CN106009158A - Calcium plastic composite honeycomb packaging carton and preparation method thereof - Google Patents
Calcium plastic composite honeycomb packaging carton and preparation method thereof Download PDFInfo
- Publication number
- CN106009158A CN106009158A CN201610442888.3A CN201610442888A CN106009158A CN 106009158 A CN106009158 A CN 106009158A CN 201610442888 A CN201610442888 A CN 201610442888A CN 106009158 A CN106009158 A CN 106009158A
- Authority
- CN
- China
- Prior art keywords
- consumption
- preparation
- weight
- weight portion
- calcium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a calcium plastic composite honeycomb packaging carton and a preparation method thereof. The preparation method comprises the steps that polyethylene, polypropylene, calcium carbonate, zinc stearate, barium stearate, isobutyltriethoxysilane and an antioxidant are mixed, stirred and subjected to extruding granulation, and master batches M are obtained; the master batches M are subjected to rolling and cooling, and a base plate material N is obtained; the base plate material N is bound to the inner walls of the honeycomb carton, and the calcium plastic composite honeycomb packaging carton is obtained. The problems that due to the fact that inner paper of ordinary cartons adopts kraft paper or cardboard paper or whiteboard paper, when the ordinary cartons are used for transporting articles such as vegetables and aquatic products which are high in humidity, the cartons are prone to be affected with damp, and the mechanical property of the cartons is sharply reduced are solved.
Description
Technical field
The present invention relates to Packaging Box preparation field, in particular it relates to calcium mould composite honeycomb Packaging Box and
Its preparation method.
Background technology
In recent years, due to corrugated case have lightweight, resistance to compression, resistance to expose, anti tear and buffering, shockproof,
The easily mechanical performance such as machine-shaping, it is possible to cycling and reutilization, the advantage such as environmentally safe it is considered to be
The preferred manner of food transport packaging.But owing in it, paper is kraft paper, boxboard or white board, fortune
The article that defeated humidity is bigger, such as vegetable, aquatic products etc., easily make moist under causing carton mechanical property drastically
Fall.
Therefore it provides one can be the most waterproof, the calcium that mechanical property will be caused drastically to decline because making moist is moulded
Composite honeycomb Packaging Box and preparation method thereof is the problem that the present invention needs solution badly.
Summary of the invention
It is an object of the invention to provide a kind of calcium and mould composite honeycomb Packaging Box and preparation method thereof, solve
Common carton in it paper be kraft paper, boxboard or white board, the article that transport humidity is bigger, such as vegetables
Dish, aquatic products etc., the problem causing carton mechanical property drastically to decline of easily making moist.
To achieve these goals, the invention provides a kind of calcium and mould the preparation side of composite honeycomb Packaging Box
Method, wherein, described preparation method includes:
(1) by polyethylene, polypropylene, calcium carbonate, zinc stearate, barium stearate, isobutyl group three second
Epoxide silicon and antioxidant mix and blend, and extruding pelletization, obtain master batch M;
(2) described masterbatch M is obtained baseplate material N after calendering cooling;
(3) described baseplate material N is bonded in honeycomb carton inwall, obtains calcium and mould composite honeycomb packaging
Carton;Wherein, relative to the polyethylene of 100 weight portions, described polyacrylic consumption is 30-50 weight
Part, the consumption of described calcium carbonate is 10-20 weight portion, and the consumption of described zinc stearate is 1-5 weight portion,
The consumption of described barium stearate is 1-5 weight portion, and the consumption of described isobutyl group triethoxysilicane is 2-8 weight
Amount part, the consumption of described antioxidant is 1-4 weight portion.
Present invention also offers a kind of calcium and mould composite honeycomb Packaging Box, wherein, described calcium moulds composite honeycomb
Packaging Box is prepared by above-mentioned preparation method.
By technique scheme, the invention provides a kind of calcium and mould composite honeycomb Packaging Box and preparation thereof
Method, wherein, described preparation method includes: by polyethylene, polypropylene, calcium carbonate, zinc stearate,
Barium stearate, isobutyl group triethoxysilicane and antioxidant mix and blend, and extruding pelletization, obtain master batch
M;Described masterbatch M is obtained baseplate material N after calendering cooling;By bonding for described baseplate material N
At honeycomb carton inwall, obtaining calcium and mould composite honeycomb Packaging Box, Packaging Box is internal moulds composite wood for calcium
Material, has stronger waterproof ability, and being difficult to make moist causes carton mechanical property drastically to decline, and is simultaneously used for
The method preparing this Packaging Box is simple, raw material is easy to get.
Other features and advantages of the present invention will be described in detail in detailed description of the invention part subsequently.
Detailed description of the invention
Hereinafter the detailed description of the invention of the present invention is described in detail.It should be appreciated that this place is retouched
The detailed description of the invention stated is merely to illustrate and explains the present invention, is not limited to the present invention.
The invention provides a kind of calcium and mould the preparation method of composite honeycomb Packaging Box, wherein, described preparation
Method includes: by polyethylene, polypropylene, calcium carbonate, zinc stearate, barium stearate, isobutyl group three second
Epoxide silicon and antioxidant mix and blend, and extruding pelletization, obtain master batch M;By described masterbatch M warp
Baseplate material N is obtained after calendering cooling;Described baseplate material N is bonded in honeycomb carton inwall, obtains
Calcium moulds composite honeycomb Packaging Box;Wherein, relative to the polyethylene of 100 weight portions, described polyacrylic
Consumption is 30-50 weight portion, and the consumption of described calcium carbonate is 10-20 weight portion, described zinc stearate
Consumption is 1-5 weight portion, and the consumption of described barium stearate is 1-5 weight portion, described isobutyl group three ethoxy
The consumption of base silicon is 2-8 weight portion, and the consumption of described antioxidant is 1-4 weight portion.
So that the Packaging Box prepared possesses the most excellent waterproof ability and mechanical strength, at this
Bright one preferred embodiment in, relative to the polyethylene of 100 weight portions, described polyacrylic use
Amount is 35-45 weight portion, and the consumption of described calcium carbonate is 14-16 weight portion, the use of described zinc stearate
Amount is 2-4 weight portion, and the consumption of described barium stearate is 2-4 weight portion, described isobutyl group triethoxy
The consumption of silicon is 4-6 weight portion, and the consumption of described antioxidant is 2-3 weight portion.
In order to improve the stability of prepared baseplate material N, the present invention one preferred embodiment
In, described antioxidant is in antioxidant 1010, antioxidant 1076 or antioxidant 168
Plant or multiple.
So that the Packaging Box prepared possesses the most excellent mechanical strength, described extrusion temperature is
160-190℃。
Described polyethylene and polypropylene are the conventional use of types of those skilled in the art, such as, the present invention's
One preferred embodiment in, in order to improve mechanical strength and the water resistance of prepared Packaging Box,
The weight average molecular weight of described polyethylene is 6000-9000, and described polyacrylic weight average molecular weight is
7000-8000。
Present invention also offers a kind of calcium and mould composite honeycomb Packaging Box, wherein, described calcium moulds composite honeycomb
Packaging Box is prepared by above-mentioned preparation method.
Hereinafter will be described the present invention by embodiment.In following example, polyethylene is with poly-
The commercially available product that propylene provides for Dongying City Hong Tai waterproof material company limited.
Embodiment 1
By 100g polyethylene, 35g polypropylene, 14g calcium carbonate, 2g zinc stearate, 2g barium stearate,
4g isobutyl group triethoxysilicane and 2g antioxidant 1010 mix and blend, and extrude that (extrusion temperature is
160 DEG C) pelletize, obtain master batch M;Described masterbatch M is obtained baseplate material N after calendering cooling;
Described baseplate material N is bonded in honeycomb carton inwall, obtains calcium and mould composite honeycomb Packaging Box A1.
Embodiment 2
By 100g polyethylene, 45g polypropylene, 16g calcium carbonate, 4g zinc stearate, 4g barium stearate,
6g isobutyl group triethoxysilicane and 3g antioxidant 1076 mix and blend, and extrude that (extrusion temperature is
190 DEG C) pelletize, obtain master batch M;Described masterbatch M is obtained baseplate material N after calendering cooling;
Described baseplate material N is bonded in honeycomb carton inwall, obtains calcium and mould composite honeycomb Packaging Box A2.
Embodiment 3
By 100g polyethylene, 40g polypropylene, 15g calcium carbonate, 3g zinc stearate, 3g barium stearate,
5g isobutyl group triethoxysilicane and 2.5g antioxidant 168 mix and blend, and extrude that (extrusion temperature is
180 DEG C) pelletize, obtain master batch M;Described masterbatch M is obtained baseplate material N after calendering cooling;
Described baseplate material N is bonded in honeycomb carton inwall, obtains calcium and mould composite honeycomb Packaging Box A3.
Embodiment 4
Being prepared according to the method for embodiment 1, except for the difference that, the consumption of polyethylene is 100g, described
Polyacrylic consumption is 30g, and the consumption of described calcium carbonate is 10g, and the consumption of described zinc stearate is 1g,
The consumption of described barium stearate is 1g, and the consumption of described isobutyl group triethoxysilicane is 2g, described antioxygen
The consumption of agent 1010 is 1g, obtains calcium and moulds composite honeycomb Packaging Box A4.
Embodiment 5
Being prepared according to the method for embodiment 1, except for the difference that, the consumption of polyethylene is 100g, described
Polyacrylic consumption is 50g, and the consumption of described calcium carbonate is 20g, and the consumption of described zinc stearate is 5g,
The consumption of described barium stearate is 5g, and the consumption of described isobutyl group triethoxysilicane is 8g, described antioxygen
The consumption of agent 1010 is 4g, obtains calcium and moulds composite honeycomb Packaging Box A5.
Comparative example 1
Being prepared according to the method for embodiment 1, except for the difference that, the consumption of polyethylene is 100g, described
Polyacrylic consumption is 20g, and the consumption of described calcium carbonate is 5g, and the consumption of described zinc stearate is 0.5g,
The consumption of described barium stearate is 0.5g, and the consumption of described isobutyl group triethoxysilicane is 1g, described antioxygen
The consumption of agent 1010 is 0.5g, obtains calcium and moulds composite honeycomb Packaging Box D1.
Comparative example 2
Being prepared according to the method for embodiment 1, except for the difference that, the consumption of polyethylene is 100g, described
Polyacrylic consumption is 60g, and the consumption of described calcium carbonate is 30g, and the consumption of described zinc stearate is 10g,
The consumption of described barium stearate is 10g, and the consumption of described isobutyl group triethoxysilicane is 12g, described anti-
The consumption of oxidant 1010 is 7g, obtains calcium and moulds composite honeycomb Packaging Box D2.
Test case 1
Prepared Packaging Box A1-A5, D1 and D2 are curved strength test, and to A1-A5,
The inwall of D1 and D2 is persistently sprayed water after 20min, measures Packaging Box A1-A5, D1 and D2
Bending strength.
Table 1
By above table data it can be seen that the bending of the Packaging Box prepared within the scope of the present invention is strong
Degree is higher than outside the scope of the invention and prepares Packaging Box D1 and D2, and in currently preferred scope
The bending strength of the Packaging Box A1-A3 prepared is higher, and the bending strength of the carton after water spray is lower slightly
In the carton do not sprayed water, illustrate that carton has stronger waterproof ability, after humidity, also do not interfere with carton
Mechanical strength.
The preferred embodiment of the present invention described in detail above, but, the present invention is not limited to above-mentioned reality
Execute the detail in mode, in the technology concept of the present invention, can be to the technical side of the present invention
Case carries out multiple simple variant, and these simple variant belong to protection scope of the present invention.
It is further to note that each the concrete technology described in above-mentioned detailed description of the invention is special
Levy, in the case of reconcilable, can be combined by any suitable means, in order to avoid need not
The repetition wanted, various possible compound modes are illustrated by the present invention the most separately.
Additionally, combination in any can also be carried out between the various different embodiment of the present invention, as long as its
Without prejudice to the thought of the present invention, it should be considered as content disclosed in this invention equally.
Claims (7)
1. a calcium moulds the preparation method of composite honeycomb Packaging Box, it is characterised in that described preparation side
Method includes:
(1) by polyethylene, polypropylene, calcium carbonate, zinc stearate, barium stearate, isobutyl group three second
Epoxide silicon and antioxidant mix and blend, and extruding pelletization, obtain master batch M;
(2) described masterbatch M is obtained baseplate material N after calendering cooling;
(3) described baseplate material N is bonded in honeycomb carton inwall, obtains calcium and mould composite honeycomb packaging
Carton;Wherein, relative to the polyethylene of 100 weight portions, described polyacrylic consumption is 30-50 weight
Part, the consumption of described calcium carbonate is 10-20 weight portion, and the consumption of described zinc stearate is 1-5 weight portion,
The consumption of described barium stearate is 1-5 weight portion, and the consumption of described isobutyl group triethoxysilicane is 2-8 weight
Amount part, the consumption of described antioxidant is 1-4 weight portion.
Preparation method the most according to claim 1, wherein, relative to the poly-second of 100 weight portions
Alkene, described polyacrylic consumption is 35-45 weight portion, and the consumption of described calcium carbonate is 14-16 weight portion,
The consumption of described zinc stearate is 2-4 weight portion, and the consumption of described barium stearate is 2-4 weight portion, institute
The consumption stating isobutyl group triethoxysilicane is 4-6 weight portion, and the consumption of described antioxidant is 2-3 weight
Part.
Preparation method the most according to claim 1 and 2, wherein, described antioxidant is antioxygen
One or more in agent 1010, antioxidant 1076 or antioxidant 168.
Preparation method the most according to claim 1, wherein, described extrusion temperature is 160-190
℃。
Preparation method the most according to claim 1, wherein, the weight average molecular weight of described polyethylene
For 6000-9000.
Preparation method the most according to claim 1, wherein, described polyacrylic weight average molecular weight
For 7000-8000.
7. a calcium moulds composite honeycomb Packaging Box, it is characterised in that described calcium moulds composite honeycomb packaging
Carton is prepared by the preparation method described in any one in claim 1-6.