CN106186967A - A kind of water-retaining type ornament materials and preparation method - Google Patents
A kind of water-retaining type ornament materials and preparation method Download PDFInfo
- Publication number
- CN106186967A CN106186967A CN201610637231.2A CN201610637231A CN106186967A CN 106186967 A CN106186967 A CN 106186967A CN 201610637231 A CN201610637231 A CN 201610637231A CN 106186967 A CN106186967 A CN 106186967A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- ornament materials
- retaining type
- type ornament
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water-retaining type ornament materials and preparation method, described water-retaining type ornament materials is mainly made up of than component following quality: latex powder: 13 parts, MC cellulose: 0.3 0.8 parts, wood fibre: 0.2 0.6 parts, alkali proof fiber: 0.1 0.5 parts, white cement: 50 60 parts, ash calcium: 26 parts, calcium sulphate dihydrate: 0.3 0.5 parts, ground calcium carbonate: 20 25 parts, precipitated calcium carbonate: 5 10 parts, hydrous magnesium silicate: 35 parts, kieselguhr: 13 parts, hydroxyalkyl starch: 0.05 0.16 parts, sepiolite powder: 0.3 0.5 parts, titanium dioxide: 0.3 0.5 parts, inorganic pigment: 0.3 0.5 parts, present invention also offers the preparation method of a kind of water-retaining type ornament materials.
Description
Technical field
The present invention relates to building material field, be specifically related to a kind of water-retaining type ornament materials and preparation method.
Background technology
Putty is usually and is made up of base material, filler, water and auxiliary agent etc., and base material, also referred to as binding agent, be the most critical group of putty
Point, acting primarily as the various effects such as bonding, the most frequently used binding agent of putty is cement and organic polymer, and organic polymer has again breast
Liquid and latex powder point, cement is that caking property is good, durable and the rational binding agent of cost performance, but hot strength and crack resistance are relatively
Difference, organic polymer can be modified and toughness reinforcing to it, thus improves putty performance, and filler acts primarily as filling effect, and conventional has carbon
Acid calcium, Pulvis Talci and quartz sand etc., it should be noted that the collocation of filler fineness uses, auxiliary agent has thickening agent, a water-retaining agent etc., thickening agent and
Water-retaining agent plays water conservation, improves storage and the effect of workability, generally uses cellulose family.Antifreeze mainly improves putty and exists
Bin stability under low temperature, slipping agent and water reducer etc. are commonly used in high-grade putty, improve the workability of putty, have
It is additionally added fiber, plays cracking resistance effect.
Architectural decoration water-retaining agent uses cellulose ether more the most on the market, but it is higher to be because its price, causes portion
Man of subsidiary factory, businessman for reduce cost, reduce its add and usage amount, cause in fitment process, the most cracking, bubble,
The phenomenons such as shedding, study carefully its main cause for the most thoroughly parching construction, substrate is the most coarse, a construct putty layer is blocked up, be more than
2.0mm, powder of lacquer putty for use on polishing time are grasped the best, the dry and wet time being simultaneously not sure between surface and bottom and moisture evaporation
Speed, season, difference basic unit different with the drying time on surface was caused, and existing product is in terms of water conservation or effect can expire
Foot requirement, but on the high side, or there is certain harmful substance exactly, building, decoration construction quality are all produced by these
Adverse influence.
Summary of the invention
The problem existed for prior art, the invention provides a kind of preparation technology rationally, formula design science, construction
Simple and easy-operating water-retaining type ornament materials and preparation method, obtained product has preferable combination property.
A kind of water-retaining type ornament materials and preparation method, wherein water-retaining type ornament materials mainly by following quality than component group
Become: latex powder: 1-3 part, MC cellulose: 0.3-0.8 part, wood fibre: 0.2-0.6 part, alkali proof fiber: 0.1-0.5 part, plain boiled water
Mud: 50-60 part, ash calcium: 2-6 part, calcium sulphate dihydrate: 0.3-0.5 part, ground calcium carbonate: 20-25 part, precipitated calcium carbonate: 5-10
Part, hydrous magnesium silicate: 3-5 part, kieselguhr: 1-3 part, hydroxyalkyl starch: 0.05-0.16 part, sepiolite powder: 0.3-0.5 part, titanium
White lead: 0.3-0.5 part, inorganic pigment: 0.3-0.5 part.
A kind of water-retaining type ornament materials and preparation method, its main preparation process is as follows:
(1) it is first according to part by weight and weighs each component element of water-retaining type ornament materials, be individually positioned in dustless hermetic container
In；
(2) by latex powder, MC cellulose, wood fibre, alkali proof fiber, white cement, ash calcium, calcium sulphate dihydrate, ground calcium carbonate,
Precipitated calcium carbonate adds blender and is sufficiently stirred for, and mixing time is 15-20 minute；
(3) hydrous magnesium silicate, kieselguhr, hydroxyalkyl starch, sepiolite powder, titanium dioxide are added blender and carry out forward and reverse stirring
Mixing, mixing time is 10-20 minute；
(4) in blender, add inorganic pigment, judge according to the uniformity of stirring, forward stirring 10-30 minute, reverse agitating function
10-30 minute, blender can be closed；
(5) material after stirring is inserted drying baker and is dried, and 30-50 DEG C dry 10-40 hour, will use after drying
Polyethylene packaging bag carries out subpackage, packs.
Detailed description of the invention
Embodiment 1
A kind of water-retaining type ornament materials and preparation method, wherein water-retaining type ornament materials is mainly made up of than component following quality:
Latex powder: 3 parts, MC cellulose: 0.8 part, wood fibre: 0.6 part, alkali proof fiber: 0.5 part, white cement: 60 parts, ash calcium: 6 parts,
Calcium sulphate dihydrate: 0.5 part, ground calcium carbonate: 25 parts, precipitated calcium carbonate: 10 parts, hydrous magnesium silicate: 5 parts, kieselguhr: 3 parts, hydroxyl
Alkyl starches: 0.16 part, sepiolite powder: 0.5 part, titanium dioxide: 0.5 part, inorganic pigment: 0.5 part.
A kind of water-retaining type ornament materials and preparation method, its main preparation process is as follows:
(1) it is first according to part by weight and weighs each component element of water-retaining type ornament materials, be individually positioned in dustless hermetic container
In；
(2) by latex powder, MC cellulose, wood fibre, alkali proof fiber, white cement, ash calcium, calcium sulphate dihydrate, ground calcium carbonate,
Precipitated calcium carbonate adds blender and is sufficiently stirred for, and mixing time is 15 minutes；
(3) hydrous magnesium silicate, kieselguhr, hydroxyalkyl starch, sepiolite powder, titanium dioxide are added blender and carry out forward and reverse stirring
Mixing, mixing time is 10 minutes；
(4) in blender, add inorganic pigment, judge according to the uniformity of stirring, forward stirring 30 minutes, reverse agitating function 30
Minute, blender can be closed；
(5) material after stirring is inserted drying baker and is dried, and 50 DEG C are dried 10 hours, will use polyethylene after drying
Packaging bag carries out subpackage, packs.
Embodiment 2
A kind of water-retaining type ornament materials and preparation method, wherein water-retaining type ornament materials is mainly made up of than component following quality:
Latex powder: 1 part, MC cellulose: 0.3 part, wood fibre: 0.2 part, alkali proof fiber: 0.1 part, white cement: 50 parts, ash calcium: 2 parts,
Calcium sulphate dihydrate: 0.3 part, ground calcium carbonate: 20 parts, precipitated calcium carbonate: 5 parts, hydrous magnesium silicate: 3 parts, kieselguhr: 1 part, hydroxyl
Alkyl starches: 0.05 part, sepiolite powder: 0.3 part, titanium dioxide: 0.3 part, inorganic pigment: 0.3 part.
A kind of water-retaining type ornament materials and preparation method, its main preparation process is as follows:
(1) it is first according to part by weight and weighs each component element of water-retaining type ornament materials, be individually positioned in dustless hermetic container
In；
(2) by latex powder, MC cellulose, wood fibre, alkali proof fiber, white cement, ash calcium, calcium sulphate dihydrate, ground calcium carbonate,
Precipitated calcium carbonate adds blender and is sufficiently stirred for, and mixing time is 15 minutes；
(3) hydrous magnesium silicate, kieselguhr, hydroxyalkyl starch, sepiolite powder, titanium dioxide are added blender and carry out forward and reverse stirring
Mixing, mixing time is 10 minutes；
(4) in blender, add inorganic pigment, judge according to the uniformity of stirring, forward stirring 10 minutes, reverse agitating function 10
Minute, blender can be closed；
(5) material after stirring is inserted drying baker and is dried, and 30 DEG C are dried 10 hours, will use polyethylene after drying
Packaging bag carries out subpackage, packs.
Embodiment 3
A kind of water-retaining type ornament materials and preparation method, wherein water-retaining type ornament materials is mainly made up of than component following quality:
Latex powder: 2 parts, MC cellulose: 0.5 part, wood fibre: 0.5 part, alkali proof fiber: 0.5 part, white cement: 55 parts, ash calcium: 2 parts,
Calcium sulphate dihydrate: 0.3 part, ground calcium carbonate: 25 parts, precipitated calcium carbonate: 5 parts, hydrous magnesium silicate: 5 parts, kieselguhr: 1 part, hydroxyl
Alkyl starches: 0.05 part, sepiolite powder: 0.3 part, titanium dioxide: 0.5 part, inorganic pigment: 0.5 part.
A kind of water-retaining type ornament materials and preparation method, its main preparation process is as follows:
(1) it is first according to part by weight and weighs each component element of water-retaining type ornament materials, be individually positioned in dustless hermetic container
In；
(2) by latex powder, MC cellulose, wood fibre, alkali proof fiber, white cement, ash calcium, calcium sulphate dihydrate, ground calcium carbonate,
Precipitated calcium carbonate adds blender and is sufficiently stirred for, and mixing time is 15 minutes；
(3) hydrous magnesium silicate, kieselguhr, hydroxyalkyl starch, sepiolite powder, titanium dioxide are added blender and carry out forward and reverse stirring
Mixing, mixing time is 10 minutes；
(4) in blender, add inorganic pigment, judge according to the uniformity of stirring, forward stirring 30 minutes, reverse agitating function 30
Minute, blender can be closed；
(5) material after stirring is inserted drying baker and is dried, and 40 DEG C are dried 15 hours, will use polyethylene after drying
Packaging bag carries out subpackage, packs.
Claims (2)
1. a water-retaining type ornament materials and preparation method, it is characterised in that water-retaining type ornament materials is mainly by following mass ratio
Component forms: latex powder: 1-3 part, MC cellulose: 0.3-0.8 part, wood fibre: 0.2-0.6 part, alkali proof fiber: 0.1-0.5
Part, white cement: 50-60 part, ash calcium: 2-6 part, calcium sulphate dihydrate: 0.3-0.5 part, ground calcium carbonate: 20-25 part, lightweight carbonic acid
Calcium: 5-10 part, hydrous magnesium silicate: 3-5 part, kieselguhr: 1-3 part, hydroxyalkyl starch: 0.05-0.16 part, sepiolite powder: 0.3-
0.5 part, titanium dioxide: 0.3-0.5 part, inorganic pigment: 0.3-0.5 part.
A kind of water-retaining type ornament materials the most according to claim 1 and preparation method, it is characterised in that main preparation process
As follows:
(1) it is first according to part by weight and weighs each component element of water-retaining type ornament materials, be individually positioned in dustless hermetic container
In；
(2) by latex powder, MC cellulose, wood fibre, alkali proof fiber, white cement, ash calcium, calcium sulphate dihydrate, ground calcium carbonate,
Precipitated calcium carbonate adds blender and is sufficiently stirred for, and mixing time is 15-20 minute；
(3) hydrous magnesium silicate, kieselguhr, hydroxyalkyl starch, sepiolite powder, titanium dioxide are added blender and carry out forward and reverse stirring
Mixing, mixing time is 10-20 minute；
(4) in blender, add inorganic pigment, judge according to the uniformity of stirring, forward stirring 10-30 minute, reverse agitating function
10-30 minute, blender can be closed；
(5) material after stirring is inserted drying baker and is dried, and 30-50 DEG C dry 10-40 hour, will use after drying
Polyethylene packaging bag carries out subpackage, packs.