CN106085027B - A kind of waterproof staining-proof coating and preparation method thereof - Google Patents
A kind of waterproof staining-proof coating and preparation method thereof Download PDFInfo
- Publication number
- CN106085027B CN106085027B CN201610450343.7A CN201610450343A CN106085027B CN 106085027 B CN106085027 B CN 106085027B CN 201610450343 A CN201610450343 A CN 201610450343A CN 106085027 B CN106085027 B CN 106085027B
- Authority
- CN
- China
- Prior art keywords
- parts
- triethanolamine
- waterproof
- staining
- methyl naphthalene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of waterproof staining-proof coatings and preparation method thereof, are prepared by the raw material of following parts by weight：Styrene-acrylic emulsion, 45~55 parts；107 glue, 10~20 parts；White cement, 6~12 parts；Bentonite, 1~3 part；Titanium dioxide, 8~14 parts；Powdered whiting, 10~14 parts；Talcum powder, 1~3 part；Emulsifier, 1~3 part；SN auxiliary agents, 2~4 parts；Antifoaming agent, 0.5~1.5 part；The weight ratio of totally 6~8 parts of triethanolamine and methyl naphthalene, the triethanolamine and methyl naphthalene is 5~7:1；Water, 10~14 parts.Waterproof staining-proof coating provided by the invention has excellent water permeability resistance and stain resistance, and water absorbing force is weak, and greasy dirt adhesive force is weak, and the exterior wall using the coating application is not in infiltration phenomenon, and is not easy sticking oil stain, even if sticking oil stain is also easy to wipe.
Description
Technical field
The invention belongs to building fields, and in particular to a kind of waterproof staining-proof coating and preparation method thereof.
Background technology
The coating used on external wall, drenches with rain with exposing to the weather, and in air, dust is liable to stick to coating for exposure
Surface layer, by one or two years, brand-new exterior coating will be dirty, and cleans inconvenience, in order to which beauty can only brush again, causes
The great wasting of resources.But stain-resistant exterior wall coating anti-fouling effect currently on the market is all less desirable.
It is necessary to develop a kind of high effect leakage proof water staining-proof coating.
Invention content
For overcome the deficiencies in the prior art, the purpose of the present invention is to provide a kind of waterproof staining-proof coating and its systems
Preparation Method improves the waterproof stain resistant of building.
The above-mentioned purpose of the present invention is achieved by following technical solution：
A kind of waterproof staining-proof coating, is made of the raw material of following parts by weight：Styrene-acrylic emulsion, 45~55 parts；107 glue
Water, 10~20 parts；White cement, 6~12 parts；Bentonite, 1~3 part；Titanium dioxide, 8~14 parts；Powdered whiting, 10~14 parts；
Talcum powder, 1~3 part；Emulsifier, 1~3 part；SN auxiliary agents, 2~4 parts；Antifoaming agent, 0.5~1.5 part；Triethanolamine and methyl naphthalene
Totally 6~8 parts, the weight ratio of the triethanolamine and methyl naphthalene is 5~7:1；Water, 10~14 parts.
Further, the waterproof staining-proof coating is made of following raw material：Styrene-acrylic emulsion, 50 parts；107
Glue, 15 parts；White cement, 9 parts；Bentonite, 2 parts；Titanium dioxide, 11 parts；Powdered whiting, 12 parts；Talcum powder, 2 parts；Emulsification
Agent, 2 parts；SN auxiliary agents, 3 parts；Antifoaming agent, 1 part；Totally 7 parts of triethanolamine and methyl naphthalene, the weight of the triethanolamine and methyl naphthalene
The ratio between part is 6:1；Water, 12 parts.
Further, the waterproof staining-proof coating is made of following raw material：Styrene-acrylic emulsion, 45 parts；107
Glue, 10 parts；White cement, 6 parts；Bentonite, 1 part；Titanium dioxide, 8 parts；Powdered whiting, 10 parts；Talcum powder, 1 part；Emulsifier,
1 part；SN auxiliary agents, 2 parts；Antifoaming agent, 0.5 part；Totally 6 parts of triethanolamine and methyl naphthalene, the weight of the triethanolamine and methyl naphthalene
The ratio between part is 5:1；Water, 10 parts.
Further, the waterproof staining-proof coating is made of following raw material：Styrene-acrylic emulsion, 55 parts；107
Glue, 20 parts；White cement, 12 parts；Bentonite, 3 parts；Titanium dioxide, 14 parts；Powdered whiting, 14 parts；Talcum powder, 3 parts；Emulsification
Agent, 3 parts；SN auxiliary agents, 4 parts；Antifoaming agent, 1.5 parts；Totally 8 parts of triethanolamine and methyl naphthalene, the weight of the triethanolamine and methyl naphthalene
It is 7 to measure the ratio between part:1；Water, 14 parts.
Further, the emulsifier is ethoxylated dodecyl alcohol, polyoxyethylene stearic acid ester or phenethyl xenol
It is one or more in polyoxyethylene ether.
Further, SN auxiliary agents are SN-640.
Further, antifoaming agent OTD.
The preparation method of above-mentioned waterproof staining-proof coating, includes the following steps：
By 107 glue, bentonite and water, in 80 DEG C of mixing in blending tank, stir evenly；It is cooled to room temperature, breast is added
Agent, SN auxiliary agents, white cement, titanium dioxide, powdered whiting and talcum powder, are further continued for stirring, then be ground；After grinding,
Styrene-acrylic emulsion, triethanolamine, methyl naphthalene and antifoaming agent is added, is further continued for stirring；It finally filters, packs.
Advantages of the present invention：
Waterproof staining-proof coating provided by the invention has excellent water permeability resistance and stain resistance, and water absorbing force is weak, oil
Dirty adhesive force is weak, and the exterior wall using the coating application is not in infiltration phenomenon, and is not easy sticking oil stain, even if sticking oil stain also holds very much
Easily erasing has substantive distinguishing features outstanding and significant progress compared with prior art.
Specific implementation mode
The essentiality content further illustrated the present invention with reference to embodiment, but present invention protection model is not limited with this
It encloses.Although being explained in detail to the present invention with reference to preferred embodiment, it will be understood by those of ordinary skill in the art that, it can be right
Technical scheme of the present invention is modified or replaced equivalently, without departing from the spirit and scope of technical solution of the present invention.
Embodiment 1：The preparation of waterproof staining-proof coating
Raw material proportioning：
Styrene-acrylic emulsion, 50 parts；107 glue, 15 parts；White cement, 9 parts；Bentonite, 2 parts；Titanium dioxide, 11 parts；Heavy carbonic acid
Calcium, 12 parts；Talcum powder, 2 parts；Emulsifier, 2 parts；SN auxiliary agents, 3 parts；Antifoaming agent, 1 part；Totally 7 parts of triethanolamine and methyl naphthalene, institute
The weight ratio for stating triethanolamine and methyl naphthalene is 6:1；Water, 12 parts.Emulsifier is ethoxylated dodecyl alcohol；SN auxiliary agents are
SN-640；Antifoaming agent is OTD antifoaming agent.It is weight part ratio.
Preparation method：
By 107 glue, bentonite and water, in 80 DEG C of mixing in blending tank, stir evenly；It is cooled to room temperature, breast is added
Agent, SN auxiliary agents, white cement, titanium dioxide, powdered whiting and talcum powder, are further continued for stirring, then be ground；After grinding,
Styrene-acrylic emulsion, triethanolamine, methyl naphthalene and antifoaming agent is added, is further continued for stirring；It finally filters, packs.
Embodiment 2：The preparation of waterproof staining-proof coating
Raw material proportioning：
Styrene-acrylic emulsion, 45 parts；107 glue, 10 parts；White cement, 6 parts；Bentonite, 1 part；Titanium dioxide, 8 parts；Heavy carbonic acid
Calcium, 10 parts；Talcum powder, 1 part；Emulsifier, 1 part；SN auxiliary agents, 2 parts；Antifoaming agent, 0.5 part；Totally 6 parts of triethanolamine and methyl naphthalene,
The weight ratio of the triethanolamine and methyl naphthalene is 5:1；Water, 10 parts.Emulsifier is polyoxyethylene stearic acid ester；SN auxiliary agents
For SN-640；Antifoaming agent is OTD antifoaming agent.It is weight part ratio.
Preparation method：
By 107 glue, bentonite and water, in 80 DEG C of mixing in blending tank, stir evenly；It is cooled to room temperature, breast is added
Agent, SN auxiliary agents, white cement, titanium dioxide, powdered whiting and talcum powder, are further continued for stirring, then be ground；After grinding,
Styrene-acrylic emulsion, triethanolamine, methyl naphthalene and antifoaming agent is added, is further continued for stirring；It finally filters, packs.
Embodiment 3：The preparation of waterproof staining-proof coating
Raw material proportioning：
Styrene-acrylic emulsion, 55 parts；107 glue, 20 parts；White cement, 12 parts；Bentonite, 3 parts；Titanium dioxide, 14 parts；Heavy carbon
Sour calcium, 14 parts；Talcum powder, 3 parts；Emulsifier, 3 parts；SN auxiliary agents, 4 parts；Antifoaming agent, 1.5 parts；Triethanolamine and methyl naphthalene totally 8
Part, the weight ratio of the triethanolamine and methyl naphthalene is 7:1；Water, 14 parts.Emulsifier is phenethyl biphenyl phenol polyethenoxy
Ether；SN auxiliary agents are SN-640；Antifoaming agent is OTD antifoaming agent.It is weight ratio.
Preparation method：
By 107 glue, bentonite and water, in 80 DEG C of mixing in blending tank, stir evenly；It is cooled to room temperature, breast is added
Agent, SN auxiliary agents, white cement, titanium dioxide, powdered whiting and talcum powder, are further continued for stirring, then be ground；After grinding,
Styrene-acrylic emulsion, triethanolamine, methyl naphthalene and antifoaming agent is added, is further continued for stirring；It finally filters, packs.
Embodiment 4：The preparation of waterproof staining-proof coating
Raw material proportioning：
Styrene-acrylic emulsion, 50 parts；107 glue, 15 parts；White cement, 9 parts；Bentonite, 2 parts；Titanium dioxide, 11 parts；Heavy carbonic acid
Calcium, 12 parts；Talcum powder, 2 parts；Emulsifier, 2 parts；SN auxiliary agents, 3 parts；Antifoaming agent, 1 part；Totally 7 parts of triethanolamine and methyl naphthalene, institute
The weight ratio for stating triethanolamine and methyl naphthalene is 5:1；Water, 12 parts.Emulsifier is ethoxylated dodecyl alcohol；SN auxiliary agents are
SN-640；Antifoaming agent is OTD antifoaming agent.It is weight part ratio.
Preparation method：
By 107 glue, bentonite and water, in 80 DEG C of mixing in blending tank, stir evenly；It is cooled to room temperature, breast is added
Agent, SN auxiliary agents, white cement, titanium dioxide, powdered whiting and talcum powder, are further continued for stirring, then be ground；After grinding,
Styrene-acrylic emulsion, triethanolamine, methyl naphthalene and antifoaming agent is added, is further continued for stirring；It finally filters, packs.
Embodiment 5：The preparation of waterproof staining-proof coating
Raw material proportioning：
Styrene-acrylic emulsion, 50 parts；107 glue, 15 parts；White cement, 9 parts；Bentonite, 2 parts；Titanium dioxide, 11 parts；Heavy carbonic acid
Calcium, 12 parts；Talcum powder, 2 parts；Emulsifier, 2 parts；SN auxiliary agents, 3 parts；Antifoaming agent, 1 part；Totally 7 parts of triethanolamine and methyl naphthalene, institute
The weight ratio for stating triethanolamine and methyl naphthalene is 7:1；Water, 12 parts.Emulsifier is ethoxylated dodecyl alcohol；SN auxiliary agents are
SN-640；Antifoaming agent is OTD antifoaming agent.It is weight part ratio.
Preparation method：
By 107 glue, bentonite and water, in 80 DEG C of mixing in blending tank, stir evenly；It is cooled to room temperature, breast is added
Agent, SN auxiliary agents, white cement, titanium dioxide, powdered whiting and talcum powder, are further continued for stirring, then be ground；After grinding,
Styrene-acrylic emulsion, triethanolamine, methyl naphthalene and antifoaming agent is added, is further continued for stirring；It finally filters, packs.
Embodiment 6：The weight ratio of comparative example, triethanolamine and methyl naphthalene is 4:1
Raw material proportioning：
Styrene-acrylic emulsion, 50 parts；107 glue, 15 parts；White cement, 9 parts；Bentonite, 2 parts；Titanium dioxide, 11 parts；Heavy carbonic acid
Calcium, 12 parts；Talcum powder, 2 parts；Emulsifier, 2 parts；SN auxiliary agents, 3 parts；Antifoaming agent, 1 part；Totally 7 parts of triethanolamine and methyl naphthalene, institute
The weight ratio for stating triethanolamine and methyl naphthalene is 4:1；Water, 12 parts.Emulsifier is ethoxylated dodecyl alcohol；SN auxiliary agents are
SN-640；Antifoaming agent is OTD antifoaming agent.It is weight part ratio.
Preparation method：
By 107 glue, bentonite and water, in 80 DEG C of mixing in blending tank, stir evenly；It is cooled to room temperature, breast is added
Agent, SN auxiliary agents, white cement, titanium dioxide, powdered whiting and talcum powder, are further continued for stirring, then be ground；After grinding,
Styrene-acrylic emulsion, triethanolamine, methyl naphthalene and antifoaming agent is added, is further continued for stirring；It finally filters, packs.
Embodiment 7：The weight ratio of comparative example, triethanolamine and methyl naphthalene is 8:1
Raw material proportioning：
Styrene-acrylic emulsion, 50 parts；107 glue, 15 parts；White cement, 9 parts；Bentonite, 2 parts；Titanium dioxide, 11 parts；Heavy carbonic acid
Calcium, 12 parts；Talcum powder, 2 parts；Emulsifier, 2 parts；SN auxiliary agents, 3 parts；Antifoaming agent, 1 part；Totally 7 parts of triethanolamine and methyl naphthalene, institute
The weight ratio for stating triethanolamine and methyl naphthalene is 8:1；Water, 12 parts.Emulsifier is ethoxylated dodecyl alcohol；SN auxiliary agents are
SN-640；Antifoaming agent is OTD antifoaming agent.It is weight part ratio.
Preparation method：
By 107 glue, bentonite and water, in 80 DEG C of mixing in blending tank, stir evenly；It is cooled to room temperature, breast is added
Agent, SN auxiliary agents, white cement, titanium dioxide, powdered whiting and talcum powder, are further continued for stirring, then be ground；After grinding,
Styrene-acrylic emulsion, triethanolamine, methyl naphthalene and antifoaming agent is added, is further continued for stirring；It finally filters, packs.
Embodiment 8：Effect example
Measure the compression strength and density of building brick prepared by Examples 1 to 7.As a result it see the table below：
| Test sample | Storage stability (day) | Water absorption rate (%) | Antifouling test film contact angle |
| Embodiment 1 | ＞ 180 | 0.8 | 140 |
| Embodiment 4 | ＞ 180 | 1.0 | 136 |
| Embodiment 5 | ＞ 180 | 1.0 | 137 |
| Embodiment 6 | ＜ 100 | 3.3 | 76 |
| Embodiment 7 | ＜ 100 | 3.2 | 73 |
The effect and embodiment 4,5 of embodiment 2,3 are almost the same.
Film contact angle is the important indicator for weighing low surface energy anti-fouling paint antifouling property, and contact angle is bigger to represent the material
The antifouling property of material is better.Upper table detection can be seen that：Waterproof staining-proof coating water absorption rate provided by the invention is low, film connects
Feeler is high, has excellent waterproof function and anti-pollution function.This performance characteristics of coating of the present invention may be in raw material three
Ethanol amine is related with the weight ratio of methyl naphthalene.
The effect of above-described embodiment indicates that the essentiality content of the present invention, but the protection of the present invention is not limited with this
Range.It will be understood by those of ordinary skill in the art that technical scheme of the present invention can be modified or replaced equivalently,
Without departing from the essence and protection domain of technical solution of the present invention.
Claims (7)
1. a kind of preparation method of waterproof staining-proof coating, it is characterised in that：By 10 ~ 20 part of 107 glue, 1 ~ 3 part of bentonite
It is stirred evenly in 80 DEG C of mixing in blending tank with 10 ~ 14 parts of water；It is cooled to room temperature, 1 ~ 3 part of emulsifier, 2 ~ 4 parts of SN is added
Auxiliary agent, 6 ~ 12 parts of white cements, 8 ~ 14 parts of titanium dioxides, 10 ~ 14 parts of powdered whitings and 1 ~ 3 part of talcum powder, are further continued for stirring, then
It is ground；After grinding, be added 45 ~ 55 parts of styrene-acrylic emulsions, 6 ~ 8 parts press triethanolamine and methyl naphthalene 5 ~ 7:1 weight ratio
Triethanolamine and methyl naphthalene and 0.5 ~ 1.5 part of antifoaming agent, are further continued for stirring；It finally filters, packs.
2. the preparation method of waterproof staining-proof coating according to claim 1, which is characterized in that by following parts by weight original
Material is made：Styrene-acrylic emulsion, 50 parts；107 glue, 15 parts；White cement, 9 parts；Bentonite, 2 parts；Titanium dioxide, 11 parts；Heavy carbonic acid
Calcium, 12 parts；Talcum powder, 2 parts；Emulsifier, 2 parts；SN auxiliary agents, 3 parts；Antifoaming agent, 1 part；Totally 7 parts of triethanolamine and methyl naphthalene, institute
The weight ratio for stating triethanolamine and methyl naphthalene is 6:1；Water, 12 parts.
3. the preparation method of waterproof staining-proof coating according to claim 1, which is characterized in that by following parts by weight original
Material is made：Styrene-acrylic emulsion, 45 parts；107 glue, 10 parts；White cement, 6 parts；Bentonite, 1 part；Titanium dioxide, 8 parts；Heavy carbonic acid
Calcium, 10 parts；Talcum powder, 1 part；Emulsifier, 1 part；SN auxiliary agents, 2 parts；Antifoaming agent, 0.5 part；Totally 6 parts of triethanolamine and methyl naphthalene,
The weight ratio of the triethanolamine and methyl naphthalene is 5:1；Water, 10 parts.
4. the preparation method of waterproof staining-proof coating according to claim 1, which is characterized in that by following parts by weight original
Material is made：Styrene-acrylic emulsion, 55 parts；107 glue, 20 parts；White cement, 12 parts；Bentonite, 3 parts；Titanium dioxide, 14 parts；Heavy carbonic acid
Calcium, 14 parts；Talcum powder, 3 parts；Emulsifier, 3 parts；SN auxiliary agents, 4 parts；Antifoaming agent, 1.5 parts；Totally 8 parts of triethanolamine and methyl naphthalene,
The weight ratio of the triethanolamine and methyl naphthalene is 7:1；Water, 14 parts.
5. according to the preparation method of any waterproof staining-proof coating of claim 1 ~ 4, it is characterised in that：The emulsification
Agent is one or more in ethoxylated dodecyl alcohol, polyoxyethylene stearic acid ester or phenethyl biphenyl phenol polyethenoxy ether.
6. according to the preparation method of any waterproof staining-proof coating of claim 1 ~ 4, it is characterised in that：SN auxiliary agents are
SN-640。
7. according to the preparation method of any waterproof staining-proof coating of claim 1 ~ 4, it is characterised in that：Antifoaming agent is
OTD。