CN106116383A - A kind of environment protection tile gap filler - Google Patents
A kind of environment protection tile gap filler Download PDFInfo
- Publication number
- CN106116383A CN106116383A CN201610459696.3A CN201610459696A CN106116383A CN 106116383 A CN106116383 A CN 106116383A CN 201610459696 A CN201610459696 A CN 201610459696A CN 106116383 A CN106116383 A CN 106116383A
- Authority
- CN
- China
- Prior art keywords
- gap filler
- environment protection
- powder
- tile gap
- protection tile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of environment protection tile gap filler, by weight percentage, including following component: white cement 35 45%, building waste powder 30 40%, silica flour 0 15%, titanium dioxide 0 10%, polymer dispersion powder 5 10%, cellulose ether 1.5%, sodium silicate 1%, hydrophober 0.1%, ferrum oxide serial pigment 0 5%；The present invention, using white cement and building waste powder as primary raw material, not only increases gap filler early strength, meets working procedure requirement, and can deal carefully with building waste, reach the effect of environmental protection, decrease cost of manufacture simultaneously.
Description
Technical field
The present invention relates to building engineering field, refer in particular to a kind of environment protection tile gap filler.
Background technology
Ceramic Tiles has become one of the main building and ornament materials on inner-outer wall and floor, in order to avoid Ceramic Tiles and Ceramic Tiles
Between produce hollowing owing to expanding with heat and contract with cold, need reserved certain gap between Ceramic Tiles, and come with construction materials such as gap fillers
Filling gap；At present, main gap filler is portland cement, silica flour, methylcellulose, synthetic resin and antifungus agent
Deng, but these technology employ substantial amounts of industrial chemicals and mineral resources (i.e. base material), and the most not environmentally, production cost compares again
Height, does not meets the developing long-term strategy of country；Additionally, China's building waste annual emissions is more than 6.4 hundred million tons, the most substantial amounts of
Building waste directly fills if do not carried out dealing carefully with, and has both tied up soil, contaminant water soil resource and air ambient, has wasted again me
The mineral resources that state is valuable.
Summary of the invention
The invention aims to overcome the deficiencies in the prior art to provide a kind of environment protection tile gap filler, with white cement and
Building waste powder, as primary raw material, not only increases gap filler early strength, meets working procedure requirement, and can be to building
Rubbish is dealt carefully with, and reaches the effect of environmental protection, decreases cost of manufacture simultaneously.
For reaching above-mentioned purpose, the technical solution used in the present invention is: a kind of environment protection tile gap filler, with percentage by weight
Meter, including following component: white cement 35-45%, building waste powder 30-40%, silica flour 0-15%, titanium dioxide 0-10%,
Polymer dispersion powder 5-10%, cellulose ether 1.5%, sodium silicate 1%, hydrophober 0.1%, ferrum oxide serial pigment 0-5%.
Preferably, the particle diameter of described building waste powder is 800-1200 mesh.
Preferably, described white cement is that No. 42.5 white quick hardening sulphoaluminate cements or alumina content are more than 70%
White aluminate cement.
Preferably, described silica flour is dicalcium powder, and the particle diameter of described dicalcium powder and titanium dioxide is between 100 mesh-400 mesh.
Preferably, described cellulose ether is ethoxyl methyl cellulose ether or hydroxypropyl methyl cellulose ether.
Preferably, described hydrophober is powder organosilicon moisture repellent.
Due to the utilization of technique scheme, the present invention compared with prior art has the advantage that
Environment protection tile gap filler of the present invention, using white cement and building waste powder as primary raw material, not only improves
Gap filler early strength, meets working procedure requirement, and can deal carefully with building waste, reach the effect of environmental protection,
Decrease cost of manufacture simultaneously.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described in further detail.
Embodiment 1, environment protection tile gap filler of the present invention, by weight percentage, including following component: white cement
35%, building waste powder 40%, silica flour 8.5%, titanium dioxide 5%, polymer dispersion powder 10%, cellulose ether 1.5%, silicon
Acid sodium 1%, hydrophober 0.1%, ferrum oxide serial pigment 0%.
I.e. obtaining the gap filler of the present invention after above each component uniformly being mixed, after tested, the gap filler of the present invention is not only
Improve gap filler early strength, meet working procedure requirement, and building waste can be dealt carefully with, reach the effect of environmental protection
Really, decrease cost of manufacture 32% simultaneously.
Embodiment 2, environment protection tile gap filler of the present invention, by weight percentage, including following component: plain boiled water
Mud 40%, building waste powder 35%, silica flour 6%, titanium dioxide 8%, polymer dispersion powder 6%, cellulose ether 1.5%, silicon
Acid sodium 1%, hydrophober 0.1%, ferrum oxide serial pigment 3%.
I.e. obtaining the gap filler of the present invention after above each component uniformly being mixed, after tested, the gap filler of the present invention is not only
Improve gap filler early strength, meet working procedure requirement, and building waste can be dealt carefully with, reach the effect of environmental protection
Really, decrease cost of manufacture 30% simultaneously.
Embodiment 3, environment protection tile gap filler of the present invention, by weight percentage, including following component: white cement
45%, building waste powder 30%, silica flour 3%, titanium dioxide 10%, polymer dispersion powder 5%, cellulose ether 1.5%, silicic acid
Sodium 1%, hydrophober 0.1%, ferrum oxide serial pigment 5%.
I.e. obtaining the gap filler of the present invention after above each component uniformly being mixed, after tested, the gap filler of the present invention is not only
Improve gap filler early strength, meet working procedure requirement, and building waste can be dealt carefully with, reach the effect of environmental protection
Really, decrease cost of manufacture 28% simultaneously.
Below it is only the concrete exemplary applications of the present invention, protection scope of the present invention is not constituted any limitation.All employings
The technical scheme that equivalents or equivalence are replaced and formed, within the scope of all falling within rights protection of the present invention.
Claims (6)
1. an environment protection tile gap filler, it is characterised in that: by weight percentage, including following component: white cement 35-
45%, building waste powder 30-40%, silica flour 0-15%, titanium dioxide 0-10%, polymer dispersion powder 5-10%, cellulose
Ether 1.5%, sodium silicate 1%, hydrophober 0.1%, ferrum oxide serial pigment 0-5%.
Environment protection tile gap filler the most according to claim 1, it is characterised in that: the particle diameter of described building waste powder is
800-1200 mesh.
Environment protection tile gap filler the most according to claim 1, it is characterised in that: described white cement is that No. 42.5 whites are the hardest
Sulphate aluminium cement or the alumina content white aluminate cement more than 70%.
Environment protection tile gap filler the most according to claim 1, it is characterised in that: described silica flour is dicalcium powder, described heavy
The particle diameter of calcium powder and titanium dioxide is between 100 mesh-400 mesh.
Environment protection tile gap filler the most according to claim 1, it is characterised in that: described cellulose ether is that hydroxyethyl methyl is fine
Dimension element ether or hydroxypropyl methyl cellulose ether.
Environment protection tile gap filler the most according to claim 1, it is characterised in that: described hydrophober is powder organosilicon hydrophobic
Agent.