CN106116218B - 一种复配型混凝土轻质墙板早强减水剂 - Google Patents
一种复配型混凝土轻质墙板早强减水剂 Download PDFInfo
- Publication number
- CN106116218B CN106116218B CN201610471173.0A CN201610471173A CN106116218B CN 106116218 B CN106116218 B CN 106116218B CN 201610471173 A CN201610471173 A CN 201610471173A CN 106116218 B CN106116218 B CN 106116218B
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- wall panel
- reducing agent
- light wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种复配型混凝土轻质墙板早强减水剂，由以下重量份配比的各组分制成：聚羧酸减水剂30～35份、纳米硅藻土6～8份、三乙醇胺3～5份、二乙醇胺2～4份、氟硅酸镁3～5份、氧化镁4～6份、硫酸铁2～4份、十二烷基硫酸钠3～5份、水200～300份。本发明所公开的复配型混凝土轻质墙板早强减水剂具有高的抗压强度、低的收缩率和短的生产周期，可克服混凝土轻质墙板自然养护的缺陷，促进混凝土轻质墙板的发展。
Description
技术领域
本发明涉及一种复配型混凝土轻质墙板早强减水剂，属于建筑材料技术领域。
背景技术
墙板是建筑的重要组成部分之一，可分为传统的墙板和现代的墙板。传统的墙板主要是指采用砖、砌块、钢筋混凝土或预应力混凝土制成，虽然其施工简便、造价低，但自重较大，而且墙体的抗地震性能较差，墙板的保温、隔音、防水防潮能力较差，已难以满足现代建筑的要求；现代的墙板，主要是指由水泥、粉煤灰、聚乙烯醇、氯化镁、六篇磷酸钠、氧化镁、植物纤维等原料制成的混凝土轻质墙板，作为一种新型墙体材料，具有轻质、高强、保温、隔热、防火、防水、干缩率低、导热系数低、隔声性能好、安装造价低等优点，以其优异的性能适合于作内墙隔板或外墙板推广应用。
当前市场上的混凝土轻质墙板主要以蒸压加气混凝土墙板、泡沫混凝土墙板、陶粒混凝土墙板为主。尽管已被广泛应用在建筑物内，发展前景广阔，但混凝土轻质墙板因自然养护带来的缺陷制约其本身的发展。按一般规范规定，混凝土轻质墙板自然养护期不少于35天。虽经35天的自然养护，但混凝土的水化反应作用缓慢，水化反应并没有充分进行，由此产生混凝土轻质墙板的抗压强度差、收缩裂缝和生产周期长等，甚至还有可能影响正常使用。这在很大程度上制约了混凝土轻质墙板的发展。因此，需要寻找新的方法来克服混凝土轻质墙板的缺陷是非常重要的。
发明内容
针对上述现有技术中混凝土轻质墙板抗压强度差、收缩裂缝和生产周期长的不足，本发明所要解决的技术问题是提出了一种能有效地提高抗压强度、降低收缩率和缩短生产周期的复配型混凝土轻质墙板早强减水剂。
一种复配型混凝土轻质墙板早强减水剂，由以下重量份配比的各组分制成：聚羧酸减水剂30～35份、纳米硅藻土6～8份、三乙醇胺3～5份、二乙醇胺2～4份、氟硅酸镁3～5份、氧化镁4～6份、硫酸铁2～4份、十二烷基硫酸钠3～5份、水200～300份。
优选地，
一种复配型混凝土轻质墙板早强减水剂，由以下重量份配比的各组分制成：聚羧酸减水剂32份、纳米硅藻土7份、三乙醇胺4份、二乙醇胺3份、氟硅酸镁4份、氧化镁5份、硫酸铁3份、十二烷基硫酸钠4份、水250份。
所述的聚羧酸减水剂，由以下重量份配比的各组分制成：丙烯酸40～45份、甲基丙烯酸甲酯40～45份、丙烯酰胺5～9份、羟甲基丙烯酰胺15～20份、甲基丙烯磺酸钠3～5份、烯丙基聚乙二醇4～6份、烯丙醇聚氧烷基醚6～8份、木质素磺酸镁20～25份、纳米伊利石10～15份。
优选地，
所述的聚羧酸减水剂，由以下重量份配比的各组分制成：丙烯酸42份、甲基丙烯酸甲酯42份、丙烯酰胺7份、羟甲基丙烯酰胺18份、甲基丙烯磺酸钠4份、烯丙基聚乙二醇5份、烯丙醇聚氧烷基醚7份、木质素磺酸镁23份、纳米伊利石12份。
所述的纳米硅藻土、纳米伊利石的粒径为80～100nm；
在使用时，所述的早强减水剂占混凝土轻质墙板总重量的1～3％。
本发明的复配型混凝土轻质墙板早强减水剂的原理如下：
首先，由丙烯酸、甲基丙烯酸甲酯、丙烯酰胺、羟甲基丙烯酰胺、甲基丙烯磺酸钠、烯丙基聚乙二醇和烯丙醇聚氧烷基醚合成具有早强作用的丙烯酸系减水剂和甲基丙烯酸系减水剂，同时，这两种减水剂进行复配，得到新的减水剂；其次，木质素磺酸镁和纳米伊利石共同改性聚羧酸减水剂，改善其结构，使其性能更佳；然后，纳米硅藻土的加入，不仅起到进到进一步改性聚羧酸减水剂的作用，而且还起到诱导混凝土轻质墙板水化反应和改善水化产物的显微结构，从而提高混凝土轻质墙板的抗压强度和密实性，进而降低收缩率和缩短生产周期，同时还具有晶核的作用，在混凝土轻质墙板原有的网络结构的基础上，又建立了一个以纳米硅藻土为结点的新网络结构，两种网络结构相互结合，形成稳定的三维网络，大大地提高混凝土轻质墙板的性能，同时，还使混凝土轻质墙板具备自我修复功能，大大地减少裂纹等缺陷，延长寿命，提高安全性；最后，与有机早强剂(三乙醇胺和二乙醇胺)、无机早强剂(氟硅酸镁、氧化镁和硫酸铁)和表面活性剂(十二烷基硫酸钠)进行复配，得到复配型混凝土轻质墙板早强减水剂。
与现有技术相比，本发明的有益效果是：
首先，本发明的聚羧酸减水剂，不仅根据分子结构进行分子结构设计，而且还结合不同的减水剂复配原理，同时还结合木质素磺酸镁和纳米伊利石共同改性得到的；然后，本发明采用纳米矿物，相对比其他纳米材料，纳米硅藻土经济成本低，为混凝土轻质墙板的推广和应用提供了有力的基础；最后，本发明的早强减水剂能有效地提高混凝土轻质墙板的抗压强度、降低收缩率和缩短生产周期，促进混凝土轻质墙板的发展。
具体实施方式
本发明提供一种复配型混凝土轻质墙板早强减水剂，为使本发明的目的、技术方案及效果更加清楚、明确，以下对本发明进一步详细说明。
一种复配型混凝土轻质墙板早强减水剂，由以下重量份配比的各组分制成：聚羧酸减水剂30～35份、纳米硅藻土6～8份、三乙醇胺3～5份、二乙醇胺2～4份、氟硅酸镁3～5份、氧化镁4～6份、硫酸铁2～4份、十二烷基硫酸钠3～5份、水200～300份；
所述的聚羧酸减水剂，由以下重量份配比的各组分制成：丙烯酸40～45份、甲基丙烯酸甲酯40～45份、丙烯酰胺5～9份、羟甲基丙烯酰胺15～20份、甲基丙烯磺酸钠3～5份、烯丙基聚乙二醇4～6份、烯丙醇聚氧烷基醚6～8份、木质素磺酸镁20～25份、纳米伊利石10～15份。
所述的纳米硅藻土、纳米伊利石的粒径为80～100nm；
在使用时，所述的早强减水剂占混凝土轻质墙板总重量的1～3％。
实施例1
一种复配型混凝土轻质墙板早强减水剂，由以下重量份配比的各组分制成：聚羧酸减水剂32份、纳米硅藻土7份、三乙醇胺4份、二乙醇胺3份、氟硅酸镁4份、氧化镁5份、硫酸铁3份、十二烷基硫酸钠4份、水250份；
所述的聚羧酸减水剂，由以下重量份配比的各组分制成：丙烯酸42份、甲基丙烯酸甲酯42份、丙烯酰胺7份、羟甲基丙烯酰胺18份、甲基丙烯磺酸钠4份、烯丙基聚乙二醇5份、烯丙醇聚氧烷基醚7份、木质素磺酸镁23份、纳米伊利石12份。
实施例2
一种复配型混凝土轻质墙板早强减水剂，由以下重量份配比的各组分制成：聚羧酸减水剂30份、纳米硅藻土6份、三乙醇胺3份、二乙醇胺2份、氟硅酸镁3份、氧化镁4份、硫酸铁2份、十二烷基硫酸钠3份、水200份；
所述的聚羧酸减水剂，由以下重量份配比的各组分制成：丙烯酸40份、甲基丙烯酸甲酯40份、丙烯酰胺5份、羟甲基丙烯酰胺15份、甲基丙烯磺酸钠3份、烯丙基聚乙二醇4份、烯丙醇聚氧烷基醚6份、木质素磺酸镁20份、纳米伊利石10份。
实施例3
一种复配型混凝土轻质墙板早强减水剂，由以下重量份配比的各组分制成：聚羧酸减水剂35份、纳米硅藻土8份、三乙醇胺5份、二乙醇胺4份、氟硅酸镁5份、氧化镁6份、硫酸铁4份、十二烷基硫酸钠5份、水300份；
所述的聚羧酸减水剂，由以下重量份配比的各组分制成：丙烯酸45份、甲基丙烯酸甲酯45份、丙烯酰胺9份、羟甲基丙烯酰胺20份、甲基丙烯磺酸钠5份、烯丙基聚乙二醇6份、烯丙醇聚氧烷基醚8份、木质素磺酸镁25份、纳米伊利石15份。
对比例1
一种复配型混凝土轻质墙板早强减水剂，由以下重量份配比的各组分制成：聚羧酸减水剂32份、三乙醇胺4份、二乙醇胺3份、氟硅酸镁4份、氧化镁5份、硫酸铁3份、十二烷基硫酸钠4份、水250份；
所述的聚羧酸减水剂，由以下重量份配比的各组分制成：丙烯酸42份、甲基丙烯酸甲酯42份、丙烯酰胺7份、羟甲基丙烯酰胺18份、甲基丙烯磺酸钠4份、烯丙基聚乙二醇5份、烯丙醇聚氧烷基醚7份、木质素磺酸镁23份、纳米伊利石12份。
对比例2
一种复配型混凝土轻质墙板早强减水剂，由以下重量份配比的各组分制成：聚羧酸减水剂32份、纳米硅藻土7份、三乙醇胺4份、二乙醇胺3份、氟硅酸镁4份、氧化镁5份、硫酸铁3份、十二烷基硫酸钠4份、水250份；
所述的聚羧酸减水剂，由以下重量份配比的各组分制成：丙烯酸42份、甲基丙烯酸甲酯42份、丙烯酰胺7份、羟甲基丙烯酰胺18份、甲基丙烯磺酸钠4份、烯丙基聚乙二醇5份、烯丙醇聚氧烷基醚7份、木质素磺酸镁23份。
对比例3
一种复配型混凝土轻质墙板早强减水剂，由以下重量份配比的各组分制成：聚羧酸减水剂32份、三乙醇胺4份、二乙醇胺3份、氟硅酸镁4份、氧化镁5份、硫酸铁3份、十二烷基硫酸钠4份、水250份；
所述的聚羧酸减水剂，由以下重量份配比的各组分制成：丙烯酸42份、甲基丙烯酸甲酯42份、丙烯酰胺7份、羟甲基丙烯酰胺18份、甲基丙烯磺酸钠4份、烯丙基聚乙二醇5份、烯丙醇聚氧烷基醚7份、木质素磺酸镁23份。
对比例4
一种复配型混凝土轻质墙板早强减水剂，由以下重量份配比的各组分制成：聚羧酸减水剂32份、纳米硅藻土7份、三乙醇胺4份、二乙醇胺3份、氟硅酸镁4份、氧化镁5份、硫酸铁3份、十二烷基硫酸钠4份、水250份；
所述的聚羧酸减水剂，由以下重量份配比的各组分制成：甲基丙烯酸甲酯42份、丙烯酰胺7份、羟甲基丙烯酰胺18份、甲基丙烯磺酸钠4份、烯丙基聚乙二醇5份、烯丙醇聚氧烷基醚7份、木质素磺酸镁23份、纳米伊利石12份。
另外，为了说明本发明的性能效果，申请人进行了试验，试验结果如表1所示：
表1 复配型混凝土轻质墙板早强减水剂的主要性能检测结果
由表1可知，与现有技术相比，本发明具有高的抗压强度、小的收缩率和短的生产周期，这表明本发明所提供的复配型混凝土轻质墙板早强减水剂的效果显著。
当然，上面只是本发明优选的具体实施方式作了详细描述，并非以此限制本发明的实施范围，凡依本发明的原理、构造以及结构所作的等效变化，均应涵盖于本发明的保护范围内。
Claims (4)
1.一种复配型混凝土轻质墙板早强减水剂，其特征在于：由以下重量份配比的各组分制成：聚羧酸减水剂30～35份、纳米硅藻土6～8份、三乙醇胺3～5份、二乙醇胺2～4份、氟硅酸镁3～5份、氧化镁4～6份、硫酸铁2～4份、十二烷基硫酸钠3～5份、水200～300份，其中聚羧酸减水剂，由以下重量份配比的各组分制成：丙烯酸40～45份、甲基丙烯酸甲酯40～45份、丙烯酰胺5～9份、羟甲基丙烯酰胺15～20份、甲基丙烯磺酸钠3～5份、烯丙基聚乙二醇4～6份、烯丙醇聚氧烷基醚6～8份、木质素磺酸镁20～25份、纳米伊利石10～15份。
2.根据权利要求1所述的复配型混凝土轻质墙板早强减水剂，其特征在于：由以下重量份配比的各组分制成：聚羧酸减水剂32份、纳米硅藻土7份、三乙醇胺4份、二乙醇胺3份、氟硅酸镁4份、氧化镁5份、硫酸铁3份、十二烷基硫酸钠4份、水250份。
3.根据权利要求1所述的复配型混凝土轻质墙板早强减水剂，其特征在于：所述的聚羧酸减水剂，由以下重量份配比的各组分制成：所述的聚羧酸减水剂，由以下重量份配比的各组分制成：丙烯酸42份、甲基丙烯酸甲酯42份、丙烯酰胺7份、羟甲基丙烯酰胺18份、甲基丙烯磺酸钠4份、烯丙基聚乙二醇5份、烯丙醇聚氧烷基醚7份、木质素磺酸镁23份、纳米伊利石12份。
4. 根据权利要求1所述的复配型混凝土轻质墙板早强减水剂，其特征在于：所述的纳米硅藻土、纳米伊利石的粒径为80～100 nm。