CN106048153A - 一种合金钢的快速热处理工艺 - Google Patents

一种合金钢的快速热处理工艺 Download PDF

Info

Publication number
CN106048153A
CN106048153A CN201610571577.7A CN201610571577A CN106048153A CN 106048153 A CN106048153 A CN 106048153A CN 201610571577 A CN201610571577 A CN 201610571577A CN 106048153 A CN106048153 A CN 106048153A
Authority
CN
China
Prior art keywords
alloy steel
heat treatment
treatment technology
steel alloy
rapid heat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610571577.7A
Other languages
English (en)
Inventor
何拥军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LIUZHOU KEERTE FORGING MACHINERY Co Ltd
Original Assignee
LIUZHOU KEERTE FORGING MACHINERY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LIUZHOU KEERTE FORGING MACHINERY Co Ltd filed Critical LIUZHOU KEERTE FORGING MACHINERY Co Ltd
Priority to CN201610571577.7A priority Critical patent/CN106048153A/zh
Publication of CN106048153A publication Critical patent/CN106048153A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种合金钢的快速热处理工艺，包括如下步骤：1）将合金钢以1000C/s的速度快速加热至1000摄氏度，然后保温5s；2）将步骤1）得到的合金钢以8000C/s的速度冷却至马氏体温度以下；3）将步骤2）得到的合金钢重新加热至300摄氏度，保温20~25min后，冷却至室温。本发明公开的一种合金钢的快速热处理工艺，相比常规方法，在保证合金钢的高强度的同时，还可以将其力学性能控制在最佳状态。

Description

一种合金钢的快速热处理工艺
技术领域
本发明涉及钢材技术领域,尤其涉及一种合金钢的快速热处理工艺。
背景技术
通常情况下，汽车用高强度钢材都需要经过热压加工后成型使用，热加工过程中钢材的组织性能发生变化（如动态/静态回复与再结晶等等），不同的合金元素及加热工艺对其钢材的热变行为会产生影响，从而直接影响钢材的性能。
发明内容
为解决现有技术和实际情况中存在的上述问题，本发明提供了一种合金钢的快速热处理工艺，其特征在于，包括如下步骤：
1）将合金钢以1000C/s的速度快速加热至1000摄氏度，然后保温5s；
2）将步骤1）得到的合金钢以8000C/s的速度冷却至马氏体温度以下；
3）将步骤2）得到的合金钢重新加热至300摄氏度，保温20~25min后，冷却至室温。
有益效果：
本发明公开的一种合金钢的快速热处理工艺，相比常规方法，在保证合金钢的高强度的同时，还可以将其力学性能控制在最佳状态。
具体实施方式
下面详细介绍本发明技术方案。
本发明提供了一种合金钢的快速热处理工艺，其特征在于，包括如下步骤：
1）将合金钢以1000C/s的速度快速加热至1000摄氏度，然后保温5s；
2）将步骤1）得到的合金钢以8000C/s的速度冷却至马氏体温度以下；
3）将步骤2）得到的合金钢重新加热至300摄氏度，保温20~25min后，冷却至室温。
有益效果：
本发明公开的一种合金钢的快速热处理工艺，相比常规方法，在保证合金钢的高强度的同时，还可以将其力学性能控制在最佳状态。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (1)

1.一种合金钢的快速热处理工艺，其特征在于，包括如下步骤：
（1）将合金钢以1000C/s的速度快速加热至1000摄氏度，然后保温5s；
（2）将步骤1）得到的合金钢以8000C/s的速度冷却至马氏体温度以下；
（3）将步骤2）得到的合金钢重新加热至300摄氏度，保温20~25min后，冷却至室温。
CN201610571577.7A 2016-07-20 2016-07-20 一种合金钢的快速热处理工艺 Pending CN106048153A (zh)