CN105733371A - Anti-seepage contamination-resistant paint for construction and preparation method thereof - Google Patents
Anti-seepage contamination-resistant paint for construction and preparation method thereof Download PDFInfo
- Publication number
- CN105733371A CN105733371A CN201610262318.6A CN201610262318A CN105733371A CN 105733371 A CN105733371 A CN 105733371A CN 201610262318 A CN201610262318 A CN 201610262318A CN 105733371 A CN105733371 A CN 105733371A
- Authority
- CN
- China
- Prior art keywords
- parts
- butyl acrylate
- lauryl mercaptan
- defoamer
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses anti-seepage contamination-resistant paint for construction and a preparation method thereof.The paint is prepared from, by weight, 45-55 parts of ethylene propylene emulsion, 10-20 parts of 107 glue, 6-12 parts of white cement, 1-3 parts of bentonite, 8-14 parts of titanium dioxide, 10-14 parts of heavy calcium carbonate, 1-3 parts of talcum powder, 1-3 parts of an emulsification agent, 2-4 parts of SN auxiliaries, 0.5-1.5 parts of a defoaming agent, 2-4 parts of n-butyl acrylate and lauryl mercaptan and 10-14 parts of water, wherein the weight ratio of n-butyl acrylate to lauryl mercaptan is (1-3):1.The anti-seepage contamination-resistant paint for construction has excellent anti-seepage performance and contamination resistance, weak in water suction force and weak in greasy dirt adhesive force.When an outer wall is painted with the paint, the water seepage phenomenon will not occur, the outer wall is not likely to be contaminated by greasy dirt, and the greasy dirt can be easily wiped away even if the outer wall is contaminated by the greasy dirt.
Description
Technical field
The invention belongs to building field, be specifically related to impervious water staining-proof coating of a kind of building and preparation method thereof.
Background technology
The exploitation of building coating new product is always up the study hotspot of coating worker, and many R&D institutions and enterprise are devoted to development of new Functional Architectural Coatings in China.The coating used on external wall, drenches with rain along with exposing to the weather, and exposes in atmosphere, dust is liable to stick to coating top layer, and through one or two years, brand-new exterior coating will be dirty, and clean inconvenience, can only again brush in order to attractive in appearance, cause the great wasting of resources.
Stain-resistant exterior wall coating anti-fouling effect currently on the market is all less desirable, the fluorine-containing styrene-acrylic emulsion of existing one, improve film hydrophobicity, oleophobic property and compactness, the film spot in dry run making coating will not be sucked in film with moisture, even if film is stained with spot, also it is easy to when scrubbing wash spot, so that film has high-leveling and stain resistance;But owing to the price comparison of fluorochemical monomer is high, and kind is relatively fewer, causes the relatively costly of fluorine-containing styrene-acrylic emulsion.
Summary of the invention
In order to overcome the deficiencies in the prior art, it is an object of the invention to provide a kind of impervious water staining-proof coating and preparation method thereof of building, the impervious water stain resistant of raising building.
The above-mentioned purpose of the present invention is achieved by the techniques below scheme:
The impervious water staining-proof coating of a kind of building, is made up of following raw material: vinyl acetate emulsion, 45~55 parts;107 glue, 10~20 parts;White cement, 6~12 parts;Bentonite, 1~3 part;Titanium dioxide, 8~14 parts;Ground calcium carbonate, 10~14 parts;Pulvis Talci, 1~3 part;Emulsifying agent, 1~3 part;SN auxiliary agent, 2~4 parts;Defoamer, 0.5~1.5 part;N-butyl acrylate and lauryl mercaptan totally 2~4 parts, the weight ratio of n-butyl acrylate and lauryl mercaptan is 1~3:1;Water, 10~14 parts.
Further, described building impervious water staining-proof coating is made up of following raw material: vinyl acetate emulsion, 50 parts;107 glue, 15 parts;White cement, 9 parts;Bentonite, 2 parts;Titanium dioxide, 11 parts;Ground calcium carbonate, 12 parts;Pulvis Talci, 2 parts;Emulsifying agent, 2 parts;SN auxiliary agent, 3 parts;Defoamer, 1 part;N-butyl acrylate and lauryl mercaptan totally 3 parts, the weight ratio of described n-butyl acrylate and lauryl mercaptan is 2:1;Water, 12 parts.
Further, described building impervious water staining-proof coating is made up of following raw material: vinyl acetate emulsion, 45 parts;107 glue, 10 parts;White cement, 6 parts;Bentonite, 1 part;Titanium dioxide, 8 parts;Ground calcium carbonate, 10 parts;Pulvis Talci, 1 part;Emulsifying agent, 1 part;SN auxiliary agent, 2 parts;Defoamer, 0.5 part;N-butyl acrylate and lauryl mercaptan totally 2 parts, the weight ratio of described n-butyl acrylate and lauryl mercaptan is 1:1;Water, 10 parts.
Further, described building impervious water staining-proof coating is made up of following raw material: vinyl acetate emulsion, 55 parts;107 glue, 20 parts;White cement, 12 parts;Bentonite, 3 parts;Titanium dioxide, 14 parts;Ground calcium carbonate, 14 parts;Pulvis Talci, 3 parts;Emulsifying agent, 3 parts;SN auxiliary agent, 4 parts;Defoamer, 1.5 parts;N-butyl acrylate and lauryl mercaptan totally 4 parts, the weight ratio of described n-butyl acrylate and lauryl mercaptan is 3:1;Water, 14 parts.
Further, described emulsifying agent is one or more in polyoxyethylene lauryl ether, polyoxyethylene stearic acid ester or phenethyl xenol polyoxyethylene ether.
Further, SN auxiliary agent is SN-640.
Further, defoamer is OTD.
The preparation method of above-mentioned impervious water staining-proof coating, comprises the steps:
By 107 glue, bentonite and water, in 80 DEG C of mixing in blending tank, stir;After being down to room temperature, add emulsifying agent, SN auxiliary agent, white cement, titanium dioxide, ground calcium carbonate and Pulvis Talci, be further continued for stirring, be then ground;After grinding, add vinyl acetate emulsion, n-butyl acrylate, lauryl mercaptan and defoamer, be further continued for stirring;Finally filter, packaging.
Advantages of the present invention:
The impervious water staining-proof coating of building provided by the invention has water permeability resistance and the stain resistance of excellence, water absorbing force is weak, greasy dirt adhesive force is weak, the exterior wall using this coating application does not have infiltration phenomenon, and not easily sticking oil stain, even if sticking oil stain is also easy to erasing, compared with prior art there is prominent substantive distinguishing features and significant progressive.
Detailed description of the invention
Further illustrate the essentiality content of the present invention below in conjunction with embodiment, but do not limit scope with this.Although the present invention being explained in detail with reference to preferred embodiment, it will be understood by those within the art that, it is possible to technical scheme is modified or equivalent replacement, without deviating from the spirit and scope of technical solution of the present invention.
Embodiment 1: the preparation of impervious water staining-proof coating
Proportioning raw materials:
Vinyl acetate emulsion, 50 parts;107 glue, 15 parts;White cement, 9 parts;Bentonite, 2 parts;Titanium dioxide, 11 parts;Ground calcium carbonate, 12 parts;Pulvis Talci, 2 parts;Emulsifying agent, 2 parts;SN auxiliary agent, 3 parts;Defoamer, 1 part;N-butyl acrylate and lauryl mercaptan totally 3 parts, the weight ratio of described n-butyl acrylate and lauryl mercaptan is 2:1;Water, 12 parts.Emulsifying agent is polyoxyethylene lauryl ether;SN auxiliary agent is SN-640;Defoamer is OTD defoamer.It is weight part ratio.
Preparation method:
By 107 glue, bentonite and water, in 80 DEG C of mixing in blending tank, stir;After being down to room temperature, add emulsifying agent, SN auxiliary agent, white cement, titanium dioxide, ground calcium carbonate and Pulvis Talci, be further continued for stirring, be then ground;After grinding, add vinyl acetate emulsion, n-butyl acrylate, lauryl mercaptan and defoamer, be further continued for stirring;Finally filter, packaging.
Embodiment 2: the preparation of impervious water staining-proof coating
Proportioning raw materials:
Vinyl acetate emulsion, 45 parts;107 glue, 10 parts;White cement, 6 parts;Bentonite, 1 part;Titanium dioxide, 8 parts;Ground calcium carbonate, 10 parts;Pulvis Talci, 1 part;Emulsifying agent, 1 part;SN auxiliary agent, 2 parts;Defoamer, 0.5 part;N-butyl acrylate and lauryl mercaptan totally 2 parts, the weight ratio of described n-butyl acrylate and lauryl mercaptan is 1:1;Water, 10 parts.Emulsifying agent is polyoxyethylene stearic acid ester;SN auxiliary agent is SN-640;Defoamer is OTD defoamer.It is weight part ratio.
Preparation method:
By 107 glue, bentonite and water, in 80 DEG C of mixing in blending tank, stir;After being down to room temperature, add emulsifying agent, SN auxiliary agent, white cement, titanium dioxide, ground calcium carbonate and Pulvis Talci, be further continued for stirring, be then ground;After grinding, add vinyl acetate emulsion, n-butyl acrylate, lauryl mercaptan and defoamer, be further continued for stirring;Finally filter, packaging.
Embodiment 3: the preparation of impervious water staining-proof coating
Proportioning raw materials:
Vinyl acetate emulsion, vinyl acetate emulsion, 55 parts;107 glue, 20 parts;White cement, 12 parts;Bentonite, 3 parts;Titanium dioxide, 14 parts;Ground calcium carbonate, 14 parts;Pulvis Talci, 3 parts;Emulsifying agent, 3 parts;SN auxiliary agent, 4 parts;Defoamer, 1.5 parts;N-butyl acrylate and lauryl mercaptan totally 4 parts, the weight ratio of described n-butyl acrylate and lauryl mercaptan is 3:1;Water, 14 parts.Emulsifying agent is phenethyl xenol polyoxyethylene ether;SN auxiliary agent is SN-640;Defoamer is OTD defoamer.It is weight ratio.
Preparation method:
By 107 glue, bentonite and water, in 80 DEG C of mixing in blending tank, stir;After being down to room temperature, add emulsifying agent, SN auxiliary agent, white cement, titanium dioxide, ground calcium carbonate and Pulvis Talci, be further continued for stirring, be then ground;After grinding, add vinyl acetate emulsion, n-butyl acrylate, lauryl mercaptan and defoamer, be further continued for stirring;Finally filter, packaging.
Embodiment 4: the preparation of impervious water staining-proof coating
Proportioning raw materials:
Vinyl acetate emulsion, 50 parts;107 glue, 15 parts;White cement, 9 parts;Bentonite, 2 parts;Titanium dioxide, 11 parts;Ground calcium carbonate, 12 parts;Pulvis Talci, 2 parts;Emulsifying agent, 2 parts;SN auxiliary agent, 3 parts;Defoamer, 1 part;N-butyl acrylate and lauryl mercaptan totally 3 parts, the weight ratio of described n-butyl acrylate and lauryl mercaptan is 1:1;Water, 12 parts.Emulsifying agent is polyoxyethylene lauryl ether;SN auxiliary agent is SN-640;Defoamer is OTD defoamer.It is weight part ratio.
Preparation method:
By 107 glue, bentonite and water, in 80 DEG C of mixing in blending tank, stir;After being down to room temperature, add emulsifying agent, SN auxiliary agent, white cement, titanium dioxide, ground calcium carbonate and Pulvis Talci, be further continued for stirring, be then ground;After grinding, add vinyl acetate emulsion, n-butyl acrylate, lauryl mercaptan and defoamer, be further continued for stirring;Finally filter, packaging.
Embodiment 5: the preparation of impervious water staining-proof coating
Proportioning raw materials:
Vinyl acetate emulsion, 50 parts;107 glue, 15 parts;White cement, 9 parts;Bentonite, 2 parts;Titanium dioxide, 11 parts;Ground calcium carbonate, 12 parts;Pulvis Talci, 2 parts;Emulsifying agent, 2 parts;SN auxiliary agent, 3 parts;Defoamer, 1 part;N-butyl acrylate and lauryl mercaptan totally 3 parts, the weight ratio of described n-butyl acrylate and lauryl mercaptan is 3:1;Water, 12 parts.Emulsifying agent is polyoxyethylene lauryl ether;SN auxiliary agent is SN-640;Defoamer is OTD defoamer.It is weight part ratio.
Preparation method:
By 107 glue, bentonite and water, in 80 DEG C of mixing in blending tank, stir;After being down to room temperature, add emulsifying agent, SN auxiliary agent, white cement, titanium dioxide, ground calcium carbonate and Pulvis Talci, be further continued for stirring, be then ground;After grinding, add vinyl acetate emulsion, n-butyl acrylate, lauryl mercaptan and defoamer, be further continued for stirring;Finally filter, packaging.
The weight ratio of embodiment 6: comparative example, n-butyl acrylate and lauryl mercaptan is 0.5:1
Proportioning raw materials:
Vinyl acetate emulsion, 50 parts;107 glue, 15 parts;White cement, 9 parts;Bentonite, 2 parts;Titanium dioxide, 11 parts;Ground calcium carbonate, 12 parts;Pulvis Talci, 2 parts;Emulsifying agent, 2 parts;SN auxiliary agent, 3 parts;Defoamer, 1 part;N-butyl acrylate and lauryl mercaptan totally 3 parts, the weight ratio of described n-butyl acrylate and lauryl mercaptan is 0.5:1;Water, 12 parts.Emulsifying agent is polyoxyethylene lauryl ether;SN auxiliary agent is SN-640;Defoamer is OTD defoamer.It is weight ratio.
Preparation method:
By 107 glue, bentonite and water, in 80 DEG C of mixing in blending tank, stir;After being down to room temperature, add emulsifying agent, SN auxiliary agent, white cement, titanium dioxide, ground calcium carbonate and Pulvis Talci, be further continued for stirring, be then ground;After grinding, add vinyl acetate emulsion, n-butyl acrylate, lauryl mercaptan and defoamer, be further continued for stirring;Finally filter, packaging.
The weight ratio of embodiment 7: comparative example, n-butyl acrylate and lauryl mercaptan is 3.5:1
Proportioning raw materials:
Vinyl acetate emulsion, 50 parts;107 glue, 15 parts;White cement, 9 parts;Bentonite, 2 parts;Titanium dioxide, 11 parts;Ground calcium carbonate, 12 parts;Pulvis Talci, 2 parts;Emulsifying agent, 2 parts;SN auxiliary agent, 3 parts;Defoamer, 1 part;N-butyl acrylate and lauryl mercaptan totally 3 parts, the weight ratio of described n-butyl acrylate and lauryl mercaptan is 3.5:1;Water, 12 parts.Emulsifying agent is polyoxyethylene lauryl ether;SN auxiliary agent is SN-640;Defoamer is OTD defoamer.It is weight ratio.
Preparation method:
By 107 glue, bentonite and water, in 80 DEG C of mixing in blending tank, stir;After being down to room temperature, add emulsifying agent, SN auxiliary agent, white cement, titanium dioxide, ground calcium carbonate and Pulvis Talci, be further continued for stirring, be then ground;After grinding, add vinyl acetate emulsion, n-butyl acrylate, lauryl mercaptan and defoamer, be further continued for stirring;Finally filter, packaging.
Embodiment 8: effect example
Measure comprcssive strength and the density of the building brick of embodiment 1~7 preparation.
Result is shown in following table:
Test sample | Storage stability (my god) | Water absorption rate (%) | Antifouling test film contact angle |
Embodiment 1 | > 180 | 0.9 | 138 |
Embodiment 2 | > 180 | 1.2 | 135 |
Embodiment 3 | > 180 | 1.3 | 133 |
Embodiment 4 | > 180 | 1.0 | 135 |
Embodiment 5 | > 180 | 1.1 | 134 |
Embodiment 6 | < 100 | 3.0 | 74 |
Embodiment 7 | < 100 | 3.2 | 75 |
Film contact angle is the important indicator weighing low surface energy anti-fouling paint antifouling property, and contact angle is more big, and to represent the antifouling property of this material more good.The detection of upper table, it can be seen that impervious water staining-proof coating water absorption rate provided by the invention is low, film contact angle high, has impervious water function and the anti-pollution function of excellence.This performance characteristics of coating of the present invention is likely to relevant with the part by weight of n-butyl acrylate in raw material and lauryl mercaptan.
The effect of above-described embodiment indicates that the essentiality content of the present invention, but does not limit protection scope of the present invention with this.It will be understood by those within the art that, it is possible to technical scheme is modified or equivalent replacement, without deviating from essence and the protection domain of technical solution of the present invention.
Claims (8)
1. build impervious water staining-proof coating for one kind, it is characterised in that be prepared from by the raw material of following weight portion: vinyl acetate emulsion, 45~55 parts;107 glue, 10~20 parts;White cement, 6~12 parts;Bentonite, 1~3 part;Titanium dioxide, 8~14 parts;Ground calcium carbonate, 10~14 parts;Pulvis Talci, 1~3 part;Emulsifying agent, 1~3 part;SN auxiliary agent, 2~4 parts;Defoamer, 0.5~1.5 part;N-butyl acrylate and lauryl mercaptan totally 2~4 parts, the weight ratio of described n-butyl acrylate and lauryl mercaptan is 1~3:1;Water, 10~14 parts.
2. the impervious water staining-proof coating of building according to claim 1, it is characterised in that be made up of following raw material: vinyl acetate emulsion, 50 parts;107 glue, 15 parts;White cement, 9 parts;Bentonite, 2 parts;Titanium dioxide, 11 parts;Ground calcium carbonate, 12 parts;Pulvis Talci, 2 parts;Emulsifying agent, 2 parts;SN auxiliary agent, 3 parts;Defoamer, 1 part;N-butyl acrylate and lauryl mercaptan totally 3 parts, the weight ratio of described n-butyl acrylate and lauryl mercaptan is 2:1;Water, 12 parts.
3. the impervious water staining-proof coating of building according to claim 1, it is characterised in that be made up of following raw material: vinyl acetate emulsion, 45 parts;107 glue, 10 parts;White cement, 6 parts;Bentonite, 1 part;Titanium dioxide, 8 parts;Ground calcium carbonate, 10 parts;Pulvis Talci, 1 part;Emulsifying agent, 1 part;SN auxiliary agent, 2 parts;Defoamer, 0.5 part;N-butyl acrylate and lauryl mercaptan totally 2 parts, the weight ratio of described n-butyl acrylate and lauryl mercaptan is 1:1;Water, 10 parts.
4. the impervious water staining-proof coating of building according to claim 1, it is characterised in that be made up of following raw material: vinyl acetate emulsion, 55 parts;107 glue, 20 parts;White cement, 12 parts;Bentonite, 3 parts;Titanium dioxide, 14 parts;Ground calcium carbonate, 14 parts;Pulvis Talci, 3 parts;Emulsifying agent, 3 parts;SN auxiliary agent, 4 parts;Defoamer, 1.5 parts;N-butyl acrylate and lauryl mercaptan totally 4 parts, the weight ratio of described n-butyl acrylate and lauryl mercaptan is 3:1;Water, 14 parts.
5. according to the arbitrary described impervious water staining-proof coating of building of Claims 1 to 4, it is characterised in that: described emulsifying agent is one or more in polyoxyethylene lauryl ether, polyoxyethylene stearic acid ester or phenethyl xenol polyoxyethylene ether.
6. according to the arbitrary described impervious water staining-proof coating of building of Claims 1 to 4, it is characterised in that: SN auxiliary agent is SN-640.
7. according to the arbitrary described impervious water staining-proof coating of building of Claims 1 to 4, it is characterised in that: defoamer is OTD.
8. the preparation method of the arbitrary described impervious water staining-proof coating of Claims 1 to 4, it is characterised in that comprise the steps: 107 glue, bentonite and water, in 80 DEG C of mixing in blending tank, stir;After being down to room temperature, add emulsifying agent, SN auxiliary agent, white cement, titanium dioxide, ground calcium carbonate and Pulvis Talci, be further continued for stirring, be then ground;After grinding, add vinyl acetate emulsion, n-butyl acrylate, lauryl mercaptan and defoamer, be further continued for stirring;Finally filter, packaging.