CN106149371A - 一种纺织白玉霜润滑脂及其制备方法 - Google Patents
一种纺织白玉霜润滑脂及其制备方法 Download PDFInfo
- Publication number
- CN106149371A CN106149371A CN201610517145.8A CN201610517145A CN106149371A CN 106149371 A CN106149371 A CN 106149371A CN 201610517145 A CN201610517145 A CN 201610517145A CN 106149371 A CN106149371 A CN 106149371A
- Authority
- CN
- China
- Prior art keywords
- frost
- grease
- white jade
- weaving
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种纺织白玉霜润滑脂，按质量百分比，由以下成分组成：C18H36O2 10％‑80％；C21H42O410％‑80％；KOH 0.05％‑5％；玉米淀粉5％‑15％；杀菌剂0.02％‑0.1％。本发明具有以下优点和效果：采用C18H36O2作为主要原料，加入油脂类的C21H42O4，起到增稠、润滑、平滑光亮和增白的作用，使纺织白玉霜被涂抹到纱线后既能被粘贴到管纱上端，防止纱线脱落，干燥后又能在纱线表面形成一层C18H36O2膜，增强纱线的拉伸强度和韧性，提升倍捻后纱线的整体性能。
Description
技术领域
本发明涉及纺织辅料领域，特别涉及一种纺织白玉霜润滑脂及其制备方法。
背景技术
倍捻是将两股或两股以上的单纱通过加捻粘合成股线，从而达到增强原纱的性能，以实现纺织过程中对纱线性能的需求。在倍捻工序中，纱线容易在退绕过程中滑脱，造成脱圈，生产过程中脱圈不仅影响产量，而且降低了效率，增加工人的劳动强度，更重要的是影响纱线质量。
发明内容
本发明人在实际生产过程中意外发现，在退绕过程中对管纱的上端纱线表面涂抹一层润滑脂，将即将滑脱的纱线粘附在管纱上端，能有效防止纱线在退绕过程中滑脱。
本发明的目的是提供一种纺织白玉霜润滑脂，具有涂抹在纱线表面后增强粘性的效果。本申请的纺织白玉霜润滑脂由于理化性质类似化妆品雪花膏，在轻纺辅料行业内也被称为纺织雪花膏。
本发明的上述技术目的是通过以下技术方案得以实现的：一种纺织白玉霜润滑脂，按质量百分比，由以下成分组成：
C18H36O2即十八烷酸，也被称为硬脂酸，结构简式为CH3(CH2)16COOH，作为本申请的纺织白玉霜润滑脂的主要原料，C18H36O2具有长碳链作为亲油基团，也具有羧基作为亲水基团，同时也作为表面活性剂使用，提升纺织白玉霜润滑脂中其他有机化合物的可溶性。同时C18H36O2电离趋势较小，性质稳定。
C21H42O4即硬脂酸甘油酯，是油脂化工和日用化工行业中应用最广泛、用量最大的一种添加剂，将C21H42O4加入C18H36O2后，能提高本申请的纺织白玉霜润滑脂的细腻感，避免纺织白玉霜润滑脂涂抹在纱线表面后导致倍捻的纱线表面呈现颗粒感，影响倍捻后纱线的性能。同时C21H42O4的加入，也能对本申请的纺织白玉霜润滑脂起到增稠的作用，使C18H36O2由固体粒子变成浓稠的浆液，能被均匀地涂抹到纱线表面，C21H42O4采取质量百分比为10％-80％的范围，既不会过稀而浸润整个纱线，又不会过浓形凝结成固体附着于纱线表层而影响纱线的退绕。
C21H42O4加入后也能作为上浆剂、整理剂和柔软剂，将纺织白玉霜润滑脂浸轧在纱线表层，使用时涂抹到纱线表层后使纱线表面平滑光亮，减小纤维之间的摩擦，抑制静电的积累，在纱线倍捻完成后，纺织白玉霜干燥后即成皮膜将纱线表面包裹，从而赋予织物平滑、厚实、丰满、柔软的手感，能对浅色的纱线进行增白，提升纱线的整体性能。
本申请的纺织白玉霜润滑脂中由于加入C18H36O2，C18H36O2电离会产生氢离子，使纺织白玉霜润滑脂pH变小，偏酸性，既能对纱线造成腐蚀，使纱线容易折断，又能对车间工人的手部造成损伤，存在潜在的安全风险，为弥补上述缺陷，在本申请的纺织白玉霜润滑脂内加入KOH作为pH调节剂，调节本申请的纺织白玉霜润滑脂的pH至合适的状态，既不会腐蚀纱线，又不会对人体皮肤造成损伤，从而提高纺织白玉霜润滑脂的安全性。
本申请的纺织白玉霜润滑脂在用于将即将滑脱的纱线粘附在管纱上端时，粘性是本申请的纺织白玉霜润滑脂的一项重要参数，玉米淀粉又称玉蜀黍淀粉，俗名六谷粉，白色微带淡黄色的粉末。将玉米用0.3％亚硫酸浸渍后，通过破碎、过筛、沉淀、干燥、磨细等工序而制成。加入玉米淀粉在高温和C18H36O、C21H42O4下发生变性后，使本申请的纺织白玉霜润滑脂在高温下仍然保持较高的粘度稳定性和保持增稠能力，提高纺织白玉霜润滑脂的粘附能力。
产品保质期是指产品在正常条件下的质量保证期限，在保质期内保证纺织白玉霜润滑脂的稳定性对产品保质期是至关重要的。由于纺织白玉霜润滑脂中的C18H36O2和C21H42O4化学性质均很稳定，但是没有抗菌能力，故在本申请的纺织白玉霜甘油酯内添加杀菌剂，将纺织白玉霜甘油酯内的霉菌、细菌杀灭，防止纱线被霉菌腐蚀、细菌侵入，进一步提高产品的安全性。
本发明的进一步设置为：所述C18H36O2质量百分比含量在20％-35％，所述C21H42O4质量百分比含量在55％-78％。
通过采用上述技术方案，C18H36O2质量百分比较小，C21H42O4质量百分比较大，由于C21H42O4有增稠的功能，所以以上述比例配置的纺织白玉霜润滑脂，黏度和稠度均较大，适用于涂抹较粗的纱线，使本申请的纺织白玉霜润滑脂能被均匀地涂抹到纱线表面。
本发明的进一步设置为：所述C18H36O2质量百分比含量为25％，所述C21H42O4质量百分比含量为64.8％。
通过采用上述技术方案，采用质量百分比为30％的C18H36O2和69.8％的C21H42O4，使本申请的纺织白玉霜润滑脂既具有较好的细腻度，不会有颗粒磨砂感，又不会黏度和稠度过小而无法附着在纱线的弧形表面。
本发明的进一步设置为：所述C18H36O2质量百分比含量在55％-75％，所述C21H42O4质量百分比含量在20％-40％。
通过采用上述技术方案，C18H36O2比例较大，C21H42O4比例较小，本申请的纺织白玉霜润滑脂的黏度和稠度减小，纺织白玉霜润滑脂涂抹到较细的纱线后，避免过稠而涂抹不均匀，纺织白玉霜润滑脂干燥后在纱线表面形成一层C18H36O2膜，提高较细纱线的拉伸强度和韧性，不易被打断，从而提高倍捻后纱线的整体性能。
本发明的进一步设置为：所述C21H42O4为单硬脂酸甘油酯。
通过采用上述技术方案，单硬脂酸甘油酯是油脂化工和日用化工行业中应用最广泛、用量最大的一种添加剂和乳化剂，属油溶性，是一种典型的非离子型表面活性剂，兼具乳化剂和润滑剂的功能，加入后能使纺织白玉霜润滑脂具有黏性和润滑的作用，既能将纱线黏住不让纱线脱落，又能减少摩擦，对纱线润滑后进行退绕。
本发明的进一步设置为：所述杀菌剂为C8H8O4、CH3CH＝CHCH＝CHCOOK中的一种。
通过采用上述技术方案，C8H8O4，分子式为C8H8O4，主要用途是低毒、高效、广谱杀菌剂，用于对本申请的纺织白玉霜进行高效地广谱杀菌，此外，通过加入C8H8O4，也能在KOH加入过量后对本申请的纺织白玉霜的pH进行微调。CH3CH＝CHCH＝CHCOOK能有效抑制霉菌、酵母菌和好氧性细菌的活性，从而达到有效地延长纺织白玉霜的保存时间，防腐效果是同类产品苯甲酸钠的5-10倍。
本发明的另一个目的在于提供一种纺织白玉霜的制备方法。
本发明的上述技术目的是通过以下技术方案得以实现的：
a)加入配方量的C18H36O2、C21H42O4和玉米淀粉，加热至95℃后混合均匀，得到液体a；
b)向a)步骤得到的液体a中加入配方量的KOH，调节pH至7.0-7.5，得到液体b；
c)向b)步骤得到的液体b中加入配方量的杀菌剂，得到液体c；
d)向c)步骤中得到的液体c降温至50℃，再次测定pH，如果pH值在7.0-7.5之间，则冷却至25℃，得到液体d；
e)将步骤d)得到的液体d密封包装成产品。
通过采用上述技术方案，C18H36O2熔点为56℃-69.6℃，沸点为232℃(2.0kPa)，C21H42O4选用单硬脂酸甘油酯，单硬脂酸甘油酯熔点为78℃-81℃，沸点为232℃(2.0kPa)，通过将C18H36O2和单硬脂酸甘油酯混合后加热至95℃，C18H36O2和C21H42O4都呈液态后混合，相比于在固态下进行混合，混合效果更好，C18H36O2分布更加均匀。
C21H42O4优选为单硬脂酸甘油酯，单硬脂酸甘油酯具有α、β两种异构体，两种异构体都具有优良的乳化、润滑性，但是α-单硬脂酸甘油酯性能更优，β-单硬脂酸甘油酯在受热后会转化成α-单硬脂酸甘油酯，进一步提高单硬脂酸甘油酯的乳化和润滑性能。
加入KOH后调节纺织白玉霜的pH值为7.0-7.5，使本申请的纺织白玉霜偏弱碱性，不会对纱线造成酸性腐蚀和破坏，而且也在人体皮肤pH中和缓冲范围内，不会对皮肤造成影响，保证产品使用过程中的安全性。
将混合后的C18H36O2、C21H42O4pH调节至合适范围后，冷却降温至50℃，对pH值再次检测，确认pH不会出现较大的变化，确认无误后再次冷却至25℃后密封包装即可。
综上所述，本发明具有以下有益效果：采用C18H36O2作为主要原料，加入油脂类的C21H42O4，起到增稠、润滑的作用，使纺织白玉霜被涂抹到纱线后既能被粘贴到管纱上端，防止纱线脱落，干燥后又能在纱线表面形成一层C18H36O2膜，增强纱线的拉伸强度和韧性，提升倍捻后纱线的整体性能。
具体实施方式
具体实施例仅仅是对本发明的解释，其并不是对本发明的限制，本领域技术人员在阅读完本说明书后可以根据需要对本实施例做出没有创造性贡献的修改，但只要在本发明的权利要求范围内都受到专利法的保护。
以下实施例和对比例中，C18H36O2仅代表硬脂酸，C21H42O4仅代表硬脂酸甘油酯。C8H8O4仅代表脱氢醋酸，CH3CH＝CHCH＝CHCOOK仅代表山梨酸钾。
实施例1：一种纺织白玉霜润滑脂，按质量份，分别按照以下表1指定的各组分，将C18H36O2和C21H42O4混合后，加热至95℃熔融共混2小时，混合均匀后，再加入KOH，检测pH如果在7.0-7.5之间，载加入杀菌剂C8H8O4混合均匀，降温至50℃再次确认，如果pH在7.0-7.5之间，冷却至25℃用密封的小桶包装成产品即可。参照GB4789.2-94、GB265-88的测定方法，测试纺织白玉霜润滑脂的pH、粘度、每克产品内的菌落数。
实施例2：一种纺织白玉霜润滑脂，按照以下表1指定的各组分重复实施例1的方法，并在表1中列出测试结果。
实施例3：一种纺织白玉霜润滑脂，按照以下表1指定的各组分重复实施例1的方法，并在表1中列出测试结果。
实施例4：一种纺织白玉霜润滑脂，按照以下表1指定的各组分重复实施例1的方法，并在表1中列出测试结果。
实施例5:一种纺织白玉霜润滑脂，按照以下表1指定的各组分重复实施例1的方法，并在表1中列出测试结果。
实施例6:一种纺织白玉霜润滑脂，按照以下表1指定的各组分重复实施例1的方法，并在表1中列出测试结果。
实施例7：一种纺织白玉霜润滑脂，按照以下表1指定的各组分重复实施例1的方法，杀菌剂用并在表1中列出测试结果。
实施例8：一种纺织白玉霜润滑脂，按照以下表1指定的各组分重复实施例1的方法，杀菌剂用CH3CH＝CHCH＝CHCOOK代替C8H8O4，并在表1中列出测试结果。
实施例9：一种纺织白玉霜润滑脂，按照以下表1指定的各组分重复实施例1的方法，杀菌剂用CH3CH＝CHCH＝CHCOOK代替C8H8O4，并在表1中列出测试结果。
实施例10：一种纺织白玉霜润滑脂，按照以下表1指定的各组分重复实施例1的方法，杀菌剂用CH3CH＝CHCH＝CHCOOK代替C8H8O4，并在表1中列出测试结果。
实施例11：一种纺织白玉霜润滑脂，按照以下表1指定的各组分重复实施例1的方法，杀菌剂用CH3CH＝CHCH＝CHCOOK代替C8H8O4，并在表1中列出测试结果。
实施例12：一种纺织白玉霜润滑脂，按照以下表1指定的各组分重复实施例1的方法，杀菌剂用CH3CH＝CHCH＝CHCOOK代替C8H8O4，并在表1中列出测试结果。
对比例1：一种纺织白玉霜润滑脂，按照以下表1指定的各组分重复实施例1的方法，并在表1中列出测试结果。
表1
Claims (7)
1.一种纺织白玉霜润滑脂，按质量百分比，由以下成分组成：
2.根据权利要求1所述的一种纺织白玉霜润滑脂，其特征在于：所述C18H36O2质量百分比含量在20％-35％，所述C21H42O4质量百分比含量在55％-78％。
3.根据权利要求2所述的一种纺织白玉霜润滑脂，其特征在于：所述C18H36O2质量百分比含量为25％，所述C21H42O4质量百分比含量为64.8％。
4.根据权利要求1所述的一种纺织白玉霜润滑脂，其特征在于：所述C18H36O2质量百分比含量在55％-75％，所述C21H42O4质量百分比含量在20％-40％。
5.根据权利要求1所述的一种纺织白玉霜润滑脂，其特征在于：所述C21H42O4为单硬脂酸甘油酯。
6.根据权利要求1所述的一种纺织白玉霜润滑脂，其特征在于：所述杀菌剂为C8H8O4、CH3CH＝CHCH＝CHCOOK中的一种或多种。
7.一种制备如权利要求1所述的纺织白玉霜润滑脂的方法，其特征在于：
a)加入配方量的C18H36O2、C21H42O4和玉米淀粉，加热至95℃后混合均匀，得到液体a；
b)向a)步骤得到的液体a中加入配方量的KOH，调节pH至7.0-7.5，得到液体b；
c)向b)步骤得到的液体b中加入配方量的杀菌剂，得到液体c；
d)向c)步骤中得到的液体c降温至50℃，再次测定pH，如果pH值在7.0-7.5之间，则冷却至25℃，得到液体d；
e)将步骤d)得到的液体d密封包装成产品。