one of them inclined-plane of described transverse profile or longitudinal profile is provided with the falcon protruded out by timber sandwich layer
Head, another inclined-plane is provided with the falcon groove being positioned at timber sandwich layer；Described falcon head is right angled triangle, its of described right angled triangle
Middle while flushing with the side of section bar, described tenon is provided with pair of parallel sub-tongue-and-groove, and the oral area of described sub-tongue-and-groove is towards type
Material side；Being additionally provided with the pair of parallel sub-tenon protruded out in described falcon groove, described sub-tenon is right angled triangle, wherein
Flush with the side of section bar.
A kind of wood-plastic window frame the most according to claim 1, it is characterised in that described wood moulds the material of clad for a kind of resistance to
Mill type wood plastic composite.