CN1060516A - The production method of dual-shouldered bimetallic thrust axle bush

Info

Publication number: CN1060516A
Application number: CN 90108188
Authority: CN
Inventors: 胡长安
Original assignee: Individual
Current assignee: Individual
Priority date: 1990-10-10
Filing date: 1990-10-10
Publication date: 1992-04-22
Anticipated expiration: 2005-10-10
Also published as: CN1022436C

Abstract

The present invention makes watt back of the body with high-intensity low carbon steel, make the bimetal plate of bearing bush with the antifriction alloy layer, make semicircle bearing shell through blanking, punching press, after again two semicircle bearing shells all being cut to synthetic axle sleeve shape with the antifriction alloy layer of bearing shell two ends and thrust ring joint, place and carry out rolling spinning on the rotary forging machine, flange is rolled over the production technology of the manufacturing dual-shouldered bimetallic thrust axle bush blank of system both sides thrust ring.On multinomial economic and technical norms such as equipment investment, spillage of material, work efficiency, product overall construction intensity and mechanical property thereof, remarkable benefit is arranged all, solved the technical barrier of industrialness production double-turnup bearing shell.

Description

The production method of dual-shouldered bimetallic thrust axle bush

The present invention relates to a kind of manufacturing technique method that uses rotary forging machine manufacturing bimetal double-turnup thrust Sliding bush, belong to spinning sheet metal is put rolling processing, manufacturing machine is the production technical field of part blank in addition.

By the metal watt back of the body and its go up the sliding bearing reliable operation that constitutes coated with the thin antifriction alloy layer (claiming bearing bush again) of one deck with pouring process, sintering process or roll-bonding method, turn round steady, use is easy to maintenance, cost is low, be widely used in the machines such as metal-cutting machine tool, steam turbine, internal-combustion engine.The plain thrust bearing that the present invention relates to is the double-turnup thrust bearing shell (referring to Fig. 1) by the bimetal thrust garden ring formation at a bimetal half garden shape sleeve (bearing shell) and its two ends.This bearing shell because of its assembling, open and inspect conveniently, in the crankshaft support of various high speed engines, be used widely especially.Because this bearing shell need be at three surfaces (two side planes add in garden cylinder) top pouring antifriction alloy, the manufacturing process complexity, process equipment is huge, and the setting process appearance that a cover is simple, the adaptation industrialness of comparative maturity is produced is not arranged so far as yet.Method now relatively more commonly used is to utilize a cover rolling equipment, earlier bimetal plate is rolled into the Qian flute profile, and then the Qian frid is rolled into half garden shape bearing shell carries out cutting, needs a whole set of rolling equipment and strict and numerous and diverse technological process.Manufacturing process and requirement that milling method is manufactured flanger bearing liner specifically introduced in article " manufacture method of flanger bearing liner and equipment thereof " on the 4th phase of nineteen eighty-three " internal combustion engine part " periodical.The rolling equipment investment is expensive, and the manufacturing process link is many, and work efficiency is low.

The objective of the invention is to design the production technology that a kind of comparison is reasonable, can carry out the bimetal double-turnup sliding bearing blank of industrialness production, just utilize rotary forging machine to the bimetal plate spreading of rolling, the new process of manufacturing double-turnup thrust bearing shell.

The present invention is achieved in that earlier be the bearing shell that the bimetallic bearing sheet material integral body of two thrust ring width and sleeve length sum strikes out half garden shape to its length, again the synthetic axle sleeve shape of two and half garden shape bearing shell alignment, then, the antifriction alloy layer of the two ends of this axle sleeve and thrust ring joint is all machined away, form two width and all be not less than 2 millimeters garden annular groove, put into and place the spreading of rolling of horizontal rotary forging machine in the specialized mould, at this moment, the rotational speed of two horizontal pendulum swagings is identical, direction is opposite, and feeding in opposite directions simultaneously, applying same pressure and roll rolling, pendulum swaging rotating speed is 200-300 rev/min, pressure is the 50-200 MPa, two pendulum swagings are spreading rotation 5-25 circle separately, just can roll over thrust ring end face of system at both sides while flange, realizes the moulding of pendulum rolling flange.

Utilize the double-turnup Sliding bush of production technology manufacturing of the present invention to belong to overall structure, the structural strength height, easy to use and reliable, the present invention has solved the difficult problem of industrialized production double-turnup bearing shell better, can save expensive rolling equipment investment, having simplified processing process, reduced materials consumption, reduce production costs, is at present a kind of manufacturing process of more satisfactory bimetal double-turnup bearing shell.

Fig. 1 is the double-turnup bearing shell processed of the present invention part figure in addition.

Fig. 2 is flow figure of the present invention.

Fig. 3 is that the present invention rolls the process schematic representation of rolling over flange on horizontal rotary forging press.

Fig. 4 is the schematic representation of the pendulum swaging female mould cavities of rotary forging press.

Below in conjunction with accompanying drawing, specifically introduce the present invention

The double-turnup thrust bearing shell is widely used on the crankshaft support of motor, except guaranteeing the axially locating of bent axle, bear outside the radial load, also to bear the end thrust that clutch etc. causes, bear thrust load, its structure is referring to Fig. 1, includes the bearing shell 1 that bears these two kinds of load respectively and the thrust garden ring 2 at two ends.Consider from mechanical strength and processing technology, half bearing thickness should not be thin excessively, usually liner wall thickness should be not less than 0.75 millimeter, often bearing shell is made bimetallic in order further to save antifriction material again, promptly be that backing 3(claims a watt back of the body again with low carbon steel), on backing, can be Cuprum alloy, aluminum alloy, metallo-plastic class coated with the thin antifriction material 4(of one deck) as bearing bush (claiming alloy-layer again).The bimetal plate that the present invention uses can be cast or rolling compound or sinter molding.

Manufacturing process of the present invention as shown in Figure 2.At first be that blanking-its length is the bearing shell that the half garden shape that meets the technological requirement diameter is made in the whole punching press of bimetallic bearing sheet material of two thrust ring width and bearing shell length sum, again the synthetic axle sleeve shape of two and half garden shape bearing shell alignment, then, utilize stock-removing machine that the antifriction alloy layer of axle sleeve and thrust ring joint, two ends is all cut and remove, two width of formation are not less than 2 millimeters garden annular groove near bearing shell and two ends thrust ring intersection interface.If make the antifriction bearing lining with aluminum alloy or metallo-plastic, can omit cutting garden this operation of annular groove.At this moment, can put into two involutory bearing shells and place the spreading of rolling of horizontal rotary forging machine in the specialized mould.Add man-hour, the rotational speed of two horizontal pendulum swagings is identical, and direction is opposite, and feeding in opposite directions simultaneously, applying same pressure and roll rolling, pendulum swaging rotating speed is 200-300 rev/min, pressure is the 50-200 MPa, and the pivot angle of the axis of two swagings and thrust ring Transverse plane is 0 °-3 °.When pendulum is rolled over (referring to Fig. 3), two conical-pendulum swagings 5 extend transversely in the bearing shell sleeve 6, female mould cavities on the pendulum swaging poppet surface contacts earlier with the antifriction alloy layer at bearing shell sleeve two ends, along with the continuous rotation of pendulum swaging with to centre pressurization feeding, realized screwfeed, making the double-metal layer at whole bearing shell sleeve two ends is root outwards overturning moulding successively gradually along its groove that is cut.Roll at this and to run in the journey, the low carbon steel watt back of the body that plastic deformation is good and antifriction layer bearing bush are always along the surperficial calendering forming of the matrix cavity of pendulum swaging, the matrix cavity external diameter a of yaw, degree of depth h and bottom width b should with the external diameter of two ends thrust ring, thickness and width equate, the home record limit of die cavity then is to be that awl point in garden, the end is the conical surface (referring to Fig. 4) on summit with the end in the cavity, bimetal plate is squeezed in the matrix cavity when pendulum is rolled over along this conical surface, at last, the double-metal layer at bearing shell two ends is that the root overturning becomes the thrust of double-turnup garden ring in specialized mould 7 both sides and crowded being filled in of rolling in the cavity with the garden annular groove all, again through the rotation of the several times of overswing swaging with exert pressure, yaw reposefully repeatedly spreading move past thrust garden ring surface, make the thrust ring surface reach very high finishingness and dimensional accuracy, can guarantee the vertical precision of thrust garden ring and bearing shell simultaneously again.During leaded more bimetal plate bearing shell, should heat in, the antifriction alloy layer relatively poor, in 150 ° of-600 ℃ of scopes, select suitable temperature to carry out temperature rolling, to prevent the cracking of antifriction alloy layer to workpiece in the spreading plastic deformation.Except with the moulding of horizontal rotary forging press spreading flange, can also place the spreading of rolling of vertical rotary forging press putting into two and half garden shape bearing shells in the specialized mould, process parameter with horizontal roll when rolling over identical, after rolling rolling flange one side thrust ring end face, be inverted workpiece again and roll the thrust ring end face of rolling over opposite side.Add man-hour and roll to roll on vertical rotary forging press, can be the feeding of exerting pressure downwards of pendulum swaging, also can use the feeding of act formula oil cylinder pushing workpiece.

(this moment, little fan-shaped half damaged rather than complete garden ring was left at the Ban Yuan two ends of thrust ring except two synthetic axle sleeve shapes of bearing shell alignment are processed in the present invention, but can not influence its application under various operating modes) in addition, can also put into specialized mould to single bearing shell and put rolling, can obtain complete Ban Yuan garden ring like this.At this moment should this bearing shell settle a similar bearing shell thrust ring of its shape on the position in relative other half garden elastic damping device or ebonite module, rotation in order to the balance yaw is stressed, at this moment, it is similar that process parameter and above-mentioned two bearing shells add man-hour to synthetic axle sleeve, and just yaw vertical feed speed should take the circumstances into consideration to slow down.

Claims

1, a kind of production technology of bimetal double-turnup thrust Sliding bush blank, it is characterized in that earlier be the bearing shell that half garden shape is made in the whole punching press of bimetallic bearing sheet material of two thrust ring width and bearing shell length sum to its length, again the synthetic axle sleeve shape of two and half garden shape bearing shell alignment, then, the antifriction alloy layer of the two ends of this axle sleeve and thrust ring joint is all machined away, form two width and all be not less than 2 millimeters garden annular groove, put into and place the spreading of rolling of horizontal rotary forging machine in the specialized mould, at this moment, the rotational speed of two horizontal pendulum swagings is identical, direction is opposite, and feeding in opposite directions simultaneously, apply same pressure and roll rolling, pendulum swaging rotating speed is 200-300 rev/min, pressure is the 50-200 MPa, and the axis of two pendulum swagings and the angle of thrust ring Transverse plane are 0 °-3 °, and two pendulum swagings are spreading rotation 5-25 circle separately, just can flange rolling simultaneously make a thrust ring end face, realize the moulding of roll extrusion flange on both sides.

2, production method as claimed in claim 1, it is characterized in that except with the moulding of horizontal rotary forging press spreading flange, can also place the spreading of rolling of vertical rotary forging press putting into two and half garden shape bearing shells in the specialized mould, process parameter with horizontal roll when rolling over identical, after rolling rolling flange one side thrust ring end face, be inverted workpiece again, roll the thrust ring end face of rolling over opposite side.

3, production method as claimed in claim 1 is characterized in that bimetallic bearing sheet material is is watt back of the body with low carbon steel, is bearing bush with Cuprum alloy, aluminum alloy, metallo-plastic.

4, as claim 1 or 3 described production methods, it is characterized in that with aluminum alloy, metallo-plastic be the operation that the bimetal plate of bearing bush can omit cutting antifriction bearing lining machined grooves, after to synthetic axle sleeve garden tubular, can directly roll and roll over the flange moulding.

5,, it is characterized in that bimetallic bearing sheet material can be cast molding or sinter molding or rolling compound as claim 1 or 3 described production methods.

6, production method as claimed in claim 1 or 2 is characterized in that rolling on vertical rotary forging press rolling over and adds man-hour, can be the feeding of exerting pressure downwards of pendulum swaging, also can use the feeding of act formula oil cylinder pushing workpiece.

7, production method as claimed in claim 1 is characterized in that serving as a contrast for leaded copper/copper alloy bearing more, that plasticity is relatively poor, should be heated to 150 °-600 ℃ to workpiece and carry out the temperature rolling.

8, production method as claimed in claim 1, the external diameter, the degree of depth and the bottom width that it is characterized in that putting the outer rib of the spill work die cavity on the swaging poppet surface all equate with external diameter, thickness and the width of the thrust garden ring of being processed, and the inner retaining side of die cavity is then for being that the pinnacle of garden, the end, poppet surface is the conical surface on summit with the end in this cavity.

9, production method as claimed in claim 1, it is characterized in that except two synthetic axle sleeve shapes of bearing shell alignment being carried out flange processing, can also put into single bearing shell and roll the rolling flange in the specialized mould, make the double-turnup half garden bearing shell of complete Ban Yuan garden ring thrust ring; At this moment, should this bearing shell in the mould lay a similar bearing shell thrust ring of its shape on the relative other Ban Yuan position elastic damping device or ebonite module, process parameter and above-mentioned condition are basic identical, but feed speed will take the circumstances into consideration to slow down.