CN106147653A - A kind of aluminium alloy extrusions product installation binding agent - Google Patents
A kind of aluminium alloy extrusions product installation binding agent Download PDFInfo
- Publication number
- CN106147653A CN106147653A CN201610520520.4A CN201610520520A CN106147653A CN 106147653 A CN106147653 A CN 106147653A CN 201610520520 A CN201610520520 A CN 201610520520A CN 106147653 A CN106147653 A CN 106147653A
- Authority
- CN
- China
- Prior art keywords
- parts
- binding agent
- aluminium alloy
- alloy extrusions
- product installation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of aluminium alloy extrusions product installation binding agent, composed of the following components: DEF, chitin, aluminium-hydroxide powder, pottery ground-slag end, polyamide, castor oil, basalt fibre, hydroxypropyl methyl cellulose, chlorosulfonated polyethylene, cobalt naphthenate, linseed oil alkyd resin, N phenyl 2 naphthylamines, trbasic zinc phosphate, potassium titanate crystal whisker reinforcement, graphite fibre, paraffin oil, triethylene tetramine, calcium phosphate, dimethyl silicone polymer, trimethylolpropane, Cocoamidopropyl betaine, rock wool powder, cobalt iso-octoate, toluene-2,4-diisocyanate, sodium metasilicate, acrylic acid, pentachloronitrobenzene, Sandofan, vancomycin.Raw material of the present invention produces synergy, and the ageing resistace being greatly improved binding agent, the Acclimation temperature scope improving binding agent, its Acclimation temperature scope is 80~250 DEG C.
Description
Technical field
The present invention relates to a kind of aluminium alloy extrusions product installation binding agent, belong to aluminium alloy extrusions production and prepare skill
Art field.
Background technology
Aluminium alloy extrusions is a most widely used class non-ferrous metal structural material in industry, Aeronautics and Astronautics, automobile,
Machine-building, boats and ships, building, finishing and chemical industry are widely applied.With scientific and technical in recent years and industrial economy
Develop rapidly, increasing to the demand of Welded structural member.In aluminium alloy extrusions product installation process, it is often necessary to
Use suitable binding agent, in order to improve its using effect as required.
Content of the invention
It is an object of the invention to provide a kind of aluminium alloy extrusions product installation binding agent, in order to aluminium is better achieved and closes
The function of gold product forms installation binding agent.
To achieve these goals, technical scheme is as follows.
A kind of aluminium alloy extrusions product installation binding agent, is made up of the component of following mass fraction: DEF
16~20 parts, chitin 18~22 parts, aluminium-hydroxide powder 14~18 parts, pottery 12~16 parts of ground-slag end, polyamide 18~22
Part, castor oil 14~18 parts, basalt fibre 12~16 parts, hydroxypropyl methyl cellulose 18~22 parts, chlorosulfonated polyethylene 14
~18 parts, cobalt naphthenate 12~16 parts, linseed oil alkyd resin 18~22 parts, N-phenyl-2-naphthylamine 14~18 parts, trbasic zinc phosphate 14
~18 parts, potassium titanate crystal whisker reinforcement 12~16 parts, graphite fibre 18~22 parts, paraffin oil 14~18 parts, triethylene tetramine 12
~16 parts, 18~22 parts of calcium phosphate, dimethyl silicone polymer 14~18 parts, trimethylolpropane 12~16 parts, coconut oleoyl amine third
Base glycine betaine 18~22 parts, 14~18 parts of rock wool powder, cobalt iso-octoate 12~16 parts, toluene-2,4-diisocyanate 18~22 parts, silicon
14~18 parts of sodium of acid, 14~18 parts of acrylic acid, pentachloronitrobenzene 14~18 parts, Sandofan 14~18 parts, vancomycin 14~18
Part.
Further, above-mentioned aluminium alloy extrusions product installation binding agent, is made up of the component of following mass fraction: rich horse
Diethyl phthalate 16 parts, chitin 18 parts, aluminium-hydroxide powder 14 parts, 12 parts of pottery ground-slag end, polyamide 18 parts, castor oil 14
Part, basalt fibre 12 parts, hydroxypropyl methyl cellulose 18 parts, chlorosulfonated polyethylene 14 parts, cobalt naphthenate 12 parts, flax oleyl alcohol
Acid resin 18 parts, N-phenyl-2-naphthylamine 14 parts, trbasic zinc phosphate 14 parts, potassium titanate crystal whisker reinforcement 12 parts, graphite fibre 18 parts, stone
Wax oil 14 parts, triethylene tetramine 12 parts, 18 parts of calcium phosphate, dimethyl silicone polymer 14 parts, trimethylolpropane 12 parts, cocounut oil acyl
Amine CAB 18 parts, 14 parts of rock wool powder, cobalt iso-octoate 12 parts, toluene-2,4-diisocyanate 18 parts, sodium metasilicate 14 parts, propylene
Acid 14 parts, pentachloronitrobenzene 14 parts, Sandofan 14 parts, vancomycin 14 parts.
Further, above-mentioned aluminium alloy extrusions product installation binding agent, is made up of the component of following mass fraction: rich horse
Diethyl phthalate 18 parts, chitin 20 parts, aluminium-hydroxide powder 16 parts, 14 parts of pottery ground-slag end, polyamide 20 parts, castor oil 16
Part, basalt fibre 14 parts, hydroxypropyl methyl cellulose 20 parts, chlorosulfonated polyethylene 16 parts, cobalt naphthenate 14 parts, flax oleyl alcohol
Acid resin 20 parts, N-phenyl-2-naphthylamine 16 parts, trbasic zinc phosphate 16 parts, potassium titanate crystal whisker reinforcement 14 parts, graphite fibre 20 parts, stone
Wax oil 16 parts, triethylene tetramine 14 parts, 20 parts of calcium phosphate, dimethyl silicone polymer 16 parts, trimethylolpropane 14 parts, cocounut oil acyl
Amine CAB 20 parts, 16 parts of rock wool powder, cobalt iso-octoate 14 parts, toluene-2,4-diisocyanate 20 parts, sodium metasilicate 16 parts, propylene
Acid 16 parts, pentachloronitrobenzene 16 parts, Sandofan 16 parts, vancomycin 16 parts.
Further, above-mentioned aluminium alloy extrusions product installation binding agent, is made up of the component of following mass fraction: rich horse
Diethyl phthalate 20 parts, chitin 22 parts, aluminium-hydroxide powder 18 parts, 16 parts of pottery ground-slag end, polyamide 22 parts, castor oil 18
Part, basalt fibre 16 parts, hydroxypropyl methyl cellulose 22 parts, chlorosulfonated polyethylene 18 parts, cobalt naphthenate 16 parts, flax oleyl alcohol
Acid resin 22 parts, N-phenyl-2-naphthylamine 18 parts, trbasic zinc phosphate 18 parts, potassium titanate crystal whisker reinforcement 16 parts, graphite fibre 22 parts, stone
Wax oil 18 parts, triethylene tetramine 16 parts, 22 parts of calcium phosphate, dimethyl silicone polymer 18 parts, trimethylolpropane 16 parts, cocounut oil acyl
Amine CAB 22 parts, 18 parts of rock wool powder, cobalt iso-octoate 16 parts, toluene-2,4-diisocyanate 22 parts, sodium metasilicate 18 parts, propylene
Acid 18 parts, pentachloronitrobenzene 18 parts, Sandofan 18 parts, vancomycin 18 parts.
Further, above-mentioned aluminium alloy extrusions product installation binding agent preparation method step is as follows:
(1) by the DEF of described mass fraction, chitin, aluminium-hydroxide powder, pottery ground-slag end, polyamides
Amine, castor oil, basalt fibre, hydroxypropyl methyl cellulose, chlorosulfonated polyethylene, cobalt naphthenate, linseed oil alkyd resin, N-
Phenyl-2-naphthylamine, trbasic zinc phosphate, potassium titanate crystal whisker reinforcement, dimethyl silicone polymer, trimethylolpropane, sodium metasilicate, propylene
Acid, pentachloronitrobenzene, Sandofan, vancomycin are mixed, and are sequentially added in agitator tank, are sufficiently stirred for the speed of 200rpm
30 minutes;
(2) Cocoamidopropyl betaine of described mass fraction, rock wool powder, cobalt iso-octoate, two isocyanic acid first are added
Phenyl ester, is sufficiently stirred for 60 minutes with the speed of 300rpm;
(3) graphite fibre of described mass fraction, paraffin oil, triethylene tetramine, calcium phosphate are added, with the speed of 400rpm
It is sufficiently stirred for 90 minutes, obtain binder product.
This beneficial effect of the invention is: the present invention relates to a kind of aluminium alloy extrusions product installation binding agent, by following
Component forms: DEF, chitin, aluminium-hydroxide powder, pottery ground-slag end, polyamide, castor oil, basalt are fine
Dimension, hydroxypropyl methyl cellulose, chlorosulfonated polyethylene, cobalt naphthenate, linseed oil alkyd resin, N-phenyl-2-naphthylamine, phosphoric acid
Zinc, potassium titanate crystal whisker reinforcement, graphite fibre, paraffin oil, triethylene tetramine, calcium phosphate, dimethyl silicone polymer, trihydroxy methyl
Propane, Cocoamidopropyl betaine, rock wool powder, cobalt iso-octoate, toluene-2,4-diisocyanate, sodium metasilicate, acrylic acid, pentachloro-nitre
Base benzene, Sandofan, vancomycin.This aluminium alloy extrusions product is installed with binding agent process of preparing simple, prepared product
Product, by rational proportioning and mixing, make to produce between each component synergy, overcome deficiency when being each used alone, shape
Become the cross-linked structure with performances such as excellent high temperature resistant, anticorrosive, high-adhesion, mechanicalnesses.The room temperature that the present invention provides
Down cut intensity can reach more than 45MPa, and shear strength when 250 DEG C is more than 18MPa, disclosure satisfy that glued part exists
The requirement of long-term work at 250 DEG C.Raw material of the present invention produces synergy, is greatly improved the anti-aging of binding agent
Performance, the Acclimation temperature scope improving binding agent, its Acclimation temperature scope is-80~250 DEG C.
Detailed description of the invention
It is described below in conjunction with the detailed description of the invention to the present invention for the embodiment, in order to be better understood from the present invention.
Embodiment 1
Aluminium alloy extrusions product installation binding agent in the present embodiment, is made up of the component of following mass fraction: rich horse
Diethyl phthalate 16 parts, chitin 18 parts, aluminium-hydroxide powder 14 parts, 12 parts of pottery ground-slag end, polyamide 18 parts, castor oil 14
Part, basalt fibre 12 parts, hydroxypropyl methyl cellulose 18 parts, chlorosulfonated polyethylene 14 parts, cobalt naphthenate 12 parts, flax oleyl alcohol
Acid resin 18 parts, N-phenyl-2-naphthylamine 14 parts, trbasic zinc phosphate 14 parts, potassium titanate crystal whisker reinforcement 12 parts, graphite fibre 18 parts, stone
Wax oil 14 parts, triethylene tetramine 12 parts, 18 parts of calcium phosphate, dimethyl silicone polymer 14 parts, trimethylolpropane 12 parts, cocounut oil acyl
Amine CAB 18 parts, 14 parts of rock wool powder, cobalt iso-octoate 12 parts, toluene-2,4-diisocyanate 18 parts, sodium metasilicate 14 parts, propylene
Acid 14 parts, pentachloronitrobenzene 14 parts, Sandofan 14 parts, vancomycin 14 parts.
Above-mentioned aluminium alloy extrusions product installation binding agent preparation method step is as follows:
(1) by the DEF of described mass fraction, chitin, aluminium-hydroxide powder, pottery ground-slag end, polyamides
Amine, castor oil, basalt fibre, hydroxypropyl methyl cellulose, chlorosulfonated polyethylene, cobalt naphthenate, linseed oil alkyd resin, N-
Phenyl-2-naphthylamine, trbasic zinc phosphate, potassium titanate crystal whisker reinforcement, dimethyl silicone polymer, trimethylolpropane, sodium metasilicate, propylene
Acid, pentachloronitrobenzene, Sandofan, vancomycin are mixed, and are sequentially added in agitator tank, are sufficiently stirred for the speed of 200rpm
30 minutes;
(2) Cocoamidopropyl betaine of described mass fraction, rock wool powder, cobalt iso-octoate, two isocyanic acid first are added
Phenyl ester, is sufficiently stirred for 60 minutes with the speed of 300rpm;
(3) graphite fibre of described mass fraction, paraffin oil, triethylene tetramine, calcium phosphate are added, with the speed of 400rpm
It is sufficiently stirred for 90 minutes, obtain binder product.
Embodiment 2
Aluminium alloy extrusions product installation binding agent in the present embodiment, is made up of the component of following mass fraction: rich horse
Diethyl phthalate 18 parts, chitin 20 parts, aluminium-hydroxide powder 16 parts, 14 parts of pottery ground-slag end, polyamide 20 parts, castor oil 16
Part, basalt fibre 14 parts, hydroxypropyl methyl cellulose 20 parts, chlorosulfonated polyethylene 16 parts, cobalt naphthenate 14 parts, flax oleyl alcohol
Acid resin 20 parts, N-phenyl-2-naphthylamine 16 parts, trbasic zinc phosphate 16 parts, potassium titanate crystal whisker reinforcement 14 parts, graphite fibre 20 parts, stone
Wax oil 16 parts, triethylene tetramine 14 parts, 20 parts of calcium phosphate, dimethyl silicone polymer 16 parts, trimethylolpropane 14 parts, cocounut oil acyl
Amine CAB 20 parts, 16 parts of rock wool powder, cobalt iso-octoate 14 parts, toluene-2,4-diisocyanate 20 parts, sodium metasilicate 16 parts, propylene
Acid 16 parts, pentachloronitrobenzene 16 parts, Sandofan 16 parts, vancomycin 16 parts.
Above-mentioned aluminium alloy extrusions product installation binding agent preparation method step is as follows:
(1) by the DEF of described mass fraction, chitin, aluminium-hydroxide powder, pottery ground-slag end, polyamides
Amine, castor oil, basalt fibre, hydroxypropyl methyl cellulose, chlorosulfonated polyethylene, cobalt naphthenate, linseed oil alkyd resin, N-
Phenyl-2-naphthylamine, trbasic zinc phosphate, potassium titanate crystal whisker reinforcement, dimethyl silicone polymer, trimethylolpropane, sodium metasilicate, propylene
Acid, pentachloronitrobenzene, Sandofan, vancomycin are mixed, and are sequentially added in agitator tank, are sufficiently stirred for the speed of 200rpm
30 minutes;
(2) Cocoamidopropyl betaine of described mass fraction, rock wool powder, cobalt iso-octoate, two isocyanic acid first are added
Phenyl ester, is sufficiently stirred for 60 minutes with the speed of 300rpm;
(3) graphite fibre of described mass fraction, paraffin oil, triethylene tetramine, calcium phosphate are added, with the speed of 400rpm
It is sufficiently stirred for 90 minutes, obtain binder product.
Embodiment 3
Aluminium alloy extrusions product installation binding agent in the present embodiment, is made up of the component of following mass fraction: rich horse
Diethyl phthalate 20 parts, chitin 22 parts, aluminium-hydroxide powder 18 parts, 16 parts of pottery ground-slag end, polyamide 22 parts, castor oil 18
Part, basalt fibre 16 parts, hydroxypropyl methyl cellulose 22 parts, chlorosulfonated polyethylene 18 parts, cobalt naphthenate 16 parts, flax oleyl alcohol
Acid resin 22 parts, N-phenyl-2-naphthylamine 18 parts, trbasic zinc phosphate 18 parts, potassium titanate crystal whisker reinforcement 16 parts, graphite fibre 22 parts, stone
Wax oil 18 parts, triethylene tetramine 16 parts, 22 parts of calcium phosphate, dimethyl silicone polymer 18 parts, trimethylolpropane 16 parts, cocounut oil acyl
Amine CAB 22 parts, 18 parts of rock wool powder, cobalt iso-octoate 16 parts, toluene-2,4-diisocyanate 22 parts, sodium metasilicate 18 parts, propylene
Acid 18 parts, pentachloronitrobenzene 18 parts, Sandofan 18 parts, vancomycin 18 parts.
Above-mentioned aluminium alloy extrusions product installation binding agent preparation method step is as follows:
(1) by the DEF of described mass fraction, chitin, aluminium-hydroxide powder, pottery ground-slag end, polyamides
Amine, castor oil, basalt fibre, hydroxypropyl methyl cellulose, chlorosulfonated polyethylene, cobalt naphthenate, linseed oil alkyd resin, N-
Phenyl-2-naphthylamine, trbasic zinc phosphate, potassium titanate crystal whisker reinforcement, dimethyl silicone polymer, trimethylolpropane, sodium metasilicate, propylene
Acid, pentachloronitrobenzene, Sandofan, vancomycin are mixed, and are sequentially added in agitator tank, are sufficiently stirred for the speed of 200rpm
30 minutes;
(2) Cocoamidopropyl betaine of described mass fraction, rock wool powder, cobalt iso-octoate, two isocyanic acid first are added
Phenyl ester, is sufficiently stirred for 60 minutes with the speed of 300rpm;
(3) graphite fibre of described mass fraction, paraffin oil, triethylene tetramine, calcium phosphate are added, with the speed of 400rpm
It is sufficiently stirred for 90 minutes, obtain binder product.
Comparative example 1
1) thermoplastic acrylic resin that weight average molecular weight is 70000~75,000 25 parts is weighed respectively, organic-silicon-modified third
Olefin(e) acid resin 20 parts, is sequentially added in agitator tank, is sufficiently stirred for 40 minutes with the speed of 100rpm;
B) melmac 10 parts is continuously added, phenyl trichlorosilane 7 parts, vinyltrimethoxy silane 5 parts, with
The speed of 100rpm is sufficiently stirred for 60 minutes;
C) in the mixture of step b), titanium dioxide 7 parts is continuously added, attapulgite 5 parts, dichlorotetra-fluoroethane 5 parts, second
Glycol monobutyl ether 20 parts, is sufficiently stirred for 60 minutes with the speed of 100rpm, obtains the binder product in this comparative example.
Comparative example 2
1) weighing epoxy modified hydroxyl acrylic resin 25 parts respectively, weight average molecular weight is the thermoplasticity of 70000~75000
Acrylic resin 25 parts, is sequentially added in agitator tank, is sufficiently stirred for 40 minutes with the speed of 100rpm;
2) melmac 10 parts is continuously added, phenyl trichlorosilane 7 parts, vinyltrimethoxy silane 5 parts, with
The speed of 100rpm is sufficiently stirred for 60 minutes;
3) in the mixture of step b), titanium dioxide 7 parts is continuously added, attapulgite 5 parts, dichlorotetra-fluoroethane 5 parts, second
Glycol monobutyl ether 20 parts, is sufficiently stirred for 60 minutes with the speed of 100rpm, obtains binder product.
By the binding agent prepared by embodiment the 1st, embodiment the 2nd, embodiment 3 and comparative example the 1st, comparative example 2 at-80~280 DEG C
The respective shear strength of lower test and tolerance time, the testing time is 360 days, and concrete outcome is as shown in following table 1-5:
Binder Properties test result at 1-80 DEG C of table
Group | Tolerance time | Shear strength |
Embodiment 1 | Not fragmentation in 50 days, does not falls off | 15MPa |
Embodiment 2 | Not fragmentation in 52 days, does not falls off | 17MPa |
Embodiment 3 | Not fragmentation in 48 days, does not falls off | 16MPa |
Comparative example 1 | 0 day, binding agent fragmentation came off | 0 |
Comparative example 2 | 0 day, binding agent fragmentation came off | 0 |
Binder Properties test result at 20 DEG C of table
Group | Tolerance time | Shear strength |
Embodiment 1 | Not fragmentation in 50 days, does not falls off | 25MPa |
Embodiment 2 | Not fragmentation in 52 days, does not falls off | 28MPa |
Embodiment 3 | Not fragmentation in 48 days, does not falls off | 24MPa |
Comparative example 1 | Binding agent fragmentation after 30 days comes off | 10MPa |
Comparative example 2 | Binding agent fragmentation after 20 days comes off | 8MPa |
Binder Properties test result at 3 20 DEG C of table
Group | Tolerance time | Shear strength |
Embodiment 1 | Not fragmentation in 360 days, does not falls off | 45MPa |
Embodiment 2 | Not fragmentation in 360 days, does not falls off | 46MPa |
Embodiment 3 | Not fragmentation in 360 days, does not falls off | 47MPa |
Comparative example 1 | Not fragmentation in 360 days, does not falls off | 18MPa |
Comparative example 2 | Not fragmentation in 360 days, does not falls off | 16MPa |
Binder Properties test result at 4 150 DEG C of table
Group | Tolerance time | Shear strength |
Embodiment 1 | 360 days not softening and sheddings | 22MPa |
Embodiment 2 | 360 days not softening and sheddings | 24MPa |
Embodiment 3 | 360 days not softening and sheddings | 23MPa |
Comparative example 1 | After 10 days, binding agent softens | 10MPa |
Comparative example 2 | After 10 days, binding agent softens | 8MPa |
Binder Properties test result at 5 250 DEG C of table
Group | Tolerance time | Shear strength |
Embodiment 1 | 280 days not softening and sheddings | 18MPa |
Embodiment 2 | 280 days not softening and sheddings | 19MPa |
Embodiment 3 | 280 days not softening and sheddings | 18MPa |
Comparative example 1 | After 3 days, binding agent softens | 4MPa |
Comparative example 2 | After 3 days, binding agent softens | 3MPa |
The above is the preferred embodiment of the present invention, it is noted that for those skilled in the art
For, under the premise without departing from the principles of the invention, some improvements and modifications can also be made, these improvements and modifications are also considered as
Protection scope of the present invention.
Claims (5)
1. an aluminium alloy extrusions product installation binding agent, it is characterised in that: it is made up of the component of following mass fraction: rich horse
Diethyl phthalate 16~20 parts, chitin 18~22 parts, aluminium-hydroxide powder 14~18 parts, 12~16 parts of ground-slag end of pottery, polyamides
Amine 18~22 parts, castor oil 14~18 parts, basalt fibre 12~16 parts, hydroxypropyl methyl cellulose 18~22 parts, chlorosulfonation
Polyethylene 14~18 parts, cobalt naphthenate 12~16 parts, linseed oil alkyd resin 18~22 parts, N-phenyl-2-naphthylamine 14~18 parts,
Trbasic zinc phosphate 14~18 parts, potassium titanate crystal whisker reinforcement 12~16 parts, graphite fibre 18~22 parts, paraffin oil 14~18 parts, three second
Alkene tetramine 12~16 parts, 18~22 parts of calcium phosphate, dimethyl silicone polymer 14~18 parts, trimethylolpropane 12~16 parts, coconut palm
Oleamide CAB 18~22 parts, 14~18 parts of rock wool powder, cobalt iso-octoate 12~16 parts, toluene-2,4-diisocyanate 18~
22 parts, sodium metasilicate 14~18 parts, 14~18 parts of acrylic acid, pentachloronitrobenzene 14~18 parts, Sandofan 14~18 parts, vancomycin
14~18 parts.
2. aluminium alloy extrusions product installation binding agent according to claim 1, it is characterised in that: described aluminium alloy extrusions
Product installation binding agent is made up of the component of following mass fraction: DEF 16 parts, chitin 18 parts, aluminium hydroxide
14 parts of powder, 12 parts of pottery ground-slag end, polyamide 18 parts, castor oil 14 parts, basalt fibre 12 parts, hydroxypropyl methyl cellulose
18 parts, chlorosulfonated polyethylene 14 parts, cobalt naphthenate 12 parts, linseed oil alkyd resin 18 parts, N-phenyl-2-naphthylamine 14 parts, phosphoric acid
14 parts of zinc, potassium titanate crystal whisker reinforcement 12 parts, graphite fibre 18 parts, paraffin oil 14 parts, triethylene tetramine 12 parts, calcium phosphate 18
Part, dimethyl silicone polymer 14 parts, trimethylolpropane 12 parts, Cocoamidopropyl betaine 18 parts, 14 parts of rock wool powder, different
Cobalt octoate 12 parts, toluene-2,4-diisocyanate 18 parts, sodium metasilicate 14 parts, 14 parts of acrylic acid, pentachloronitrobenzene 14 parts, Sandofan 14
Part, vancomycin 14 parts.
3. aluminium alloy extrusions product installation binding agent according to claim 1, it is characterised in that: described aluminium alloy extrusions
Product installation binding agent is made up of the component of following mass fraction: DEF 18 parts, chitin 20 parts, aluminium hydroxide
16 parts of powder, 14 parts of pottery ground-slag end, polyamide 20 parts, castor oil 16 parts, basalt fibre 14 parts, hydroxypropyl methyl cellulose
20 parts, chlorosulfonated polyethylene 16 parts, cobalt naphthenate 14 parts, linseed oil alkyd resin 20 parts, N-phenyl-2-naphthylamine 16 parts, phosphoric acid
16 parts of zinc, potassium titanate crystal whisker reinforcement 14 parts, graphite fibre 20 parts, paraffin oil 16 parts, triethylene tetramine 14 parts, calcium phosphate 20
Part, dimethyl silicone polymer 16 parts, trimethylolpropane 14 parts, Cocoamidopropyl betaine 20 parts, 16 parts of rock wool powder, different
Cobalt octoate 14 parts, toluene-2,4-diisocyanate 20 parts, sodium metasilicate 16 parts, 16 parts of acrylic acid, pentachloronitrobenzene 16 parts, Sandofan 16
Part, vancomycin 16 parts.
4. aluminium alloy extrusions product installation binding agent according to claim 1, it is characterised in that: described aluminium alloy extrusions
Product installation binding agent is made up of the component of following mass fraction: DEF 20 parts, chitin 22 parts, aluminium hydroxide
18 parts of powder, 16 parts of pottery ground-slag end, polyamide 22 parts, castor oil 18 parts, basalt fibre 16 parts, hydroxypropyl methyl cellulose
22 parts, chlorosulfonated polyethylene 18 parts, cobalt naphthenate 16 parts, linseed oil alkyd resin 22 parts, N-phenyl-2-naphthylamine 18 parts, phosphoric acid
18 parts of zinc, potassium titanate crystal whisker reinforcement 16 parts, graphite fibre 22 parts, paraffin oil 18 parts, triethylene tetramine 16 parts, calcium phosphate 22
Part, dimethyl silicone polymer 18 parts, trimethylolpropane 16 parts, Cocoamidopropyl betaine 22 parts, 18 parts of rock wool powder, different
Cobalt octoate 16 parts, toluene-2,4-diisocyanate 22 parts, sodium metasilicate 18 parts, 18 parts of acrylic acid, pentachloronitrobenzene 18 parts, Sandofan 18
Part, vancomycin 18 parts.
5. aluminium alloy extrusions product installation binding agent according to claim 1, it is characterised in that: described aluminium alloy extrusions
Product installation binding agent preparation method step is as follows:
(1) by the DEF of described mass fraction, chitin, aluminium-hydroxide powder, pottery ground-slag end, polyamide, castor
Sesame oil, basalt fibre, hydroxypropyl methyl cellulose, chlorosulfonated polyethylene, cobalt naphthenate, linseed oil alkyd resin, N-phenyl-
2-naphthylamines, trbasic zinc phosphate, potassium titanate crystal whisker reinforcement, dimethyl silicone polymer, trimethylolpropane, sodium metasilicate, acrylic acid, pentachloro-
Nitrobenzene, Sandofan, vancomycin are mixed, and are sequentially added in agitator tank, are sufficiently stirred for 30 minutes with the speed of 200rpm
Left and right;
(2) Cocoamidopropyl betaine of described mass fraction, rock wool powder, cobalt iso-octoate, toluene-2,4-diisocyanate are added,
It is sufficiently stirred for about 60 minutes with the speed of 300rpm;
(3) adding the graphite fibre of described mass fraction, paraffin oil, triethylene tetramine, calcium phosphate, the speed with 400rpm is abundant
Stir about 90 minutes, obtains binder product.