CN106047142A - Elastic floor paint composition formula - Google Patents

Elastic floor paint composition formula Download PDF

Info

Publication number
CN106047142A
CN106047142A CN201610602353.8A CN201610602353A CN106047142A CN 106047142 A CN106047142 A CN 106047142A CN 201610602353 A CN201610602353 A CN 201610602353A CN 106047142 A CN106047142 A CN 106047142A
Authority
CN
China
Prior art keywords
parts
pigment
compositing formula
terrace paint
solvent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610602353.8A
Other languages
Chinese (zh)
Inventor
陈红旗
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610602353.8A priority Critical patent/CN106047142A/en
Publication of CN106047142A publication Critical patent/CN106047142A/en
Pending legal-status Critical Current

Abstract

The invention discloses an elastic floor paint composition formula, and belongs to the field of building materials. The elastic floor paint composition formula consists of the following raw materials in parts by weight: 30 to 50 parts of acrylic-polyurethane, 7 to 11 parts of phenolic aldehyde-modified diethylenetriamine, 0.10 to 0.14 part of an aluminum zirconium coupling agent, 6 to 9 parts of glass micro-beads, 0.3 to 0.5 part of an acrylate flatting agent, 0.3 to 0.5 part of a GP type deforming agent, 4 to 7 parts of a fire retardant, 12 to 18 parts of a pigment, 40 to 60 parts of packing, and 25 to 40 parts of a solvent. The elastic floor paint composition formula provided by the invention is wide in curing condition and can be cured at a low temperature, has excellent chemical resistance, wear resistance and elasticity, high breaking elongation and better flame retardant property; the performance can be kept stable at a higher temperature.

Description

A kind of elastic terrace paint compositing formula
Technical field
The present invention relates to building material field, be specifically related to a kind of elastic terrace paint compositing formula
Background technology
Floor paint is since invention, just closely coupled with industrial circle, is widely used in polyurethane floor paint and has solidification The features such as speed is fast, quick construction is convenient, corrosion-resistanting waterproofing performance is good, technique is simple, anti-weight, impact resistance, high abrasion, especially It is applicable to all kinds of industrial and mining establishment, parking lot, sports ground etc. and has anti-skidding, anticorrosion, the terrace application of wear-resisting requirement.But produce now The ratio of the production processing that manufacturing enterprise carries out high technology content is gradually increasing,
Summary of the invention
For above-mentioned, it is an object of the invention to provide a kind of elastic terrace paint compositing formula
The concrete technical scheme that the present invention takes is:
A kind of elastic terrace paint compositing formula, it is characterised in that by weight, be made up of following raw material: the poly-ammonia of acrylic acid Ester 30-50 part, phenol aldehyde modified diethylenetriamine 7-11 part, aluminum zirconate coupling agent 0.10-0.14 part, glass bead 6-9 part, Esters of acrylic acid levelling agent 0.3-0.5 part, GP type defoamer 0.3-0.5 part, fire retardant 4-7 part, pigment 12-18 part, filler 40- 60 parts, solvent 25-40 part.
Described fire retardant is: the mixture of aluminium hydroxide, antimony oxide and APP, aluminium hydroxide: three oxidations Two antimony: APP=2:2:1.
Described pigment is: the one of which of titanium white powder pigment, oxidation inscription green pigment and solid pink pigment forever.
Described filler is: blanc fixe, organobentonite and talcous mixture, blanc fixe: organic bentonite Profit soil: Pulvis Talci=5:2:3.
Described solvent is: the mixture of dimethylbenzene, ether and Ketohexamethylene, dimethylbenzene: ether: Ketohexamethylene=3:2:2.
The invention have the advantage that condition of cure is wide in range, can be in low-temperature setting, chemical resistance, wearability and excellent spring, disconnected Split percentage elongation high, and have preferable fire resistance, stable performance can be kept at higher temperatures.
Detailed description of the invention
Below presently preferred embodiments of the present invention is described in detail so that advantages and features of the invention can be easier to by It will be appreciated by those skilled in the art that thus protection scope of the present invention is made apparent clear and definite defining.
Embodiment 1
A kind of elastic terrace paint compositing formula, it is characterised in that by weight, be made up of following raw material: the poly-ammonia of acrylic acid Ester 30-50 part, phenol aldehyde modified diethylenetriamine 7-11 part, aluminum zirconate coupling agent 0.10-0.14 part, glass bead 6-9 part, Esters of acrylic acid levelling agent 0.3-0.5 part, GP type defoamer 0.3-0.5 part, fire retardant 4-7 part, pigment 12-18 part, filler 40- 60 parts, solvent 25-40 part.
Described fire retardant is: the mixture of aluminium hydroxide, antimony oxide and APP, aluminium hydroxide: three oxidations Two antimony: APP=2:2:1.
Described pigment is: the one of which of titanium white powder pigment, oxidation inscription green pigment and solid pink pigment forever.
Described filler is: blanc fixe, organobentonite and talcous mixture, blanc fixe: organic bentonite Profit soil: Pulvis Talci=5:2:3.
Described solvent is: the mixture of dimethylbenzene, ether and Ketohexamethylene, dimethylbenzene: ether: Ketohexamethylene=3:2:2.
Embodiment 2
A kind of elastic terrace paint compositing formula, it is characterised in that by weight, be made up of following raw material: the poly-ammonia of acrylic acid Ester 40 parts, phenol aldehyde modified diethylenetriamine 9 parts, aluminum zirconate coupling agent 0.12 part, glass bead 7.5 parts, esters of acrylic acid Levelling agent 0.4 part, GP type defoamer 0.4 part, fire retardant 5.5 parts, pigment 15 parts, filler 50 parts, solvent 32.5 parts.
Described fire retardant is: the mixture of aluminium hydroxide, antimony oxide and APP, aluminium hydroxide: three oxidations Two antimony: APP=2:2:1.
Described pigment is: the one of which of titanium white powder pigment, oxidation inscription green pigment and solid pink pigment forever.
Described filler is: blanc fixe, organobentonite and talcous mixture, blanc fixe: organic bentonite Profit soil: Pulvis Talci=5:2:3.
Described solvent is: the mixture of dimethylbenzene, ether and Ketohexamethylene, dimethylbenzene: ether: Ketohexamethylene=3:2:2.
Embodiment 3
A kind of elastic terrace paint compositing formula, it is characterised in that by weight, be made up of following raw material: the poly-ammonia of acrylic acid Ester 30-50 part, phenol aldehyde modified diethylenetriamine 7-11 part, aluminum zirconate coupling agent 0.10-0.14 part, glass bead 6-9 part, Esters of acrylic acid levelling agent 0.3-0.5 part, GP type defoamer 0.3-0.5 part, fire retardant 4-7 part, pigment 12-18 part, filler 40- 60 parts, solvent 25-40 part.
Described fire retardant is: the mixture of aluminium hydroxide, antimony oxide and APP, aluminium hydroxide: three oxidations Two antimony: APP=2:2:1.
Described pigment is: the one of which of titanium white powder pigment, oxidation inscription green pigment and solid pink pigment forever.
Described filler is: blanc fixe, organobentonite and talcous mixture, blanc fixe: organic bentonite Profit soil: Pulvis Talci=5:2:3.
Described solvent is: the mixture of dimethylbenzene, ether and Ketohexamethylene, dimethylbenzene: ether: Ketohexamethylene=3:2:2.

Claims (7)

1. an elastic terrace paint compositing formula, it is characterised in that by weight, be made up of following raw material: acroleic acid polyurethane 30-50 part, phenol aldehyde modified diethylenetriamine 7-11 part, aluminum zirconate coupling agent 0.10-0.14 part, glass bead 6-9 part, third Olefin(e) acid esters levelling agent 0.3-0.5 part, GP type defoamer 0.3-0.5 part, fire retardant 4-7 part, pigment 12-18 part, filler 40-60 Part, solvent 25-40 part.
Elastic terrace paint compositing formula the most according to claim 1, it is characterised in that by weight, by following raw material group Become: acroleic acid polyurethane 35-45 part, phenol aldehyde modified diethylenetriamine 8-10 part, aluminum zirconate coupling agent 0.11-0.13 part, Glass bead 7-8 part, esters of acrylic acid levelling agent 0.35-0.45 part, GP type defoamer 0.35-0.45 part, fire retardant 5-6 part, Pigment 13.5-16.5 part, filler 45-55 part, solvent 29-36 part.
Elastic terrace paint compositing formula the most according to claim 1, it is characterised in that by weight, by following raw material group Become: acroleic acid polyurethane 40 parts, phenol aldehyde modified diethylenetriamine 9 parts, aluminum zirconate coupling agent 0.12 part, glass bead 7.5 Part, esters of acrylic acid levelling agent 0.4 part, GP type defoamer 0.4 part, fire retardant 5.5 parts, pigment 15 parts, filler 50 parts, solvent 32.5 parts.
4. according to the elastic terrace paint compositing formula described in claim 1,2 or 3, it is characterised in that fire retardant is: aluminium hydroxide, Antimony oxide and the mixture of APP, aluminium hydroxide: antimony oxide: APP=2:2:1.
5. according to the elastic terrace paint compositing formula described in claim 1,2 or 3, it is characterised in that pigment is: titanium white powder pigment, The one of which of oxidation inscription green pigment and forever solid pink pigment.
6. according to the elastic terrace paint compositing formula described in claim 1,2 or 3, it is characterised in that filler is: blanc fixe, Organobentonite and talcous mixture, blanc fixe: organobentonite: Pulvis Talci=5:2:3.
7. according to the elastic terrace paint compositing formula described in claim 1,2 or 3, it is characterised in that solvent is: dimethylbenzene, ether With the mixture of Ketohexamethylene, dimethylbenzene: ether: Ketohexamethylene=3:2:2.
CN201610602353.8A 2016-07-27 2016-07-27 Elastic floor paint composition formula Pending CN106047142A (en)