CN106121173A - A kind of composite wood-plastic floor - Google Patents
A kind of composite wood-plastic floor Download PDFInfo
- Publication number
- CN106121173A CN106121173A CN201610533441.7A CN201610533441A CN106121173A CN 106121173 A CN106121173 A CN 106121173A CN 201610533441 A CN201610533441 A CN 201610533441A CN 106121173 A CN106121173 A CN 106121173A
- Authority
- CN
- China
- Prior art keywords
- wood
- plastic
- floor
- sheet material
- material layers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of composite wood-plastic floor, it is characterised in that include that Wood-plastic floor cell body, described cell body include that wearing layer, overwood mould sheet metal layer, solid wood board sheet material layers, lower wood-plastic board sheet material layers from top to bottom.The described solid wood board sheet material layers side that connects between cell body is provided with the tenon protruding out to cell body outer surface and the tenon groove structure being positioned at solid wood board sheet material layers.The Wood-plastic floor of MULTILAYER COMPOSITE that the present invention provides not only has saved wooden resource, and this being moulded by wood is coated on structure solid wood sandwich layer outside and makes solid wood sandwich layer be difficult to drying shrinkage bulking and cause deformation, and the structural stability of floor entirety is had important effect；The setting of wearing layer makes the wearability on floor strengthen, and can preferably retain the gloss of floor surface, extend the service life on floor；In the Tenon course of processing, because structure needs the timber of excision to can be used to make Wood plastic boards so that raw material maximally utilizes, cost-effective, protects timber resources.
Description
Technical field
The present invention relates to a kind of Wood-plastic floor, specifically a kind of composite wood-plastic floor.
Background technology
Floor mostly is solid wooden floor board and solid wooden compound floor in the market, wherein solid wooden floor board processed by natural timber and
Becoming, in afforestation rate declines today, the price of solid wooden floor board is the most of a relatively high, and in addition, solid wooden floor board is yielding, dry
Contracting bulking is the shortcoming that solid wooden floor board is main.Solid wooden compound floor typically pastes one layer of famousr and precious bark on top layer, but solid wood
The wearability of material is the most poor, the problem that whether solid wooden floor board or solid wooden compound floor all exist.But due to solid wood ground
Plate decorated style is recovered one's original simplicity, and texture is natural, is deeply liked by consumers in general.
The decorations materials such as wood plastic composite is the material of a kind of novel environment friendly, is commonly used in indoor and outdoor wallboard, floor
Material, with the outer matrix of waste or used plastics, wood fibre, bamboo fiber or agricultural crop straw are that packing material is made, and have waterproof
The advantages such as protection against the tide, agent of low hygroscopicity, low morphotropism, and mechanical strength are good.
With solid wood, wood plastic composite is combined Manufacture of Floor, and the psychology not only meeting client is sought, and can improve real
The some shortcomings that timber floor exists.
Summary of the invention
It is an object of the invention to provide a kind of composite wood-plastic floor, the Wood-plastic floor of this MULTILAYER COMPOSITE has not only saved wood
Matter resource, and this wood is moulded be coated on the structure outside solid wood sandwich layer make solid wood sandwich layer be difficult to drying shrinkage bulking and cause become
Shape, the structural stability overall to floor has important effect
The present invention realizes goal of the invention and adopts the following technical scheme that
A kind of composite wood-plastic floor, it is characterised in that including Wood-plastic floor cell body, described cell body is from top to bottom
Sheet metal layer, solid wood board sheet material layers, lower wood-plastic board sheet material layers is moulded including wearing layer, overwood.
Further, described solid wood board sheet material layers connection side between cell body is provided with and protrudes out to cell body outer surface
Tenon and be positioned at the tenon groove structure of solid wood board sheet material layers.
Further, described upper and lower wood-plastic board sheet material layers is imitation wood stricture of vagina co-extrusion Wood-plastic material, in mass ratio by following component structure
Becoming, base material 50-80wt% moulded by wood, and colorant 20-50wt% moulded by wood；
Described wood is moulded base material and is mainly composed of (quality is divided): polyvinylchloride (SG-8), 90-110 part；Biomass fiber,
30-100 part；Coupling agent, 0.5-10 part；Light stabilizer, 3-8 part；Compatilizer, 1-10 part；Lubricant, 1-5 part；Antioxidant,
0.2-0.4 part；Foaming agent, 0.3-0.5 part.
Described wood is moulded colorant and is mainly composed of (quality is divided): polyvinylchloride (SG-3), 50-100 part；Polyvinylchloride
(SG-5), 50-100 part；Light stabilizer, 4 parts；Lubricant, 2 parts；Pigment, 1-5 part.
Compared with the prior art, the present invention has the beneficial effect that:
The Wood-plastic floor of the MULTILAYER COMPOSITE that the present invention provides not only has saved wooden resource, and this being moulded by wood is coated on
Structure outside solid wood sandwich layer makes solid wood sandwich layer be difficult to drying shrinkage bulking and causes deformation, the structural stability tool overall to floor
There is important effect；The setting of wearing layer makes the wearability on floor strengthen, and can preferably retain the gloss of floor surface, extends
Service life on floor；The mortise-tenon joint structure of pin of galloping along on horseback is tightly combined, and does not has gap, the most attractive in appearance, makes again floor overall
Property good, be possible to prevent the heat caused because connecting gap to scatter and disappear.And in the Tenon course of processing, because structure needs excision
Timber can be used to make Wood plastic boards so that raw material maximally utilizes, cost-effective, protect timber resources.
Accompanying drawing explanation
Fig. 1 is Wood plastic floor structure schematic diagram of the present invention.
Wherein, 1 is surface wear-resistant layer, and 2 mould sheet metal layer for overwood, and 3 is solid wood sandwich layer layer, and 4 is lower wood-plastic board sheet material layers, and 31 are
Joinery and its construction, 311 is tenon, and 312 is tongue-and-groove.
Fig. 2 is joinery and its construction detail drawing and installs index, and arrow represents installation direction, and wherein 311 is tenon structure, and 312 are
Tenon groove structure；
Fig. 3 is the internal structure of tongue-and-groove 312.
Below by way of detailed description of the invention, technical solution of the present invention is described further.
Detailed description of the invention
As it is shown in figure 1, Wood-plastic floor cell body, include that wearing layer 1, overwood mould sheet metal layer 2, solid wood board from top to bottom
Layer 3, lower wood-plastic board sheet material layers 4.
Wood-plastic floor unit connected mode uses joinery and its construction 31, is interconnected to an entirety by joinery and its construction.Tenon
Fourth of the twelve Earthly Branches structure 31 is to process in the both sides of solid wood sandwich layer, is i.e. provided with convex in solid wood board sheet material layers connection side between cell body
Extend cell body outer surface tenon 311 and be positioned at tongue-and-groove 312 structure of solid wood board sheet material layers.
The multiple structure of Wood-plastic floor that the present invention provides is by each laminate material surface coating, and hot pressing forms whole
Plate.
Wherein, upper and lower wood-plastic board sheet material layers is imitation wood stricture of vagina co-extrusion Wood-plastic material, is made up of following component in mass ratio, and wood is moulded
Base material 50-80wt%, colorant 20-50wt% moulded by wood；
Described wood is moulded base material and is mainly composed of (quality is divided): polyvinylchloride (SG-8), 90-110 part；Biomass fiber,
30-100 part；Coupling agent, 0.5-10 part；Light stabilizer, 3-8 part；Compatilizer, 1-10 part；Lubricant, 1-5 part；Antioxidant,
0.2-0.4 part；Foaming agent, 0.3-0.5 part.
Described wood is moulded colorant and is mainly composed of (quality is divided): polyvinylchloride (SG-3), 50-100 part；Polyvinylchloride
(SG-5), 50-100 part；Light stabilizer, 4 parts；Lubricant, 2 parts；Pigment, 1-5 part.
Wherein, preparing in the composition of upper and lower Wood plastic boards, timber is wood powder or sawdust, for processing the waste material of solid wood sandwich layer
Or other wood waste.Polyvinylchloride (SG-8/5/3), coupling agent (Aluminate, silane), light stabilizer (chlorinated polyethylene
CPE), compatilizer (maleic acid liquor-saturated graft polypropylene copolymer MAH-g-PP), lubricant (paraffin), antioxidant (antioxidant
1010), foaming agent (AC), pigment (Polymerizable yellow azo dye, ferrum oxide, ferrum zinc chrome brown dye, carbon black, titanium dioxide) etc. is
Commercially available prod.
The processing method one of Wood-plastic material
1) timber is put into flour mill is worn into fiber, after screening processes, obtain 20-60 mesh granule, then in quality
Pretreatment 2h under the conditions of 110 DEG C in the sodium hydroxide of mark 20%, then dewatered drying at 60 DEG C, under 110 DEG C of temperature conditionss, dry
Within dry 24 hours, the average moisture content to biomass fiber is maintained at less than 1%；
2) prepared by PVC wood plastic base material:
(1) according to PVC wood plastic base material formulation, polyvinylchloride (SG-8) is weighed, 100 parts；Biomass fiber, 30 parts；Even
Connection agent, 0.5 part；Light stabilizer, 3 parts；Compatilizer, 4 parts；Lubricant, 5 parts；Antioxidant, 0.2 part；Put it into HM40KM120
In high-speed mixer, with mixed 15 minutes of heat under the rotating speed of 2200r/min at 180 DEG C, treat that temperature is down under room temperature, condensed
Granule.
(2) weigh step (1) to obtain the granule of cohesion and add blowing agent AC, 0.3 part, lubricant 1 part puts into
HM40KM120 high-speed mixer remixes 15 minutes at 110 DEG C, the material A that must mix.
(3) by mixture A at flat double granulator granulations that L/D is 65:1, rotating speed is 5rpm, and prilling temperature is 220 DEG C, system
Obtain PVC wood plastic base material.
3) prepared by PVC wood plastic colorant:
(1) according to PVC wood plastic colorant formulas, polyvinylchloride (SG-3) 100 parts is weighed, light stabilizer, 4 parts；Lubrication
Agent, 2 parts；Pigment: Polymerizable yellow azo dye 1 part (appoplexy involving the collateral is yellow).Put it in HM40KM120 high-speed mixer, 180
With mixed 15 minutes of heat under the rotating speed of 2200r/min at DEG C, treat that temperature is down under room temperature, obtain mixture B.
(2) by mixture B at flat double granulator granulations that L/D is 65:1, rotating speed is 50rpm, and prilling temperature is 150 DEG C,
Prepare PVC wood plastic colorant.
4) weigh: weighing wood and mould base material 50%, colorant 50wt% moulded by wood.
5) mixing: the base material weighed and colorant are stirred mixing.
6) extrusion molding: using L/D is the conical double screw extruder of 65:1, and rotating speed is 30rpm, and extrusion temperature is 200
DEG C, prepare fretting map imitation wood stricture of vagina co-extrusion Wood-plastic material.
Survey its density 0.65/g.cm-3, impact strength 2KJ.m-3, decorative pattern is yellow decorative pattern, imitative Masson Pine.
The processing method 2 of Wood-plastic material
1) timber is put into flour mill is worn into fiber, after screening processes, obtain 20-60 mesh granule, then in quality
Pretreatment 2h under the conditions of 110 DEG C in the sodium hydroxide of mark 20%, then dewatered drying at 60 DEG C, under 110 DEG C of temperature conditionss, dry
Within dry 24 hours, the average moisture content to biomass fiber is maintained at less than 1%.
2) prepared by PVC wood plastic base material:
(1) according to PVC wood plastic base material formulation, polyvinylchloride (SG-8) is weighed, 100 parts；Biomass fiber, 100 parts；
Coupling agent, 10 parts；Light stabilizer, 5 parts；Compatilizer, 8 parts；Lubricant, 5 parts；Antioxidant, puts it into HM40KM120 by 0.4 part
In high-speed mixer, with mixed 15 minutes of heat under the rotating speed of 2200r/min at 180 DEG C, treat that temperature is down under room temperature, condensed
Granule.
(2) weigh step (1) to obtain the granule of cohesion and add foaming agent, 1 part, that HM40KM120 put into by lubricant 2 parts is high
Speed mixer remixes 15 minutes at 110 DEG C, the material A that must mix.
(3) by mixture A at flat double granulator granulations that L/D is 65:1, rotating speed is 5rpm, and prilling temperature is 220 DEG C, system
Obtain PVC wood plastic base material.
3) prepared by PVC wood plastic colorant:
(1) according to PVC wood plastic colorant formulas, polyvinylchloride (SG-3) 50 parts, polyvinylchloride (SG-5) 50 are weighed
Part, light stabilizer, 4 parts；Lubricant, 2 parts；Pigment: Polymerizable yellow azo dye 0.8 part (appoplexy involving the collateral is yellow), ferrum oxide 0.1 part
(precious red).Put it in HM40KM120 high-speed mixer, with mixed 15 minutes of heat under the rotating speed of 2200r/min at 180 DEG C,
Treat that temperature is down under room temperature, obtain mixture B.
(2) by mixture B at flat double granulator granulations that L/D is 65:1, rotating speed is 50rpm, and prilling temperature is 150 DEG C,
Prepare PVC wood plastic colorant.
4) weigh: weighing wood and mould base material 60%, colorant 40wt% moulded by wood.
5) mixing: the base material weighed and colorant are stirred mixing.
6) extrusion molding: using L/D is the conical double screw extruder of 65:1, and rotating speed is 30rpm, and extrusion temperature is 200
DEG C, prepare fretting map imitation wood stricture of vagina co-extrusion Wood-plastic material.
Survey its density 0.48/g.cm-3, impact strength 3.5KJ.m-3, decorative pattern is orange-yellow decorative pattern, imitative Zelkova schneideriana Hand.-Mazz..
The processing method three of Wood-plastic material
1) timber mixing is put into and worn into fiber in flour mill, after screening processes, obtain 20-60 mesh granule, then exist
Pretreatment 2h under the conditions of 110 DEG C in the sodium hydroxide of mass fraction 20%, then dewatered drying at 60 DEG C, 110 DEG C of temperature conditionss
Under, it is dried 24 hours average moisture contents to biomass fiber and is maintained at less than 1%.
2) prepared by PVC wood plastic base material:
(1) according to PVC wood plastic base material formulation, polyvinylchloride (SG-8) is weighed, 90 parts；Biomass fiber, 110 parts；Even
Connection agent, 9 parts；Light stabilizer, 5 parts；Compatilizer, 10 parts；Lubricant, 5 parts；Antioxidant, 0.4 part.Put it into HM40KM120 high
In speed mixer, with mixed 15 minutes of heat under the rotating speed of 2200r/min at 180 DEG C, treat that temperature is down under room temperature, obtain cohesion
Granule.
(2) weigh step (1) obtain cohesion granule add foaming agent, 1.5 parts, lubricant 2 parts put into HM40KM120
High-speed mixer remixes 15 minutes at 110 DEG C, the material A that must mix.
(3) by mixture A at flat double granulator granulations that L/D is 65:1, rotating speed is 5rpm, and prilling temperature is 220 DEG C, system
Obtain PVC wood plastic base material.
3) prepared by PVC wood plastic colorant:
(1) according to PVC wood plastic colorant formulas, polyvinylchloride (SG-5) 100 parts is weighed, light stabilizer, 4 parts；Lubrication
Agent, 2 parts；Pigment: ferrum oxide 0.1 part (precious red), ferrum zinc chrome brown dye 4 parts (plastic brown), carbon black 0.5 part (white carbon black)；Put
Enter in HM40KM120 high-speed mixer, with mixed 15 minutes of heat under the rotating speed of 2200r/min at 180 DEG C, treat that temperature is down to room temperature
Under, obtain mixture B.
(2) by mixture B at flat double granulator granulations that L/D is 65:1, rotating speed is 50rpm, and prilling temperature is 150 DEG C,
Prepare PVC wood plastic colorant.
4) weigh: weighing wood and mould base material 80%, colorant 80wt% moulded by wood.
5) mixing: the base material weighed and colorant are stirred mixing.
6) extrusion molding: using L/D is the conical double screw extruder of 65:1, and rotating speed is 30rpm, and extrusion temperature is 200
DEG C, prepare fretting map imitation wood stricture of vagina co-extrusion Wood-plastic material.
Survey its density 0.5/g.cm-3, impact strength 4.0KJ.m-3, decorative pattern is reddish brown wood grain, imitative acid branch.
In above example, unless otherwise noted, its component is commercial prior art products.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of the spirit or essential attributes of the present invention, it is possible to realize the present invention in other specific forms.Therefore, no matter
From the point of view of which point, all should regard embodiment as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit requires rather than described above limits, it is intended that all by fall in the implication of equivalency and scope of claim
Change is included in the present invention.Should not be considered as limiting involved claim by any reference in claim.
Although moreover, it will be appreciated that this specification is been described by according to embodiment, but the most each embodiment only wraps
Containing an independent technical scheme, this narrating mode of description is only that for clarity sake those skilled in the art should
Description can also be formed those skilled in the art through appropriately combined as an entirety, the technical scheme in each embodiment
May be appreciated other embodiments.
Claims (3)
1. a composite wood-plastic floor, it is characterised in that include that Wood-plastic floor cell body, described cell body are wrapped from top to bottom
Include wearing layer, overwood moulds sheet metal layer, solid wood board sheet material layers, lower wood-plastic board sheet material layers.
A kind of composite wood-plastic floor the most according to claim 1, it is characterised in that described solid wood board sheet material layers is in cell body
Between connect side be provided with protrude out to cell body outer surface tenon and be positioned at the tenon groove structure of solid wood board sheet material layers.
A kind of composite wood-plastic floor the most according to claim 1, it is characterised in that described upper and lower wood-plastic board sheet material layers is imitative
Wood grain co-extrusion Wood-plastic material, is made up of following component in mass ratio, and base material 50-80wt% moulded by wood, and colorant 20-50wt% moulded by wood；
Described wood is moulded base material and is mainly composed of (quality is divided): polyvinylchloride (SG-8), 90-110 part；Biomass fiber, 30-
100 parts；Coupling agent, 0.5-10 part；Light stabilizer, 3-8 part；Compatilizer, 1-10 part；Lubricant, 1-5 part；Antioxidant, 0.2-
0.4 part；Foaming agent, 0.3-0.5 part.
Described wood is moulded colorant and is mainly composed of (quality is divided): polyvinylchloride (SG-3), 50-100 part；Polyvinylchloride (SG-
5), 50-100 part；Light stabilizer, 4 parts；Lubricant, 2 parts；Pigment, 1-5 part.