CN206106514U - Foamed ceramic decorative board - Google Patents
Foamed ceramic decorative board Download PDFInfo
- Publication number
- CN206106514U CN206106514U CN201620802103.4U CN201620802103U CN206106514U CN 206106514 U CN206106514 U CN 206106514U CN 201620802103 U CN201620802103 U CN 201620802103U CN 206106514 U CN206106514 U CN 206106514U
- Authority
- CN
- China
- Prior art keywords
- foamed ceramic
- enhancement layer
- slurry
- ceramic plate
- utility
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model relates to an ornamental material structure field, in particular to foamed ceramic decorative board, it includes: the foamed ceramic board, the foamed ceramic board is the fashioned plate material of foamed ceramic, including upper surface and lower surface, the enhancement layer, the enhancement layer sets up the upper surface and/or the lower surface of foamed ceramic board for increase foamed ceramic board intensity, an object of the utility model is to provide a thermal -insulated effect that keeps warm better, lighter, foamed ceramic decorative board that the processing cost is lower, the utility model also discloses a preparation method of this kind of decorative board.
Description
Technical field
This utility model is related to ornament materials construction applications, more particularly to a kind of foamed ceramic decorative plate, and discloses this
Plant the preparation method of decorative panel.
Background technology
The heat insulating effect of foamed ceramic is good, is most initially the inner wall of stack used in integrated mill, or in factory
The inwall of other hot environments；
Due to foamed ceramic, not only heat insulating effect is good, and very light, so it is high to apply to comparison gradually later
The field at end, such as decoration material field, but foamed ceramic has highly brittle, it is easy to just rupture broken；
So, the utilization on ornament materials, at this stage also merely by the mode of filling, such as in a packaged decoration materials
In material, in diverse location setting unit cavity, filling-foam ceramics, so that whole ornament materials thermal insulation separation thermal effect on the whole
Fruit is more preferably；
At this stage, this structure is extraordinary product, but in actual use, the insulation of this ornament materials
Effect is not good enough, while weight is also no optimize enough, or it is heavier, and the processing technique of this structure is more complicated,
High cost.
Utility model content
The purpose of this utility model is to overcome the above-mentioned deficiency in the presence of prior art, there is provided a kind of thermal insulation separation thermal effect
Fruit is more preferable, the lower foamed ceramic decorative plate of light, processing cost.
In order to realize above-mentioned utility model purpose, this utility model provides technical scheme below：
A kind of foamed ceramic decorative plate, it includes：
Foamed ceramic plate, the foamed ceramic plate for foamed ceramic molding board-like material, including upper and lower surface；
Enhancement layer, the enhancement layer is arranged on the upper surface and/or lower surface of the foamed ceramic plate, for increasing foaming
Ceramic wafer intensity.
Using the foamed ceramic of a monoblock, tabular is formed, heat insulating effect is made more preferably, gentlier, while using this knot
Structure, it is necessary to overcome the fragility of foamed ceramic, so being provided with the enhancement layer, makes the foamed ceramic of tabular not broken, and ties
From the point of view of on structure, very simply, the enhancement layer is set in foamed ceramic upper surface or lower surface, or upper and lower surface,
Foamed ceramic is embedded in the cavity of other materials in compared to existing technology, processing technique is simpler, and processing cost is lower.
Used as preferred version of the present utility model, the enhancement layer is arranged on the upper surface and following table of the foamed ceramic plate
Face, upper and lower surface is respectively provided with enhancement layer, makes overall decorative panel intensity higher, makes foamed ceramic plate less easily rupturable.
Used as preferred version of the present utility model, the enhancement layer is paved with the upper surface and following table of the foamed ceramic plate
Face, in the plan of establishment of enhancement layer, it can be provided network structure or other incomplete knots for covering upper and lower surface
Structure, enhancement layer intensity reaches can still make the intensity of Integral decoration plate reach requirement after requirement, and adopt the setting side being paved with
Formula, makes enhancement layer in the case of using equivalent material, and intensity is higher, more preferable to the stiffening effect of foamed ceramic plate.
Used as preferred version of the present utility model, the enhancement layer is made up of the slurry of glass fiber reticular cloth and solidification, glass
The performances such as material fire prevention, waterproof are very stable, and low cost.
Used as preferred version of the present utility model, the enhancement layer is made up of Chopped Strand Mat（Glass fiber reticular cloth can be present substantially
Grid, and Chopped Strand Mat is then the structure of similar wet paper towel）.
Used as preferred version of the present utility model, the enhancement layer is made up of glass fiber reticular cloth and Chopped Strand Mat superposition.
Used as preferred version of the present utility model, the enhancement layer is made up of fiberglass mesh felt（Fiberglass mesh felt is glass
The felt that filling paste is formed in grid cloth）.
Used as preferred version of the present utility model, the fiberglass mesh felt is cement fiberglass mesh felt.
Used as preferred version of the present utility model, the enhancement layer is formed after being solidified by polymer modification inorganic slurry, this
Plant in slurry and include resin, stiffening effect is relatively good.
The invention also discloses a kind of method for preparing the foamed ceramic decorative plate, its step is：
A, foamed ceramic is shaped to board-like material, forms the foamed ceramic plate, it includes upper and lower surface；
B, the foamed ceramic plate upper surface and/or lower surface arrange enhancement layer, strengthen foamed ceramic plate intensity.
Adopt the decorative board heat insulation effect of heat insulation for processing in this way more preferably, gentlier, meanwhile, this processing mode adds
Work cost compared to existing technology for, it is lower.
As preferred version of the present utility model, in step B, arrange in the upper and lower surface of the foamed ceramic plate
Enhancement layer.
Used as preferred version of the present utility model, in step B, the detailed process for arranging enhancement layer is：
Glass fiber reticular cloth is set in the foamed ceramic plate upper surface and/or lower surface, then by solutioning machine to arranging
The foamed ceramic plate surface of glass fiber reticular cloth carries out scraping slurry, and slurry and the glass fiber reticular cloth combine to form a layer to be solidified,
The enhancement layer is formed after the layer solidification.
Used as preferred version of the present utility model, in step B, the detailed process for arranging enhancement layer is：
The foamed ceramic plate upper surface and/or lower surface are carried out scraping slurry（Foamed ceramic surface relatively porous hole, is carried out
Scrape and form smooth plane after slurry, make that the connection area of enhancement layer and foamed ceramic plate is bigger, stiffening effect is more preferable）, treat slurry
Gluing is carried out to the surface that slurry is formed after solidification, then bonded and glass fiber felt, form the enhancement layer.
Used as preferred version of the present utility model, in step B, the detailed process for arranging enhancement layer is：
Glass fiber reticular cloth is set in the foamed ceramic plate upper surface and/or lower surface, then by solutioning machine to arranging
The foamed ceramic plate surface of glass fiber reticular cloth carries out scraping slurry, and slurry and the glass fiber reticular cloth combine to form a layer to be solidified,
After the layer solidification, gluing is carried out to the layer surface, then bonded and glass fiber felt, form glass fiber reticular cloth and Chopped Strand Mat is superimposed what is constituted
Enhancement layer.
Used as preferred version of the present utility model, in rapid B, the detailed process for arranging enhancement layer is：
The foamed ceramic plate upper surface and/or lower surface are carried out scraping slurry, the table for forming slurry after slurry curing
Face carries out gluing, then bonded and glass fiber felt, carries out gluing to Chopped Strand Mat surface, then bonded and glass fiber felt, sets on Chopped Strand Mat surface
Glass fiber reticular cloth is put, then by solutioning machine the Chopped Strand Mat surface for arranging glass fiber reticular cloth is carried out scraping slurry, slurry and the glass
Fine grid cloth combines to form a layer to be solidified, and enhancement layer is formed with Chopped Strand Mat stack combinations after the layer solidification.
Used as preferred version of the present utility model, in step B, the detailed process for arranging enhancement layer is：
The foamed ceramic plate upper surface and/or lower surface are carried out scraping slurry, the table for forming slurry after slurry curing
Face carries out gluing, then bonded and glass fiber grid felt, forms the enhancement layer.
Used as preferred version of the present utility model, in step B, the detailed process for arranging enhancement layer is：
The foamed ceramic plate upper surface and/or lower surface are carried out to scrape slurry, slurry therewith is the inorganic slurry of polymer modification
Material, forms the enhancement layer after the slurry curing.
Used as preferred version of the present utility model, the foamed ceramic plate is formed by foamed ceramic cutting, in hgher efficiency.
Compared with prior art, the beneficial effects of the utility model：
More preferably, lighter, processing cost is lower for heat insulating effect.
Description of the drawings：
Fig. 1 is the structural representation of this utility model embodiment 1；
Fig. 2 is the partial enlarged drawing in Fig. 1 at A；
Fig. 3 is method flow schematic diagram in embodiment 1；
Labelling in figure：1- foamed ceramic plates, 2- enhancement layers, 3- glass fiber reticular cloths.
Specific embodiment
This utility model is described in further detail with reference to embodiment and specific embodiment.But should not be by this
The scope for being interpreted as the above-mentioned theme of this utility model is only limitted to below example, all to be realized based on this utility model content
Technology belongs to scope of the present utility model.
Embodiment 1
As Fig. 1,2, a kind of foamed ceramic decorative plate, it includes：
Foamed ceramic plate 1, the foamed ceramic plate 1 for foamed ceramic molding board-like material, including upper surface and following table
Face；
Enhancement layer 2, the enhancement layer 2 is arranged on the upper surface and/or lower surface of the foamed ceramic plate 1, for increasing
The intensity of foamed ceramic plate 1（The metal level 2 can be made up of copper, rustless steel, steel or ferrum）.
The enhancement layer 2 is paved with the upper surface and following table of the foamed ceramic plate 1, and the enhancement layer 2 is by glass fiber reticular cloth 3
Constitute with the slurry of solidification.
As Fig. 3, the present embodiment also disclose a kind of method for preparing the foamed ceramic decorative plate, its step is：
A, cutting foamed ceramic raw material, form foamed ceramic plate 1, including upper and lower surface；
B, enhancement layer 2 is set in the upper and lower surface of the foamed ceramic plate 1, strengthens the intensity of foamed ceramic plate 1, tool
Body, glass fiber reticular cloth 3 is set in the upper and lower surface of foamed ceramic plate 1, then by solutioning machine to arranging glass
The surface of foamed ceramic plate 1 of grid cloth 3 carries out scraping slurry, and slurry and the combination of the glass fiber reticular cloth 3 form a layer to be solidified, should
The enhancement layer 2 is formed after layer solidification.
Embodiment 2
In the present embodiment, and the difference of embodiment 1 is, the enhancement layer 2 can also be other constructions, different structures
Make corresponding step B also different, it is specific as follows：
When the enhancement layer is made up of Chopped Strand Mat, step B is, to the foamed ceramic plate upper surface and/or lower surface
Carry out scraping slurry, gluing is carried out to the surface that slurry is formed after slurry curing, then bonded and glass fiber felt, form the enhancement layer.
When the enhancement layer by glass fiber reticular cloth and Chopped Strand Mat superposition constitute when, step B include 2 in situation：
One kind is that glass fiber reticular cloth is arranged on innermost layer, and in the foamed ceramic plate upper surface and/or lower surface glass is arranged
Fine grid cloth, then carries out scraping slurry, slurry and the glass by solutioning machine to the foamed ceramic plate surface for arranging glass fiber reticular cloth
Fine grid cloth combines to form a layer to be solidified, after the layer solidification, carries out gluing to the layer surface, then bonded and glass fiber felt, shape
Into the enhancement layer that glass fiber reticular cloth and Chopped Strand Mat superposition are constituted.
One kind is that Chopped Strand Mat is arranged on innermost layer, and the foamed ceramic plate upper surface and/or lower surface are carried out scraping slurry, is treated
Gluing is carried out to the surface that slurry is formed after slurry curing, then bonded and glass fiber felt, to Chopped Strand Mat surface gluing is carried out, and is then glued
Chopped Strand Mat is connect, glass fiber reticular cloth is set on Chopped Strand Mat surface, then the Chopped Strand Mat table by solutioning machine to setting glass fiber reticular cloth
Face carries out scraping slurry, and slurry and the glass fiber reticular cloth combine to form a layer to be solidified, with Chopped Strand Mat superposition group after the layer solidification
Conjunction forms enhancement layer.
When the enhancement layer is by fiberglass mesh felt（Cement fiberglass mesh felt can be adopted）During composition, step B is, to described
Bubble ceramic wafer upper surface and/or lower surface carry out scraping slurry, and gluing is carried out to the surface that slurry is formed after slurry curing, then glue
Fiberglass mesh felt is connect, the enhancement layer is formed.
When being formed after the enhancement layer is by the solidification of polymer modification inorganic slurry, step B is, to the foamed ceramic plate
Upper surface and/or lower surface carry out scraping slurry, and slurry therewith is polymer modification inorganic slurry, and described adding is formed after the slurry curing
Strong layer.
Claims (1)
1. a kind of foamed ceramic decorative plate, it includes：
Foamed ceramic plate, the foamed ceramic plate for foamed ceramic molding board-like material, including upper and lower surface；
Enhancement layer, the enhancement layer is arranged on the upper and lower surface of the foamed ceramic plate, for increasing foamed ceramic plate
Intensity, the enhancement layer is paved with the upper and lower surface of the foamed ceramic plate, and the enhancement layer is by glass fiber reticular cloth and admittedly
The slurry of change is constituted.