CN106046789A - 一种窗体缝隙密封材料 - Google Patents

一种窗体缝隙密封材料 Download PDF

Info

Publication number
CN106046789A
CN106046789A CN201610549975.9A CN201610549975A CN106046789A CN 106046789 A CN106046789 A CN 106046789A CN 201610549975 A CN201610549975 A CN 201610549975A CN 106046789 A CN106046789 A CN 106046789A
Authority
CN
China
Prior art keywords
parts
sealing material
gap sealing
water
absorbent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610549975.9A
Other languages
English (en)
Inventor
占生宝
张�杰
闻军
吴文进
王鹏
李伶俐
江善和
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anqing Normal University
Original Assignee
Anqing Normal University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anqing Normal University filed Critical Anqing Normal University
Priority to CN201610549975.9A priority Critical patent/CN106046789A/zh
Publication of CN106046789A publication Critical patent/CN106046789A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种窗体缝隙密封材料，由以下重量份原料组成：聚硫橡胶30‑34份、松节油8‑10份、低密度聚乙烯4.5‑5.8份、抗氧化剂3.2‑3.5份、润滑剂2‑3份、水30‑40份、氢氧化铝阻燃剂5‑7份、UV吸收剂2‑4份、碳酸丙烯酯5.2‑6.2份、硬质陶土5‑7份；本发明的密封材料配合涉及合理，特别适用于窗体缝隙密封的应用，同时具有良好的物理和机械性能、回弹性高、压缩永久变形小、密封可靠、加工方便和使用寿命长。

Description

一种窗体缝隙密封材料
技术领域
本发明涉及密封材料领域，具体属于一种建筑用嵌缝防水密封材料。
背景技术
密封材料就是指能承受接缝位移以达到气密、水密目的而嵌入建筑接缝中的材料称为密封材料。 密封件材料有金属材料（铝、铅、铟、不锈钢等），也有非金属材料（橡胶、塑料、陶瓷、石墨等）、复合材料（如橡胶-石棉板、气凝胶毡-聚氨酯），但使用最多的是橡胶类弹性体材料。但是应用于窗体缝隙专用的密封材料种类很少。
发明内容
本发明的目的是提供一种窗体缝隙密封材料，具有良好的物理和机械性能、回弹性高、压缩永久变形小、密封可靠、加工方便和使用寿命长。
本发明的技术方案如下：
一种窗体缝隙密封材料，由以下重量份原料组成：聚硫橡胶 30-34份、松节油8-10份、低密度聚乙烯4.5-5.8份、抗氧化剂3.2-3.5份、润滑剂2-3份、水 30-40份、氢氧化铝阻燃剂5-7份、UV吸收剂 2-4份、碳酸丙烯酯 5.2-6.2份、硬质陶土5-7份；
该密封材料具体制备工艺为：将硬质陶土、UV吸收剂、氢氧化铝阻燃剂、润滑剂、抗氧化剂和水总重量30-40%按比例混合，放入搅拌机中搅拌直至混合均匀，静置1.2-2.2h，得到添加剂混合料；继续向添加剂混合料中加入其它剩余物料和剩余的水混合，发泡50-60min后，温度控制在80-110℃，继续搅拌45-55min，得到成品密封材料。
一种窗体缝隙密封材料，由以下重量份原料组成：聚硫橡胶 32份、松节油9份、低密度聚乙烯5.1份、抗氧化剂3.3份、润滑剂2.5份、水 35份、氢氧化铝阻燃剂6份、UV吸收剂3份、碳酸丙烯酯 5.7份、硬质陶土6份。
本发明的密封材料配合涉及合理，特别适用于窗体缝隙密封的应用，同时具有良好的物理和机械性能、回弹性高、压缩永久变形小、密封可靠、加工方便和使用寿命长。
具体实施方式
一种窗体缝隙密封材料，由以下重量份原料组成：聚硫橡胶 32份、松节油9份、低密度聚乙烯5.1份、抗氧化剂3.3份、润滑剂2.5份、水 35份、氢氧化铝阻燃剂6份、UV吸收剂3份、碳酸丙烯酯 5.7份、硬质陶土6份；
该密封材料具体制备工艺为：将硬质陶土、UV吸收剂、氢氧化铝阻燃剂、润滑剂、抗氧化剂和水总重量30-40%按比例混合，放入搅拌机中搅拌直至混合均匀，静置1.2-2.2h，得到添加剂混合料；继续向添加剂混合料中加入其它剩余物料和剩余的水混合，发泡50-60min后，温度控制在80-110℃，继续搅拌45-55min，得到成品密封材料。
本发明密封胶的耐热耐水性试验数据如下：
将密封材料在80℃、0％RH 环境下放置24 小时后，24 小时以上无漏水，密度100Kg/m3，气泡数90个/25mm。

Claims (2)

1.一种窗体缝隙密封材料，其特征在于，由以下重量份原料组成：聚硫橡胶 30-34份、松节油8-10份、低密度聚乙烯4.5-5.8份、抗氧化剂3.2-3.5份、润滑剂2-3份、水 30-40份、氢氧化铝阻燃剂5-7份、UV吸收剂 2-4份、碳酸丙烯酯 5.2-6.2份、硬质陶土5-7份；
该密封材料具体制备工艺为：将硬质陶土、UV吸收剂、氢氧化铝阻燃剂、润滑剂、抗氧化剂和水总重量30-40%按比例混合，放入搅拌机中搅拌直至混合均匀，静置1.2-2.2h，得到添加剂混合料；继续向添加剂混合料中加入其它剩余物料和剩余的水混合，发泡50-60min后，温度控制在80-110℃，继续搅拌45-55min，得到成品密封材料。
2.根据权利要求1所述的一种窗体缝隙密封材料，其特征在于，由以下重量份原料组成：聚硫橡胶 32份、松节油9份、低密度聚乙烯5.1份、抗氧化剂3.3份、润滑剂2.5份、水 35份、氢氧化铝阻燃剂6份、UV吸收剂 3份、碳酸丙烯酯 5.7份、硬质陶土6份。
CN201610549975.9A 2016-07-14 2016-07-14 一种窗体缝隙密封材料 Pending CN106046789A (zh)