CN101450589A - Production method of artificial transparent slate emboss - Google Patents
Production method of artificial transparent slate emboss Download PDFInfo
- Publication number
- CN101450589A CN101450589A CNA2007101506434A CN200710150643A CN101450589A CN 101450589 A CN101450589 A CN 101450589A CN A2007101506434 A CNA2007101506434 A CN A2007101506434A CN 200710150643 A CN200710150643 A CN 200710150643A CN 101450589 A CN101450589 A CN 101450589A
- Authority
- CN
- China
- Prior art keywords
- grams
- mould
- light
- artificial
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an artificial light transmitting stone relief sculpture. An unsaturated polyester resin is adopted as a bonding agent, is mixed with aluminum hydroxide powder and talcum powder, and relief sculptures with various subject matters are manufactured. The artificial light transmitting stone relief sculpture can emit light from a colored lamp of a product, so that the relief sculpture generates dreamy color. The artificial relief sculpture can decorate various high-grade hotels, bath centers, villas and families, and is a novel high-grade decorative artwork.
Description
Technical field:
The invention belongs to decorated articles, particularly a kind of preparation method of artificial transparent slate emboss.
Background technology:
The vigorous fluffy development of artificial stone industry of China now, the use field of artificial stone is more and more broader, except various use in toilet deck plates, also be useful on the printing opacity stone class of lamp box and floor-lamp lamp decoration, also have the various cultural walls that are used for, be used to decorate the snowflake class of printing opacity cylinder, these product colors are gorgeous, decorative pattern is rich and varied, especially at present popular light penetrating stone slab series is made something perfect even more perfect especially, these artificial stone light-passing boards mostly are flat-type, if produce the printing opacity stone relief with the material of making these light-passing boards, that will make printing opacity stone manufacturing industry promote a new grade again, and the present invention is exactly in order to make printing opacity stone open up a new use field, promptly to make a kind of printing opacity stone relief.A kind of artificial transparent stone relief of the present invention, adopt insatiable hunger to close mylar and make bond, sneak into aluminium hydrate powder and talcum powder, produce the embossment of various subject matters, this artificial transparent stone relief can be penetrated light from the back lampion of product, makes embossment produce fantasy color, this artificial transparent stone relief, can decorate various high-grade hotels, bath center, can decorate villa, family, become a kind of new high-grade decorative art.
Technology contents:
Make mould with the color embossed glass that present decoration city is bought, this embossment can be the personage also can be animal, can also be various flower plants, with this scraggly glass cameo as mould, then on the mould of 1 cm thick, directly pour light penetrating stone slab batch mixing slip into, the slip of this liquid is along with the embossment of glass cameo mould rises and falls, produce the effect the same with the original work embossment, fallen horizontal vibrating levelling behind the material, after the demoulding the printing opacity stone relief back of casting complete, be affixed to together with 10 cm thick epoxy glass laminate plates, because this to water the printing opacity stone relief that outpours be former, producing works just can be identical with original stained glass embossment.
What more than produce is the former mould, on this former mould, brush releasing agent, the slip of snowflake light-passing board of being mixed is again poured on the flat plate mold, plastic sheeting is placed on the top of flat plate mold, pour the light penetrating stone slab slip initial set of flat plate mold into, its full wafer is soft, with a plate is dull and stereotyped this soft flat board is being pasted former plastic sheeting, put in the mould, concavo-convex fluctuating along with mould, do not have the initial set light penetrating stone slab of 5 millimeters thick of intensity can collapse to recess, use hand again the not local compacting of sticking real mould, because be the initial set state of snowflake, can not produce stress cracking, can play the die sinking tool after intensity reaches, blasting treatment is carried out on the surface of transparent slate emboss, reaches till the technological requirement.
Specific embodiments:
1. prepare the light-passing board slip of 1000 grams, it is as follows to fill a prescription:
Mylar 191A 200 gram curing agent 8 grams are closed in insatiable hunger
Aluminium hydrate powder (toothpaste level) 200 gram promoter 8 grams
Yellow 20 grams of talcum powder (500 orders～700 orders) 400 gram polyester mill bases
Red 14 grams of styrene 50 grams～100 gram polyester mill bases
Titanium dioxide 50 grams
2. above material is mixed together, stirs with de-airing mixer, material of main part is light yellow and white, takes out 100 fens from the material that is mixed in 3 batch mixing bowls, yellow slurry 10 grams in adding.Add red mill base 3 grams in the 2nd the batch mixing bowl, add white titanium dioxide 10 grams in the 3rd bowl, above three kinds of slips are mixed.
3. make color embossed glass mould one cover, the epoxy glass laminate plate that adds sticking one deck 12 millimeters thick below the mould, so that product is indeformable, make long 2 meters wide 1 meter of flat plate mold with a thick safety glass of 16～20 millimeters again, cling with 5 millimeters thick standard rubbers bars on four limits, and mould is placed on the horizontal vibrating platform.
4. the dominant hue slip that is mixed is poured in the stained glass relief die and shaken levelling, this is a duplicate of making artificial light penetrating stone slab, be cast on the duplicate again with above light penetrating stone slab slip then, produce light penetrating stone slab mould like this, pourablely on this mould go out artificial stone light-passing board embossment works.
5. on dull and stereotyped chilled glass die, make Zhang Ping's plate light penetrating stone slab earlier, this Zhang Ping's plate light penetrating stone slab is just transferred to it on the artificial stone light-passing board relief die when just solidifying, soft so dull and stereotyped light-passing board can sink, and is attached to recess all recesses of mould can both be sticked.The concavo-convex place of a kind of transparent slate emboss like this is equally thick entirely, the song of the various embossments that each is present is not that there is rough embossment the front, and the back is dull and stereotyped state entirely.
6. the artificial transparent stone relief of throwing off mould, load onto diamond dust with sand-blasting machine and spray on the surface one time, make the surface of product that the effect of ground glass be arranged.
Claims (1)
1. the preparation method of an artificial transparent slate emboss is characterized in that:
(1) the light-passing board slip of preparation 1000 grams, it is as follows to fill a prescription:
Mylar 191A 200 gram curing agent 8 grams are closed in insatiable hunger
Aluminium hydrate powder (toothpaste level) 200 gram promoter 8 grams
Yellow 20 grams of talcum powder (500 orders～700 orders) 400 gram polyester mill bases
Red 14 grams of styrene 50 grams～100 gram polyester mill bases
Titanium dioxide 50 grams
(2) above material is mixed together, stirs with de-airing mixer, material of main part is light yellow and white, takes out 100 fens from the material that is mixed in 3 batch mixing bowls, yellow slurry 10 grams in adding.Add red mill base 3 grams in the 2nd the batch mixing bowl, add white titanium dioxide 10 grams in the 3rd bowl, above three kinds of slips are mixed.
(3) make color embossed glass mould one cover, the epoxy glass laminate plate that adds sticking one deck 12 millimeters thick below the mould, so that product is indeformable, make long 2 meters wide 1 meter of flat plate mold with a thick safety glass of 16～20 millimeters again, cling with 5 millimeters thick standard rubbers bars on four limits, and mould is placed on the horizontal vibrating platform.
(4) the dominant hue slip that is mixed is poured in the stained glass relief die shaken levelling, this is a duplicate of making artificial light penetrating stone slab, be cast on the duplicate again with above light penetrating stone slab slip then, produce light penetrating stone slab mould like this, pourablely on this mould go out artificial stone light-passing board embossment works.
(5) on dull and stereotyped chilled glass die, make Zhang Ping's plate light penetrating stone slab earlier, this Zhang Ping's plate light penetrating stone slab is just transferred to it on the artificial stone light-passing board relief die when just solidifying, soft so dull and stereotyped light-passing board can sink, and is attached to recess all recesses of mould can both be sticked.The concavo-convex place of a kind of transparent slate emboss like this is equally thick entirely, the song of the various embossments that each is present is not that there is rough embossment the front, and the back is dull and stereotyped state entirely.
(6) the artificial transparent stone relief of throwing off mould, load onto diamond dust with sand-blasting machine and spray on the surface one time, make the surface of product that the effect of ground glass be arranged.