CN106042517A - Foam ceramic metal composite plate and preparation method thereof - Google Patents
Foam ceramic metal composite plate and preparation method thereof Download PDFInfo
- Publication number
- CN106042517A CN106042517A CN201610600013.1A CN201610600013A CN106042517A CN 106042517 A CN106042517 A CN 106042517A CN 201610600013 A CN201610600013 A CN 201610600013A CN 106042517 A CN106042517 A CN 106042517A
- Authority
- CN
- China
- Prior art keywords
- foamed ceramic
- plate
- ceramic plate
- metal level
- foam ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of decorative material structures, in particular to a foam ceramic metal composite plate. The foam ceramic metal composite plate comprises a foam ceramic plate and a metal layer; the foam ceramic plate is a plate material formed by foam ceramic and comprises an upper surface and a lower surface; the metal layer is arranged on the upper surface and/or the lower surface of the foam ceramic plate and used for improving strength of the foam ceramic plate. The foam ceramic metal composite plate is excellent in heat insulation and heat preservation effect, light in weight and low in processing cost. The invention further discloses a preparation method of the foam ceramic metal composite plate.
Description
Technical field
The present invention relates to ornament materials construction applications, particularly to a kind of foamed ceramic composite metal plate, and disclose this
Plant the preparation method of decorative panel.
Background technology
The heat insulating effect of foamed ceramic is good, is most initially the inner wall of stack being used in integrated mill, or in factory
The inwall of other hot environments；
Owing to foamed ceramic not only heat insulating effect is good, and very light, so the most gradually applying to than higher-end
Field, such as decoration material field, but foamed ceramic is highly brittle, it is easy to and just fracture is broken；
So, the utilization on ornament materials, present stage is also merely by the mode filled, such as at a packaged exterior material
In, at diverse location setting unit cavity, filling-foam is ceramic, so that the heat insulating effect that whole ornament materials is on the whole
More preferably；
Present stage, this structure is extraordinary product, but in actual use, the heat insulating effect of this ornament materials
The best, weight the most enough optimizes simultaneously, or heavier, and the processing technique of this structure is more complicated, cost
Too high.
Summary of the invention
It is an object of the invention to overcome the above-mentioned deficiency in the presence of prior art, it is provided that a kind of heat insulating effect is more
Foamed ceramic composite metal plate good, that lighter, processing cost is lower.
In order to realize foregoing invention purpose, the invention provides techniques below scheme:
A kind of foamed ceramic composite metal plate, comprising:
Foamed ceramic plate, described foamed ceramic plate is the board-like material of foamed ceramic molding, including upper and lower surface；
Metal level, described metal level is arranged on upper surface and/or the lower surface of described foamed ceramic plate, is used for increasing foamed ceramic
Plate intensity.
Use the foamed ceramic of a monoblock, form tabular, make heat insulating effect more preferably, gentlier, use this knot simultaneously
Structure, it is necessary to overcome the fragility of foamed ceramic, so being provided with described metal level, the foamed ceramic making tabular is the most broken, and ties
From the point of view of on structure, the most simply, at foamed ceramic upper surface or lower surface, or upper and lower surface arranges described metal level,
Layer on surface of metal then can arrange pattern, directly forms ornament finished product, compares the technique before relatively, step and less, fall
Low cost.
As the preferred version of the present invention, described metal level is arranged on the upper and lower surface of described foamed ceramic plate,
Upper and lower surface is respectively provided with metal level, and the decorative panel intensity making entirety is higher, makes foamed ceramic plate be less susceptible to rupture.
As the preferred version of the present invention, described metal level is paved with the upper and lower surface of described foamed ceramic plate,
In the plan of establishment of metal level, it can be provided network structure or other incomplete structures covering upper and lower surface, gold
Belong to and the intensity of Integral decoration plate after layer intensity reaches requirement, still can be made to reach requirement, and use the set-up mode being paved with, make
Metal level is in the case of using equivalent material, and intensity is higher, more preferable to the stiffening effect of foamed ceramic plate, prevents fires simultaneously, prevents
Water and heat insulation effect are more preferable.
The invention also discloses a kind of method preparing described foamed ceramic composite metal plate, the steps include:
A, foamed ceramic being shaped to board-like material, form described foamed ceramic plate, it includes upper and lower surface；
B, metal level is set at the upper surface of described foamed ceramic plate and/or lower surface, strengthens foamed ceramic plate intensity.
Adopt the decorative board heat insulation effect of heat insulation processed in this way more preferably, gentlier, meanwhile, compare the work before relatively
Skill, step and less, reduce cost.
As the preferred version of the present invention, in step B, the upper and lower surface at described foamed ceramic plate arranges metal
Layer.
As the preferred version of the present invention, in step B, the detailed process arranging metal level is:
Described foamed ceramic plate upper surface and/or lower surface are scraped slurry, and the surface formed slurry after slurry curing is entered
Row gluing, then bonded metal sheet material, form described metal level.
As the preferred version of the present invention, described foamed ceramic plate is formed by foamed ceramic cutting, in hgher efficiency.
Compared with prior art, beneficial effects of the present invention:
Heat insulating effect is more preferably, lighter, processing cost is lower.
Accompanying drawing illustrates:
Fig. 1 is the structural representation of the present invention；
Fig. 2 is method flow schematic diagram in embodiment 1；
Labelling in figure: 1-foamed ceramic plate, 2-metal level.
Detailed description of the invention
Below in conjunction with embodiment and detailed description of the invention, the present invention is described in further detail.But this should not understood
Scope for the above-mentioned theme of the present invention is only limitted to below example, and all technology realized based on present invention belong to this
The scope of invention.
Embodiment 1
Such as Fig. 1, a kind of foamed ceramic composite metal plate, comprising:
Foamed ceramic plate 1, described foamed ceramic plate 1 is the board-like material of foamed ceramic molding, including upper and lower surface；
Metal level 2, described metal level 2 is arranged on upper surface and/or the lower surface of described foamed ceramic plate 1, is used for increasing foaming
Ceramic wafer 1 intensity (described metal level 2 is made up of aluminium alloy plate, Al-Zn coated steel or titanium alloy sheet).
Described metal level 2 is paved with the upper and lower surface of described foamed ceramic plate 1, and metal level 2 is by the metallic plate of monoblock
Material is formed.
Such as Fig. 2, the present embodiment also discloses a kind of method preparing described foamed ceramic composite metal plate, the steps include:
A, cutting foamed ceramic raw material, form foamed ceramic plate 1, including upper and lower surface；
B, metal level 2 is set in the upper and lower surface of described foamed ceramic plate 1, strengthens foamed ceramic plate 1 intensity, specifically
, described foamed ceramic plate upper surface and/or lower surface are scraped slurry, the surface formed slurry after slurry curing is carried out
Gluing, then bonded metal sheet material, form described metal level 2.
Claims (7)
1. a foamed ceramic composite metal plate, comprising:
Foamed ceramic plate, described foamed ceramic plate is the board-like material of foamed ceramic molding, including upper and lower surface；
Metal level, described metal level is arranged on upper surface and/or the lower surface of described foamed ceramic plate, is used for increasing foamed ceramic
Plate intensity.
A kind of foamed ceramic composite metal plate the most according to claim 1, it is characterised in that described metal level is arranged on institute
State the upper and lower surface of foamed ceramic plate.
A kind of foamed ceramic composite metal plate the most according to claim 2, it is characterised in that described metal level is paved with described
The upper and lower surface of foamed ceramic plate.
4. the method preparing foamed ceramic composite metal plate described in claim 1-3 any one, the steps include:
Foamed ceramic being shaped to board-like material, forms described foamed ceramic plate, it includes upper and lower surface；
Upper surface and/or lower surface at described foamed ceramic plate arrange metal level, strengthen foamed ceramic plate intensity.
Preparation method the most according to claim 4, it is characterised in that in step B, at the upper surface of described foamed ceramic plate
It is respectively provided with metal level with lower surface.
Preparation method the most according to claim 5, it is characterised in that in step B, the detailed process arranging metal level is:
Described foamed ceramic plate upper surface and/or lower surface are scraped slurry, and the surface formed slurry after slurry curing is entered
Row gluing, then bonded metal sheet material, form described metal level.
Preparation method the most according to claim 4, it is characterised in that described foamed ceramic plate cut by foamed ceramic and
Become.