CN106012528A - Preparation method of antibacterial and deodorizing hot air nonwoven fabric - Google Patents
Preparation method of antibacterial and deodorizing hot air nonwoven fabric Download PDFInfo
- Publication number
- CN106012528A CN106012528A CN201610488612.9A CN201610488612A CN106012528A CN 106012528 A CN106012528 A CN 106012528A CN 201610488612 A CN201610488612 A CN 201610488612A CN 106012528 A CN106012528 A CN 106012528A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- preparation
- hot
- cyclodextrin
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of an antibacterial and deodorizing hot air nonwoven fabric. The preparation method comprises the following steps: I. preparation of a fiber assembly; II. web carding; III. cross lapping; IV. spray of an antibacterial and deodorizing agent; and V. preparation of an ES (ethylene-propylene side by side) hot air nonwoven fabric. The preparation method has the beneficial effects that cyclodextrin nanosilver colloid with a stable structure is prepared by utilizing aminated modification of cyclodextrin and has the deodorizing and antibacterial effects at the same time; and the surfaces of fibers are coated with the aminocyclodextrin nanosilver colloid through hot melting of the fibers, thus achieving the antibacterial and deodorizing effects.
Description
Technical field
The present invention relates to a kind of antibacterial and deodouring hot-wind nonwoven cloth preparation method, belong to nonwoven techniques field.
Background technology
Comparing other processing method, Through-Air Thermal Bonded Nonwovens has higher material thickness and outward appearance evenly
Sensation can make the liquid permeation rate of non-weaving cloth accelerate, and returns moisture and reduces, this for as sanitary towel and
For the surface material of urine pants rather favourable, thus the material of Through-Air Thermal Bonded Nonwovens class more can be by client's
Pay close attention to and favor.Mercaptan, Beta-methyl indole (scatol) and fecaluria oxidation Decomposition in human body fecaluria are produced
The harmful gass such as raw H2S, NH3 have stench, the existence of a little foul smell make people feel living environment is not
Happy.Therefore exploitation has the hygienic material of deodorizing antibiotic effect and has realistic meaning.
Cyclodextrin is to be made up of the cyclic oligosaccharide of 6-12 D-glucopyranose units, and whole molecule becomes cone
Post and truncated cones shape garland, have hollow and inner hydrophobic, the construction features of external hydrophilic.In liquid manure
Effective ingredient mercaptan, Beta-methyl indole (scatol) and other stink substance all can preferably be adsorbed to ring
In the hydrophobic cavity of dextrin, formed inclusion complex, thus deodorization.In order to improve the particle bag of cyclodextrin
Cover performance, the alcoholic extract hydroxyl group of cyclodextrin molecular hole outer surface is carried out amination modified.After utilizing amination
Nano-Ag particles prepared by cyclodextrin, it is possible to obtain relatively stable nano silver dispersion.The cyclodextrin of preparation
Nano silver colloid has antibacterial, the effect of deodorization concurrently.
Summary of the invention
It is an object of the invention to provide a kind of antibacterial and deodouring hot-wind nonwoven cloth preparation method, there is safety collar
Protect, of good performance there is antibacterial, deodouring effect.
For achieving the above object, the present invention provides following technical scheme: a kind of antibacterial and deodouring hot-wind nonwoven cloth
Preparation method, comprises the following steps, step one: prepared by fiber assembly;Step 2, netted combing;Step
Rapid three, cross lapping;Step 4, antibacterial deodorant sprays;Step 5, prepared by ES Through-Air Thermal Bonded Nonwovens;
In described step one, ES fibrous raw material obtains having good dispersion after opener
Fiber assembly.
In described step 2, the ES fiber after shredding is carded to netted through carding machine.
In described step 3, the grammes per square metre controlling ES Through-Air Thermal Bonded Nonwovens in laid process is
10-30g/m2。
In described step 4, spraying antibacterial deodorant on fibre web, wherein antibacterial deodorant is amino
The cyclodextrin changed and nanometer silver dispersion.
In described step 5, fiber forms resistance after 100 DEG C of-140 DEG C of hot blasts are reinforced antibacterial removing
The ES Through-Air Thermal Bonded Nonwovens of smelly function.
Wherein in described step 4, the proportion of deodorizer used is 2-5%, the ratio of eutectic ES fiber
It is heavily 95-98%.
As the further technical scheme of the present invention, described ES fiber is skin-core composite fibre, wherein
Cortex is PE, and sandwich layer is PET or PP, or containing at least one in PP, PA, PLA.
As the further technical scheme of the present invention, the non-weaving cloth being upwardly oriented in plant running side passes through
Hot-air blower, temperature 100 DEG C-140 DEG C, is shaped under the conditions of blast 500Pa-2000Pa, is then obtained function
Property non-weaving cloth.
As the further technical scheme of the present invention, described cyclodextrin nano silver dispersions is containing 6-12
The cyclic oligosaccharide of individual D-glucopyranose units is through amination modified product, nanometer silver preparation method
It is with amination modified cyclodextrin as stabilizer and reducing agent, using silver nitrate or silver sulfate as silver source system
Standby dispersion;Its cyclodextrin primarily serves absorbing and deodorizing effect, and nanometer silver plays antibacterial action.
The beneficial effects of the present invention is:
1, utilize cyclodextrin amination modified, prepare the cyclodextrin nano silver colloid of rock-steady structure;Ring is stuck with paste
Essence nano silver colloid has deodorization, antibacterial effect simultaneously.
2, Tanabe Seiyoku nano silver colloid is coated on fiber surface by the hot melt of fiber, reaches antibacterial and removes
Smelly effect.
3, the good endurance of Through-Air Thermal Bonded Nonwovens product, the reliability that prepare are high, non-environmental-pollution, and
Without special arranging process, production procedure is short, and low cost is suitable for scale production.
This Through-Air Thermal Bonded Nonwovens can be widely used in medical and health industry.
Detailed description of the invention
Technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that institute
The embodiment described is only a part of embodiment of the present invention rather than whole embodiments.Based on this
Embodiment in bright, those of ordinary skill in the art are obtained under not making creative work premise
Every other embodiment, broadly falls into the scope of protection of the invention.
A kind of antibacterial and deodouring hot-wind nonwoven cloth preparation method, comprises the following steps, step one: fiber assembly
Preparation;Step 2, netted combing;Step 3, cross lapping;Step 4, antibacterial deodorant sprays;
Step 5, prepared by ES Through-Air Thermal Bonded Nonwovens;
In described step one, ES fibrous raw material obtains having good dispersion after opener
Fiber assembly;
In described step 2, the ES fiber after shredding is carded to netted through carding machine;
In described step 3, the grammes per square metre controlling ES Through-Air Thermal Bonded Nonwovens in laid process is
10-30g/m2;
In described step 4, spraying antibacterial deodorant on fibre web, wherein antibacterial deodorant is amino
The cyclodextrin changed and nanometer silver dispersion;
In described step 5, fiber forms resistance after 100 DEG C of-140 DEG C of hot blasts are reinforced antibacterial removing
The ES Through-Air Thermal Bonded Nonwovens of smelly function;
Wherein in described step 4, the proportion of deodorizer used is 2-5%, the ratio of eutectic ES fiber
It is heavily 95-98%.
As the further technical scheme of the present invention, described ES fiber is skin-core composite fibre, wherein
Cortex is PE, and sandwich layer is PET or PP, or containing at least one in PP, PA, PLA.
As the further technical scheme of the present invention, the non-weaving cloth being upwardly oriented in plant running side passes through
Hot-air blower, temperature 100 DEG C-140 DEG C, is shaped under the conditions of blast 500Pa-2000Pa, is then obtained function
Property non-weaving cloth.
As the further technical scheme of the present invention, described cyclodextrin nano silver dispersions is containing 6-12
The cyclic oligosaccharide of individual D-glucopyranose units is through amination modified product, nanometer silver preparation method
It is with amination modified cyclodextrin as stabilizer and reducing agent, using silver nitrate or silver sulfate as silver source system
Standby dispersion;Its cyclodextrin primarily serves absorbing and deodorizing effect, and nanometer silver plays antibacterial action.
Embodiment 1,
1. 0.2g amino-6-deoxidation-beta-schardinger dextrin-is dissolved in 100ml deionized water, obtains 2g/L
Amino modified cyclodextrin solution.10ml silver nitrate solution o.1mo/L is added in cyclodextrin solution,
Join 60 DEG C of stirring 20min, the cyclodextrin nano silver colloid of 10-50nm can be obtained.
2, by air lay, the PP/PE hot melt ES fleece of 10g/m2 fabric width 50cm is obtained.Logical
Crossing sprayer unit and 100ml cyclodextrin nano silver dispersions is sprayed at the fleece of 10 meters, fibre web is by warm
Blower fan, temperature 120 DEG C, is shaped under the conditions of blast 500pa, is then obtained the functional hot blast of antibacterial and deodouring
Non-weaving cloth.
Embodiment 2,
1, the amino dissaving polymer taking the pungent group-beta-cyclodextrin of 0.1g and 0.1g is dissolved in 100ml
In deionized water, stirring and dissolving.The silver nitrate solution adding 1ml 0.1mol/L is heated to 80 DEG C of stirrings
10min, obtains cyclodextrin nano silver dispersions.
2, by air lay, the PE/PET hot melt ES fleece of 20g/m2 fabric width 60cm is obtained.Logical
Crossing sprayer unit and 100ml cyclodextrin nano silver dispersions is sprayed at 5 meters of long fleeces, fibre web passes through
Hot-air blower, temperature 130 DEG C, is shaped under the conditions of blast 100pa, is then obtained the functional hot blast of antibacterial and deodouring
Non-weaving cloth.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment,
And without departing from the spirit or essential characteristics of the present invention, it is possible to real in other specific forms
The existing present invention.Therefore, no matter from the point of view of which point, embodiment all should be regarded as exemplary, and
Being nonrestrictive, the scope of the present invention is limited by claims rather than described above, therefore purport
All changes in falling in the implication of equivalency and scope of claim are included in the present invention.
Moreover, it will be appreciated that although this specification is been described by according to embodiment, but the most each reality
Mode of executing only comprises an independent technical scheme, and this narrating mode of description is only for understand
Seeing, those skilled in the art should be using description as an entirety, and the technical scheme in each embodiment is also
Other embodiments that it will be appreciated by those skilled in the art that can be formed through appropriately combined.
Claims (4)
1. an antibacterial and deodouring hot-wind nonwoven cloth preparation method, comprises the following steps, step one: fiber collection
Prepared by body;Step 2, netted combing;Step 3, cross lapping;Step 4, antibacterial deodorant sprays;
Step 5, prepared by ES Through-Air Thermal Bonded Nonwovens;It is characterized in that:
In described step one, ES fibrous raw material obtains having good dispersion after opener
Fiber assembly;
In described step 2, the ES fiber after shredding is carded to netted through carding machine;
In described step 3, the grammes per square metre controlling ES Through-Air Thermal Bonded Nonwovens in laid process is
10-30g/m2;
In described step 4, spraying antibacterial deodorant on fibre web, wherein antibacterial deodorant is amino
The cyclodextrin changed and nanometer silver dispersion;
In described step 5, fiber forms resistance after 100 DEG C of-140 DEG C of hot blasts are reinforced antibacterial removing
The ES Through-Air Thermal Bonded Nonwovens of smelly function;
Wherein in described step 4, the proportion of deodorizer used is 2-5%, the ratio of eutectic ES fiber
It is heavily 95-98%.
A kind of antibacterial and deodouring hot-wind nonwoven cloth preparation method the most according to claim 1, its feature exists
In, described ES fiber is skin-core composite fibre, and its mediopellis is PE, and sandwich layer is PET or PP, or
Containing at least one in PP, PA, PLA.
A kind of antibacterial and deodouring hot-wind nonwoven cloth preparation method the most according to claim 1, its feature exists
In, the non-weaving cloth being upwardly oriented in plant running side passes through hot-air blower at temperature 100 DEG C-140 DEG C, blast
Shape under the conditions of 500Pa-2000Pa, then obtain Functional Nonwoven Fabrics.
A kind of antibacterial and deodouring hot-wind nonwoven cloth preparation method the most according to claim 1, its feature exists
In, described cyclodextrin nano silver dispersions is the cyclic oligomer containing 6-12 D-glucopyranose units
Sugar is through amination modified product, and nanometer silver preparation method is to be stable with amination modified cyclodextrin
Agent and reducing agent, the dispersion prepared as silver source using silver nitrate or silver sulfate;Its cyclodextrin acts primarily as
To absorbing and deodorizing effect, nanometer silver plays antibacterial action.