CN106009622A - 一种防霉二氧化硅气凝胶聚氨酯复合保温墙板及其制备方法 - Google Patents

一种防霉二氧化硅气凝胶聚氨酯复合保温墙板及其制备方法 Download PDF

Info

Publication number
CN106009622A
CN106009622A CN201610148690.4A CN201610148690A CN106009622A CN 106009622 A CN106009622 A CN 106009622A CN 201610148690 A CN201610148690 A CN 201610148690A CN 106009622 A CN106009622 A CN 106009622A
Authority
CN
China
Prior art keywords
parts
mildew
thermal insulation
composite thermal
polyurethane composite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201610148690.4A
Other languages
English (en)
Inventor
董良清
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dangtu County Kehui Trading Co Ltd
Original Assignee
Dangtu County Kehui Trading Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dangtu County Kehui Trading Co Ltd filed Critical Dangtu County Kehui Trading Co Ltd
Priority to CN201610148690.4A priority Critical patent/CN106009622A/zh
Publication of CN106009622A publication Critical patent/CN106009622A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种防霉二氧化硅气凝胶聚氨酯复合保温墙板,由下列重量份的原料制成:纳米碳酸锶0.6‑0.9、电木粉3‑4、胡椒碱1.2‑1.5、羧基丁腈橡胶6‑7、多孔陶瓷球100‑105、水玻璃100、Span‑80适量、Tween‑80适量、1mol/L氨水适量、丙酮适量、乙醇适量、聚醚多元醇DSU‑365 90‑94、三乙醇胺0.5‑0.54、水15‑16、二月桂酸二丁基锡0.75‑0.9、多亚甲基多苯基多异氰酸酯100‑110。本发明通过使用纳米碳酸锶、电木粉、胡椒碱、羧基丁腈橡胶,使得聚氨酯泡沫具有优良的防霉性和抗拉强度,还能够防静电,减缓老化,延长了聚氨酯泡沫的使用时间。

Description

一种防霉二氧化硅气凝胶聚氨酯复合保温墙板及其制备方法
技术领域
本发明涉及保温墙板技术领域,尤其涉及一种防霉二氧化硅气凝胶聚氨酯复合保温墙板及其制备方法。
背景技术
聚苯乙烯板是一种常见的建筑用保温材料。其密度低,力学强度好、耐腐蚀、防水、容易分割施工,但是它的导热系数相对较高(k≈0.042W/m·K)。硅气凝胶的纳米多孔结构及其超轻、超绝热、极强的紫外吸收、红外反射等特性极大的限制了热传递过程的热传导和热对流。以SiO2气凝胶/聚苯乙烯型复合结构可以进一步降低EPS保温板的导热系数,在不影响EPS板力学性能的条件下提高EPS保温板的阻燃性能。与此同时,二者复合能够有效弥补硅气凝胶在实际应用中结构强度低、亲水的缺点,同时降低导热系数,改善其阻燃性能。《SiO2气凝胶核/聚苯乙烯壳复合阻燃保温板实验研究》采用热压浸渍方法将发泡剂浸入复合珠粒,从而得到发泡型的SiO2气凝胶核/聚苯乙烯壳型复合珠粒,同时用蒸汽发泡法研究其发泡制作工艺。
但是该方法得到的保温材料因为SiO2气凝胶容易破碎而保温性能不能持续稳定。同时该保温材料的韧性、耐热性、耐水性、发热性、防静电性、防霉性、抗菌性、强度、回弹性、抗老化性、耐腐蚀性都有待提高。聚氨酯泡沫具有优异的保温性能,但是不如SiO2气凝胶保温性好,但是阻燃性不好。
《全水发泡聚氨酯硬泡的制备及其阻燃性能的研究》一文制备出了阻燃和力学性能优异的聚氨酯泡沫,但是保温性能还是不能满足科学发展的需要。
如果将SiO2气凝胶与聚氨酯泡沫结合,能够提高聚氨酯泡沫的保温性和阻燃性,但是直接复合,SiO2气凝胶容易破碎,保温效果容易消失,需要进一步改进。
发明内容
本发明目的就是为了弥补已有技术的缺陷,提供一种防霉二氧化硅气凝胶聚氨酯复合保温墙板及其制备方法。
本发明是通过以下技术方案实现的:
一种防霉二氧化硅气凝胶聚氨酯复合保温墙板,由下列重量份的原料制成:纳米碳酸锶0.6-0.9、电木粉3-4、胡椒碱1.2-1.5、羧基丁腈橡胶6-7、多孔陶瓷球100-105、水玻璃100、Span-80适量、Tween-80适量、1mol/L氨水适量、丙酮适量、乙醇适量、聚醚多元醇DSU-365 90-94、三乙醇胺0.5-0.54、水15-16、二月桂酸二丁基锡0.75-0.9、多亚甲基多苯基多异氰酸酯100-110。
所述防霉二氧化硅气凝胶聚氨酯复合保温墙板的制备方法,包括以下步骤:
(1)按体积比VSpan-80:VTween-80=1:4配比得到混合液体,将水玻璃与所述混合液体按体积比1:10混合均匀,在400r/min下搅拌30min,然后滴加1mol/L的氨水调节pH值至6-7;加入多孔陶瓷微球、纳米碳酸锶、胡椒碱,搅拌10-15min,用丙酮洗涤2-3次,静置后除去上层清液,得到混合物料;
(2)将第(1)步得到的混合物料加入2-2.5倍体积的乙醇搅拌均匀,陈化48h,过滤得到滤料,再将滤料浸泡在2-2.5倍体积的正己烷中,过滤,将滤料在45-46℃下恒温干燥,得到改性多孔陶瓷微球;
(3)将改性多孔陶瓷微球放入反应容器中,加入聚醚多元醇DSU-365、三乙醇胺、水和二月桂酸二丁基锡,在2000r/min高速搅拌下进行预混合,再加入其他剩余成分,然后在1000r/min速度下搅拌9-11s,倒入模具中,在室温下静止发泡,待反应完毕后在69-70℃温度下熟化29-31min,再在室温下存放70-72h后,即得;
所述模具的上表面设置有陶瓷板,下表面设置有4-6毫米的硅酸钙板。
所述二氧化硅气凝胶聚氨酯复合保温墙板,所述的多孔陶瓷球的气孔率为65-80%,孔径为100-500μm。
本发明的优点是:本发明使用水玻璃制备二氧化硅气凝胶,使气凝胶填充在多孔陶瓷球的孔中,再与聚氨酯泡沫反应,使得气凝胶微球被完全包裹起来,防止破碎,提高了聚氨酯泡沫的隔热性和抗压强度,还提高了泡沫的耐久性、隔音性;通过使用纳米碳酸锶、电木粉、胡椒碱、羧基丁腈橡胶,使得聚氨酯泡沫具有优良的防霉性和抗拉强度,还能够防静电,减缓老化,延长了聚氨酯泡沫的使用时间。
具体实施方式
一种防霉二氧化硅气凝胶聚氨酯复合保温墙板,由下列重量份(公斤)的原料制成:纳米碳酸锶0.6、电木粉3、胡椒碱1.2、羧基丁腈橡胶6、多孔陶瓷球100、水玻璃100、Span-80适量、Tween-80适量、1mol/L氨水适量、丙酮适量、乙醇适量、聚醚多元醇DSU-365 90、三乙醇胺0.5、水15、二月桂酸二丁基锡0.75、多亚甲基多苯基多异氰酸酯100。
所述防霉二氧化硅气凝胶聚氨酯复合保温墙板的制备方法,包括以下步骤:
(1)按体积比VSpan-80:VTween-80=1:4配比得到混合液体,将水玻璃与所述混合液体按体积比1:10混合均匀,在400r/min下搅拌30min,然后滴加1mol/L的氨水调节pH值至6;加入多孔陶瓷微球、纳米碳酸锶、胡椒碱,搅拌10min,用丙酮洗涤2次,静置后除去上层清液,得到混合物料;
(2)将第(1)步得到的混合物料加入2倍体积的乙醇搅拌均匀,陈化48h,过滤得到滤料,再将滤料浸泡在2倍体积的正己烷中,过滤,将滤料在45℃下恒温干燥,得到改性多孔陶瓷微球;
(3)将改性多孔陶瓷微球放入反应容器中,加入聚醚多元醇DSU-365、三乙醇胺、水和二月桂酸二丁基锡,在2000r/min高速搅拌下进行预混合,再加入其他剩余成分,然后在1000r/min速度下搅拌9s,倒入模具中,在室温下静止发泡,待反应完毕后在69℃温度下熟化29min,再在室温下存放70h后,即得;
所述模具的上表面设置有陶瓷板,下表面设置有4毫米的硅酸钙板。
所述二氧化硅气凝胶聚氨酯复合保温墙板,所述的多孔陶瓷球的气孔率为65%,孔径为100μm。
该实施例聚氨酯泡沫的压缩强度为322kPa,保温墙板的导热系数为0.01W/( m·K)。

Claims (3)

1.一种防霉二氧化硅气凝胶聚氨酯复合保温墙板,其特征在于:由下列重量份的原料制成:纳米碳酸锶0.6-0.9、电木粉3-4、胡椒碱1.2-1.5、羧基丁腈橡胶6-7、多孔陶瓷球100-105、水玻璃100、Span-80适量、Tween-80适量、1mol/L氨水适量、丙酮适量、乙醇适量、聚醚多元醇DSU-365 90-94、三乙醇胺0.5-0.54、水15-16、二月桂酸二丁基锡0.75-0.9、多亚甲基多苯基多异氰酸酯100-110。
2.根据权利要求1所述防霉二氧化硅气凝胶聚氨酯复合保温墙板的制备方法,其特征在于包括以下步骤:
(1)按体积比VSpan-80:VTween-80=1:4配比得到混合液体,将水玻璃与所述混合液体按体积比1:10混合均匀,在400r/min下搅拌30min,然后滴加1mol/L的氨水调节pH值至6-7;加入多孔陶瓷微球、纳米碳酸锶、胡椒碱,搅拌10-15min,用丙酮洗涤2-3次,静置后除去上层清液,得到混合物料;
(2)将第(1)步得到的混合物料加入2-2.5倍体积的乙醇搅拌均匀,陈化48h,过滤得到滤料,再将滤料浸泡在2-2.5倍体积的正己烷中,过滤,将滤料在45-46℃下恒温干燥,得到改性多孔陶瓷微球;
(3)将改性多孔陶瓷微球放入反应容器中,加入聚醚多元醇DSU-365、三乙醇胺、水和二月桂酸二丁基锡,在2000r/min高速搅拌下进行预混合,再加入其他剩余成分,然后在1000r/min速度下搅拌9-11s,倒入模具中,在室温下静止发泡,待反应完毕后在69-70℃温度下熟化29-31min,再在室温下存放70-72h后,即得;
所述模具的上表面设置有陶瓷板,下表面设置有4-6毫米的硅酸钙板。
3.根据权利要求1所述二氧化硅气凝胶聚氨酯复合保温墙板,其特征在于:所述的多孔陶瓷球的气孔率为65-80%,孔径为100-500μm。
CN201610148690.4A 2016-03-16 2016-03-16 一种防霉二氧化硅气凝胶聚氨酯复合保温墙板及其制备方法 Withdrawn CN106009622A (zh)