CN106032443A - 一种防火涂料的制备方法 - Google Patents
一种防火涂料的制备方法 Download PDFInfo
- Publication number
- CN106032443A CN106032443A CN201510561281.2A CN201510561281A CN106032443A CN 106032443 A CN106032443 A CN 106032443A CN 201510561281 A CN201510561281 A CN 201510561281A CN 106032443 A CN106032443 A CN 106032443A
- Authority
- CN
- China
- Prior art keywords
- parts
- speed
- added
- stirring
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明是有关于一种防火涂料的制备方法,其包括以下步骤:1)取以下重量份的各材料备用:无水氯化钙30-50份、阻燃剂400-450份、氯化石蜡50-70份,石粉30-50份、镁粉8-12份、复合磷酸锌15-30份、钛白粉8-10份、云母粉10-20份、增稠剂15-25份、成膜剂150-200份、去离子水150-250份;2)将去离子水加入分散缸中,开启中速搅拌状态,向其中添加增稠剂,搅拌2-3min,然后依次加入配方中的成膜剂,搅拌5-8min后,加入阻燃剂、氯化石蜡、石粉、镁粉、复合磷酸锌、钛白粉、云母粉,增大搅拌速度至高速,打浆分散40-50min,然后降低转速至中速状态,控制最终稠度为19-25℃,得到所述防火涂料。
Description
技术领域
本发明属于涂料领域,具体涉及一种新型防火涂料的制备方法。
背景技术
随着人们安全意识的增加,防火涂料的应用越来越广泛。但是对于防火涂料的研制,仍存在着很多技术难点,需要解决的主要问题是提高耐水性、缩短干燥时间、延长耐火时间、提高储存稳定性、增加装饰性等。
综上所述,目前市场上的室内薄型钢结构防火涂料耐水性差,储存稳定性差,耐火时间短,干燥时间长,装饰性差等缺点。因此研究开发性能优异、环境友好的室内薄型钢结构防火涂料是室内钢结构防火保护的必然趋势。
发明内容
为了解决现有技术中存在的问题,本发明提供了一种提高防火涂料的耐水性能和改善涂层粘结性的新型防火涂料的制备方法。
本发明的目的及解决其技术问题是采用以下技术方案来实现的。依据本发明提出的一种防火涂料的制备方法,所述方法包括以下步骤:
1)取以下重量份的各材料备用:无水氯化钙30-50份、阻燃剂400-450份、氯化石蜡50-70份,石粉30-50份、镁粉8-12份、复合磷酸锌15-30份、钛白粉8-10份、云母粉10-20份、增稠剂15-25份、成膜剂150-200份、去离子水150-250份;
2)将去离子水加入分散缸中,开启中速搅拌状态,向其中添加增稠剂,搅拌2-3min,然后依次加入配方中的成膜剂,搅拌5-8min后,加入阻燃剂、氯化石蜡、石粉、镁粉、复合磷酸锌、钛白粉、云母粉,增大搅拌速度至高速,打浆分散40-50min,然后降低转速至中速状态,控制最终稠度为19-25℃,得到所述防火涂料。
本发明与现有技术相比具有以下优点:
本发明制备方法简单,制备产品属于绿色环保性涂料,该涂料不仅具有耐火时间长,装饰性能好,粘结性好、耐水性优等特点。
具体实施方式
为更进一步阐述本发明为达成预定发明目的所采取的技术手段及功 效,对依据本发明提出的一种防火涂料的制备方法其具体实施方式详细说明如后。
实施例1
本发明一种防火涂料的制备方法,所述方法包括以下步骤:
1)取以下重量份的各材料备用:无水氯化钙30份、阻燃剂400份、氯化石蜡70份,石粉30份、镁粉8份、复合磷酸锌15份、钛白粉8份、云母粉10份、增稠剂25份、成膜剂200份、去离子水150份。
2)将去离子水加入分散缸中,开启中速搅拌状态,向其中添加增稠剂,搅拌2min,然后依次加入配方中的成膜剂,搅拌5min后,加入阻燃剂、氯化石蜡、石粉、镁粉、复合磷酸锌、钛白粉、云母粉,增大搅拌速度至高速,打浆分散40min,然后降低转速至中速状态,控制最终稠度为22℃,得到所述防火涂料。
其中阻燃剂为聚磷酸铵、季戊四醇和三聚氰胺中的一种;其中所述的成膜剂为氨基树脂和丙烯树脂的混合物,其重量比为3:1。
实施例2
本发明一种防火涂料的制备方法,所述方法包括以下步骤:
1)取以下重量份的各材料备用:无水氯化钙40份、阻燃剂430份、氯化石蜡60份,石粉40份、镁粉10份、复合磷酸锌22份、钛白粉9份、云母粉15份、增稠剂20份、成膜剂170份、去离子水200份。
2)将去离子水加入分散缸中,开启中速搅拌状态,向其中添加增稠剂,搅拌3min,然后依次加入配方中的成膜剂,搅拌8min后,加入阻燃剂、氯化石蜡、石粉、镁粉、复合磷酸锌、钛白粉、云母粉,增大搅拌速度至高速,打浆分散50min,然后降低转速至中速状态,控制最终稠度为25℃,得到所述防火涂料。
其中所述阻燃剂为聚磷酸铵、季戊四醇和三聚氰胺中的任两种的混合物。所述的成膜剂为氨基树脂和丙烯树脂的混合物,其重量比为3:1。
实施例3
本发明一种防火涂料的制备方法,所述方法包括以下步骤:
1)取以下重量份的各材料备用:无水氯化钙50份、阻燃剂450份、氯化石蜡50份,石粉50份、镁粉12份、复合磷酸锌30份、钛白粉10份、云母粉20份、增稠剂15份、成膜剂150份、去离子水250份。
3)将去离子水加入分散缸中,开启中速搅拌状态,向其中添加增稠剂,搅拌3min,然后依次加入配方中的成膜剂,搅拌7min后,加入阻燃剂、氯化石蜡、石粉、镁粉、复合磷酸锌、钛白粉、云母粉,增大搅拌速度至高速,打浆分散45min,然后降低转速至中速状态,控制最终稠度为19℃,得到所述防火涂料。
其中所述阻燃剂为聚磷酸铵、季戊四醇和三聚氰胺中的混合物。所述的成膜剂为氨基树脂和丙烯树脂的混合物,其重量比为3:1。
以上所述,仅是本发明的较佳实施例而已,并非对本发明做任何形式上的限制,虽然本发明已以较佳实施例揭露如上,然而并非用以限定本发明,任何熟悉本专业的技术人员,在不脱离本发明技术方案范围内,当可利用上述揭示的技术内容做出些许更动或修饰为等同变化的等效实施例,但凡是未脱离本发明技术方案的内容,依据本发明的技术实质对以上实施例所做的任何简单修改、等同变化与修饰,均仍属于本发明技术方案的范围内。
Claims (1)
1.一种防火涂料的制备方法,其特征在于,所述方法包括以下步骤:
1)取以下重量份的各材料备用:无水氯化钙30-50份、阻燃剂400-450份、氯化石蜡50-70份,石粉30-50份、镁粉8-12份、复合磷酸锌15-30份、钛白粉8-10份、云母粉10-20份、增稠剂15-25份、成膜剂150-200份、去离子水150-250份;
2)将去离子水加入分散缸中,开启中速搅拌状态,向其中添加增稠剂,搅拌2-3min,然后依次加入配方中的成膜剂,搅拌5-8min后,加入阻燃剂、氯化石蜡、石粉、镁粉、复合磷酸锌、钛白粉、云母粉,增大搅拌速度至高速,打浆分散40-50min,然后降低转速至中速状态,控制最终稠度为19-25℃,得到所述防火涂料。