CN106117690B - A kind of preparation method of toy train dome - Google Patents
A kind of preparation method of toy train dome Download PDFInfo
- Publication number
- CN106117690B CN106117690B CN201610493524.8A CN201610493524A CN106117690B CN 106117690 B CN106117690 B CN 106117690B CN 201610493524 A CN201610493524 A CN 201610493524A CN 106117690 B CN106117690 B CN 106117690B
- Authority
- CN
- China
- Prior art keywords
- parts
- preparation
- transition face
- face layer
- toy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The preparation method of toy train dome disclosed by the invention, including body preparation, prime, mend ash, priming paint polishing, the spraying of secondary priming paint, finishing coat and test package, wherein body preparation includes sawing sheet, setting sanding, milling semicircle, groove milling, sanding and polishing, fracture, punching and drum, preparation method further includes the preparation of transition face layer, transition face layer is formed on the green body surface layer that body preparation obtains, priming paint is formed in by prime on transition face layer, and transition face layer includes according to the raw material of parts by weight：100 120 parts of rubber, 50 80 parts of high-dispersion white carbon black, 10 20 parts of coupling agent, 58 parts of stearic acid, 58 parts of activating agent, 13 parts of microwax, 13 parts of polyethylene glycol.The present invention program's is simple for process, and product structure stability is good, and brushing interlayer is firmly combined with, and is effectively improved the quality and antiseptic property of toy train dome, extends its service life.
Description
Technical field
The present invention relates to a kind of preparation method of toy, particularly a kind of preparation method of toy train dome.
Background technology
The wooden toy in ancient times generation, is single wooden toy, and all different degrees of practicality of modern wooden toy is different
The contact of material technique and processing reach the diversification of play function, multifunction.
Wooden toy is one main kind of in toy classification, and history is of long standing and well established, and wooden toy is in European and American developed countries
Each each stage of historical development, in unique culture and realization configuration for being possessed of America and Europe, respective country in history, German wood
It is also most notable earliest that toy processed, which is,.In the ancient times of Germany, just there is the appearance of belt driven lathe, wooden toy is exactly belt driven lathe
Processing, it polishes by hand later, the size of this kind of wooden toy has from several feet of very little to very big toy, this kind of object for appreciation
Has the works entering the coffin-die Asia Noah's ark most represented.
There is the people for being A Erbai in U.S. Philadelphia, he is German, and the U.S. migrated in 1872, he starts as circus
Group makes wooden horse toy, the wooden saddlery made by him have nimbly and freely, it is life-like the characteristics of, by local many circus troupes
It is used, can still see its trace always, be wooden horse popular at that time.Later, circus troupe was mounted with four in wooden horse
Wheel has reformed into the blank of ancient times carriage.
Because of the inspiration of wooden horse, in wooden toy manufacture afterwards, wooden train, wooden vehicle, wooden steamer, wood
Tractor processed etc. occurs in succession, by now until, wooden aircraft into favorite in children's toy, from this point it can be seen that
Come, wooden toy existing long history and cultural connotation have the breath in imparting epoch.
In other wooden toys, stilt and gyro are also the toy that children are delithted with, and stilt are very simple wood
Toy processed, teaches through lively activities, and gyro is the simplest wooden toy of practical manufacture craft, but application is most in child, small
When make gyro on ice, when gyro rotates, therefrom acquired the knowledge such as mechanics principle, acceleration, it may be said that wooden
Toy in people's intellectual development to performing meritorious deeds never to be obliterated.
In China, wooden toy history is more long, and famous ' Huarongdao ' in ancient times was as a child always played, and understands every
The effect of a personage, power and the skill mutually fought all are critically important, later, and wooden toy building blocks occur, are taking
During building building blocks, the reason of building has been understood, having put up would not fall, and the not science built is exactly to fall down, this is perhaps
Many building designers are developed, thus, toy is the intelligence teacher of mankind's initiation, and the good children's intelligence of object for appreciation will be apparent
Outstanding, this also gives the glorious responsibility of toy manufacturing enterprise.
Wooden toy generally morphologically has nature, is abstracted, point of the form of art.Natural morphologic appearance toy
Essence, to the comfort of popular feeling spirit, the mental factor of abstract morphologic appearance toy gives people unlimited reverie.The morphologic appearance of art
The appreciation factor of toy, to the feeling of people U.S..When people is when mood is gloomy, if he is appreciating one very big very stupid object for appreciation
Tool, then he is more painful, and at this time, he appreciates in bright gay color, a shape gracefulness, it appears that just very happy toy, the heart
Feelings can be different.
Wooden toy is not only to have unique charm in intellectual development, also has the characteristics that fine, reality in other respects
It is first with safety, it is non-toxic and tasteless since wooden toy is processed with timber, there is very much side to the physical and mental health of children
It helps, then it is exactly to fall not bad, wear-resisting, resistance to the advantages that beating to have, this is also the external factor for being keen to buy Chinese wooden.
Although existing wooden toy has the advantages that aforementioned, it is difficult without doubt as natural organic
To avoid to make moist, go mouldy, corruption, deformation etc. the problem of, bring difficulty to be used for a long time, cause more high push away
Wide application cost.
Invention content
To solve the above problems, the invention discloses a kind of preparation method of toy train dome, simple for process, cost can
Control property is good, and product structure stability is good, and brushing interlayer is firmly combined with, and is effectively improved the quality and anti-corrosive properties of wooden toy
Can, extend its service life.
The preparation method of toy train dome disclosed by the invention, including body preparation, prepared by transition face layer, priming paint applies
Brush, mend ash, priming paint polishing, secondary priming paint, finishing coat spraying and test package, wherein body preparation including sawing sheet, shape sanding,
Milling semicircle, groove milling, sanding and polishing, fracture, punching and drum, transition face layer are formed in the green body surface layer that body preparation obtains
On, priming paint is formed in by prime on transition face layer, and transition face layer includes according to the raw material of parts by weight：Rubber 100-120
Part, 50-80 parts of high-dispersion white carbon black, 10-20 parts of coupling agent, 5-8 parts of stearic acid, 5-8 parts of activating agent, 1-3 parts of microwax, poly- second
1-3 parts of glycol.Coupling agent (such as silane coupling agent), activating agent etc. are this field commonly common substance, and to the present invention
Scheme has universal adaptability.By using the transition face layer of setting in this programme, transition is formed in billet surface by it
Property structure, to enhance the binding performance of the wooden structures of green body and skin of paint, while reduce the green body renovation process in toy
In to mending the dependence of grey technique, reduce and mend mortar and influence skin of paint in the larger amount of use of surface or part
Binding performance, so as to improve the overall structure performance and quality stability of toy.
A kind of improvement of the preparation method of toy train dome disclosed by the invention, the preparation of transition face layer includes being kneaded,
Molding is kneaded by rubber, stearic acid, activating agent, microwax and polyethylene glycol, to carry out mixing 50-60s, melting temperature 90-
200 DEG C, pressure 0.5-0.6Mpa add high-dispersion white carbon black and are kneaded 120-150s, and melting temperature is 120-220 DEG C, pressure
Power is 0.45-0.58Mpa, and wherein coupling agent adds in mixing.
A kind of improvement of the preparation method of toy train dome disclosed by the invention, in mixing process, coupling agent at least divides
Two steps are added, and part of it mixes in advance with rubber, stearic acid, activating agent, microwax and polyethylene glycol, another part and height
Dispersion white carbon is pre-mixed (such as after two step addition, coupling agent also has residue, can be added in mixing process).
By at least being added in two steps in mixing process in this programme, it can be realized in entire mixing process and all original is filled
Divide mixing to carry out sufficient surface modified active to all substances, while substep is added and can all be added in avoid disposable
And the transition that the materials such as rubber occur absorbs coupling agent generation swelling, strand translation capability is strengthened and causes to be kneaded open chain effect
It reduces and liquid phase composition (coupling agent) disposably adds in excessive and utilizes insufficient, the distribution addition coupling of this programme as a result,
Agent can be effectively improved the mixed and modified quality of transition face stock, make it have preferable transition fitting and mechanical performance and
Cushion performance.
A kind of improvement of the preparation method of toy train dome disclosed by the invention, it is that ash material is prepared into slurry to mend ash
Afterwards, coated on workpiece, through polishing, ash material includes the raw material of following parts by weight：30~60 parts of Portland cement,
0.1~0.3 part of 10~30 parts of gypsum, 1~4 part of penetrant crystalline material, 1~4 part of rubber powder, 0~0.3 part of water-retaining agent and fiber.This
It is formed in scheme by using special ash material, the higher structure sheaf of hardness is formed in workpiece surface, conducive to processing and post-processing
Operation, at the same by simple grinding process after, addition fiber can by polish strength control its protrude surface be formed
Structure similar to " burr " simultaneously controls the structure to protrude the length on surface, so as to form interlaminar improvement connection in subsequent processing
Structure, so as to enhance the fastness of Coating combination so that the surface structure of toy is more stable and firm, and processability is more preferable, wear-resistant
Damage property is stronger.
A kind of improvement of the preparation method of toy train dome disclosed by the invention, water-retaining agent are cellulose ether.
A kind of improvement of the preparation method of toy train dome disclosed by the invention, cellulose ether are selected from methylcellulose
It is one or more in ether, hydroxypropyl methyl cellulose ether, ethoxyl methyl cellulose ether, hydroxyethyl ether cellulose.
A kind of improvement of the preparation method of toy train dome disclosed by the invention, finishing coat outer layer are also formed with glass deposition
Layer, glass sedimentary are formed on finishing coat outer layer.The glass sedimentary is sodium metasilicate alkaline aqueous solution brushing to dried painting
Enamelled coating surface obtains, and it is 0.5-0.8 microns that glass sedimentary, which forms thickness,.It is deposited in the technical program by the glass of formation
Layer, is formed with one layer of comparatively dense glass structure layer, so as to play effective oxygen barrier, water proof very with the outermost layer structure of toy
To the effect for playing fire protection flame retarding to a certain extent, (other parts of wooden toy are respectively provided with combustibility, and the glass deposits
Layer then plays certain mitigation, and is not easy simply to be lighted), while convenient for being polished to surface or frosted, change
The appearance of kind product, has good case hardness and wearability.
Toy disclosed by the invention has good surface texture, has good surface processing performance and performance,
And simple for process, cost controllability is good, and product structure stability is good, and brushing interlayer is firmly combined with, and is effectively improved wooden
The quality and antiseptic property of toy extend its service life, and with good safety in utilization.
Specific embodiment
With reference to embodiment, the present invention is furture elucidated, it should be understood that following specific embodiments are only used for
It is bright the present invention rather than limit the scope of the invention.
Embodiment 1
The preparation method of the present embodiment toy is beaten including body preparation, the preparation of transition face layer, prime, benefit ash, priming paint
Mill, the spraying of secondary priming paint, finishing coat and test package, wherein body preparation include sawing sheet, setting sanding, milling semicircle, groove milling, beat
Grinding and polishing light, fracture, punching and drum, transition face layer are formed on the green body surface layer that body preparation obtains, and priming paint passes through priming paint
Brushing is formed on transition face layer, and transition face layer includes according to the raw material of parts by weight：100 parts of rubber, 70 parts of high-dispersion white carbon black,
20 parts of coupling agent, 6.4 parts of stearic acid, 5.8 parts of activating agent, 1.6 parts of microwax, 2.3 parts of polyethylene glycol.
Embodiment 2
The preparation method of the present embodiment toy is beaten including body preparation, the preparation of transition face layer, prime, benefit ash, priming paint
Mill, the spraying of secondary priming paint, finishing coat and test package, wherein body preparation include sawing sheet, setting sanding, milling semicircle, groove milling, beat
Grinding and polishing light, fracture, punching and drum, transition face layer are formed on the green body surface layer that body preparation obtains, and priming paint passes through priming paint
Brushing is formed on transition face layer, and transition face layer includes according to the raw material of parts by weight：103 parts of rubber, 73 parts of high-dispersion white carbon black,
10 parts of coupling agent, 7.2 parts of stearic acid, 8 parts of activating agent, 2.7 parts of microwax, 3 parts of polyethylene glycol.
Embodiment 3
The preparation method of the present embodiment toy is beaten including body preparation, the preparation of transition face layer, prime, benefit ash, priming paint
Mill, the spraying of secondary priming paint, finishing coat and test package, wherein body preparation include sawing sheet, setting sanding, milling semicircle, groove milling, beat
Grinding and polishing light, fracture, punching and drum, transition face layer are formed on the green body surface layer that body preparation obtains, and priming paint passes through priming paint
Brushing is formed on transition face layer, and transition face layer includes according to the raw material of parts by weight：109 parts of rubber, 50 parts of high-dispersion white carbon black,
15 parts of coupling agent, 5.5 parts of stearic acid, 5 parts of activating agent, 2 parts of microwax, 1 part of polyethylene glycol.
Embodiment 4
The preparation method of the present embodiment toy is beaten including body preparation, the preparation of transition face layer, prime, benefit ash, priming paint
Mill, the spraying of secondary priming paint, finishing coat and test package, wherein body preparation include sawing sheet, setting sanding, milling semicircle, groove milling, beat
Grinding and polishing light, fracture, punching and drum, transition face layer are formed on the green body surface layer that body preparation obtains, and priming paint passes through priming paint
Brushing is formed on transition face layer, and transition face layer includes according to the raw material of parts by weight：110 parts of rubber, 80 parts of high-dispersion white carbon black,
12 parts of coupling agent, 8 parts of stearic acid, 6.2 parts of activating agent, 3 parts of microwax, 1.8 parts of polyethylene glycol.
Embodiment 5
The preparation method of the present embodiment toy is beaten including body preparation, the preparation of transition face layer, prime, benefit ash, priming paint
Mill, the spraying of secondary priming paint, finishing coat and test package, wherein body preparation include sawing sheet, setting sanding, milling semicircle, groove milling, beat
Grinding and polishing light, fracture, punching and drum, transition face layer are formed on the green body surface layer that body preparation obtains, and priming paint passes through priming paint
Brushing is formed on transition face layer, and transition face layer includes according to the raw material of parts by weight：113 parts of rubber, 60 parts of high-dispersion white carbon black,
17 parts of coupling agent, 7 parts of stearic acid, 7 parts of activating agent, 1 part of microwax, 2 parts of polyethylene glycol.
Embodiment 6
The preparation method of the present embodiment toy is beaten including body preparation, the preparation of transition face layer, prime, benefit ash, priming paint
Mill, the spraying of secondary priming paint, finishing coat and test package, wherein body preparation include sawing sheet, setting sanding, milling semicircle, groove milling, beat
Grinding and polishing light, fracture, punching and drum, transition face layer are formed on the green body surface layer that body preparation obtains, and priming paint passes through priming paint
Brushing is formed on transition face layer, and transition face layer includes according to the raw material of parts by weight：116 parts of rubber, 70 parts of high-dispersion white carbon black,
16 parts of coupling agent, 6 parts of stearic acid, 6 parts of activating agent, 2.4 parts of microwax, 1.2 parts of polyethylene glycol.
Embodiment 7
The preparation method of the present embodiment toy is beaten including body preparation, the preparation of transition face layer, prime, benefit ash, priming paint
Mill, the spraying of secondary priming paint, finishing coat and test package, wherein body preparation include sawing sheet, setting sanding, milling semicircle, groove milling, beat
Grinding and polishing light, fracture, punching and drum, transition face layer are formed on the green body surface layer that body preparation obtains, and priming paint passes through priming paint
Brushing is formed on transition face layer, and transition face layer includes according to the raw material of parts by weight：120 parts of rubber, 56 parts of high-dispersion white carbon black,
13 parts of coupling agent, 5 parts of stearic acid, 7.8 parts of activating agent, 1.3 parts of microwax, 2.6 parts of polyethylene glycol.
It being distinguished with above-described embodiment, the preparation of transition face layer is illustrated by following some examples, without
As the restriction of claimed range, and can be applicable in the present invention program：
The preparation example 1 of transition face layer
In this example, the preparation of transition face layer includes being kneaded, molding, is kneaded as by rubber, stearic acid, activating agent, microwax
And polyethylene glycol, mixing 50s is carried out, melting temperature is 100 DEG C, pressure 0.5Mpa, adds high-dispersion white carbon black mixing
147s, melting temperature are 220 DEG C, and pressure 0.56Mpa, wherein coupling agent are added in mixing.
The preparation example 2 of transition face layer
In this example, the preparation of transition face layer includes being kneaded, molding, is kneaded as by rubber, stearic acid, activating agent, microwax
And polyethylene glycol, mixing 52s is carried out, melting temperature is 120 DEG C, pressure 0.6Mpa, adds high-dispersion white carbon black mixing
125s, melting temperature are 210 DEG C, and pressure 0.46Mpa, wherein coupling agent are added in mixing.
The preparation example 3 of transition face layer
In this example, the preparation of transition face layer includes being kneaded, molding, is kneaded as by rubber, stearic acid, activating agent, microwax
And polyethylene glycol, mixing 54s is carried out, melting temperature is 160 DEG C, pressure 0.55Mpa, adds high-dispersion white carbon black mixing
130s, melting temperature are 190 DEG C, and pressure 0.48Mpa, wherein coupling agent are added in mixing.
The preparation example 4 of transition face layer
In this example, the preparation of transition face layer includes being kneaded, molding, is kneaded as by rubber, stearic acid, activating agent, microwax
And polyethylene glycol, mixing 56s is carried out, melting temperature is 180 DEG C, pressure 0.52Mpa, adds high-dispersion white carbon black mixing
140s, melting temperature are 150 DEG C, and pressure 0.5Mpa, wherein coupling agent are added in mixing.
The preparation example 5 of transition face layer
In this example, the preparation of transition face layer includes being kneaded, molding, is kneaded as by rubber, stearic acid, activating agent, microwax
And polyethylene glycol, mixing 58s is carried out, melting temperature is 200 DEG C, pressure 0.58Mpa, adds high-dispersion white carbon black mixing
150s, melting temperature are 170 DEG C, and pressure 0.58Mpa, wherein coupling agent are added in mixing.
The preparation example 6 of transition face layer
In this example, the preparation of transition face layer includes being kneaded, molding, is kneaded as by rubber, stearic acid, activating agent, microwax
And polyethylene glycol, mixing 60s is carried out, melting temperature is 90 DEG C, pressure 0.56Mpa, adds high-dispersion white carbon black mixing
120s, melting temperature are 120 DEG C, and pressure 0.45Mpa, wherein coupling agent are added in mixing.
Distinguished with above-described embodiment, in mixing process, coupling agent adds in two steps, part of it in advance with raw material shape
The high-dispersion white carbon black of rubber, stearic acid, activating agent, microwax and the polyethylene glycol mixing of state, remainder and raw material form
It is pre-mixed.Or in mixing process, the addition of coupling agent point three steps, part of it in advance with the rubber of raw material form, stearic acid,
Activating agent, microwax and polyethylene glycol mixing, another part and the high-dispersion white carbon black of raw material form are pre-mixed, remainder
It is added in real time in mixing process.
It is distinguished with above-described embodiment, mends ash after ash material is prepared into slurry, coated on workpiece, to be through polishing
Can, the composition of ash material is illustrated by following some examples, and not as the restriction of claimed range, and in present invention side
It can be applicable in case：
The composition embodiment 1 of ash material
Ash material includes the raw material of following parts by weight in this implementation：30 parts of Portland cement, 12 parts of gypsum, penetrant crystalline
0.22 part of 3 parts of material, 3.3 parts of rubber powder and fiber.
The composition embodiment 2 of ash material
Ash material includes the raw material of following parts by weight in this implementation：40 parts of Portland cement, 30 parts of gypsum, penetrant crystalline
0.2 part of 1 part of material, 2.5 parts of rubber powder, 0.3 part of water-retaining agent and fiber.
The composition embodiment 3 of ash material
Ash material includes the raw material of following parts by weight in this implementation：50 parts of Portland cement, 26 parts of gypsum, penetrant crystalline
0.3 part of 2 parts of material, 3 parts of rubber powder, 0.1 part of water-retaining agent and fiber.
The composition embodiment 4 of ash material
Ash material includes the raw material of following parts by weight in this implementation：60 parts of Portland cement, 20 parts of gypsum, penetrant crystalline
0.1 part of 4 parts of material, 2 parts of rubber powder, 0.2 part of water-retaining agent and fiber.
The composition embodiment 5 of ash material
Ash material includes the raw material of following parts by weight in this implementation：38 parts of Portland cement, 17 parts of gypsum, penetrant crystalline
0.28 part of 1.8 parts of material, 4 parts of rubber powder, 0.15 part of water-retaining agent and fiber.
The composition embodiment 6 of ash material
Ash material includes the raw material of following parts by weight in this implementation：52 parts of Portland cement, 10 parts of gypsum, penetrant crystalline
0.13 part of 3.2 parts of material, 1 part of rubber powder, 0.23 part of water-retaining agent and fiber.
It is distinguished with above-described embodiment, penetrant crystalline material is activated silica penetrant crystalline masterbatch.
It is distinguished with above-described embodiment, water-retaining agent is cellulose ether.
It is distinguished with above-described embodiment, cellulose ether is the one kind included but not limited in following scheme：Methyl cellulose
Plain ether；Hydroxypropyl methyl cellulose ether；Ethoxyl methyl cellulose ether；Hydroxyethyl ether cellulose；Methyl cellulose ether, hydroxypropyl
Methyl cellulose ether；Methyl cellulose ether, ethoxyl methyl cellulose ether；Hydroxypropyl methyl cellulose ether, hydroxyethyl methyl are fine
The plain ether of dimension；Methyl cellulose ether, hydroxyethyl ether cellulose；Hydroxypropyl methyl cellulose ether, hydroxyethyl ether cellulose；Methyl cellulose
Plain ether, hydroxypropyl methyl cellulose ether；Hydroxypropyl methyl cellulose ether, ethoxyl methyl cellulose ether, hydroxyethyl ether cellulose；
Methyl cellulose ether, ethoxyl methyl cellulose ether, hydroxyethyl ether cellulose；Methyl cellulose ether, hydroxypropyl methyl cellulose
Ether, hydroxyethyl ether cellulose；Methyl cellulose ether, hydroxypropyl methyl cellulose ether, ethoxyl methyl cellulose ether；Methyl cellulose
Plain ether, hydroxypropyl methyl cellulose ether, ethoxyl methyl cellulose ether, hydroxyethyl ether cellulose.When cellulose ether is with a variety of
During raw material, combined for arbitrary mass ratio.
Include but not limited in embodiments above, obtained toy product, through different batches sampling 10, carry out water
Immersion, oil immersion bubble, 1m high concrete floor bottom plates drop 3 times, solid desktop continuously rubs, and 100 inferior experiments nothing is apparent to be damaged.
It is distinguished with above-described embodiment, finishing coat outer layer is also formed with glass sedimentary, and glass sedimentary is formed in finishing coat
On outer layer.
It is distinguished with above-described embodiment, glass sedimentary is sodium metasilicate alkaline aqueous solution brushing to the dried coat of paint
Surface obtains, glass sedimentary formed thickness for 0.5 micron (glass sedimentary formed thickness can also be include but not limited to as
Under it is any：0.54 micron, 0.6 micron, 0.62 micron, 0.7 micron, 0.78 micron, 0.8 micron and 0.5-0.8 microns).
Include but not limited in embodiments above, the obtained toy product with glass sedimentary, through different batches
Sampling 10 carries out water immersion, oil immersion bubble, 1m high concrete floor bottom plates drop 3 times, solid desktop continuously rubs 100 inferior examinations
The apparent damage of equal nothing is tested, and under conventional chambers environment, with general flame calcination 3min without apparent peeling and combustion phenomena.
This place embodiment is in place of the claimed non-limit of technical scope midrange and in embodiment technology
The new technical solution formed is replaced on an equal basis to single or multiple technical characteristics in scheme, equally all the present invention claims
In the range of protection；Simultaneously the present invention program it is all enumerate or unrequited embodiment in, in the same embodiment each
Parameter is merely representative of an example (i.e. a kind of feasible scheme) for its technical solution, and between parameters and is not present stringent
Cooperation and qualified relation, wherein each parameter can be replaced mutually when stating and asking without prejudice to axiom and the present invention, special declaration
Except.
The technical means disclosed in the embodiments of the present invention is not limited to the technical means disclosed in the above technical means, and is further included
By more than technical characteristic arbitrarily the formed technical solution of combination.The above is the specific embodiment of the present invention, should be referred to
Go out, for those skilled in the art, without departing from the principle of the present invention, can also make several
Improvements and modifications, these improvements and modifications are also considered as protection scope of the present invention.
Claims (6)
1. a kind of preparation method of toy train dome including body preparation, prime, mends ash, priming paint polishing, secondary bottom
Paint, finishing coat spraying and test package, wherein body preparation include sawing sheet, setting sanding, milling semicircle, groove milling, sanding and polishing, break
Material, punching and drum, it is characterised in that：The preparation method further includes the preparation of transition face layer, and the transition face layer is formed in
On the green body surface layer that body preparation obtains, the priming paint is formed in by prime on transition face layer, and the transition face layer is pressed
Include according to the raw material of parts by weight：100-120 parts of rubber, 50-80 parts of high-dispersion white carbon black, 10-20 parts of coupling agent, stearic acid 5-8
Part, 5-8 parts of activating agent, 1-3 parts of microwax, 1-3 parts of polyethylene glycol；
The finishing coat outer layer is also formed with glass sedimentary, and glass sedimentary is formed on finishing coat outer layer, which is
Sodium metasilicate alkaline aqueous solution brushing to dried japanning layer surface obtains, and it is 0.5-0.8 microns that glass sedimentary, which forms thickness,.
2. the preparation method of toy train dome according to claim 1, it is characterised in that：The preparation of the transition face layer
Including being kneaded, being molded, described be kneaded is by rubber, stearic acid, activating agent, microwax and polyethylene glycol, carries out mixing 50-60s,
Melting temperature is 90-200 DEG C, pressure 0.5-0.6Mpa, adds high-dispersion white carbon black and is kneaded 120-150s, melting temperature is
120-220 DEG C, pressure 0.45-0.58Mpa, wherein coupling agent are added in mixing.
3. the preparation method of toy train dome according to claim 2, it is characterised in that：It is even in the mixing process
Connection agent is at least added in two steps, and part of it mixes in advance with rubber, stearic acid, activating agent, microwax and polyethylene glycol, again
A part is pre-mixed with high-dispersion white carbon black.
4. the preparation method of toy train dome according to claim 1, it is characterised in that：The ash of mending is by ash material system
It is standby into after slurry, coated on workpiece, through polishing, the ash material includes the raw material of following parts by weight：Normal silicate
30~60 parts of cement, 10~30 parts of gypsum, 1~4 part of penetrant crystalline material, 1~4 part of rubber powder, 0~0.3 part of water-retaining agent and fiber
0.1~0.3 part.
5. the preparation method of toy train dome according to claim 4, it is characterised in that：The water-retaining agent is cellulose
Ether.
6. the preparation method of toy train dome according to claim 5, it is characterised in that：The cellulose ether be selected from
One kind or more in methyl cellulose ether, hydroxypropyl methyl cellulose ether, ethoxyl methyl cellulose ether, hydroxyethyl ether cellulose
Kind.