CN106010712A - Solid biomass fuel product and production method thereof - Google Patents
Solid biomass fuel product and production method thereof Download PDFInfo
- Publication number
- CN106010712A CN106010712A CN201610468228.2A CN201610468228A CN106010712A CN 106010712 A CN106010712 A CN 106010712A CN 201610468228 A CN201610468228 A CN 201610468228A CN 106010712 A CN106010712 A CN 106010712A
- Authority
- CN
- China
- Prior art keywords
- bamboo willow
- processing step
- bamboo
- fuel product
- willow
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a solid biomass fuel product and a production method thereof. The solid biomass fuel product is prepared from, in percentage by weight, 100% of bamboo willow, or 70% of bamboo willow and 30% of tobacco stems, or 50% of bamboo willow and 50% of corn straw, or 80% of bamboo willow and 20% corn stalks, or 50% of bamboo willow and 50% of bagasse, or 50% of bamboo willow, 30% of corn stalks and 20% of tobacco stems in formulas. The raw materials are cut off, crushed, ground into powder, dried and shaped under high pressure. The solid biomass fuel product is large in density, small in size, safe and convenient to store and clean; the content of volatile matters in the fuel is high, and accordingly, the fuel product is easy to ignite, good in combustion characteristic and high in burn-out rate and can be used for replacing fossil energy.
Description
Technical field
The invention belongs to energy field, particularly relate to a kind of producer utilizing biomass processing to become solid molding fuel
Method.
Background technology
The source of biomass energy:
Agricultural resource: agro-ecology mass-energy resource refers to agricultural crops, including energy crop；Discarding in agricultural production process
Thing, remains in the agricultural crop straw in farmland, corn stalk, sorghum stalks, wheat straw, Caulis et Folium Oryzae, beanstalk and cotton stalk during such as crop harvesting
Deng；The garbage of agricultural machining industry, such as remaining rice husk etc. in agricultural production process.Energy-source plant refers to various in order to provide energy
The plant in source, generally includes draft energy crop, oil crop, produces several classes such as Hydrocarbon plant and water plant.
Forest resourceies: forestry biomass resource refers to the biomass energy that Forest Growth and production of forestry process provide, bag
Include firewood forests, scattered timber, the branch of residual, leaves and wood flour etc. in the tending of woods and Chose cutting；Logging and
Branch, sawdust, wood flour, the tip of a branch, slab and butt etc. in the course of processing；The garbage of forestry byproducts, such as shell and pit
Deng.
Although biomass energy technical threshold is higher, capital centralization degree is high, but biomass energy is uniquely can be the most real
The now new forms of energy of preferable profit, are also the huge new forms of energy of market capacity.Biomass energy abundant raw material source, range are wide
General, bioenergy industry has powerful delayed effect of development.
Bamboo willow is Salicaceae (Salicaceae) sallow.Arbor, growth potential is big, and height is up to more than 20 meters.Tree
During skin children, green, smooth.Apical dominance is obvious, and axillary bud sprouting power is strong, branch relatively morning, side shoot and trunk angle 30～45 degree.Tree
Hat turriform, branch is uniform.Leaf lanceolar, single leaf alternate, blade is up to 15 22cm, and wide 3.5-6.2cm tip length is tapering, base portion
Wedge shape, there is obvious serration at edge, and face of blade is green, and back side canescence, petiole is micro-red, shorter.Bamboo willow is new bamboo
With willow transformed variety, inherit tradition willow kind numerous a little on the basis of, this tree kind is in fast-growing and disease resistance
Aspect performance is more excellent.Bamboo willow changes China's existing situation of fast-growing tree emphasis, promotes that fast-growing, high-yield woods, will to development in pluralism
The development of Hui Shi China forestry industry brings broader space.In terms of bioenergy, bamboo willow is in terms of Energy Conversion Technology,
Have been carried out solid molding fuel technological development.Bamboo willow high heating value, carbon-nitrogen ratio are high, high-biomass, are suitable for adopting energy seeds
Cut down phase, the period of felling in turn and specific yield requirement.Outstanding energy forest seeds should be 1 period of felling in turn for 3-5, can fell continuously
5-7 time；Energy density is big, quality better.These requirements are to the most eligible from the point of view of bamboo willow.Greatly develop bamboo willow can overcome completely
Other energy forest per unit area yield is low, trophophase length, resistance are weak, economic benefit is low at present, and the masses lack implantation in large scale enthusiasm etc.
Problem, accelerates energy-source plant bamboo willow and breeds and energy forest base construction, provide resource guarantee for biomass energy sustainable development.
Wherein bamboo willow is considered to be worth doing by being either physically or chemically processed into little granular fuel containing high heat energy timber or wood fragments.This solid forming
Fuel, is also available for producing the aspect application such as alcohol fuel, pyrolytic gasification supply and generating.
Summary of the invention
For overcoming existing energy shortage, and preferably utilize clean energy resource, reduce the use of non-renewable energy resources, invent one
Planting utilizes biomass processing to become solid molding fuel product and production method thereof.
It is an object of the invention to realize by following technical solution.
A kind of biomass solid formed fuel product, described biomass solid formed fuel product is according to following formula system
Become, by weight percentage: bamboo willow 100%；Or bamboo willow 70%+ tobacco rod 30%；Or bamboo willow 80%+ corn stalk 20%；Or bamboo willow
50%+ corn stalk 50%；Or bamboo willow 80%+ corn stalk 20%；Bamboo willow 50%+ bagasse 50%；Or bamboo willow 50%+ Semen Maydis
Bar 30%+ tobacco rod 20%.
The present invention also provides for the production method of a kind of biomass solid formed fuel product prepared according to above-mentioned formula:
(1) processing step of pure bamboo willow is as follows:
A) selection: in the bamboo osiery district of plantation, selects minimum diameter not less than 1cm, and maximum gauge is not more than the bamboo willow of 10cm
Branch does raw material；
Raw material length: bamboo Ramulus Salicis Babylonicae is cut into the length of every 20cm-40cm；
Natural drying: make somebody a mere figurehead natural drying in ventilation 24 hours；
Broken: bamboo willow raw material is all broken for the length chips less than 13mm；
Pulverizing: the chips crushed is passed through pulverizer, pulverizes the wood flour being less than 3mm into length；
It is dried: the wood flour crushed being put into traditional flue-curing barn and is dried baking, temperature is arranged at 35 degrees Celsius, and the time is set as 20 points
The baking of clock, when the moisture drying in wood flour to the moisture content less than or equal to 15%, takes out barn；
B) molding: dried wood flour is inserted grain forming equipment, by high temperature extruding forming, becomes the solid of 8-15mm
Granule；
C) cool: by the solid particle of molding by cooling, pack warehouse-in.
(2) processing step of bamboo willow+tobacco rod is as follows:
A-2) processing step of bamboo willow is with the processing step of (one) pure bamboo willow, repeats no more；
B-2) processing step of tobacco rod is with the processing step of (one) pure bamboo willow；
C-2) take by weight percentage bamboo willow bits 70% and tobacco rod bits 30% be sufficiently mixed after, insert grain forming equipment,
By high temperature extruding forming, become the solid particle of 8-15mm；
D-2) cool: by the solid particle of molding by cooling, pack warehouse-in.
(3) processing step of bamboo willow+corn stalk is as follows:
A-3) processing step of bamboo willow is with the processing step of (one) pure bamboo willow, repeats no more；
B-3) processing step of corn stalk is with the processing step of (one) pure bamboo willow；
C-3) take by weight percentage bamboo willow bits 50% and corn stalk bits 50% be sufficiently mixed after, insert grain forming and set
Standby, by high temperature extruding forming, become the solid particle of 8-15mm；
D-3) cool: by the solid particle of molding by cooling, pack warehouse-in.
(4) processing step of bamboo willow+corn stalk is as follows:
Take bamboo willow bits 80% by weight percentage and after corn stalk bits 20% are sufficiently mixed, insert grain forming equipment, logical
Cross high temperature extruding forming, become the solid particle of 8-15mm；Remaining is identical, no with the processing step of (three) bamboo willow+corn stalk
Repeat again.
(5) processing step of bamboo willow+bagasse is as follows:
A-5) processing step of bamboo willow is with the processing step of (one) pure bamboo willow, repeats no more；
B-5) processing step of bagasse is with the processing step of (one) pure bamboo willow；
C-5) take bamboo willow bits 50% by weight percentage and after bagasse 50% is sufficiently mixed, insert grain forming equipment,
By high temperature extruding forming, become the solid particle of 8-15mm；
D-5) cool: by the solid particle of molding by cooling, pack warehouse-in.
(6) processing step of bamboo willow+tobacco rod+corn stalk is as follows:
Take by weight percentage bamboo willow bits 50% and corn stalk bits 30% and tobacco rod bits 20% be sufficiently mixed after, insert granule
Type equipment, by high temperature extruding forming, becomes the solid particle of 8-15mm；The processing step of remaining (two) bamboo willow+tobacco rod with
And the processing step of (three) bamboo willow+corn stalk is identical, repeats no more.
The marked improvement of the present invention and be technically characterized by comprising the steps as follows: the characteristic of biomass granule fuel: the homogenizing as high-quality fires
Material product, granule can automatically control in terms of conveying, storage, transmission and burning, and its comfort level can be with light fuel
Compare favourably；Solid particle, density is big, and volume is little, stores safe ready, and cleaning is clean；Fuel fugitive constituent is high, catches fire easily, combustion
Burning characteristic is good, and burnout rate is high；Sulfur content is extremely low, only about the 1/20 of fuel oil, need not take any desulphurization denitration measure i.e.
Can reach environmental requirement；Low containing ash, conventional dust removal devices can meet environmental requirement；Discharge: the CO2 of biomass combustion discharge
The CO absorbed in growth course with it2Identical, and instead of fossil energy, decrease clean discharge.
The following embodiment of the present invention further illustrates, but does not form covering scope of the present invention for embodiment and limit.
Embodiment one:
(1) processing step of pure bamboo willow is as follows:
A) selection: in the bamboo osiery district of plantation, selects bamboo Ramulus Salicis Babylonicae diameter 1cm, and 100000 kilograms are done raw material；
B) raw material length: bamboo Ramulus Salicis Babylonicae is cut into the length of every 20cm；
C) natural drying: make somebody a mere figurehead natural drying in ventilation 24 hours；
D) broken: bamboo willow raw material is all broken for the length chips less than 13cm；Wood chipper: brand: space dragon, model
GX126。
E) pulverizing: the chips crushed is passed through pulverizer, pulverizes the wood flour being less than 8mm into length；Efficient pulverizing
Machine: brand: space dragon, model GXP65*55.
F) it is dried: the wood flour crushed being put into traditional flue-curing barn and is dried baking, temperature is arranged at 35 degrees Celsius, and the time sets
It is set to the baking of 20 minutes, when the moisture drying in wood flour to the moisture content less than or equal to 10%, takes out barn；Roller drying machine
Brand: space dragon, model: GHG Φ 1.2 × 12 meters.
G) molding: dried wood flour is inserted grain forming equipment, by high temperature extruding forming, becomes 8-15mm's
Solid particle；Centrifugal efficient granulator: brand: space dragon, model: XGJ560.
H) cool: by the solid particle of molding by cooling, pack warehouse-in.Cooler: brand: space dragon, type
Number: LQC-1.5.
The highest fuel value of solid particle of pure bamboo willow: 4110kca/kg；Ash: 4.05%.
Embodiment two:
(2) processing step of bamboo willow+tobacco rod is as follows:
A-2) selection: in the bamboo osiery district of plantation, selects diameter 10cm, and bamboo Ramulus Salicis Babylonicae 70000 kilograms does raw material；
Raw material length: bamboo Ramulus Salicis Babylonicae is cut into the length of every 30cm；
B-2) processing step of tobacco rod is with the c of processing step of (one) pure bamboo willow) to f)；
C-2) take by weight percentage bamboo willow consider to be worth doing 70000 kilograms and tobacco rod consider to be worth doing 3000 kilograms be sufficiently mixed after, insert granule
Former, by high temperature extruding forming, becomes the solid particle of 8-15mm；Centrifugal efficient granulator: brand: space dragon, type
Number: XGJ560.
D-2) cool: by the solid particle of molding by cooling, pack warehouse-in.Cooler: brand: space dragon,
Model: LQC-1.5.
The solid particle fuel value of bamboo willow 70%+ tobacco rod 30%: 3963kca/kg.
Embodiment three:
(3) processing step of bamboo willow+corn stalk is as follows:
A-3) selection: in the bamboo osiery district of plantation, selects bamboo Ramulus Salicis Babylonicae diameter 5cm, and weight 50000 kilograms does raw material；
Raw material length: bamboo Ramulus Salicis Babylonicae is cut into the length of every 40cm；
B-3) processing step of corn stalk is with the c of processing step of (one) pure bamboo willow) to f)；
C-3) take by weight percentage bamboo willow consider to be worth doing 50000 kilograms and corn stalk consider to be worth doing 50000 kilograms be sufficiently mixed after, insert
Grain forming equipment, by high temperature extruding forming, becomes the solid particle of 8-15mm；Centrifugal efficient granulator: brand: space dragon,
Model: XGJ560.
D-3) cool: by the solid particle of molding by cooling, pack warehouse-in.Cooler: brand: space dragon,
Model: LQC-1.5.
Bamboo willow 50%+ corn stalk 50% solid particle fuel value: 4184kca/kg.
Embodiment four:
(4) processing step of bamboo willow+corn stalk is as follows:
Take by weight percentage bamboo willow consider to be worth doing 80000 kilograms and corn stalk consider to be worth doing 20000 kilograms be sufficiently mixed after, insert granule
Type equipment, by high temperature extruding forming, becomes the solid particle of 8-15mm；Remaining walks with the technique of (three) bamboo willow+corn stalk
The most identical, repeat no more.Bamboo willow 80%+ corn stalk 20% solid particle fuel value: 4100kca/kg.
Embodiment five:
(5) processing step of bamboo willow+bagasse is as follows:
A-5) processing step of bamboo willow is with the processing step of (one) pure bamboo willow, repeats no more；
B-5) processing step of bagasse is with the c of processing step of (one) pure bamboo willow) to f)；
C-5) take bamboo willow by weight percentage and consider to be worth doing after 50000 kilograms and bagasse 50000 kilograms is sufficiently mixed, insert
Grain former, by high temperature extruding forming, becomes the solid particle of 8-15mm；Centrifugal efficient granulator: brand: space dragon, type
Number: XGJ560.
D-5) cool: by the solid particle of molding by cooling, pack warehouse-in.Cooler: brand: space dragon,
Model: LQC-1.5.
The fuel value of the solid particle of bamboo willow 50%+ bagasse 50%: 3775kca/kg.
Embodiment six:
(6) processing step of bamboo willow+tobacco rod+corn stalk is as follows:
Take bamboo willow by weight percentage and consider 50000 kilograms to be worth doing with 30000 kilograms of corn stalk bits with 20000 kilograms of tobacco rod bits fully
After mixing, insert granular pattern equipment, by high temperature extruding forming, become the solid particle of 8-15mm；Remaining with (two) bamboo willow+
The processing step of tobacco rod with and the processing step of (three) bamboo willow+corn stalk identical, repeat no more.
The fuel value of the solid particle of bamboo willow 50% and corn stalk 30% and tobacco rod 20%: 3775kca/kg.
Claims (7)
1. a biomass solid formed fuel product, it is characterised in that: described biomass solid formed fuel product according to
Following formula is made, by weight percentage: bamboo willow 100%；Or bamboo willow 70%+ tobacco rod 30%；Or bamboo willow 80%+ corn stalk
20%；Or bamboo willow 50%+ corn stalk 50%；Or bamboo willow 80%+ corn stalk 20%；Bamboo willow 50%+ bagasse 50%；Or bamboo
Willow 50%+ corn stalk 30%+ tobacco rod 20%.
2. the production method according to the biomass solid formed fuel product of claim 1 formula, it is characterised in that: described
The production method of biomass solid formed fuel product:
(1) processing step of pure bamboo willow is as follows:
Selection: in the bamboo osiery district of plantation, selects minimum diameter not less than 1cm, and maximum gauge is not more than the bamboo willow of 10cm
Branch does raw material；
Raw material length: bamboo Ramulus Salicis Babylonicae is cut into the length of every 20cm-40cm；
Natural drying: make somebody a mere figurehead natural drying in ventilation 24 hours；
Broken: bamboo willow raw material is all broken for the length chips less than 13mm；
Pulverizing: the chips crushed is passed through pulverizer, pulverizes the wood flour being less than 3mm into length；
It is dried: the wood flour crushed being put into traditional flue-curing barn and is dried baking, temperature is arranged at 35 degrees Celsius, and the time is set as 20 points
The baking of clock, when the moisture drying in wood flour to the moisture content less than or equal to 15%, takes out barn；
Molding: dried wood flour is inserted grain forming equipment, by high temperature extruding forming, becomes the solid of 8-15mm
Grain；
Cool: by the solid particle of molding by cooling, pack warehouse-in.
The production method of a kind of biomass solid formed fuel product the most as claimed in claim 2, it is characterised in that: described
The production method of biomass solid formed fuel product:
(2) processing step of bamboo willow+tobacco rod is as follows:
A-2) processing step of bamboo willow is with the processing step of (one) pure bamboo willow, repeats no more；
B-2) processing step of tobacco rod is with the c of processing step of (one) pure bamboo willow) to f)；
C-2) take by weight percentage bamboo willow bits 70% and tobacco rod bits 30% be sufficiently mixed after, insert grain forming equipment,
By high temperature extruding forming, become the solid particle of 8-15mm；
D-2) cool: by the solid particle of molding by cooling, pack warehouse-in.
The production method of a kind of biomass solid formed fuel product the most as claimed in claim 2, it is characterised in that: described
The production method of biomass solid formed fuel product:
(3) processing step of bamboo willow+corn stalk is as follows:
A-3) processing step of bamboo willow is with the processing step of (one) pure bamboo willow, repeats no more；
B-3) processing step of corn stalk is with the c of processing step of (one) pure bamboo willow) to f)；
C-3) take by weight percentage bamboo willow bits 50% and corn stalk bits 50% be sufficiently mixed after, insert grain forming and set
Standby, by high temperature extruding forming, become the solid particle of 8-15mm；
D-3) cool: by the solid particle of molding by cooling, pack warehouse-in.
The production method of a kind of biomass solid formed fuel product the most as claimed in claim 3, it is characterised in that: described
The production method of biomass solid formed fuel product:
(4) processing step of bamboo willow+corn stalk is as follows:
Take bamboo willow bits 80% by weight percentage and after corn stalk bits 20% are sufficiently mixed, insert grain forming equipment, logical
Cross high temperature extruding forming, become the solid particle of 8-15mm；Remaining is identical, no with the processing step of (three) bamboo willow+corn stalk
Repeat again.
The production method of a kind of biomass solid formed fuel product the most as claimed in claim 2, it is characterised in that: described
The production method of biomass solid formed fuel product:
(5) processing step of bamboo willow+bagasse is as follows:
A-5) processing step of bamboo willow is with the processing step of (one) pure bamboo willow, repeats no more；
B-5) processing step of bagasse is with the c of processing step of (one) pure bamboo willow) to f)；
C-5) take bamboo willow bits 50% by weight percentage and after bagasse 50% is sufficiently mixed, insert grain forming equipment,
By high temperature extruding forming, become the solid particle of 8-15mm；
D-5) cool: by the solid particle of molding by cooling, pack warehouse-in.
The production method of a kind of biomass solid formed fuel product the most as claimed in claim 2, it is characterised in that: described
The production method of biomass solid formed fuel product:
(6) processing step of bamboo willow+tobacco rod+corn stalk is as follows:
Take by weight percentage bamboo willow bits 50% and corn stalk bits 30% and tobacco rod bits 20% be sufficiently mixed after, insert granule
Type equipment, by high temperature extruding forming, becomes the solid particle of 8-15mm；The processing step of remaining (two) bamboo willow+tobacco rod with
And the processing step of (three) bamboo willow+corn stalk is identical, repeats no more.