CN106113880A - The preparation method of inorganic composite decorating board and inorganic composite decorating board - Google Patents
The preparation method of inorganic composite decorating board and inorganic composite decorating board Download PDFInfo
- Publication number
- CN106113880A CN106113880A CN201610385809.XA CN201610385809A CN106113880A CN 106113880 A CN106113880 A CN 106113880A CN 201610385809 A CN201610385809 A CN 201610385809A CN 106113880 A CN106113880 A CN 106113880A
- Authority
- CN
- China
- Prior art keywords
- paper
- inorganic composite
- wood pulp
- decorating board
- composite decorating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses preparation method and the inorganic composite decorating board of a kind of inorganic composite decorating board, prepare the method for above-mentioned inorganic composite decorating board and include following operation: allotment glue, wood pulp cellulose paper is impregnated with glue precuring, at all viscous pressure delta wood pulp fibres paper of substrate upper and lower surface, more viscous pressure decorative refractory slab on overstory pulp fibres paper.The inorganic composite decorating board utilizing said method to prepare steams without asbestos fibre element cement board as inorganic substrate with pressure, the upper and lower surface of inorganic substrate is respectively equipped with overstory pulp fibres paper and understorey pulp fibres paper, and overstory pulp fibres paper upper surface is provided with decorative refractory slab；Overstory pulp fibres paper and understorey pulp fibres paper are made by the delta wood pulp fibres paper that impregnated of glue, and decorative refractory slab is made up of the facing paper that impregnated of melmac.This inorganic composite decorating board is lightweight, intensity is high, good toughness, be unlikely to deform and rupture, and fire protection flame retarding, waterproof and dampproof and environmental protection, service life is long.
Description
Technical field
The invention belongs to technical field of construction and decoration materials, be specifically related to the preparation method of inorganic composite decorating board and inorganic
Composite decorating board.
Background technology
In building decoration and woodwork industry, decorative panel is widely applied, existing decorative panel mainly with marble,
Timber is main.
Hard and service life is long with the decorative panel material that marble prepares for material of main part, but marble slabs does not has
Plasticity, is easily broken in transportation；Additionally, marble slabs is heavy, it is not suitable for the decoration of high-altitude building；Secondly, greatly
Gypsum Fibrosum sheet material easily produces a large amount of dust in the course of processing, easily pollutes environment；Furthermore, marble slabs usually contains radiation
Property element, if applying in Furniture manufacture, has certain harm to human body.
It is that it is lightweight with the timber decorative panel major advantage that material prepares that is the theme, but this sheet material is the most fire-resistant and not
Waterproof.
Traditional PLASTIC LAMINATED with fire-proof function is mainly obtained by hundreds of layer of kraft paper and outside facing paper hot pressing, this plate
Although material has certain fire-proof function, but it is heavy, it is not easy to carrying；Additionally, outside after this sheet material life-time service
Facing paper easily comes off and ruptures, and service life is the longest.
Summary of the invention
It is an object of the invention to overcome disadvantages mentioned above present in prior art, it is provided that a kind of lightweight, fire protection flame retarding,
Waterproof and dampproof and the inorganic composite decorating board of environmental protection.
To achieve these goals, the preparation method of a kind of inorganic composite decorating board of the present invention includes following operation:
Allotment glue operation, with waterglass resin with add epistasis additive as raw material, stirs mixing plastic in the ratio of 1000:3
Water, this glue is in order to solve the problem that inorganic matter and Organic substance cannot the most stably bond, wherein silicic acid in waterglass resin
The content of sodium is 22-26%, and the content of phenolic resin is 28-32%；Adding and including mass fraction in epistasis additive is 24-28%
Silicon dioxde solution, the pure water of 18-22%.
After allotment glue operation, there is the impregnation operation of wood pulp cellulose paper and the viscous pressure operation of wood pulp cellulose paper, will
The wood pulp cellulose paper of 100g/ is immersed in glue, and in cement dipping machine, the speed with 12 ms/min carries out impregnation, makes wood pulp fine
Dimension paper is completely moistening to be impregnated with；Be covered with wood pulp cellulose paper on the two sides of inorganic compounding substrate, then by hot press pressure be 20Mpa,
Temperature is hot pressing 60 minutes at 140 DEG C.
It addition, between the impregnation operation and viscous pressure operation of wood pulp cellulose paper, also there is the precuring work of wood pulp cellulose paper
Sequence, in the precuring operation of wood pulp cellulose paper, enters the wood pulp cellulose paper after impregnation in the baking oven that temperature is 135 DEG C-145 DEG C
Row is dried, and drying rate is 15 ms/min, and in the wood pulp cellulose paper after making impregnation dry, the volatile quantity of moisture content is 5%-6%, thus
Precuring wood pulp cellulose paper.This operation makes wood pulp cellulose paper reach a kind of brittle state, and meanwhile, glue forms thin film.Pre-solid
Wood pulp cellulose paper after change is again by viscous pressure, under the effect of hot press, is achieved answering of inorganic substrate and wood pulp cellulose paper
Close, and do not come off.
Further, after the viscous pressure operation of wood pulp cellulose paper, also there is preparation section and the decoration of decorative refractory slab
The viscous pressure operation of refractory slab, in the preparation section of decorative refractory slab, is immersed in melmac by the facing paper of 100g/ molten
In liquid, impregnate with the speed of 15 ms/min in cement dipping machine, make facing paper moisten completely and be impregnated with；Gluing of decorative refractory slab
In pressure operation, after being glued pressure by wood pulp cellulose paper, it is covered with decorative refractory slab on the sheet material of gained, via hot press at pressure is
20Mpa, temperature are 60 minutes prepared inorganic composite decorating boards of hot pressing at 140 DEG C.
Preferably, melmac solution contains the tripolycyanamide of 40-50%, the formaldehyde of 40-50%.
A kind of inorganic composite decorating board, it is obtained by the preparation method of above-mentioned inorganic composite decorating board, and, this is inorganic
Composite decorating board includes inorganic compounding substrate, and inorganic compounding substrate steams without asbestos fibre element cement board for pressure.
Further, the upper and lower surface of inorganic compounding substrate is respectively equipped with overstory pulp fibres paper and lower floor's wood pulp
Fibrous paper, described overstory pulp fibres paper upper surface is provided with decorative refractory slab；Described overstory pulp fibres paper and lower floor's wood pulp are fine
Dimension paper is made by the delta wood pulp fibres paper that impregnated of glue, and described decorative refractory slab is by the dress that impregnated of melmac
Decorations paper is made.
Preferably, it is considered to the weight of inorganic composite decorating board and intensity thereof, the thickness of inorganic composite decorating board is designed as
5-31mm。
Further, it is considered to the manufacturing cost of inorganic composite decorating board, the thickness of inorganic substrate is designed as 4-30mm.
Further, overstory pulp fibres paper is made up of 2-8 layer wood pulp cellulose paper；Understorey pulp fibres paper is by 3-9 layer wood
Pulp fibres paper is made.
The invention has the beneficial effects as follows: inorganic composite decorating board of the present invention is compared to traditional PLASTIC LAMINATED, and it is thick
Degree is mainly steamed by pressure and determines without asbestos fibre element cement board, compared to the traditional PLASTIC LAMINATED prepared by hundreds of layer of kraft paper,
The inorganic composite decorating board of the present invention is lightweight；Pressure is steamed without having without asbestos, benzene and formaldehyde etc. in asbestos fibre element cement board
Pest matter, will not produce toxic gas or radiation during use；Steaming without asbestos fibre element cement board because of pressure is incombustible material,
Will not burn, even if toxic smog the most also will not be produced, not transmit flame, there is good fire retardant performance；This
Inorganic composite decorating board stable performance described in invention, the wet rate that rises, contract with dry rate are low, even if in the open or humid area also has relatively
Good waterproof, moistureproof, frost protection performance, has the weatherability of excellence, and service life is long.
Although inorganic composite decorating board lighter in weight of the present invention, but its intensity is high, good toughness, is unlikely to deform and breaks
Split；This decorative panel need not spray paint, easily hole when construction, dig the secondary operations such as limit, sawing, efficient and convenient；The present invention
Described inorganic composite decorating board heat conductivity is low, heat insulation, good heat insulating, can regulate temperature, increases environmental degree of comfort, again
Energy consumption can be reduced.
Based on above-mentioned plurality of advantages, inorganic composite decorating board of the present invention is widely used in market, hotel, writes
The indoor of the large-scale public places such as building, conference and exhibition center, airport and outdoor decoration.
Accompanying drawing explanation
For the technical scheme being illustrated more clearly that in the present invention, below embodiment is described used in accompanying drawing and attached
Icon is denoted as simply introducing.
Fig. 1 is the structural representation of the embodiment of the present invention.
Description of reference numerals: 1-substrate, 2-overstory pulp fibres paper, 3-understorey pulp fibres paper, 4-fancy fire-proof version.
Detailed description of the invention
In order to be further appreciated by the present invention, below in conjunction with the accompanying drawing in the embodiment of the present invention, in the embodiment of the present invention
Scheme is clearly and completely described.
With the inorganic composite decorating board of 10mm thickness as embodiment, the preparation method of inorganic composite decorating board includes following work
Sequence:
Allotment glue operation: with waterglass resin with add epistasis additive as raw material, stirs mixing plastic in the ratio of 1000:3
Water, wherein, in waterglass resin, the content of sodium silicate is 24%, and the content of phenolic resin is 30%；Add in epistasis additive and contain
Mass fraction is silicon dioxde solution, the pure water of 20% of 26%.
The impregnation operation of wood pulp cellulose paper: the wood pulp cellulose paper of 100g/ is immersed in glue, with 12 in cement dipping machine
M/min speed carry out impregnation, make that wood pulp cellulose paper is completely moistening to be impregnated with.
The precuring operation of wood pulp cellulose paper: again the wood pulp cellulose paper after impregnation is entered in the baking oven that temperature is 140 DEG C
Row is dried, and drying rate is 15 ms/min, and in the wood pulp cellulose paper after impregnation drying, the volatile quantity of moisture content is 5%-6%, thus in advance
Solidification wood pulp cellulose paper, makes the flowing glue curing of absorption on wood pulp cellulose paper form thin film.
The viscous pressure operation of wood pulp cellulose paper: steam without asbestos fibre element cement board for substrate 1, at inorganic substrate with 10mm pressure
The upper surface of 1 is covered with the wood pulp cellulose paper after 2 layers of precuring, then by hot press pressure be 20Mpa, temperature be heat at 140 DEG C
Press 60 minutes, form overstory pulp fibres paper 2, then the wood pulp cellulose after the lower surface of inorganic substrate 1 is covered with 2 layers of precuring
Paper, then by hot press pressure be 20Mpa, temperature be hot pressing 60 minutes at 140 DEG C, formed understorey pulp fibres paper 3.
The preparation section of decorative refractory slab: the facing paper of 100g/ is immersed in melmac solution, at impregnation
Machine impregnates with the speed of 15 ms/min, makes facing paper moisten completely and be impregnated with, above-mentioned melmac solution contains
The tripolycyanamide of 45%, the formaldehyde of 45% and the water of 10%.
The viscous pressure operation of decorative refractory slab: at the overstory pulp fibres of the sheet material by the viscous pressure operation gained of wood pulp cellulose paper
Paper 2 upper surface is covered with decorative refractory slab 4, via hot press pressure be 20Mpa, temperature be that at 140 DEG C, hot pressing 60 minutes prepares
The inorganic composite decorating board that 10mm is thick.
With sampling basic number for 1800, specification be the inorganic composite decorating board of 2440mm × 1220mm × 10mm be sample,
Carry out combustibility inspection by GB20286-2006 " public place fire-retardant product and assembly combustibility requirement and mark ", draw
Following assay:
Being shown by above-mentioned assay, specification is that the inorganic composite decorating board combustibility of 2440mm × 1220mm × 10mm meets
Not so the A level requirement of GB20286-2006 regulation.
From above-mentioned assay, the inorganic composite decorating board of the embodiment of the present invention is the non-combustible plate of fire protection flame retarding
Material, even if this inorganic composite decorating board also will not produce toxic smog in a fire.
Shown in Figure 1, the inorganic composite decorating board of the embodiment of the present invention includes inorganic substrate 1, and this inorganic substrate 1 is pressure
Steaming without asbestos fibre element cement board, the upper and lower surface of inorganic substrate 1 is respectively equipped with overstory pulp fibres paper 2 and lower floor
Wood pulp cellulose paper 3, wherein, overstory pulp fibres paper 2 upper surface is provided with decorative refractory slab 4.
Overstory pulp fibres paper 2 in the inorganic composite decorating board of the embodiment of the present invention and understorey pulp fibres paper 3 by
The delta wood pulp fibres paper that impregnated of glue is made, and decorative refractory slab 4 is made up of the facing paper that impregnated of melmac.
The thickness of the inorganic composite decorating board of said structure is controllable to 5-31mm.
With inorganic composite decorating board thick for 8.6mm as sample, the material property of this sample is tested, draw following inspection
Test result:
Being shown by the above results, the inorganic composite decorating board water absorption rate of the embodiment of the present invention is low, and boiling water resistance can be strong, xeothermic,
Under high humidity environment, dimensional stability is high, and surface dry heat resistance performance is strong, has weatherability and the water proofing property of excellence；Additionally, the present invention
The inorganic composite decorating board hardness of embodiment, intensity are high, good toughness, and impact resistance is unlikely to deform and ruptures；The embodiment of the present invention
The resistance to heating of inorganic composite decorating board, high temperature resistant contact with medicated cigarette or contact after, do not have naked light burning or glow, have stronger
Fire protecting performance.
It should be pointed out that, and be described above embodiments of the invention.But, art technology it is to be understood by the skilled artisans that
The present invention is not restricted to the described embodiments, and the principle that the present invention is simply described described in above-described embodiment, without departing from this
On the premise of invention scope, the present invention also has multiple changes and improvements, and these changes and improvements both fall within claimed this
In bright scope.
Claims (10)
1. a preparation method for inorganic composite decorating board, this inorganic composite decorating board is used for body of wall and the decoration on ground, also may be used
For woodwork industry etc., it is characterized in that the method includes following operation:
Allotment glue operation, with waterglass resin with add epistasis additive as raw material, stirs mixing plastic in the ratio of 1000:3
Water；
In above-mentioned waterglass resin, the content of sodium silicate is 22-26%, and the content of phenolic resin is 28-32%；Add epistasis additive
In include the pure water that mass fraction is the silicon dioxde solution of 24-28%, 18-22%.
The preparation method of inorganic composite decorating board the most according to claim 1, wherein, described allotment glue operation it
After, there is the impregnation operation of wood pulp cellulose paper and the viscous pressure operation of wood pulp cellulose paper, in the impregnation operation of described wood pulp cellulose paper,
Being immersed in glue by the wood pulp cellulose paper of 100g/, in cement dipping machine, the speed with 12 ms/min carries out impregnation, makes wood pulp
Fibrous paper is completely moistening to be impregnated with；In the viscous pressure operation of described wood pulp cellulose paper, it is covered with wood pulp cellulose paper on the two sides of inorganic substrate,
Again by hot press pressure be 20Mpa, temperature be hot pressing 60 minutes at 140 DEG C.
The preparation method of inorganic composite decorating board the most according to claim 2, wherein, in the impregnation operation of wood pulp cellulose paper
And between viscous pressure operation, also there is the precuring operation of wood pulp cellulose paper, and in the precuring operation of described wood pulp cellulose paper, will leaching
Wood pulp cellulose paper after glue is dried in the baking oven that temperature is 135 DEG C-145 DEG C, and drying rate is 15 ms/min, makes leaching
In wood pulp cellulose paper after glue drying, the volatile quantity of moisture content is 5%-6%, thus precuring wood pulp cellulose paper.
The preparation method of inorganic composite decorating board the most according to claim 3, wherein, in the viscous pressure operation of wood pulp cellulose paper
Afterwards, also there is the preparation section of decorative refractory slab and the viscous pressure operation of decorative refractory slab, the preparation work of described decorative refractory slab
In sequence, the facing paper of 100g/ is immersed in melmac solution, enters with the speed of 15 ms/min in cement dipping machine
Row dipping, makes facing paper moisten completely and is impregnated with；In the viscous pressure operation of described decorative refractory slab, institute after by the viscous pressure of wood pulp cellulose paper
Sheet material on be covered with decorative refractory slab, via hot press pressure be 20Mpa, temperature be that at 140 DEG C, hot pressing 60 minutes prepares
Inorganic composite decorating board.
The preparation method of inorganic composite decorating board the most according to claim 4, contains in described melmac solution
The tripolycyanamide of 40-50%, the formaldehyde of 40-50%.
6. an inorganic composite decorating board, it is by the preparation of the inorganic composite decorating board according to any one of claim 1-5
Method and obtain, and, this inorganic composite decorating board includes inorganic compounding substrate, described inorganic compounding substrate for pressure steam without asbestos fibre
Dimension element cement board.
Inorganic composite decorating board the most according to claim 6, wherein, the upper and lower surface of described inorganic compounding substrate
Being respectively equipped with overstory pulp fibres paper and understorey pulp fibres paper, described overstory pulp fibres paper upper surface is provided with fancy fire-proof
Plate；Described overstory pulp fibres paper and understorey pulp fibres paper are made by the delta wood pulp fibres paper that impregnated of glue, described
Decorative refractory slab is made up of the facing paper that impregnated of melmac.
A kind of inorganic composite decorating board the most according to claim 7, the thickness of described inorganic composite decorating board is 5-31mm.
A kind of inorganic composite decorating board the most according to claim 6, the thickness of described inorganic substrate is 4-30mm.
A kind of inorganic composite decorating board the most according to claim 7, described overstory pulp fibres paper is fine by 2-8 layer wood pulp
Dimension paper is made；Described understorey pulp fibres paper is made up of 3-9 layer wood pulp cellulose paper.