CN106047192A - Computer advertising art design packing bag binder - Google Patents
Computer advertising art design packing bag binder Download PDFInfo
- Publication number
- CN106047192A CN106047192A CN201610523801.5A CN201610523801A CN106047192A CN 106047192 A CN106047192 A CN 106047192A CN 201610523801 A CN201610523801 A CN 201610523801A CN 106047192 A CN106047192 A CN 106047192A
- Authority
- CN
- China
- Prior art keywords
- parts
- epoxy resin
- binding agent
- art design
- packaging bag
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a computer advertising art design packing bag binder which is composed of benzoyl peroxide, aluminum potassium sulfate dodecahydrate, white corundum micropowder, chitin, bisphenol A type epoxy resin, polyoxyethylene ether, glass fiber, furfuryl alcohol, triethylene glycol, glutaric acid, triaryl phosphate, calcium oxide, bismaleimide, lauryl sodium sulfate, polyethylene terephathalate, wollastonite in powder, fluoroether rubber, sodium allysulfonate, bibasic lead stearate, castor oil, tributyl citrate, polybutadiene epoxy resin, tribasic lead sulfate, melamine cyanurate, methyl triethoxy silane and diisobutyl ketone. Adopted raw materials are synergistic, so that antiaging performance of the binder is improved greatly, and temperature application range of the binder is widened, being minus 80-250 DEG C.
Description
Technical field
The present invention relates to a kind of computer Advertising art design packaging bag binding agent, belong to computer advertisement project packaging raw
Produce preparing technical field.
Background technology
Advertising art refers to the expressive art carried out for merchandise sales purpose.It is that one has a definite purpose, in a lot of limits
Creative utility art form under the conditions of system.Advertising art is the unique curved formula of the one separated in modern art,
Advertising art almost relates to modern all worlds of art, is magnificent in modern art jungle one, and has the spy of its own
Point and law of development.Advertising art design needs use some packaging bags, during the design of these packaging bags uses, need
Use binding agent to be bondd use, it is necessary to provide suitable binding agent.
Summary of the invention
It is an object of the invention to provide a kind of computer Advertising art design packaging bag binding agent, in order to be better achieved
The function of computer Advertising art design packaging bag binding agent.
To achieve these goals, technical scheme is as follows.
A kind of computer Advertising art design packaging bag binding agent, is made up of the component of following mass fraction: benzoyl peroxide
Formyl chloride-1 4~18 parts, 12 hydrazine aluminum sulfate potassium 16~20 parts, white fused alumina micropowder 12~16 parts, chitin 10~14 parts, bisphenol-A
Type epoxy resin 16~20 parts, polyoxyethylene ether 12~16 parts, glass fibre 10~14 parts, furfuryl alcohol 16~20 parts, triethylene glycol
12~16 parts, 1,3-propanedicarboxylic acid 10~14 parts, triaryl phosphate 16~20 parts, calcium oxide 12~16 parts, bimaleimide resin
12~16 parts, sodium lauryl sulphate 10~14 parts, polyethylene terephthalate 16~20 parts, wollastonite in powder 12~16 parts,
Fluoroether rubber 10~14 parts, sodium allylsulfonate 16~20 parts, dibasic lead stearate 12~16 parts, Oleum Ricini 10~14
Part, tributyl citrate 16~20 parts, polybutadiene epoxy resin 12~16 parts, lead sulfate tribasic 10~14 parts, melamine
Amine cyanurate 16~20 parts, MTES 12~16 parts, isobutyrone 12~16 parts.
Further, above computer Advertising art design packaging bag binding agent, it is made up of the component of following mass fraction:
Benzoyl peroxide 14 parts, 16 parts of 12 hydrazine aluminum sulfate potassium, white fused alumina micropowder 12 parts, chitin 10 parts, bisphenol type epoxy tree
16 parts of fat, polyoxyethylene ether 12 parts, glass fibre 10 parts, furfuryl alcohol 16 parts, triethylene glycol 12 parts, 1,3-propanedicarboxylic acid 10 parts, triaryl phosphorus
Acid esters 16 parts, calcium oxide 12 parts, bimaleimide resin 12 parts, sodium lauryl sulphate 10 parts, poly terephthalic acid diethyl
Ester 16 parts, wollastonite in powder 12 parts, fluoroether rubber 10 parts, sodium allylsulfonate 16 parts, dibasic lead stearate 12 parts, Oleum Ricini
10 parts, tributyl citrate 16 parts, polybutadiene epoxy resin 12 parts, lead sulfate tribasic 10 parts, melamine cyanurate
16 parts, MTES 12 parts, isobutyrone 12 parts.
Further, above computer Advertising art design packaging bag binding agent, it is made up of the component of following mass fraction:
Benzoyl peroxide 16 parts, 18 parts of 12 hydrazine aluminum sulfate potassium, white fused alumina micropowder 14 parts, chitin 12 parts, bisphenol type epoxy tree
18 parts of fat, polyoxyethylene ether 14 parts, glass fibre 12 parts, furfuryl alcohol 18 parts, triethylene glycol 14 parts, 1,3-propanedicarboxylic acid 12 parts, triaryl phosphorus
Acid esters 18 parts, calcium oxide 14 parts, bimaleimide resin 14 parts, sodium lauryl sulphate 12 parts, poly terephthalic acid diethyl
Ester 18 parts, wollastonite in powder 14 parts, fluoroether rubber 12 parts, sodium allylsulfonate 18 parts, dibasic lead stearate 14 parts, Oleum Ricini
12 parts, tributyl citrate 18 parts, polybutadiene epoxy resin 14 parts, lead sulfate tribasic 12 parts, melamine cyanurate
18 parts, MTES 14 parts, isobutyrone 14 parts.
Further, above computer Advertising art design packaging bag binding agent, it is made up of the component of following mass fraction:
Benzoyl peroxide 18 parts, 20 parts of 12 hydrazine aluminum sulfate potassium, white fused alumina micropowder 16 parts, chitin 14 parts, bisphenol type epoxy tree
20 parts of fat, polyoxyethylene ether 16 parts, glass fibre 14 parts, furfuryl alcohol 20 parts, triethylene glycol 16 parts, 1,3-propanedicarboxylic acid 14 parts, triaryl phosphorus
Acid esters 20 parts, calcium oxide 16 parts, bimaleimide resin 16 parts, sodium lauryl sulphate 14 parts, poly terephthalic acid diethyl
Ester 20 parts, wollastonite in powder 16 parts, fluoroether rubber 14 parts, sodium allylsulfonate 20 parts, dibasic lead stearate 16 parts, Oleum Ricini
14 parts, tributyl citrate 20 parts, polybutadiene epoxy resin 16 parts, lead sulfate tribasic 14 parts, melamine cyanurate
20 parts, MTES 16 parts, isobutyrone 16 parts.
Further, above computer Advertising art design packaging bag binding agent preparation method step is as follows:
(1) by the benzoyl peroxide of described mass fraction, 12 hydrazine aluminum sulfate potassium, white fused alumina micropowder, chitin, double
Phenol A type epoxy resin, polyoxyethylene ether, glass fibre, furfuryl alcohol, triethylene glycol, 1,3-propanedicarboxylic acid, triaryl phosphate, calcium oxide, lemon
Lemon acid tributyl, polybutadiene epoxy resin, lead sulfate tribasic, melamine cyanurate, MTES, two
Isobutyl ketone is mixed, and is sequentially added in agitator tank, is sufficiently stirred for 30 minutes with the speed of 200rpm;
(2) sodium lauryl sulphate of described mass fraction, polyethylene terephthalate, wollastonite in powder, fluorine ether are added
Rubber, is sufficiently stirred for 60 minutes with the speed of 300rpm;
(3) add the bimaleimide resin of described mass fraction, sodium allylsulfonate, dibasic lead stearate,
Oleum Ricini, is sufficiently stirred for 90 minutes with the speed of 400rpm, obtains binder product.
This beneficial effect of the invention is: the present invention relates to a kind of computer Advertising art design packaging bag binding agent, by
Following components form: benzoyl peroxide, 12 hydrazine aluminum sulfate potassium, white fused alumina micropowder, chitin, bisphenol A type epoxy resin,
Polyoxyethylene ether, glass fibre, furfuryl alcohol, triethylene glycol, 1,3-propanedicarboxylic acid, triaryl phosphate, calcium oxide, BMI tree
Fat, sodium lauryl sulphate, polyethylene terephthalate, wollastonite in powder, fluoroether rubber, sodium allylsulfonate, dibasicity
Lead stearate, Oleum Ricini, tributyl citrate, polybutadiene epoxy resin, lead sulfate tribasic, melamine cyanurate,
MTES, isobutyrone.The letter of this computer Advertising art design packaging bag binding agent process of preparing
Single, prepared product, by rational proportioning and mixing, makes to produce between each component synergism, overcomes and each individually make
The deficiency of used time, defines the cross-linked structure with performances such as excellent high temperature resistant, anticorrosive, high-adhesion, mechanicalnesses.This
The room temperature down cut intensity of bright offer can reach more than 45MPa, and shear strength when 250 DEG C is more than 18MPa, it is possible to meets
Glued part is the requirement of long-term work at 250 DEG C.Raw material of the present invention produces synergism, is greatly improved bonding
The ageing resistace of agent, improving the temperature adaptation scope of binding agent, its temperature adaptation scope is-80~250 DEG C.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is described, in order to be better understood from the present invention.
Embodiment 1
Computer Advertising art design packaging bag binding agent in the present embodiment, is made up of the component of following mass fraction:
Benzoyl peroxide 14 parts, 16 parts of 12 hydrazine aluminum sulfate potassium, white fused alumina micropowder 12 parts, chitin 10 parts, bisphenol type epoxy tree
16 parts of fat, polyoxyethylene ether 12 parts, glass fibre 10 parts, furfuryl alcohol 16 parts, triethylene glycol 12 parts, 1,3-propanedicarboxylic acid 10 parts, triaryl phosphorus
Acid esters 16 parts, calcium oxide 12 parts, bimaleimide resin 12 parts, sodium lauryl sulphate 10 parts, poly terephthalic acid diethyl
Ester 16 parts, wollastonite in powder 12 parts, fluoroether rubber 10 parts, sodium allylsulfonate 16 parts, dibasic lead stearate 12 parts, Oleum Ricini
10 parts, tributyl citrate 16 parts, polybutadiene epoxy resin 12 parts, lead sulfate tribasic 10 parts, melamine cyanurate
16 parts, MTES 12 parts, isobutyrone 12 parts.
Above computer Advertising art design packaging bag binding agent preparation method step is as follows:
(1) by the benzoyl peroxide of described mass fraction, 12 hydrazine aluminum sulfate potassium, white fused alumina micropowder, chitin, double
Phenol A type epoxy resin, polyoxyethylene ether, glass fibre, furfuryl alcohol, triethylene glycol, 1,3-propanedicarboxylic acid, triaryl phosphate, calcium oxide, lemon
Lemon acid tributyl, polybutadiene epoxy resin, lead sulfate tribasic, melamine cyanurate, MTES, two
Isobutyl ketone is mixed, and is sequentially added in agitator tank, is sufficiently stirred for 30 minutes with the speed of 200rpm;
(2) sodium lauryl sulphate of described mass fraction, polyethylene terephthalate, wollastonite in powder, fluorine ether are added
Rubber, is sufficiently stirred for 60 minutes with the speed of 300rpm;
(3) add the bimaleimide resin of described mass fraction, sodium allylsulfonate, dibasic lead stearate,
Oleum Ricini, is sufficiently stirred for 90 minutes with the speed of 400rpm, obtains binder product.
Embodiment 2
Computer Advertising art design packaging bag binding agent in the present embodiment, is made up of the component of following mass fraction:
Benzoyl peroxide 16 parts, 18 parts of 12 hydrazine aluminum sulfate potassium, white fused alumina micropowder 14 parts, chitin 12 parts, bisphenol type epoxy tree
18 parts of fat, polyoxyethylene ether 14 parts, glass fibre 12 parts, furfuryl alcohol 18 parts, triethylene glycol 14 parts, 1,3-propanedicarboxylic acid 12 parts, triaryl phosphorus
Acid esters 18 parts, calcium oxide 14 parts, bimaleimide resin 14 parts, sodium lauryl sulphate 12 parts, poly terephthalic acid diethyl
Ester 18 parts, wollastonite in powder 14 parts, fluoroether rubber 12 parts, sodium allylsulfonate 18 parts, dibasic lead stearate 14 parts, Oleum Ricini
12 parts, tributyl citrate 18 parts, polybutadiene epoxy resin 14 parts, lead sulfate tribasic 12 parts, melamine cyanurate
18 parts, MTES 14 parts, isobutyrone 14 parts.
Above computer Advertising art design packaging bag binding agent preparation method step is as follows:
(1) by the benzoyl peroxide of described mass fraction, 12 hydrazine aluminum sulfate potassium, white fused alumina micropowder, chitin, double
Phenol A type epoxy resin, polyoxyethylene ether, glass fibre, furfuryl alcohol, triethylene glycol, 1,3-propanedicarboxylic acid, triaryl phosphate, calcium oxide, lemon
Lemon acid tributyl, polybutadiene epoxy resin, lead sulfate tribasic, melamine cyanurate, MTES, two
Isobutyl ketone is mixed, and is sequentially added in agitator tank, is sufficiently stirred for 30 minutes with the speed of 200rpm;
(2) sodium lauryl sulphate of described mass fraction, polyethylene terephthalate, wollastonite in powder, fluorine ether are added
Rubber, is sufficiently stirred for 60 minutes with the speed of 300rpm;
(3) add the bimaleimide resin of described mass fraction, sodium allylsulfonate, dibasic lead stearate,
Oleum Ricini, is sufficiently stirred for 90 minutes with the speed of 400rpm, obtains binder product.
Embodiment 3
Computer Advertising art design packaging bag binding agent in the present embodiment, is made up of the component of following mass fraction:
Benzoyl peroxide 18 parts, 20 parts of 12 hydrazine aluminum sulfate potassium, white fused alumina micropowder 16 parts, chitin 14 parts, bisphenol type epoxy tree
20 parts of fat, polyoxyethylene ether 16 parts, glass fibre 14 parts, furfuryl alcohol 20 parts, triethylene glycol 16 parts, 1,3-propanedicarboxylic acid 14 parts, triaryl phosphorus
Acid esters 20 parts, calcium oxide 16 parts, bimaleimide resin 16 parts, sodium lauryl sulphate 14 parts, poly terephthalic acid diethyl
Ester 20 parts, wollastonite in powder 16 parts, fluoroether rubber 14 parts, sodium allylsulfonate 20 parts, dibasic lead stearate 16 parts, Oleum Ricini
14 parts, tributyl citrate 20 parts, polybutadiene epoxy resin 16 parts, lead sulfate tribasic 14 parts, melamine cyanurate
20 parts, MTES 16 parts, isobutyrone 16 parts.
Above computer Advertising art design packaging bag binding agent preparation method step is as follows:
(1) by the benzoyl peroxide of described mass fraction, 12 hydrazine aluminum sulfate potassium, white fused alumina micropowder, chitin, double
Phenol A type epoxy resin, polyoxyethylene ether, glass fibre, furfuryl alcohol, triethylene glycol, 1,3-propanedicarboxylic acid, triaryl phosphate, calcium oxide, lemon
Lemon acid tributyl, polybutadiene epoxy resin, lead sulfate tribasic, melamine cyanurate, MTES, two
Isobutyl ketone is mixed, and is sequentially added in agitator tank, is sufficiently stirred for 30 minutes with the speed of 200rpm;
(2) sodium lauryl sulphate of described mass fraction, polyethylene terephthalate, wollastonite in powder, fluorine ether are added
Rubber, is sufficiently stirred for 60 minutes with the speed of 300rpm;
(3) add the bimaleimide resin of described mass fraction, sodium allylsulfonate, dibasic lead stearate,
Oleum Ricini, is sufficiently stirred for 90 minutes with the speed of 400rpm, obtains binder product.
Comparative example 1
1) thermoplastic acrylic resin 25 parts that weight average molecular weight is 70000~75000 is weighed respectively, organic-silicon-modified third
Olefin(e) acid resin 20 parts, is sequentially added in agitator tank, is sufficiently stirred for 40 minutes with the speed of 100rpm;
B) melmac 10 parts is continuously added, phenyl trichlorosilane 7 parts, vinyltrimethoxy silane 5 parts, with
The speed of 100rpm is sufficiently stirred for 60 minutes;
C) in the mixture of step b), titanium dioxide 7 parts is continuously added, attapulgite 5 parts, dichlorotetra-fluoroethane 5 parts, second
Glycol monobutyl ether 20 parts, is sufficiently stirred for 60 minutes with the speed of 100rpm, obtains the binder product in this comparative example.
Comparative example 2
1) weighing epoxy modified hydroxyl acrylic resin 25 parts respectively, weight average molecular weight is the thermoplasticity of 70000~75000
Acrylic resin 25 parts, is sequentially added in agitator tank, is sufficiently stirred for 40 minutes with the speed of 100rpm;
2) melmac 10 parts is continuously added, phenyl trichlorosilane 7 parts, vinyltrimethoxy silane 5 parts, with
The speed of 100rpm is sufficiently stirred for 60 minutes;
3) in the mixture of step b), titanium dioxide 7 parts is continuously added, attapulgite 5 parts, dichlorotetra-fluoroethane 5 parts, second
Glycol monobutyl ether 20 parts, is sufficiently stirred for 60 minutes with the speed of 100rpm, obtains binder product.
By the binding agent prepared by embodiment 1, embodiment 2, embodiment 3 and comparative example 1, comparative example 2 at-80~280 DEG C
The lower respective shear strength of test and tolerance time, the testing time is 360 days, and concrete outcome is as shown in following table 1-5:
Binder Properties test result at 1-80 DEG C of table
Group | Tolerance time | Shear strength |
Embodiment 1 | Not fragmentation in 50 days, does not falls off | 15MPa |
Embodiment 2 | Not fragmentation in 52 days, does not falls off | 17MPa |
Embodiment 3 | Not fragmentation in 48 days, does not falls off | 16MPa |
Comparative example 1 | 0 day, binding agent fragmentation came off | 0 |
Comparative example 2 | 0 day, binding agent fragmentation came off | 0 |
Binder Properties test result at 20 DEG C of table
Group | Tolerance time | Shear strength |
Embodiment 1 | Not fragmentation in 50 days, does not falls off | 25MPa |
Embodiment 2 | Not fragmentation in 52 days, does not falls off | 28MPa |
Embodiment 3 | Not fragmentation in 48 days, does not falls off | 23MPa |
Comparative example 1 | After 30 days, binding agent fragmentation comes off | 10MPa |
Comparative example 2 | After 20 days, binding agent fragmentation comes off | 8MPa |
Binder Properties test result at 3 20 DEG C of table
Group | Tolerance time | Shear strength |
Embodiment 1 | Not fragmentation in 360 days, does not falls off | 45MPa |
Embodiment 2 | Not fragmentation in 360 days, does not falls off | 46MPa |
Embodiment 3 | Not fragmentation in 360 days, does not falls off | 47MPa |
Comparative example 1 | Not fragmentation in 360 days, does not falls off | 18MPa |
Comparative example 2 | Not fragmentation in 360 days, does not falls off | 16MPa |
Binder Properties test result at 4 150 DEG C of table
Group | Tolerance time | Shear strength |
Embodiment 1 | 360 days not softening and sheddings | 22MPa |
Embodiment 2 | 360 days not softening and sheddings | 24MPa |
Embodiment 3 | 360 days not softening and sheddings | 23MPa |
Comparative example 1 | After 10 days, binding agent softens | 10MPa |
Comparative example 2 | After 10 days, binding agent softens | 8MPa |
Binder Properties test result at 5 250 DEG C of table
Group | Tolerance time | Shear strength |
Embodiment 1 | 280 days not softening and sheddings | 18MPa |
Embodiment 2 | 280 days not softening and sheddings | 19MPa |
Embodiment 3 | 280 days not softening and sheddings | 18MPa |
Comparative example 1 | After 3 days, binding agent softens | 4MPa |
Comparative example 2 | After 3 days, binding agent softens | 3MPa |
The above is the preferred embodiment of the present invention, it is noted that for those skilled in the art
For, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications are also considered as
Protection scope of the present invention.
Claims (5)
1. a computer Advertising art design packaging bag binding agent, it is characterised in that: it is made up of the component of following mass fraction:
Benzoyl peroxide 14~18 parts, 12 hydrazine aluminum sulfate potassium 16~20 parts, white fused alumina micropowder 12~16 parts, chitin 10~14
Part, bisphenol A type epoxy resin 16~20 parts, polyoxyethylene ether 12~16 parts, glass fibre 10~14 parts, furfuryl alcohol 16~20 parts,
Triethylene glycol 12~16 parts, 1,3-propanedicarboxylic acid 10~14 parts, triaryl phosphate 16~20 parts, calcium oxide 12~16 parts, double maleoyl
Imide resin 12~16 parts, sodium lauryl sulphate 10~14 parts, polyethylene terephthalate 16~20 parts, wollastonite in powder 12
~16 parts, fluoroether rubber 10~14 parts, sodium allylsulfonate 16~20 parts, dibasic lead stearate 12~16 parts, Oleum Ricini
10~14 parts, tributyl citrate 16~20 parts, polybutadiene epoxy resin 12~16 parts, lead sulfate tribasic 10~14 parts,
Melamine cyanurate 16~20 parts, MTES 12~16 parts, isobutyrone 12~16 parts.
Computer Advertising art design packaging bag binding agent the most according to claim 1, it is characterised in that: described computer
Advertising art design packaging bag binding agent is made up of the component of following mass fraction: benzoyl peroxide 14 parts, 12 hydration sulfur
Acid 16 parts of aluminum potassium, white fused alumina micropowder 12 parts, chitin 10 parts, bisphenol A type epoxy resin 16 parts, polyoxyethylene ether 12 parts, glass
Fiber 10 parts, furfuryl alcohol 16 parts, triethylene glycol 12 parts, 1,3-propanedicarboxylic acid 10 parts, triaryl phosphate 16 parts, calcium oxide 12 parts, span come
Imide resin 12 parts, sodium lauryl sulphate 10 parts, polyethylene terephthalate 16 parts, wollastonite in powder 12 parts, fluorine ether rubber
10 parts of glue, sodium allylsulfonate 16 parts, dibasic lead stearate 12 parts, Oleum Ricini 10 parts, tributyl citrate 16 parts, poly-fourth
Diene epoxy resin 12 parts, lead sulfate tribasic 10 parts, melamine cyanurate 16 parts, MTES 12 parts,
Isobutyrone 12 parts.
Computer Advertising art design packaging bag binding agent the most according to claim 1, it is characterised in that: described computer
Advertising art design packaging bag binding agent is made up of the component of following mass fraction: benzoyl peroxide 16 parts, 12 hydration sulfur
Acid 18 parts of aluminum potassium, white fused alumina micropowder 14 parts, chitin 12 parts, bisphenol A type epoxy resin 18 parts, polyoxyethylene ether 14 parts, glass
Fiber 12 parts, furfuryl alcohol 18 parts, triethylene glycol 14 parts, 1,3-propanedicarboxylic acid 12 parts, triaryl phosphate 18 parts, calcium oxide 14 parts, span come
Imide resin 14 parts, sodium lauryl sulphate 12 parts, polyethylene terephthalate 18 parts, wollastonite in powder 14 parts, fluorine ether rubber
12 parts of glue, sodium allylsulfonate 18 parts, dibasic lead stearate 14 parts, Oleum Ricini 12 parts, tributyl citrate 18 parts, poly-fourth
Diene epoxy resin 14 parts, lead sulfate tribasic 12 parts, melamine cyanurate 18 parts, MTES 14 parts,
Isobutyrone 14 parts.
Computer Advertising art design packaging bag binding agent the most according to claim 1, it is characterised in that: described computer
Advertising art design packaging bag binding agent is made up of the component of following mass fraction: benzoyl peroxide 18 parts, 12 hydration sulfur
Acid 20 parts of aluminum potassium, white fused alumina micropowder 16 parts, chitin 14 parts, bisphenol A type epoxy resin 20 parts, polyoxyethylene ether 16 parts, glass
Fiber 14 parts, furfuryl alcohol 20 parts, triethylene glycol 16 parts, 1,3-propanedicarboxylic acid 14 parts, triaryl phosphate 20 parts, calcium oxide 16 parts, span come
Imide resin 16 parts, sodium lauryl sulphate 14 parts, polyethylene terephthalate 20 parts, wollastonite in powder 16 parts, fluorine ether rubber
14 parts of glue, sodium allylsulfonate 20 parts, dibasic lead stearate 16 parts, Oleum Ricini 14 parts, tributyl citrate 20 parts, poly-fourth
Diene epoxy resin 16 parts, lead sulfate tribasic 14 parts, melamine cyanurate 20 parts, MTES 16 parts,
Isobutyrone 16 parts.
Computer Advertising art design packaging bag binding agent the most according to claim 1, it is characterised in that: described computer
Advertising art design packaging bag binding agent preparation method step is as follows:
(1) by the benzoyl peroxide of described mass fraction, 12 hydrazine aluminum sulfate potassium, white fused alumina micropowder, chitin, bisphenol-A
Type epoxy resin, polyoxyethylene ether, glass fibre, furfuryl alcohol, triethylene glycol, 1,3-propanedicarboxylic acid, triaryl phosphate, calcium oxide, Fructus Citri Limoniae
Acid tributyl, polybutadiene epoxy resin, lead sulfate tribasic, melamine cyanurate, MTES, two different
Butyl ketone is mixed, and is sequentially added in agitator tank, is sufficiently stirred for about 30 minutes with the speed of 200rpm;
(2) sodium lauryl sulphate of described mass fraction, polyethylene terephthalate, wollastonite in powder, fluoroether rubber are added,
It is sufficiently stirred for about 60 minutes with the speed of 300rpm;
(3) bimaleimide resin of described mass fraction, sodium allylsulfonate, dibasic lead stearate, Semen Ricini are added
Oil, is sufficiently stirred for about 90 minutes with the speed of 400rpm, obtains binder product.