CN106147423A - Water-based fluorocarbon varnish and preparation method thereof - Google Patents
Water-based fluorocarbon varnish and preparation method thereof Download PDFInfo
- Publication number
- CN106147423A CN106147423A CN201610495941.6A CN201610495941A CN106147423A CN 106147423 A CN106147423 A CN 106147423A CN 201610495941 A CN201610495941 A CN 201610495941A CN 106147423 A CN106147423 A CN 106147423A
- Authority
- CN
- China
- Prior art keywords
- water
- based fluorocarbon
- fluorocarbon resin
- coalescents
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Open a kind of water-based fluorocarbon varnish of the present invention and preparation method thereof, relates to chemical technology field.Use the raw material of following percentage by weight: the water-based fluorocarbon resin prepared by CTFE and tetrafluoroethylene monomer, aminopropyl trimethoxysilane, tetramethyl piperidine according to the ratio that weight ratio is 3:4, levelling agent, dispersant, wetting agent, defoamer, light stabilizer, coalescents and water;Stir including by water, dispersant, wetting agent, defoamer;It is subsequently adding water-based fluorocarbon resin, continues stirring;It is subsequently added into coalescents, continues stirring;It is subsequently added into aminopropyl trimethoxysilane, tetramethyl piperidine, levelling agent, light stabilizer, continues stirring.Owing to have employed specific water-based fluorocarbon resin, aminopropyl trimethoxysilane and tetramethyl piperidine so that water-based fluorocarbon varnish of the present invention has resistant, weatherability, chemical-resistant and the yellowing resistance of excellence.The present invention is a kind of environmental protection, the industrial finish of safe and nontoxic property.
Description
Technical field
The present invention relates to chemical technology field, especially a kind of water-based fluorocarbon varnish and preparation method thereof.
Background technology
Along with scientific and technological progress and the high speed development of national economy, the environmental consciousness of people strengthens, increasingly to healthy requirement
More and more higher, environmental regulation is also gradually improved, and joint money is energy-conservation, protects environment, it has also become the subject matter that whole world coating interface faces.
Along with the change of global climate and being becoming tight day of resource, the energy, countries in the world have formulated strict environmental regulation and political affairs in succession
Plan, encourages and promotes the use of the new product of environmental protection, energy-saving material-saving.
Fluorocarbon varnish is the normal temperature cured type double-component fluorocarbon varnish with fluororesin as Main Ingredients and Appearance, have super-weathering resistance and
The excellent properties such as resistance to persistence life-span, can be used for the cover protection of multiple coating and base material.Existing bottom surface unification exterior coating
The most mostly contain heavy metal element, but also be solvent type mostly, it use and be hazardous to the human body poison in a large number, to environment
There is the solvent polluting and having penetrating odor.
Summary of the invention
One of the technical problem to be solved is to provide a kind of environmental protection, the water-based fluorocarbon varnish of safety.
In order to solve above-mentioned technical problem, the technical solution adopted in the present invention is:
Include the constituent of following percentage by weight:
Water-based fluorocarbon resin 75%~86%, aminopropyl trimethoxysilane 0.1%~0.3%, tetramethyl piperidine 0.2%~0.4%, stream
Flat agent 0.1%~0.3%, dispersant 0.2%~0.4%, wetting agent 0.1%~0.3%, defoamer 0.2%~0.4%, light stabilizer
0.1%~0.2%, coalescents 6%~8%, surplus is water;
Wherein, described water-based fluorocarbon resin is according to the ratio system that weight ratio is 3:4 by CTFE and tetrafluoroethylene monomer
?.
In technique scheme, more specifically scheme is it may also is that the percentage by weight of described constituent is: water-based fluorocarbon
Resin 75%, aminopropyl trimethoxysilane 0.1%, tetramethyl piperidine 0.4%, levelling agent 0.1%, dispersant 0.2%, wetting agent
0.1%, defoamer 0.2%, light stabilizer 0.2%, coalescents 6%, surplus is water.
Further, the percentage by weight of described constituent is: the percentage by weight of described constituent is: water-based fluorocarbon
Resin 86%, aminopropyl trimethoxysilane 0.3%, tetramethyl piperidine 0.2%, levelling agent 0.3%, dispersant 0.4%, wetting agent
0.3%, defoamer 0.4%, light stabilizer 0.1%, coalescents 8%, surplus is water.
The two of the technical problem to be solved are to provide the preparation of the water-thinned antirust primer of a kind of good combination property
Method.
In order to solve the problems referred to above, the technical solution adopted in the present invention is:
Use the raw material of following percentage by weight:
Water-based fluorocarbon resin 75%~86%, aminopropyl trimethoxysilane 0.1%~0.3%, tetramethyl piperidine 0.2%~0.4%, stream
Flat agent 0.1%~0.3%, dispersant 0.2%~0.4%, wetting agent 0.1%~0.3%, defoamer 0.2%~0.4%, light stabilizer
0.1%~0.2%, coalescents 6%~8%, surplus is water;
Wherein, described water-based fluorocarbon resin is according to the ratio system that weight ratio is 3:4 by CTFE and tetrafluoroethylene monomer
?;
Its manufacture method comprises the steps:
A, first by water, dispersant, wetting agent, defoamer weigh put in reactor, start blender at 400 revs/min~600
Rev/min mixing speed under stir more than 15 minutes so that it is stir;
B, stir after, under the mixing speed of 400 revs/min~600 revs/min add water-based fluorocarbon resin, continue stirring 10
More than minute;
C, keep adding under the mixing speed of 400 revs/min~600 revs/min coalescents, continue stirring 10 minutes~15 minutes,
Rear addition aminopropyl trimethoxysilane, tetramethyl piperidine, levelling agent, light stabilizer, continue to be stirred until homogeneous.
In technique scheme, used by CTFE and tetrafluoroethylene monomer according to the ratio that weight ratio is 3:4
The water-based fluorocarbon resin that example prepares has raising stain resistance, weatherability, the effect of chemical-resistant;Aminopropyl trimethoxy silicon
Alkane has holding film non yellowing, the effect of nondiscoloration;The nanoscale that tetramethyl piperidine has absorption UV-A and UV-B simultaneously is wide
Spectrum ultraviolet, thus improve weather-proof, the effect of ageing-resistant performance of product.
Owing to using technique scheme, there is advantages that
1. owing to have employed specific water-based fluorocarbon resin, aminopropyl trimethoxysilane and tetramethyl piperidine so that this
Open fire fluorocarbon varnish has resistant, weatherability, chemical-resistant and the yellowing resistance of excellence.
2. the present invention is a kind of environmental protection, the industrial finish of safe and nontoxic property.
Detailed description of the invention
Below in conjunction with instantiation, the invention will be further described:
Wherein, the water-based fluorocarbon resin used in following example is according to weight ratio by CTFE and tetrafluoroethylene monomer
For 3:4 ratio prepare.
The water-based fluorocarbon varnish of embodiment 1--making 1000kg:
The raw material used: water-based fluorocarbon resin 750kg, aminopropyl trimethoxysilane 3kg, tetramethyl piperidine 2kg, levelling agent
1kg, dispersant 2kg, wetting agent 3kg, defoamer 2kg, light stabilizer 2kg, coalescents 60kg, water 175kg.
Making step is as follows:
A, first by water 175kg, dispersant 2kg, wetting agent 3kg, defoamer 2kg weigh put in reactor, start blender
Stir 20 minutes under the mixing speed of 400 revs/min so that it is stir;
B, stir after, under the mixing speed of 400 revs/min add water-based fluorocarbon resin 750kg, continue stirring 15 minutes;
C, keep adding under the mixing speed of 400 revs/min coalescents 60kg, continue stirring 10 minutes, rear add aminopropyl three
Methoxy silane 3kg, tetramethyl piperidine 2kg, levelling agent 1kg, light stabilizer 2kg, continue to be stirred until homogeneous.
The water-based fluorocarbon varnish of embodiment 2--making 1000kg:
The raw material used: water-based fluorocarbon resin 860kg, aminopropyl trimethoxysilane 1kg, tetramethyl piperidine 4kg, levelling agent
3kg, dispersant 4kg, wetting agent 1kg, defoamer 4kg, light stabilizer 1kg, coalescents 80kg, water 42kg.
Making step is as follows:
A, first by water 42kg, dispersant 4kg, wetting agent 1kg, defoamer 4kg weigh put in reactor, start blender and exist
Stir 25 minutes under the mixing speed of 500 revs/min so that it is stir;
B, stir after, under the mixing speed of 500 revs/min, add aqueous fluorocarbon resin 860kg, continue stirring 30 minutes;
C, keep adding under the mixing speed of 500 revs/min coalescents 80kg, continue stirring 10-15 minute, add aminopropyl afterwards
Trimethoxy silane 1kg, tetramethyl piperidine 4kg, levelling agent 3kg, light stabilizer 1kg, continue to be stirred until homogeneous.
The water-based fluorocarbon varnish of embodiment 3--making 1000kg:
The raw material used: water-based fluorocarbon resin 800kg, aminopropyl trimethoxysilane 2kg, tetramethyl piperidine 3kg, levelling agent
2kg, dispersant 3kg, wetting agent 2kg, defoamer 3kg, light stabilizer 1.5kg, coalescents 75kg, water 108.5kg.
Making step is as follows:
A, first by water 108.5kg, dispersant 3kg, wetting agent 2kg, defoamer 3kg weigh put in reactor, start stirring
Machine stirs 30 minutes under the mixing speed of 600 revs/min so that it is stir;
B, stir after, under the mixing speed of 600 revs/min, add aqueous fluorocarbon resin 800kg, continue stirring 30 minutes;
C, keep adding under the mixing speed of 600 revs/min coalescents 75kg, continue stirring 15 minutes, rear add aminopropyl three
Methoxy silane 2kg, tetramethyl piperidine 3kg, levelling agent 2kg, light stabilizer 1.5kg, continue to be stirred until homogeneous.
Through national building materials inspection center according to the standard detection of coating, the embodiment of the present invention 1,2, the aqueous of preparation
The main performance index of fluorocarbon varnish such as table 1:
Table 1
。
Claims (4)
1. a water-based fluorocarbon varnish, it is characterised in that include the constituent of following percentage by weight:
Water-based fluorocarbon resin 75%~86%, aminopropyl trimethoxysilane 0.1%~0.3%, tetramethyl piperidine 0.2%~0.4%, stream
Flat agent 0.1%~0.3%, dispersant 0.2%~0.4%, wetting agent 0.1%~0.3%, defoamer 0.2%~0.4%, light stabilizer
0.1%~0.2%, coalescents 6%~8%, surplus is water;
Wherein, described water-based fluorocarbon resin is according to the ratio system that weight ratio is 3:4 by CTFE and tetrafluoroethylene monomer
?.
Water-based fluorocarbon varnish the most according to claim 1, it is characterised in that;The percentage by weight of described constituent is: water
Property fluorocarbon resin 75%, aminopropyl trimethoxysilane 0.1%, tetramethyl piperidine 0.4%, levelling agent 0.1%, dispersant 0.2%, profit
Humectant 0.1%, defoamer 0.2%, light stabilizer 0.2%, coalescents 6%, surplus is water.
Water-based fluorocarbon varnish the most according to claim 1, it is characterised in that: the percentage by weight of described constituent is: water
Property fluorocarbon resin 86%, aminopropyl trimethoxysilane 0.3%, tetramethyl piperidine 0.2%, levelling agent 0.3%, dispersant 0.4%, profit
Humectant 0.3%, defoamer 0.4%, light stabilizer 0.1%, coalescents 8%, surplus is water.
4. the preparation method of a water-based fluorocarbon varnish, it is characterised in that:
Use the raw material of following percentage by weight:
Water-based fluorocarbon resin 75%~86%, aminopropyl trimethoxysilane 0.1%~0.3%, tetramethyl piperidine 0.2%~0.4%, stream
Flat agent 0.1%~0.3%, dispersant 0.2%~0.4%, wetting agent 0.1%~0.3%, defoamer 0.2%~0.4%, light stabilizer
0.1%~0.2%, coalescents 6%~8%, surplus is water;
Wherein, described water-based fluorocarbon resin is according to the ratio system that weight ratio is 3:4 by CTFE and tetrafluoroethylene monomer
?;
Its manufacture method comprises the steps:
A, first by water, dispersant, wetting agent, defoamer weigh put in reactor, start blender at 400 revs/min~600
Rev/min mixing speed under stir more than 15 minutes so that it is stir;
B, stir after, under the mixing speed of 400 revs/min~600 revs/min add water-based fluorocarbon resin, continue stirring 10
More than minute;
C, keep adding under the mixing speed of 400 revs/min~600 revs/min coalescents, continue stirring 10 minutes~15 minutes,
Rear addition aminopropyl trimethoxysilane, tetramethyl piperidine, levelling agent, light stabilizer, continue to be stirred until homogeneous.