CN106084295A - A kind of Multifunctional plastic additive and preparation method thereof - Google Patents
A kind of Multifunctional plastic additive and preparation method thereof Download PDFInfo
- Publication number
- CN106084295A CN106084295A CN201610741466.6A CN201610741466A CN106084295A CN 106084295 A CN106084295 A CN 106084295A CN 201610741466 A CN201610741466 A CN 201610741466A CN 106084295 A CN106084295 A CN 106084295A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- phthalate
- standby
- plastic additive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
nullThe open a kind of Multifunctional plastic additive of the present invention，It is made up of the raw material of following parts by weight proportioning: dioctyl phthalate 18 25 parts、BBP(Butyl Benzyl Phthalate 10 15 parts、Dibutyl phthalate 8 10 parts、Phosphite 13 15 parts、Sulfydryl acid esters 10 15 parts、Mica powder 6 10 parts、Silica flour 8 13 parts、47 parts of carbon fiber、Three monooctyl esters 24 parts、Benzotriazole 10 15 parts、Salicylate 20 25 parts、Aluminium hydroxide 4 10 parts、Nano titanium oxide 69 parts、Ethoxylated alkyl polyamines 13 16 parts、Alkyl trimethyl quaternary ammonium 17 20 parts、The cruel amine of ethyoxyl Laurel 5 10 parts、8 copper quinolinates 24 parts、Sodium fluoride 13 17 parts and methyl-silicone oil 26 parts，The Multifunctional plastic additive of the present invention has anti-oxidation function，Electrostatic can be made to leak in time，The demoulding of plastics can be facilitated.
Description
Technical field
The present invention relates to a kind of Multifunctional plastic additive and preparation method thereof.
Background technology
Plastic additive is again plastic additive, is that polymer (synthetic resin) is shaped adding man-hour for improving its processability
Can or by improve the performance of resin own deficiency and some compounds that must add.Such as, in order to reduce Corvic
Forming temperature, make goods soft and the plasticizer that adds；And for example in order to prepare light weight, antivibration, heat insulation, the foam plastic of sound insulation
Expect and foaming agent to be added；The heat decomposition temperature of some plastics with processing and forming temperature closely, is just added without heat stabilizer
Cannot molding.Thus, plastic additive occupies the status of particular importance in plastics processing.For plastics processing product
One big analog assistant, including plasticizer, heat stabilizer, antioxidant, light stabilizer, fire retardant, foaming agent, antistatic additive, antifungus agent,
Coloring agent and brightening agent (see pigment), filler, coupling agent, lubricant, releasing agent etc..Wherein coloring agent, brightening agent and filling
Agent is not plastics specialty chemicals, but general compounding ingredient.
Plastic additive is as the indispensable composition of general-purpose plastics through engineering approaches, engineering plastics high performance and synthetic resin
Modification realizes the key of functionalization, and the Eleventh Five-Year Plan period, the development of the whole industry is concentrated mainly on the large-scale production of general kind,
Seldom see that structural innovation product occurs, produce simultaneously and mostly use overseas enterprise's patented technology, so, high performance green
Color, environmental protection, the research and development of plastic additive nontoxic, efficient and production have become the main attack side of following China Plastics Additives development
To.Plasticizer to improve non-phthalate yield, such as epoxy soybean oil, trimellitic acid esters;Stabilizer should reduce lead
Salt ratio, improves calcium/zinc complex class, low lead terres rares, hydrotalcite and organic heat stabilizers yield;Fire retardant should reduce
Halogen ratio, greatly develops inorganic combustion inhibitor.The environmental regulation of European Union to be responded actively, and both at home and abroad to without poison ring
Protect the requirement of product.Plastic additive enterprise should join together to change unreasonable product structure, exploitation with colleges and universities, scientific research institutions
Environment-friend auxiliaries kind.
Current existing plastic additive does not have anti-oxidation function, it is not possible to make electrostatic leak in time, it is impossible to enough conveniently mould
The demoulding of material.
Summary of the invention
The technical problem to be solved in the present invention is to provide one and has anti-oxidation function, electrostatic can be made to leak in time, energy
Enough facilitate the Multifunctional plastic additive of the demoulding of plastics.
For solving the problems referred to above, the present invention adopts the following technical scheme that
A kind of Multifunctional plastic additive, is made up of the raw material of following parts by weight proportioning: dioctyl phthalate 18-25 part,
BBP(Butyl Benzyl Phthalate 10-15 part, dibutyl phthalate 8-10 part, phosphite 13-15 part, sulfydryl acid esters 10-15
Part, mica powder 6-10 part, silica flour 8-13 part, carbon fiber 4-7 part, three monooctyl ester 2-4 parts, benzotriazole 10-15 part, salicylate
20-25 part, aluminium hydroxide 4-10 part, nano titanium oxide 6-9 part, ethoxylated alkyl polyamines 13-16 part, alkyl trimethyl season
Ammonium 17-20 part, ethyoxyl Laurel cruel amine 5-10 part, copper 8-quinolinolate 2-4 part, sodium fluoride 13-17 part and methyl-silicone oil 2-6
Part.
Further, it is made up of the raw material of following parts by weight proportioning: dioctyl phthalate 18 parts, phthalic acid
Butyl benzyl 10 parts, dibutyl phthalate 8 parts, phosphite 13 parts, sulfydryl acid esters 10 parts, mica powder 6 parts, silica flour 8 parts,
4 parts of carbon fiber, three monooctyl ester 2 parts, benzotriazole 10 parts, salicylate 20 parts, aluminium hydroxide 4 parts, nano titanium oxide 6 parts, second
Epoxide alkyl polyamine 13 parts, alkyl trimethyl quaternary ammonium 17 parts, the cruel amine of ethyoxyl Laurel 5 parts, copper 8-quinolinolate 2 parts, fluorination
13 parts of sodium and methyl-silicone oil 2 parts.
Further, it is made up of the raw material of following parts by weight proportioning: dioctyl phthalate 21.5 parts, O-phthalic
Acid butyl benzyl 12.5 parts, dibutyl phthalate 9 parts, phosphite 14 parts, sulfydryl acid esters 12.5 parts, mica powder 8 parts, quartz
10.5 parts of powder, 5.5 parts of carbon fiber, three monooctyl ester 3 parts, benzotriazole 12.5 parts, salicylate 22.5 parts, aluminium hydroxide 7 parts, nanometer
Titanium dioxide 7.5 parts, ethoxylated alkyl polyamines 14.5 parts, alkyl trimethyl quaternary ammonium 18.5 parts, the cruel amine of ethyoxyl Laurel 7.5
Part, copper 8-quinolinolate 3 parts, sodium fluoride 15 parts and methyl-silicone oil 4 parts.
Further, it is made up of the raw material of following parts by weight proportioning: dioctyl phthalate 25 parts, phthalic acid
Butyl benzyl 15 parts, dibutyl phthalate 10 parts, phosphite 15 parts, sulfydryl acid esters 15 parts, mica powder 10 parts, silica flour 13
Part, 7 parts of carbon fiber, three monooctyl ester 4 parts, benzotriazole 15 parts, salicylate 25 parts, aluminium hydroxide 10 parts, nano titanium oxide 9
Part, ethoxylated alkyl polyamines 16 parts, alkyl trimethyl quaternary ammonium 20 parts, the cruel amine of ethyoxyl Laurel 10 parts, copper 8-quinolinolate 4
Part, sodium fluoride 17 parts and methyl-silicone oil 6 parts.
The preparation method of a kind of Multifunctional plastic additive, comprises the following steps:
1) by dioctyl phthalate 18-25 part, BBP(Butyl Benzyl Phthalate 10-15 part, dibutyl phthalate 8-10
Part, phosphite 13-15 part, sulfydryl acid esters 10-15 part, mica powder 6-10 part, silica flour 8-13 part, carbon fiber 4-7 part, three pungent
Ester 2-4 part and benzotriazole 10-15 part are put in reactor, standby；
2) regulating step 1) in reactor heating-up temperature be 110-130 DEG C, mixing speed is 3000-3500r/min, during reaction
Between be 10-15 minute, standby；
3) by step 2) gained raw material puts in pressurized tank, and regulation air pressure is 13 times of atmospheric pressure, stands 5-6 hour, standby；
4) by salicylate 20-25 part, aluminium hydroxide 4-10 part, nano titanium oxide 6-9 part, ethoxylated alkyl polyamines 13-
16 parts, alkyl trimethyl quaternary ammonium 17-20 part, ethyoxyl Laurel cruel amine 5-10 part, copper 8-quinolinolate 2-4 part, sodium fluoride 13-17
Part and methyl-silicone oil 2-6 part are put in drying baker, standby；
5) regulating step 4) in drying baker temperature be adjusted to 88-92 DEG C, be dried 34-40 minute, standby；
6) step 3) gained raw material and step 5) gained raw material are mixed, put in blender and stir, standby；
7) step 6) gained raw material is put in high temperature comminutor, makes particulate matter,.
The invention have the benefit that the raw material of employing makes the plastic additive made have anti-oxidation function, can make
Electrostatic leaks in time, it is possible to facilitate the demoulding of plastics；The preparation method used can keep plastic additive good forming effect, convenient
Preserve.
Detailed description of the invention
Embodiment 1
A kind of Multifunctional plastic additive, is made up of the raw material of following parts by weight proportioning: dioctyl phthalate 18 parts, adjacent benzene
Dioctyl phthalate butyl benzyl 10 parts, dibutyl phthalate 8 parts, phosphite 13 parts, sulfydryl acid esters 10 parts, mica powder 6 parts, quartz
8 parts of powder, 4 parts of carbon fiber, three monooctyl ester 2 parts, benzotriazole 10 parts, salicylate 20 parts, aluminium hydroxide 4 parts, nano titanium oxide 6
Part, ethoxylated alkyl polyamines 13 parts, alkyl trimethyl quaternary ammonium 17 parts, the cruel amine of ethyoxyl Laurel 5 parts, copper 8-quinolinolate 2 parts,
Sodium fluoride 13 parts and methyl-silicone oil 2 parts.
The preparation method of a kind of Multifunctional plastic additive, comprises the following steps:
1) by dioctyl phthalate 18 parts, BBP(Butyl Benzyl Phthalate 10 parts, dibutyl phthalate 8 parts, phosphorous acid
Salt 13 parts, sulfydryl acid esters 10 parts, mica powder 6 parts, silica flour 8 parts, 4 parts of carbon fiber, three monooctyl ester 2 parts and benzotriazole 10 parts input
In reactor, standby；
2) regulating step 1) in reactor heating-up temperature be 110-130 DEG C, mixing speed is 3000-3500r/min, during reaction
Between be 10-15 minute, standby；
3) by step 2) gained raw material puts in pressurized tank, and regulation air pressure is 13 times of atmospheric pressure, stands 5-6 hour, standby；
4) by salicylate 20 parts, aluminium hydroxide 4 parts, nano titanium oxide 6 parts, ethoxylated alkyl polyamines 13 parts, alkyl three
Methyl quaternary ammonium 17 parts, the cruel amine of ethyoxyl Laurel 5 parts, copper 8-quinolinolate 2 parts, sodium fluoride 13 parts and methyl-silicone oil 2 parts are put into
In drying baker, standby；
5) regulating step 4) in drying baker temperature be adjusted to 88-92 DEG C, be dried 34-40 minute, standby；
6) step 3) gained raw material and step 5) gained raw material are mixed, put in blender and stir, standby；
7) step 6) gained raw material is put in high temperature comminutor, makes particulate matter,.
Embodiment 2
A kind of Multifunctional plastic additive, is made up of the raw material of following parts by weight proportioning: dioctyl phthalate 21.5 parts, neighbour
Phthalic acid butyl benzyl 12.5 parts, dibutyl phthalate 9 parts, phosphite 14 parts, sulfydryl acid esters 12.5 parts, mica powder 8
Part, silica flour 10.5 parts, 5.5 parts of carbon fiber, three monooctyl ester 3 parts, benzotriazole 12.5 parts, salicylate 22.5 parts, aluminium hydroxide 7
Part, nano titanium oxide 7.5 parts, ethoxylated alkyl polyamines 14.5 parts, alkyl trimethyl quaternary ammonium 18.5 parts, ethyoxyl Laurel are cruel
Amine 7.5 parts, copper 8-quinolinolate 3 parts, sodium fluoride 15 parts and methyl-silicone oil 4 parts.
The preparation method of a kind of Multifunctional plastic additive, comprises the following steps:
1) by dioctyl phthalate 21.5 parts, BBP(Butyl Benzyl Phthalate 12.5 parts, dibutyl phthalate 9 parts, Asia
Phosphate 14 parts, sulfydryl acid esters 12.5 parts, mica powder 8 parts, silica flour 10.5 parts, 5.5 parts of carbon fiber, three monooctyl ester 3 parts and benzo
Triazole 12.5 parts is put in reactor, standby；
2) regulating step 1) in reactor heating-up temperature be 110-130 DEG C, mixing speed is 3000-3500r/min, during reaction
Between be 10-15 minute, standby；
3) by step 2) gained raw material puts in pressurized tank, and regulation air pressure is 13 times of atmospheric pressure, stands 5-6 hour, standby；
4) by salicylate 22.5 parts, aluminium hydroxide 7 parts, nano titanium oxide 7.5 parts, ethoxylated alkyl polyamines 14.5 parts,
Alkyl trimethyl quaternary ammonium 18.5 parts, the cruel amine of ethyoxyl Laurel 7.5 parts, copper 8-quinolinolate 3 parts, sodium fluoride 15 parts and methyl-silicone oil
Put in drying baker for 4 parts, standby；
5) regulating step 4) in drying baker temperature be adjusted to 88-92 DEG C, be dried 34-40 minute, standby；
6) step 3) gained raw material and step 5) gained raw material are mixed, put in blender and stir, standby；
7) step 6) gained raw material is put in high temperature comminutor, makes particulate matter,.
Embodiment 3
A kind of Multifunctional plastic additive, is made up of the raw material of following parts by weight proportioning: dioctyl phthalate 25 parts, adjacent benzene
Dioctyl phthalate butyl benzyl 15 parts, dibutyl phthalate 10 parts, phosphite 15 parts, sulfydryl acid esters 15 parts, mica powder 10 parts, stone
13 parts of English powder, 7 parts of carbon fiber, three monooctyl ester 4 parts, benzotriazole 15 parts, salicylate 25 parts, aluminium hydroxide 10 parts, nano-silica
Change titanium 9 parts, ethoxylated alkyl polyamines 16 parts, alkyl trimethyl quaternary ammonium 20 parts, the cruel amine of ethyoxyl Laurel 10 parts, 8-hydroxyquinoline
Copper 4 parts, sodium fluoride 17 parts and methyl-silicone oil 6 parts.
The preparation method of a kind of Multifunctional plastic additive, comprises the following steps:
1) by dioctyl phthalate 25 parts, BBP(Butyl Benzyl Phthalate 15 parts, dibutyl phthalate 10 parts, phosphorous acid
Salt 15 parts, sulfydryl acid esters 15 parts, mica powder 10 parts, silica flour 13 parts, 7 parts of carbon fiber, three monooctyl ester 4 parts, benzotriazole 15 parts throwing
Enter in reactor, standby；
2) regulating step 1) in reactor heating-up temperature be 110-130 DEG C, mixing speed is 3000-3500r/min, during reaction
Between be 10-15 minute, standby；
3) by step 2) gained raw material puts in pressurized tank, and regulation air pressure is 13 times of atmospheric pressure, stands 5-6 hour, standby；
4) by salicylate 25 parts, aluminium hydroxide 10 parts, nano titanium oxide 9 parts, ethoxylated alkyl polyamines 16 parts, alkyl three
Methyl quaternary ammonium 20 parts, the cruel amine of ethyoxyl Laurel 10 parts, copper 8-quinolinolate 4 parts, sodium fluoride 17 parts and methyl-silicone oil 6 parts are put into
In drying baker, standby；
5) regulating step 4) in drying baker temperature be adjusted to 88-92 DEG C, be dried 34-40 minute, standby；
6) step 3) gained raw material and step 5) gained raw material are mixed, put in blender and stir, standby；
7) step 6) gained raw material is put in high temperature comminutor, makes particulate matter,.
The invention have the benefit that the raw material of employing makes the plastic additive made have anti-oxidation function, can make
Electrostatic leaks in time, it is possible to facilitate the demoulding of plastics；The preparation method used can keep plastic additive good forming effect, convenient
Preserve.
The above, the only detailed description of the invention of the present invention, but protection scope of the present invention is not limited thereto, and any
The change expected without creative work or replacement, all should contain within protection scope of the present invention.
Claims (5)
1. a Multifunctional plastic additive, it is characterised in that: it is made up of the raw material of following parts by weight proportioning: phthalic acid two
Monooctyl ester 18-25 part, BBP(Butyl Benzyl Phthalate 10-15 part, dibutyl phthalate 8-10 part, phosphite 13-15 part, mercapto
Base acid esters 10-15 part, mica powder 6-10 part, silica flour 8-13 part, carbon fiber 4-7 part, three monooctyl ester 2-4 parts, benzotriazole 10-15
Part, salicylate 20-25 part, aluminium hydroxide 4-10 part, nano titanium oxide 6-9 part, ethoxylated alkyl polyamines 13-16 part,
Alkyl trimethyl quaternary ammonium 17-20 part, ethyoxyl Laurel cruel amine 5-10 part, copper 8-quinolinolate 2-4 part, sodium fluoride 13-17 part and
Methyl-silicone oil 2-6 part.
Multifunctional plastic additive the most according to claim 1, it is characterised in that: by the raw material system of following parts by weight proportioning
Become: dioctyl phthalate 18 parts, BBP(Butyl Benzyl Phthalate 10 parts, dibutyl phthalate 8 parts, phosphite 13
Part, sulfydryl acid esters 10 parts, mica powder 6 parts, silica flour 8 parts, 4 parts of carbon fiber, three monooctyl ester 2 parts, benzotriazole 10 parts, salicylate
20 parts, aluminium hydroxide 4 parts, nano titanium oxide 6 parts, ethoxylated alkyl polyamines 13 parts, alkyl trimethyl quaternary ammonium 17 parts, ethoxy
The cruel amine of base Laurel 5 parts, copper 8-quinolinolate 2 parts, sodium fluoride 13 parts and methyl-silicone oil 2 parts.
Multifunctional plastic additive the most according to claim 1, it is characterised in that: by the raw material system of following parts by weight proportioning
Become: dioctyl phthalate 21.5 parts, BBP(Butyl Benzyl Phthalate 12.5 parts, dibutyl phthalate 9 parts, phosphite
14 parts, sulfydryl acid esters 12.5 parts, mica powder 8 parts, silica flour 10.5 parts, 5.5 parts of carbon fiber, three monooctyl ester 3 parts, benzotriazole 12.5
Part, salicylate 22.5 parts, aluminium hydroxide 7 parts, nano titanium oxide 7.5 parts, ethoxylated alkyl polyamines 14.5 parts, alkyl three
Methyl quaternary ammonium 18.5 parts, the cruel amine of ethyoxyl Laurel 7.5 parts, copper 8-quinolinolate 3 parts, sodium fluoride 15 parts and methyl-silicone oil 4 parts.
Multifunctional plastic additive the most according to claim 1, it is characterised in that: by the raw material system of following parts by weight proportioning
Become: dioctyl phthalate 25 parts, BBP(Butyl Benzyl Phthalate 15 parts, dibutyl phthalate 10 parts, phosphite 15
Part, sulfydryl acid esters 15 parts, mica powder 10 parts, silica flour 13 parts, 7 parts of carbon fiber, three monooctyl ester 4 parts, benzotriazole 15 parts, salicylic acid
Ester 25 parts, aluminium hydroxide 10 parts, nano titanium oxide 9 parts, ethoxylated alkyl polyamines 16 parts, alkyl trimethyl quaternary ammonium 20 parts,
The cruel amine of ethyoxyl Laurel 10 parts, copper 8-quinolinolate 4 parts, sodium fluoride 17 parts and methyl-silicone oil 6 parts.
5. the preparation method of a Multifunctional plastic additive, it is characterised in that: comprise the following steps:
1) by dioctyl phthalate 18-25 part, BBP(Butyl Benzyl Phthalate 10-15 part, dibutyl phthalate 8-10
Part, phosphite 13-15 part, sulfydryl acid esters 10-15 part, mica powder 6-10 part, silica flour 8-13 part, carbon fiber 4-7 part, three pungent
Ester 2-4 part and benzotriazole 10-15 part are put in reactor, standby；
2) regulating step 1) in reactor heating-up temperature be 110-130 DEG C, mixing speed is 3000-3500r/min, during reaction
Between be 10-15 minute, standby；
3) by step 2) gained raw material puts in pressurized tank, and regulation air pressure is 13 times of atmospheric pressure, stands 5-6 hour, standby；
4) by salicylate 20-25 part, aluminium hydroxide 4-10 part, nano titanium oxide 6-9 part, ethoxylated alkyl polyamines 13-
16 parts, alkyl trimethyl quaternary ammonium 17-20 part, ethyoxyl Laurel cruel amine 5-10 part, copper 8-quinolinolate 2-4 part, sodium fluoride 13-17
Part and methyl-silicone oil 2-6 part are put in drying baker, standby；
5) regulating step 4) in drying baker temperature be adjusted to 88-92 DEG C, be dried 34-40 minute, standby；
6) step 3) gained raw material and step 5) gained raw material are mixed, put in blender and stir, standby；
7) step 6) gained raw material is put in high temperature comminutor, makes particulate matter,.