CN106080008A - A kind of stone material and the decoration production technology of lucite composite panel - Google Patents

A kind of stone material and the decoration production technology of lucite composite panel Download PDF

Info

Publication number
CN106080008A
CN106080008A CN201610424266.8A CN201610424266A CN106080008A CN 106080008 A CN106080008 A CN 106080008A CN 201610424266 A CN201610424266 A CN 201610424266A CN 106080008 A CN106080008 A CN 106080008A
Authority
CN
China
Prior art keywords
lucite
stone
decoration
production technology
composite panel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201610424266.8A
Other languages
Chinese (zh)
Inventor
黄律翔
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610424266.8A priority Critical patent/CN106080008A/en
Publication of CN106080008A publication Critical patent/CN106080008A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses the decoration production technology of a kind of stone material and lucite composite panel; by the way of drilling blind hole, various non-ferrous metal particles or the stone grain of other colors different with board body or crystal or high temperature resistant coloured plastics material grain are filled in blind hole at stone plate surface; then by high temperature, lucite solution is layed in stone surface; by being cooled into poly (methyl methacrylate) plate and the slabstone good bond of solid; form new composite material for decoration plate, solve the technical problem described in skill background art in explanation；The advantages such as having good decorating effect, decorative pattern is varied, reduces trimming cost, and the breakage-proof ability of slabstone is strong.

Description

A kind of stone material and the decoration production technology of lucite composite panel
Technical field
The present invention relates to the trailing of stone panel, a kind of stone material is raw with the decoration of lucite composite panel Production. art.
Background technology
1, existing stone decoration is that original stone is cut into slabstone, is then polished smooth by slabstone so that it is surface shape Becoming regular or original lithosporic stricture of vagina/lithosporic point, the periphery around sheet material having carries out secondary parergon；2, slabstone belongs to corpusculum Long-pending heavier material, is also belonging to more crisp material, the most dangerous decorating in wall or furred ceiling or suspension etc.；3, there is a stone material Belonging to rare stone material, if cutting into slabstone for decorating by normal thickness, it appears excessively waste, trimming cost height etc. lacks Point.
Summary of the invention
In order to solve above-mentioned technical problem, the present invention provides a kind of energy good decorating effect, and decorative pattern is varied, reduces Trimming cost, the breakage-proof ability of slabstone is strong, expands the stone material of decoration scope and the decoration production technology of lucite composite panel.
Solving above-mentioned technical problem scheme is
A kind of stone material and the decoration production technology of lucite composite panel, its production comprises the steps:
1), first with compared with bastard stone saw cutting out sheet material from original stone material, the plate surface cut out is formed regular Uneven；
2), with metal kernel sweeping and polish on sheet material, blunt to the stone thorn that will take off and wedge angle polishing, not needle-holding hand, then by stone Powder and coarse grain clean up；
3), electricity consumption is drilled in its surface and gets out several blind holes；
4), board material vertical is overturn, make the face down holed；
5), rinse from bottom to top with giant, the stone powder in hole is rinsed well；
6), sheet material is removed to brandreth, make the one of boring face down, at normal temperatures natural airing or fan dries up or with baking Case is dried, and humidity is less than 10%；
7), airing board material vertical is overturn, make that has holed to face up；
8), toward filling in the decoration particle being slightly less than blind hole diameter in blind hole, it is impossible to make particle detachment；
9), the sheet material of decoration is put into the die cavity of casting moulds；
10), toward mould intra-bladder instillation hot lucite solution；
11), lower the temperature, make lucite solution freeze solidly on sheet material front face surface, make both firmly stick to one；
12), take out the sheet material of molding after solidification, put on the package packing machine of straight-lined manufacturing, by packer toward organic glass Packaging film is sticked on glass surface；
13), trimming, edge cuts is smooth, formed composite decorative board.
Further: step 3) described in electricity consumption be drilled in its surface get out by several blind holes form certain animal or plant wheel The blind hole of hub pattern, such as horse shape wheel hub pattern, apple shape wheel hub pattern, plant leaf wheel hub pattern.
Further: step 3) described in blind hole diameter be 1mm-9mm, the degree of depth is 1mm-10mm.
Further: step 6) described in room temperature under time of natural airing be: 1-5 hour；If with fan dry up time Between be: 15 minutes-1 hour；If by oven for drying, oven temperature is 40-60 DEG C, and drying time is: 10-30 divides Clock；If oven temperature is 60-80 DEG C, drying time is: 5-20 minute.
Further: step 8) described in decoration particle be non-ferrous metal particle or other colors different with board body Stone grain or crystal or high temperature resistant coloured plastics material grain.
Further: step 9-step 11) described from pouring into a mould organic glass solution to needed for being solidified into hardware lucite Time is 1-10 minute；Described cooling frozen water is lowered the temperature or lowers the temperature by normal-temperature water.
Further: described lucite is polymethyl methacrylate.
Advantages of the present invention is:
Stone plate surface by the way of drilling blind hole by various non-ferrous metal particles or different with board body its The stone grain of his color or crystal or high temperature resistant coloured plastics material grain are filled in blind hole, are then laid by lucite solution by high temperature In stone surface, by being cooled into poly (methyl methacrylate) plate and the slabstone good bond of solid, form new composite material for decoration plate, Original stone plate surface and motif can be seen through lucite, solve the technical problem described in technical background.
Detailed description of the invention
A kind of stone material and the decoration production technology of lucite composite panel, its production comprises the steps:
1), first with compared with bastard stone saw cutting out sheet material from original stone material, the plate surface cut out is formed regular Uneven；
2), with metal kernel sweeping and polish on sheet material, blunt to the stone thorn that will take off and wedge angle polishing, not needle-holding hand, then by stone Powder and coarse grain clean up；
3), electricity consumption is drilled in its surface and gets out several blind holes；
4), board material vertical is overturn, make the face down holed；
5), rinse from bottom to top with giant, the stone powder in hole is rinsed well；
6), sheet material is removed to brandreth, make the one of boring face down, at normal temperatures natural airing or fan dries up or with baking Case is dried, and humidity is less than 10%；
7), airing board material vertical is overturn, make that has holed to face up；
8), toward filling in the decoration particle being slightly less than blind hole diameter in blind hole, it is impossible to make particle detachment；
9), the sheet material of decoration is put into the die cavity of casting moulds；
10), toward mould intra-bladder instillation hot lucite solution；
11), lower the temperature, make lucite solution freeze solidly on sheet material front face surface, make both firmly stick to one；
12), take out the sheet material of molding after solidification, put on the package packing machine of straight-lined manufacturing, by packer toward organic glass Packaging film is sticked on glass surface；
13), trimming, edge cuts is smooth, formed composite decorative board.
Further: step 3) described in electricity consumption be drilled in its surface get out by several blind holes form certain animal or plant wheel The blind hole of hub pattern, such as horse shape wheel hub pattern, apple shape wheel hub pattern, plant leaf wheel hub pattern.
Further: step 3) described in blind hole diameter be 1mm-9mm, the degree of depth is 1mm-10mm.
Further: step 6) described in room temperature under time of natural airing be: 1-5 hour；If with fan dry up time Between be: 15 minutes-1 hour；If by oven for drying, oven temperature is 40-60 DEG C, and drying time is: 10-30 divides Clock；If oven temperature is 60-80 DEG C, drying time is: 5-20 minute.
Further: step 8) described in decoration particle be non-ferrous metal particle or other colors different with board body Stone grain or crystal or high temperature resistant coloured plastics material grain.
Further: step 9-step 11) described from pouring into a mould organic glass solution to needed for being solidified into hardware lucite Time is 1-10 minute；Described cooling frozen water is lowered the temperature or lowers the temperature by normal-temperature water.
Further: described lucite is polymethyl methacrylate.
Further: described washing time is: 3-15 minute；
Further: described blind hole is circular or rectangle or polygon.
Further: described non-ferrous metal refers to the alumina particles of general silver color, the copper granule of yellow, golden gold grain Deng.
Example 1: a kind of stone material and the decoration production technology of lucite composite panel, its production comprises the steps:
1), first with compared with bastard stone saw cutting out sheet material from original stone material, the plate surface cut out is formed regular Uneven；
2), with metal kernel sweeping and polish on sheet material, blunt to the stone thorn that will take off and wedge angle polishing, not needle-holding hand, then by stone Powder and coarse grain clean up；
3), electricity consumption be drilled in its surface and get out the horse shape wheel hub pattern being made up of several blind holes, blind hole diameter is 3mm, deeply Degree is 3mm；
4), board material vertical is overturn, make the face down holed；
5), rinsing from bottom to top with giant, rinsed well by the stone powder in hole, washing time is: 2 minutes；
6), being removed to brandreth by sheet material, make the one of boring face down, at normal temperatures natural airing, the time of airing is: 1.5 hour；Humidity is less than 10%；
7), airing board material vertical is overturn, make that has holed to face up；
8), toward filling in the crystal particle being slightly less than blind hole diameter in blind hole, it is impossible to make crystal come off；
9), the sheet material of decoration is put into the die cavity of casting moulds；
10), toward the hot polymethyl methacrylate solution of mould intra-bladder instillation；
11), lower the temperature, make polymethyl methacrylate solution freeze solidly on sheet material front face surface, be formed with perspex layer, make Both firmly stick to one；
12), take out the sheet material of molding after solidification, put on the package packing machine of straight-lined manufacturing, by packer toward organic glass Packaging film is sticked on glass surface；
13), trimming, edge cuts is smooth, form compound crystal dalle.
Example 2:
A kind of stone material and the decoration production technology of lucite composite panel, its production comprises the steps:
1), first with compared with bastard stone saw cutting out sheet material from original stone material, the plate surface cut out is formed regular Uneven；
2), with metal kernel sweeping and polish on sheet material, blunt to the stone thorn that will take off and wedge angle polishing, not needle-holding hand, then by stone Powder and coarse grain clean up；
3), electricity consumption be drilled in its surface and get out the apple shape wheel hub pattern being made up of several blind holes, blind hole diameter is 2mm, The degree of depth is 3mm；
4), board material vertical is overturn, make the face down holed；
5), rinsing from bottom to top with giant, rinsed well by the stone powder in hole, washing time is: 3 minutes；
6), being removed to brandreth by sheet material, make the one of boring face down, dry up with fan, the time blown is: 20 minutes；Wet Degree is less than 10%；
7), airing board material vertical is overturn, make that has holed to face up；
8), toward filling in the alumina particles being slightly less than blind hole diameter in blind hole, it is impossible to make aluminum come off；
9), the sheet material of decoration is put into the die cavity of casting moulds；
10), toward the hot polymethyl methacrylate solution of mould intra-bladder instillation；
11), lower the temperature, make polymethyl methacrylate solution freeze solidly on sheet material front face surface, be formed with perspex layer, make Both firmly stick to one；
12), take out the sheet material of molding after solidification, put on the package packing machine of straight-lined manufacturing, by packer toward organic glass Packaging film is sticked on glass surface；
13), trimming, edge cuts is smooth, form compound crystal dalle.

Claims (8)

1. a stone material and the decoration production technology of lucite composite panel, it is characterised in that comprise the steps:
1), first with compared with bastard stone saw cutting out sheet material from original stone material, the plate surface cut out is formed regular concavo-convex Not plane；
2), with metal kernel sweep and polish on sheet material, blunt to the stone thorn that will take off and wedge angle polishing, not needle-holding hand, then by stone powder and Coarse grain cleans up；
3), electricity consumption is drilled in its surface and gets out several blind holes；
4), board material vertical is overturn, make the face down holed；
5), rinse from bottom to top with giant, the stone powder in hole is rinsed well；
6), being removed to brandreth by sheet material, make the one of boring face down, natural airing or fan dry up or dry with baking oven at normal temperatures Dry, humidity is less than 10%；
7), airing board material vertical is overturn, make that has holed to face up；
8), toward filling in the decoration particle being slightly less than blind hole diameter in blind hole, it is impossible to make particle detachment；
9), the sheet material of decoration is put into the die cavity of casting moulds；
10), toward mould intra-bladder instillation hot lucite solution；
11), lower the temperature, make lucite solution freeze solidly on sheet material front face surface, make both firmly stick to one；
12), take out the sheet material of molding after solidification, put on the package packing machine of straight-lined manufacturing, by packer toward lucite table Packaging film is sticked in face；
13), trimming, edge cuts is smooth, formed composite decorative board.
A kind of stone material the most according to claim 1 and the decoration production technology of lucite composite panel, it is characterised in that: Step 3) described in electricity consumption be drilled in its surface and get out the blind hole being made up of certain animal or plant wheel hub pattern several blind holes, as Horse shape wheel hub pattern, apple shape wheel hub pattern, plant leaf wheel hub pattern.
A kind of stone material the most according to claim 1 and the decoration production technology of lucite composite panel, it is characterised in that: Step 3) described in blind hole diameter be 1mm-9mm, the degree of depth is 1mm-10mm.
A kind of stone material the most according to claim 1 and the decoration production technology of lucite composite panel, it is characterised in that: Step 5) described in washing time be: 5 minutes-15 minutes.
A kind of stone material the most according to claim 1 and the decoration production technology of lucite composite panel, it is characterised in that: Step 6) described in room temperature under time of natural airing be: 1-5 hour；If the time dried up with fan is: 15 minutes-1 little Time；If by oven for drying, oven temperature is 40-60 DEG C, and drying time is: 10-30 minute；If oven temperature For 60-80 DEG C, drying time is: 5-20 minute.
A kind of stone material the most according to claim 1 and the decoration production technology of lucite composite panel, it is characterised in that: Step 8) described in decoration particle be non-ferrous metal particle or the stone grain of other colors different with board body or crystal or High temperature resistant coloured plastics material grain.
A kind of stone material the most according to claim 1 and the decoration production technology of lucite composite panel, it is characterised in that: Step 9-step 11) described be 1-10 minute from cast organic glass solution to the time being solidified into needed for hardware lucite； Described cooling frozen water is lowered the temperature or lowers the temperature by normal-temperature water.
A kind of stone material the most according to claim 1 and the decoration production technology of lucite composite panel, it is characterised in that: Described lucite is polymethyl methacrylate.
CN201610424266.8A 2016-06-14 2016-06-14 A kind of stone material and the decoration production technology of lucite composite panel Withdrawn CN106080008A (en)