CN106085250A - Automobile-used paint surface care solution - Google Patents
Automobile-used paint surface care solution Download PDFInfo
- Publication number
- CN106085250A CN106085250A CN201610464738.2A CN201610464738A CN106085250A CN 106085250 A CN106085250 A CN 106085250A CN 201610464738 A CN201610464738 A CN 201610464738A CN 106085250 A CN106085250 A CN 106085250A
- Authority
- CN
- China
- Prior art keywords
- automobile
- care solution
- paint surface
- surface care
- used paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to organic chemistry filed, disclose a kind of automobile-used paint surface care solution.The present invention includes following components (mass percent): fatty alcohol-polyoxyethylene ether 4 10%, microwax 4 10%, dimethicone 3 5%, double (β ethoxy) coco amine 2 5% and nano titanium oxide 2 7%, surplus is water.The present invention uses simply, low cost, integrates cleaning car paint and waxes, having antistatic and anti-ultraviolet property.
Description
Technical field
The present invention relates to organic chemistry filed, particularly relate to a kind of automobile-used paint surface care solution.
Background technology
The existing product waxing car in market, substantially first car wash clean, is then coated with wax product, slightly until after carry out again
Wiping either manually or mechanically and reach the effect of waxing of light.Current carwash The Wash to be arrived of waxing is carried out, not only wave
Time-consuming, waste resource, and process is more complicated, relatively costly.Moreover, more existing car wax products contain poisonous organic
Solvent, had both injured car paint, and can injure again the healthy of operator.Car wax the most on the market is mostly solid wax, is beating
Bigger wax bits can be produced during wax, also cannot penetrate into car paint, thus persistency is poor.And, solid wax does not clean
The function of car paint.
Summary of the invention
The technical problem to be solved in the present invention is to provide and a kind of uses simple, low cost, collects cleaning car paint and wax in one
Body, has the automobile-used paint surface care solution of antistatic and anti-ultraviolet property.
For solving above-mentioned technical problem, the present invention adopts the following technical scheme that
The automobile-used paint surface care solution of the present invention, including following components (mass percent):
Fatty alcohol-polyoxyethylene ether 4-10%, microwax 4-10%, dimethicone 3-5%, double (beta-hydroxyethyl) cocos nucifera oil
Amine 2-5% and nano titanium oxide 2-7%, surplus is water.
The automobile-used paint surface care solution of the present invention, further, including following components (mass percent):
Surfactant 6%, microwax 6%, defoamer 3%, antistatic additive 2% and ultraviolet (UV) resistant agent 4%, surplus is
Water.
The automobile-used paint surface care solution of the present invention, further, uses following methods to be prepared from: by fatty alcohol-polyoxyethylene ether
Dissolve in the hot water of 80-90 DEG C, then by microwax, dimethicone, double (beta-hydroxyethyl) coco amine and nano titanium oxide
Water is preheated to 70-80 DEG C, dissolves in water successively, and mixing homogenizing gets product.
The automobile-used paint surface care solution of the present invention, further, after carwash, is sprayed onto car table lacquer painting by automobile-used paint surface care solution
On, to wipe even, usage amount is 5-10mL/m2。
The automobile-used paint surface care solution of the present invention compared with prior art, has the advantages that
The alternative automobile-used middle wax of the automobile-used paint surface care solution of the present invention, integrates cleaning and waxes, and easy to use, dosage form is
Water preparation, after carwash, it is only necessary to be uniformly sprayed to surface of vehicle paint, with soft cloth wiping, it is not necessary to uniform application, it is not necessary to wait dry
Dry, more without polishing, it is especially suitable for using when car owner oneself wipes car, greatly reduces the maintenance cost of automobile, save
The time of vehicle maintenance beauty treatment.The present invention automobile-used paint surface care solution detergency is better than existing car wax product, adheres on lacquer painting plate
Be difficult to wash the spot removed and have a stronger dissolubility, and can by soft cloth wiping time be quickly transferred in cleaning wiping cloth, upper
While wax forms protecting film, remove the pollutant of surface attachment.The automobile-used paint surface care solution of the present invention replaces car wax to use, and has
Excellent brightness, static electricity resistance and anti-ultraviolet property, is better than car wax product, and its basic physics performance all with existing city
Sell high-end car wax product close.
Detailed description of the invention
Preparation embodiment
Prepare the automobile-used paint surface care solution of the present invention in accordance with the following methods:
(1) get the raw materials ready: get the raw materials ready according to component proportion (mass percent) shown in table 1;
(2) fatty alcohol-polyoxyethylene ether is dissolved in the hot water of 80-90 DEG C, then by microwax, dimethicone, double
(beta-hydroxyethyl) coco amine and nano titanium oxide water are preheated to 70-80 DEG C, dissolve in water successively, and mixing homogenizing gets product.
The concrete amounts of components of embodiment prepared by table 1
Preparation 1 | Preparation 2 | Preparation 3 | Preparation 4 | Preparation 5 | |
Fatty alcohol-polyoxyethylene ether | 6 | 4 | 10 | 8 | 5 |
Microwax | 6 | 10 | 8 | 4 | 7 |
Dimethicone | 3 | 5 | 5 | 4 | 4 |
Double (beta-hydroxyethyl) coco amine | 2 | 3 | 5 | 4 | 2 |
Nano titanium oxide | 4 | 2 | 7 | 5 | 3 |
The automobile-used paint surface care solution that above-mentioned preparation embodiment prepares uniformly is sprayed onto on car table lacquer painting, wipes even, usage amount
For 5-10mL/m2。
Use owing to the automobile-used paint surface care solution of the present invention substitutes automobile-used middle wax, collection cleaning and waxing and one, therefore according to GB/
Relevant regulations in T 23437-2009 automobile polish, the automobile-used paint surface care solution preparing above-mentioned preparation embodiment is carried out
Basic performance test, concrete testing result is as shown in table 2.
Table 2 properties of product testing result
As shown in Table 2, the automobile-used paint surface care solution product stability that the inventive method prepares is good, does not has car surface film
Having any harmful effect, and upper photosensitiveness is preferable, is better than in standard the parameter index of regulation, the succedaneum as automobile-used middle wax makes
With, excellent performance.
Comparative example
Selection standard white car paint panel, every block specifications 200mm × 150mm, it is exposed to 30d in natural environment, then
Carry out simple hydroblasting and fine processing respectively, for fine processing, 1 matched group and 2 experimental grouies, matched group are set
Selecting the automobile-used paint surface care solution that above-mentioned preparation embodiment 1 prepares, experimental group 1 selects commercially available superfine black wax, and manufacturer is wide
Zhou Yongshang Automobile Products company limited, experimental group 2 selects commercially available Testudinis board entirely to imitate car wash water wax, in fine processing, by conditioning liquid
Or car wax is each according to using method wiping or wax, and then lacquer painting plate is carried out performance detection.
Using color measurement and color match instrument to measure its tristimulus values, data obtain luminance factor Y after processing, and are calculated cleaning rate such as
Shown in table 3.
The cleaning rate of each sample of table 3 comparative example
Matched group | Experimental group 1 | Experimental group 2 | |
Blank plate luminance factor value Y | 85.4 | 85.4 | 85.4 |
Luminance factor value Y before cleaning | 69.2 | 69.2 | 69.2 |
Luminance factor value Y after cleaning | 85.4 | 81.4 | 82.9 |
Cleaning rate % | 100 | 75.3 | 84.6 |
Owing to only the lacquer painting plate being covered with dirt having been carried out preliminary simple hydroblasting, do not carry out the most clear
Clean, as shown in Table 3, in the case of cleaning the most thoroughly, the automobile-used paint surface care solution that the present invention the prepares cleaning rate to lacquer painting
Apparently higher than commercially available existing car wax, illustrate the present invention automobile-used paint surface care solution strong detergency in common in-vehicle wax, owing to its dosage form is
Water preparation, spraying wiping uses, and attachment on lacquer painting plate is difficult to wash the spot removed stronger dissolubility and transitivity, non-
Often it is suitable for using when car owner oneself wipes car, strong detergency, easy to use.
According to the relevant regulations in GB/T 23437-2009 automobile polish, the glossiness recording car paint panel increases
Value is as shown in table 4.
The glossiness value added of each sample of table 4 comparative example
Matched group | Experimental group 1 | Experimental group 2 | |
Glossiness value added Gs | 23 | 22 | 19 |
As shown in Table 4, the glossiness value added using the lacquer painting plate of the automobile-used paint surface care solution of the present invention is special with commercial solid
Level black wax glossiness value added very nearly the same, be slightly better than commercially available car wash water wax, it is seen then that with solid black wax need waxing, dry,
The mode of operation of polishing is compared, and the automobile-used paint surface care solution of the present invention is easy to use, after carwash, it is only necessary to be uniformly sprayed to car paint table
Face, with soft cloth wiping, it is not necessary to dry, the step such as polishing, can car owner's Self-operating, the maintenance greatly reducing automobile becomes
This, save the time of vehicle maintenance beauty treatment.
According to test of correlation method and standard in GB/T13492-1992 " assorted automobile finish paint ", above-mentioned lacquer painting plate is entered
Row Fundamental Physical Properties is tested, and test result is as shown in table 5.
Table 5 comparative example each sample Fundamental Physical Properties is tested
Matched group | Experimental group 1 | Experimental group 2 | |
Gloss 60 ° | 93.7 | 91.2 | 88.4 |
Aberration △ E | 0.64 | 0.83 | 0.76 |
Adhesive force | 2 | 2 | 2 |
Pliability mm | 1 | 1 | 1 |
Hardness H | 3 | 3 | 3 |
As shown in Table 5, adhesive force, pliability and the hardness etc. of the automobile-used paint surface care solution of the present invention all with commercial cars wax product
Performance is similar, and before and after use, aberration is less, and color is natural, and glossiness is not less than commercial cars wax product, easy to use, it is not necessary to throw
Light, the automobile-used paint surface care solution of the present invention also has antistatic and anti-ultraviolet effect simultaneously.
Embodiment described above is only to be described the preferred embodiment of the present invention, the not model to the present invention
Enclose and be defined, on the premise of designing spirit without departing from the present invention, the those of ordinary skill in the art technical side to the present invention
Various deformation that case is made and improvement, all should fall in the protection domain that claims of the present invention determines.
Claims (4)
- The most automobile-used paint surface care solution, it is characterised in that: include following components (mass percent):Fatty alcohol-polyoxyethylene ether 4-10%, microwax 4-10%, dimethicone 3-5%, double (beta-hydroxyethyl) coco amine 2- 5% and nano titanium oxide 2-7%, surplus is water.
- Automobile-used paint surface care solution the most according to claim 1, it is characterised in that: include following components (mass percent):Surfactant 6%, microwax 6%, defoamer 3%, antistatic additive 2% and ultraviolet (UV) resistant agent 4%, surplus is water.
- Automobile-used paint surface care solution the most according to claim 1, it is characterised in that: use following methods to be prepared from: by fat Fat polyoxyethylenated alcohol dissolves in the hot water of 80-90 DEG C, then by microwax, dimethicone, double (beta-hydroxyethyl) coco amine Being preheated to 70-80 DEG C with nano titanium oxide water, dissolve in water successively, mixing homogenizing gets product.
- Automobile-used paint surface care solution the most according to claim 1, it is characterised in that: after carwash, by automobile-used paint surface care solution Being sprayed onto on car table lacquer painting, wipe even, usage amount is 5-10mL/m2。