CN106084948A - A kind of clear aqueous paint of bamboo plaited article - Google Patents
A kind of clear aqueous paint of bamboo plaited article Download PDFInfo
- Publication number
- CN106084948A CN106084948A CN201610604936.4A CN201610604936A CN106084948A CN 106084948 A CN106084948 A CN 106084948A CN 201610604936 A CN201610604936 A CN 201610604936A CN 106084948 A CN106084948 A CN 106084948A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- clear aqueous
- plaited article
- aqueous paint
- bamboo plaited
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of clear aqueous paint of bamboo plaited article, be made up of following raw material: Petropols, terpene resin, gum dammar, Polyethylene Glycol, polyvinyl alcohol, α cyanoacrylate, stearic acid, magnesium hydroxide, Chinese medicine extract.The clear aqueous paint of bamboo plaited article that the present invention provides, preparation is simple, easy to use, can reuse for a long time, cost-effective 12.6% after opening packaging, without formaldehyde, wear-resisting, difficult drop-off；Water paint safety non-toxic, environmental protection, it is ensured that health；Water paint is pale yellow transparent shape, does not change the natural colored of bamboo plaited article, can add any pigment, pure color as required；Adding flame-retardant composition, the heat resisting temperature improving water paint is 530 ~ 535 DEG C, after meeting naked light, postpones burning 12 ~ 15 seconds, reduces property and hazard to person；Carrying out antibacterial and mouldproof with plurality of Chinese extract, bacteriostasis rate reaches 93.4%, safety non-toxic, health environment-friendly, increases the pliability of bamboo cane.
Description
Technical field
The invention mainly relates to bamboo weaving technical field of coatings, particularly relate to a kind of clear aqueous paint of bamboo plaited article.
Background technology
Bamboo weaving, pandemic a kind of artifacts among the people, bamboo silk section used by bamboo weaving is all rectangle, in thickness thickness
Having strict demand, thickness to be only one or two hairline thickness, width also only has four or five hair width, and root root bamboo silk all passes through even
Cutter, reaches thickness uniform, and thickness is consistent, and braiding process needs tens procedures, all manual operationss, and onlooker gasp in admirations it invariably
Difficult.It is a requisite step at bamboo plaited article painting on surface.
The most traditional bamboo plaited article paint is nearly all paint, can cause and smear uneven phenomenon, need during use
Different component is now with the current, it is impossible to reuse, and there is the biggest toxicity, all can during producing, preserve and using
Harm body health, and can only simply isolate and beautification function, it is impossible to play antibacterial and mouldproof, soften heat-resisting effect
Really, accordingly, it would be desirable to a kind of bamboo plaited article dedicated transparent water paint, any pigment, safety and Health, green can be added as needed on
Environmental protection, easy to use.
Summary of the invention
In order to make up the defect of prior art, it is an object of the invention to provide a kind of clear aqueous paint of bamboo plaited article.
A kind of clear aqueous paint of bamboo plaited article, is made up of the raw material of following weight portion: Petropols 31 ~ 33, terpene resin
26 ~ 28, gum dammar 26 ~ 28, Polyethylene Glycol 22 ~ 24, polyvinyl alcohol 6 ~ 8, a-cyanoacrylate 4 ~ 6, stearic acid 4 ~ 6, hydrogen
Magnesium oxide 4 ~ 6, Chinese medicine extract 4 ~ 6.
Described Chinese medicine extract, is made up of the raw material of following weight ratio: houttuynine sodium bisulfite: β-cedrene: matrine: Azadirachta Indica A.
Element: rheum emodin: safrole: sesamin=12 ~ 14:12 ~ 14:11 ~ 13:11 ~ 13:11 ~ 13:7 ~ 9:7 ~ 9.
The preparation method of the clear aqueous paint of a kind of bamboo plaited article, specifically includes following steps:
(1) Polyethylene Glycol is added in Petropols, be heated to 70 ~ 75 DEG C, ultrasonic 20 ~ 25 minutes of 55 ~ 57kHz, add terpenes
Resin and gum dammar, mix homogeneously, add the distilled water of terpene resin equivalent, 80 ~ 85 DEG C, ultrasonic 25 ~ 35 points of 46 ~ 48kHz
Clock, obtains mixed resin solution；
(2) in magnesium hydroxide, add the distilled water of magnesium hydroxide weight 2 ~ 3 times amount, stir to after dissolving completely, add α-cyanogen
Base acrylate and stearic acid, 60 ~ 62 revs/min are stirred 20 ~ 25 minutes, must mix magnesium hydroxide solution；
(3) mixing magnesium hydroxide solution is added in mixed resin solution, mix homogeneously, add polyvinyl alcohol, be placed in 80 ~ 85
DEG C, ultrasonic 25 ~ 35 minutes of 46 ~ 48kHz, add Chinese medicine extract, 64 ~ 66 revs/min are stirred 15 ~ 20 minutes, and mix homogeneously is coated with
Smearing property is good, obtains the clear aqueous paint of bamboo plaited article；
(4) spray bottle packaging, obtains finished product.
The using method of the clear aqueous paint of described bamboo plaited article, opens packaging, is uniformly sprayed by clear aqueous for bamboo plaited article paint
It is applied to bamboo cane or bamboo plaited article surface, it is possible to bamboo cane or bamboo plaited article are dipped in the clear aqueous paint of bamboo plaited article after 8 ~ 10 minutes
Take out, japanning be placed on temperature be 48 ~ 50 DEG C, humidity be 73 ~ 75% warehouse in be dried, firm pasting, do not fall off.
The invention have the advantage that the clear aqueous paint of a kind of bamboo plaited article that the present invention provides, preparation is simple, easy to use,
Can reuse for a long time after opening packaging, cost-effective 12.6%, without formaldehyde, wear-resisting, difficult drop-off；Each composition of water paint
Safety non-toxic, will not discharge toxic gas, environmental protection, it is ensured that health；Water paint is pale yellow transparent shape, will not change bamboo
The natural colored of establishment product, can add any pigment as required, and pigment will not be made to produce color and luster change, pure color；Add
Flame-retardant composition, the heat resisting temperature improving water paint is 530 ~ 535 DEG C, meets after naked light, postpones burning 12 ~ 15 seconds, reduce property and
Hazard to person；Carrying out antibacterial and mouldproof with plurality of Chinese extract, bacteriostasis rate reaches 93.4%, safety non-toxic, health environment-friendly, increases bamboo
The pliability of bar.
Detailed description of the invention
With specific embodiment, the present invention is described below.
Embodiment 1
A kind of clear aqueous paint of bamboo plaited article, is made up of the raw material of following weight portion: Petropols 31, terpene resin 26, Da Ma
Resin 26, Polyethylene Glycol 22, polyvinyl alcohol 6, a-cyanoacrylate 4, stearic acid 4, magnesium hydroxide 4, Chinese medicine extract 4.
Described Chinese medicine extract, is made up of the raw material of following weight ratio: houttuynine sodium bisulfite: β-cedrene: matrine: Azadirachta Indica A.
Element: rheum emodin: safrole: sesamin=12:12:11:11:11:7:7.
The preparation method of the clear aqueous paint of a kind of bamboo plaited article, specifically includes following steps:
(1) Polyethylene Glycol is added in Petropols, be heated to 75 DEG C, ultrasonic 25 minutes of 55kHz, add terpene resin and Da Ma
Resin, mix homogeneously, add the distilled water of terpene resin equivalent, 85 DEG C, ultrasonic 35 minutes of 48kHz, obtain mixed resin solution；
(2) in magnesium hydroxide, add the distilled water of magnesium hydroxide weight 3 times amount, stir to after dissolving completely, add alpha-cyano
Acrylate and stearic acid, 62 revs/min are stirred 25 minutes, must mix magnesium hydroxide solution；
(3) mixing magnesium hydroxide solution is added in mixed resin solution, mix homogeneously, adds polyvinyl alcohol, be placed in 85 DEG C,
Ultrasonic 35 minutes of 48kHz, adds Chinese medicine extract, and 66 revs/min are stirred 20 minutes, obtain the clear aqueous paint of bamboo plaited article；
(4) spray bottle packaging, obtains finished product.
The using method of the clear aqueous paint of described bamboo plaited article, opens packaging, is uniformly sprayed by clear aqueous for bamboo plaited article paint
It is applied to bamboo cane or bamboo plaited article surface, it is possible to bamboo cane or bamboo plaited article are dipped in the clear aqueous paint of bamboo plaited article and take after 10 minutes
Go out, japanning be placed on temperature be 50 DEG C, humidity be 75% warehouse in be dried, firm pasting, do not fall off.
Embodiment 2
A kind of clear aqueous paint of bamboo plaited article, is made up of the raw material of following weight portion: Petropols 32, terpene resin 27, Da Ma
Resin 27, Polyethylene Glycol 23, polyvinyl alcohol 7, a-cyanoacrylate 5, stearic acid 5, magnesium hydroxide 5, Chinese medicine extract 5.
Described Chinese medicine extract, is made up of the raw material of following weight ratio: houttuynine sodium bisulfite: β-cedrene: matrine: Azadirachta Indica A.
Element: rheum emodin: safrole: sesamin=13:13:12:12:12:8:8.
Preparation and application, with embodiment 1.
Embodiment 3
A kind of clear aqueous paint of bamboo plaited article, is made up of the raw material of following weight portion: Petropols 33, terpene resin 28, Da Ma
Resin 28, Polyethylene Glycol 24, polyvinyl alcohol 8, a-cyanoacrylate 6, stearic acid 6, magnesium hydroxide 6, Chinese medicine extract 6.
Described Chinese medicine extract, is made up of the raw material of following weight ratio: houttuynine sodium bisulfite: β-cedrene: matrine: Azadirachta Indica A.
Element: rheum emodin: safrole: sesamin=14:14:13:13:13:9:9.
Preparation and application, with embodiment 1.
Comparative example
Existing bamboo plaited article paint.
Embodiment and the index evaluation of comparative example bamboo plaited article paint:
Respectively the bamboo plaited article paint of embodiment and comparative example is used for identical bamboo plaited article, after japanning completes, to bamboo plaited article
Surface lacquer is tested, and the index evaluation of embodiment and comparative example bamboo plaited article paint is shown in Table 1.
Table 1: embodiment and the index evaluation of comparative example bamboo plaited article paint
| Project | Embodiment | Comparative example |
| Heat resistance is/(DEG C) | 530~535 | 470~480 |
| Postpone burning time/(second) | 12~15 | 0~3 |
| Bacteriostasis rate/(%) | 93.4 | 24.6 |
| Pliability improves/(%) | 6.7 | — |
| Cost-effective/(%) | 12.6 | — |
Note: " " indicate without.
The result of table 1 shows, the clear aqueous paint of embodiment bamboo plaited article, the heat resisting temperature improving straw products is 530 ~
535 DEG C, postponing burning time is 12 ~ 15 seconds, and bacteriostasis rate reaches 93.4%, hence it is evident that higher than comparative example, and pliability improves 6.7%, saves
Cost 12.6%, illustrates that the clear aqueous paint of bamboo plaited article that the present invention provides has preferable using effect.
Claims (4)
1. the clear aqueous paint of bamboo plaited article, it is characterised in that be made up of the raw material of following weight portion: Petropols 31 ~ 33,
Terpene resin 26 ~ 28, gum dammar 26 ~ 28, Polyethylene Glycol 22 ~ 24, polyvinyl alcohol 6 ~ 8, a-cyanoacrylate 4 ~ 6, tristearin
Acid 4 ~ 6, magnesium hydroxide 4 ~ 6, Chinese medicine extract 4 ~ 6.
The most according to claim 1, the clear aqueous paint of bamboo plaited article, it is characterised in that described Chinese medicine extract, by following
The raw material composition of weight ratio: houttuynine sodium bisulfite: β-cedrene: matrine: nimbin: rheum emodin: safrole: sesamin=12 ~ 14:
12~14:11~13:11~13:11~13:7~9:7~9。
The preparation method of the clear aqueous paint of bamboo plaited article the most according to claim 1, it is characterised in that specifically include following step
Rapid:
(1) Polyethylene Glycol is added in Petropols, be heated to 70 ~ 75 DEG C, ultrasonic 20 ~ 25 minutes of 55 ~ 57kHz, add terpenes
Resin and gum dammar, mix homogeneously, add the distilled water of terpene resin equivalent, 80 ~ 85 DEG C, ultrasonic 25 ~ 35 points of 46 ~ 48kHz
Clock, obtains mixed resin solution；
(2) in magnesium hydroxide, add the distilled water of magnesium hydroxide weight 2 ~ 3 times amount, stir to after dissolving completely, add α-cyanogen
Base acrylate and stearic acid, 60 ~ 62 revs/min are stirred 20 ~ 25 minutes, must mix magnesium hydroxide solution；
(3) mixing magnesium hydroxide solution is added in mixed resin solution, mix homogeneously, add polyvinyl alcohol, be placed in 80 ~ 85
DEG C, ultrasonic 25 ~ 35 minutes of 46 ~ 48kHz, add Chinese medicine extract, 64 ~ 66 revs/min are stirred 15 ~ 20 minutes, obtain bamboo plaited article
Clear aqueous paint；
(4) spray bottle packaging, obtains finished product.
4. according to the using method of the clear aqueous paint of bamboo plaited article described in claim 1 ~ 3, it is characterised in that open packaging, will
Bamboo plaited article clear aqueous paint even application is in bamboo cane or bamboo plaited article surface, it is possible to bamboo cane or bamboo plaited article are dipped in bamboo weaving system
The clear aqueous paint of product took out after 8 ~ 10 minutes, japanning be placed on temperature be 48 ~ 50 DEG C, humidity be 73 ~ 75% warehouse in carry out
It is dried.