CN106009882A - 水性涂料用多功能增稠剂 - Google Patents
水性涂料用多功能增稠剂 Download PDFInfo
- Publication number
- CN106009882A CN106009882A CN201610485850.4A CN201610485850A CN106009882A CN 106009882 A CN106009882 A CN 106009882A CN 201610485850 A CN201610485850 A CN 201610485850A CN 106009882 A CN106009882 A CN 106009882A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- container
- revs
- minutes under
- stirring conditions
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
水性涂料用多功能增稠剂,将重量份为620—640的丙二醇加入容器,然后再向容器中加入重量份为18—22的纯水并在400—600转/分钟搅拌条件下搅拌8—15分钟,然后再向容器中加入重量份为11—15的润湿分散剂,并在400—600转/分钟搅拌条件下搅拌12—18分钟,然后再向容器中加入重量份为340—360的黄原胶,并在800—1000转/分钟搅拌条件下搅拌25—35分钟,即得到水性涂料用多功能增稠剂。其目的在于提供一种在水性涂料生产、使用过程中可以更好地起到防沉、防分层、防流挂,在不同的PH值涂料中均可增稠的水性涂料用多功能增稠剂。
Description
技术领域
本发明涉及一种水性涂料用多功能增稠剂。
背景技术
水性涂料用增稠剂是一种流变助剂,可以使涂料增稠,防止施工中出现流挂现象,并能赋予涂料优异的机械性能和贮存稳定性。对于黏度较低的水性涂料来说,增稠剂实质上是一种流变助剂,加入增稠剂后能调节涂料的流变性,使胶黏剂和密封剂增稠,防止填料沉淀,并赋予涂料良好的物理机械稳定性,控制施工过程的流变性(施胶时不流挂、不滴淌、不飞液),还能起着降低成本的作用。但现有的涂料用增稠剂,无法做到在不同的PH值涂料中均可增稠的效果,并且其在防沉、防分层、防流挂方面的性能也较差,难以满足高级性能水性涂料的使用要求。
发明内容
本发明的目的在于提供一种在水性涂料生产、使用过程中可以更好地起到防沉、防分层、防流挂,在不同的PH值涂料中均可增稠的水性涂料用多功能增稠剂。
本发明的水性涂料用多功能增稠剂,包括重量份为620—640的丙二醇,重量份为18—22的纯水,重量份为11—15的润湿分散剂和重量份为340—360的黄原胶;
将重量份为620—640的丙二醇加入容器,然后再向容器中加入重量份为18—22的纯水并在400—600转/分钟搅拌条件下搅拌8—15分钟,然后再向容器中加入重量份为11—15的润湿分散剂,并在400—600转/分钟搅拌条件下搅拌12—18分钟,然后再向容器中加入重量份为340—360的黄原胶,并在800—1000转/分钟搅拌条件下搅拌25—35分钟,即得到水性涂料用多功能增稠剂。
本发明的水性涂料用多功能增稠剂,其中所述丙二醇的重量份为625—635,纯水的重量份为19—21,润湿分散剂的重量份为12—14,黄原胶的重量份为345—355;
将重量份为625—635的丙二醇加入容器,然后再向容器中加入重量份为19—21的纯水并在400—600转/分钟搅拌条件下搅拌9—13分钟,然后再向容器中加入重量份为12—14的润湿分散剂,并在400—600转/分钟搅拌条件下搅拌13—17分钟,然后再向容器中加入重量份为345—355的黄原胶,并在800—1000转/分钟搅拌条件下搅拌28—32分钟,即得水性涂料用多功能增稠剂。
本发明的水性涂料用多功能增稠剂,其中所述丙二醇的重量份为630,纯水的重量份为20,润湿分散剂的重量份为13,黄原胶的重量份为350;
将重量份为630的丙二醇加入容器,然后再向容器中加入重量份为20的纯水并在400—600转/分钟搅拌条件下搅拌10分钟,然后再向容器中加入重量份为13的润湿分散剂,并在400—600转/分钟搅拌条件下搅拌15分钟,然后再向容器中加入重量份为350的黄原胶,并在800—1000转/分钟搅拌条件下搅拌30分钟,即得水性涂料用多功能增稠剂。
本发明的水性涂料用多功能增稠剂,借助本发明特有的配方,将重量份为620—640的丙二醇加入容器,然后再向容器中加入重量份为18—22的纯水并在400—600转/分钟搅拌条件下搅拌8—15分钟,然后再向容器中加入重量份为11—15的润湿分散剂,并在400—600转/分钟搅拌条件下搅拌12—18分钟,然后再向容器中加入重量份为340—360的黄原胶,并在800—1000转/分钟搅拌条件下搅拌25—35分钟,即得到水性涂料用多功能增稠剂。将本发明的水性涂料用多功能增稠剂添加到水性涂料内,其在水性涂料生产、使用过程中可以更好地起到防沉、防分层、防流挂,在不同的PH值涂料中均可增稠,其在防止填料沉淀,赋予良好的物理机械稳定性,在控制施工过程的流变性、施胶时不流挂、不滴淌、不飞液等方面的效果更加突出。因此,本发明的水性涂料用多功能增稠剂具有突出的实质性特点和显著的进步。
下面结合对本发明水性涂料用多功能增稠剂作进一步说明。
具体实施方式
实施例1
本发明的水性涂料用多功能增稠剂,包括重量份为620—640的丙二醇,重量份为18—22的纯水,重量份为11—15的润湿分散剂和重量份为340—360的黄原胶;
将重量份为620—640的丙二醇加入容器,然后再向容器中加入重量份为18—22的纯水并在400—600转/分钟搅拌条件下搅拌8—15分钟,然后再向容器中加入重量份为11—15的润湿分散剂,并在400—600转/分钟搅拌条件下搅拌12—18分钟,然后再向容器中加入重量份为340—360的黄原胶,并在800—1000转/分钟搅拌条件下搅拌25—35分钟,即得到水性涂料用多功能增稠剂。
本发明的水性涂料用多功能增稠剂,优选所述丙二醇的重量份为625—635,纯水的重量份为19—21,润湿分散剂的重量份为12—14,黄原胶的重量份为345—355;
将重量份为625—635的丙二醇加入容器,然后再向容器中加入重量份为19—21的纯水并在400—600转/分钟搅拌条件下搅拌9—13分钟,然后再向容器中加入重量份为12—14的润湿分散剂,并在400—600转/分钟搅拌条件下搅拌13—17分钟,然后再向容器中加入重量份为345—355的黄原胶,并在800—1000转/分钟搅拌条件下搅拌28—32分钟,即得水性涂料用多功能增稠剂。
本发明的水性涂料用多功能增稠剂,进一步优选丙二醇的重量份为630,纯水的重量份为20,润湿分散剂的重量份为13,黄原胶的重量份为350;
将重量份为630的丙二醇加入容器,然后再向容器中加入重量份为20的纯水并在400—600转/分钟搅拌条件下搅拌10分钟,然后再向容器中加入重量份为13的润湿分散剂,并在400—600转/分钟搅拌条件下搅拌15分钟,然后再向容器中加入重量份为350的黄原胶,并在800—1000转/分钟搅拌条件下搅拌30分钟,即得水性涂料用多功能增稠剂。
上面所述的实施例仅仅是对本发明的优选实施方式进行描述,并非对本发明的范围进行限定,在不脱离本发明设计精神前提下,本领域普通工程技术人员对本发明技术方案作出的各种变形和改进,均应落入本发明的权利要求书确定的保护范围内。
Claims (3)
1.水性涂料用多功能增稠剂,其特征在于包括重量份为620—640的丙二醇,重量份为18—22的纯水,重量份为11—15的润湿分散剂和重量份为340—360的黄原胶;
将重量份为620—640的丙二醇加入容器,然后再向容器中加入重量份为18—22的纯水并在400—600转/分钟搅拌条件下搅拌8—15分钟,然后再向容器中加入重量份为11—15的润湿分散剂,并在400—600转/分钟搅拌条件下搅拌12—18分钟,然后再向容器中加入重量份为340—360的黄原胶,并在800—1000转/分钟搅拌条件下搅拌25—35分钟,即得到水性涂料用多功能增稠剂。
2.根据权利要求1所述的水性涂料用多功能增稠剂,其特征在于:所述丙二醇的重量份为625—635,纯水的重量份为19—21,润湿分散剂的重量份为12—14,黄原胶的重量份为345—355;
将重量份为625—635的丙二醇加入容器,然后再向容器中加入重量份为19—21的纯水并在400—600转/分钟搅拌条件下搅拌9—13分钟,然后再向容器中加入重量份为12—14的润湿分散剂,并在400—600转/分钟搅拌条件下搅拌13—17分钟,然后再向容器中加入重量份为345—355的黄原胶,并在800—1000转/分钟搅拌条件下搅拌28—32分钟,即得水性涂料用多功能增稠剂。
3.根据权利要求2所述的水性涂料用多功能增稠剂,其特征在于:所述丙二醇的重量份为630,纯水的重量份为20,润湿分散剂的重量份为13,黄原胶的重量份为350;
将重量份为630的丙二醇加入容器,然后再向容器中加入重量份为20的纯水并在400—600转/分钟搅拌条件下搅拌10分钟,然后再向容器中加入重量份为13的润湿分散剂,并在400—600转/分钟搅拌条件下搅拌15分钟,然后再向容器中加入重量份为350的黄原胶,并在800—1000转/分钟搅拌条件下搅拌30分钟,即得水性涂料用多功能增稠剂。