CN106119905B - 一种浮动曝气机轴承内轴套复合镀涂液的制备方法 - Google Patents

一种浮动曝气机轴承内轴套复合镀涂液的制备方法 Download PDF

Info

Publication number
CN106119905B
CN106119905B CN201610667887.9A CN201610667887A CN106119905B CN 106119905 B CN106119905 B CN 106119905B CN 201610667887 A CN201610667887 A CN 201610667887A CN 106119905 B CN106119905 B CN 106119905B
Authority
CN
China
Prior art keywords
parts
raw material
axle sleeve
internal axle
masking liquid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610667887.9A
Other languages
English (en)
Other versions
CN106119905A (zh
Inventor
刘美
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ASIA PACIFIC WATER TREATMENT (TIANCHANG) Co Ltd
Original Assignee
ASIA PACIFIC WATER TREATMENT (TIANCHANG) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ASIA PACIFIC WATER TREATMENT (TIANCHANG) Co Ltd filed Critical ASIA PACIFIC WATER TREATMENT (TIANCHANG) Co Ltd
Priority to CN201610667887.9A priority Critical patent/CN106119905B/zh
Publication of CN106119905A publication Critical patent/CN106119905A/zh
Application granted granted Critical
Publication of CN106119905B publication Critical patent/CN106119905B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种浮动曝气机轴承内轴套复合镀涂液，涉及化工涂料制备技术领域，由以下原料制成：碳化硼600‑700份、硫酸镍120‑130份、硼酸150‑250份、硫酸钴6‑8份、香豆素25‑35份、润湿剂35‑45份、二季戊四醇5‑7份、明胶80‑90份、硝酸钠60‑80份、氨基磺酸10‑20份、乳酸15‑25份、糖精6‑8份、去离子水2200‑2300份；本发明的有益效果是：本发明工艺流程简洁，原料配比合理，增强特殊环境金属材料达不到物理、化学的要求，使用效果明显，耐高温也耐磨，确保了曝气机轴承内套的安全性能。

Description

一种浮动曝气机轴承内轴套复合镀涂液的制备方法
技术领域
本发明涉及水处理设备加工技术领域，具体涉及一种浮动曝气机轴承内轴套复合镀涂液的制备方法。
背景技术
浮动曝气机，将“微气泡”直接注入未经处理的污水中，在混凝剂和絮凝剂的共同作用下，悬浮物发生物理絮凝和化学絮凝，从而形成大的悬浮物絮团，在气泡群的浮升作用下“絮团”浮上液面形成浮渣，利用刮渣机从水中分离，不需要清理喷嘴，不会发生阻塞现象，长期以来在同行业浮动曝气机在污水中工作，气泵的气流压力使得浮动曝气机轴支撑点上的轴承得不到充分润滑而发热膨胀将电机损毁导致主机不能工作，因此多数改用橡胶轴承来替代，但是在使用时同样没有润滑，并且橡胶受热膨胀，会将轴颈抱死，也会电机损毁、主机不能工作，因此加工耐高温且轴承内轴套是目前技术研究的主要课题。
发明内容：
本发明所要解决的技术问题在于提供一种配方合理，生产工艺简单，耐高温性能强的浮动曝气机轴承内轴套复合镀涂液的制备方法。
本发明所要解决的技术问题采用以下技术方案来实现：
一种浮动曝气机轴承内轴套复合镀涂液，其特征在于，由以下原料制成：
碳化硼600-700份、硫酸镍120-130份、硼酸150-250份、硫酸钴6-8份、香豆素25-35份、润湿剂35-45份、二季戊四醇5-7份、明胶80-90份、硝酸钠60-80份、氨基磺酸10-20份、乳酸15-25份、糖精6-8份、去离子水2200-2300份；
各原料的优选分量为：碳化硼650份、硫酸镍125份、硼酸200份、硫酸钴7份、香豆素30份、润湿剂40份、二季戊四醇6份、明胶85份、硝酸钠70份、氨基磺酸15份、乳酸20份、糖精7份、去离子水2250份；
所述的润湿剂为十二烷基硫酸钠；
上述浮动曝气机轴承内轴套复合镀涂液的制备方法为：
①、将原料中的碳化硼进行和水放入球磨机中，升温至80-90℃，球磨3-5h后，冷却，备用；
②、将润湿剂和二季戊四醇加入上述球磨机中，混合均匀后，再次球磨1-2h；
③、将原料中的剩余组分混合后，添加进入球磨机中，升温至35-40℃，持续球磨3-5h后，冷却至室温，出料即可得到。
本发明中:
碳化硼具有超高耐温，膨胀系数小，耐腐蚀，抗冲刷，理化学稳定性能优良强的特点，其与原料中的其余组分进行合并后，配置成电镀液，直接进行曝气机轴承内轴套的电镀成型，作用于曝气机中，具有超高硬度，耐腐耐磨，实现了浮动曝气机的工况要求。
本发明的有益效果是：本发明工艺流程简洁，原料配比合理，增强特殊环境金属材料达不到物理、化学的要求，使用效果明显，耐高温也耐磨，确保了曝气机轴承内套的安全性能。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1
称取：碳化硼600g、硫酸镍120g、硼酸150g、硫酸钴6g、香豆素25g、润湿剂35g、二季戊四醇5g、明胶80g、硝酸钠60g、氨基磺酸10g、乳酸15g、糖精6g、去离子水2200g。
实施例2
称取：碳化硼650kg、硫酸镍125kg、硼酸200kg、硫酸钴7kg、香豆素30kg、润湿剂40kg、二季戊四醇6kg、明胶85kg、硝酸钠70kg、氨基磺酸15kg、乳酸20kg、糖精7kg、去离子水2250kg。
上述实施例1或2的制备方法如下：
①、将原料中的碳化硼进行和水放入球磨机中，升温至80-90℃，球磨3-5h后，冷却，备用；
②、将润湿剂和二季戊四醇加入上述球磨机中，混合均匀后，再次球磨1-2h；
③、将原料中的剩余组分混合后，添加进入球磨机中，升温至35-40℃，持续球磨3-5h后，冷却至室温，出料即可得到。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (3)

1.一种浮动曝气机轴承内轴套复合镀涂液，其特征在于，由以下原料制成：
碳化硼600-700份、硫酸镍120-130份、硼酸150-250份、硫酸钴6-8份、香豆素25-35份、润湿剂35-45份、二季戊四醇5-7份、明胶80-90份、硝酸钠60-80份、氨基磺酸10-20份、乳酸15-25份、糖精6-8份、去离子水2200-2300份；
制备方法为：
①、将原料中的碳化硼进行和水放入球磨机中，升温至80-90℃，球磨3-5h后，冷却，备用；
②、将润湿剂和二季戊四醇加入上述球磨机中，混合均匀后，再次球磨1-2h；
③、将原料中的剩余组分混合后，添加进入球磨机中，升温至35-40℃，持续球磨3-5h后，冷却至室温，出料即可得到。
2.根据权利要求1所述的一种浮动曝气机轴承内轴套复合镀涂液，其特征在于：各原料的优选分量为：碳化硼650份、硫酸镍125份、硼酸200份、硫酸钴7份、香豆素30份、润湿剂40份、二季戊四醇6份、明胶85份、硝酸钠70份、氨基磺酸15份、乳酸20份、糖精7份、去离子水2250份。
3.根据权利要求1所述的一种浮动曝气机轴承内轴套复合镀涂液，其特征在于：所述的润湿剂为十二烷基硫酸钠。
CN201610667887.9A 2016-08-15 2016-08-15 一种浮动曝气机轴承内轴套复合镀涂液的制备方法 Active CN106119905B (zh)