CN1318504C - Nano modified polyvinyl alcohol as packing material in use for clothes, and fabricating method - Google Patents
Nano modified polyvinyl alcohol as packing material in use for clothes, and fabricating method Download PDFInfo
- Publication number
- CN1318504C CN1318504C CNB2004100175854A CN200410017585A CN1318504C CN 1318504 C CN1318504 C CN 1318504C CN B2004100175854 A CNB2004100175854 A CN B2004100175854A CN 200410017585 A CN200410017585 A CN 200410017585A CN 1318504 C CN1318504 C CN 1318504C
- Authority
- CN
- China
- Prior art keywords
- polyvinyl alcohol
- clothes
- nano
- calcium carbonate
- nano modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a nano modified polyvinyl alcohol packing material used by clothes and a producing method thereof. The nano modified polyvinyl alcohol packing material used by clothes is composed of polyvinyl alcohol, nano calcium carbonate and processing aids. The producing method of the nano modified polyvinyl alcohol packing material used by clothes comprises the following steps: the polyvinyl alcohol, the nano calcium carbonate and processing aids are agitated and mixed according to proportion; then, the nano modified polyvinyl alcohol packing material used by clothes is produced by a drooling method or a film blowing method. Products of the present invention have the advantages of favorable gloss, high brightness, favorable effects on electrostatic prevention and easy degradation under natural conditions. The material is suitable for packaging materials for clothes.
Description
Technical field
The present invention relates to a kind of wrapping material and production method thereof, specifically a kind of nano modified poly ethylene alcohol clothes wrapping material and production method thereof.
Background technology
Existing garment packaging film mostly is polyethylene film, and the glossiness of this polyethylene film and brightness are relatively low, and because the electrostatic effect makes dust adsorb on this kind film easily.
Summary of the invention
The objective of the invention is at above-mentioned deficiency, develop a kind of nano modified poly ethylene alcohol clothes wrapping material and production method thereof.
Nano modified poly ethylene alcohol clothes wrapping material of the present invention, its composition is polyvinyl alcohol, nano-calcium carbonate, processing aid, wherein the weight percentage of nano-calcium carbonate is 3%-80%, the weight percentage of polyvinyl alcohol is 20%-97%, the weight percentage of processing aid is 0.1%-0.3%, the polymerization degree of polyvinyl alcohol is 500-2200, and alcoholysis degree is 97-99.99%.
The nano modified poly ethylene alcohol clothes of the present invention production method of wrapping material, its production stage is: after adding polyvinyl alcohol resin in the kneading still, adding an amount of water stirs, then add nano-calcium carbonate and stirring, add processing aid again, make mixture after the mixing, by hydrostomia method or blown film method this mixture is processed into the clothes packaging film again.
Advantage of the present invention: clothes of the present invention are compared with polyethylene garment packaging film with wrapping material, and not only gloss is better, brightness is higher, and it also has stronger anti-static effect, thereby have stoped the absorption of dust.Product of the present invention in addition is easily degraded under field conditions (factors).
Embodiment
The invention will be further described below in conjunction with embodiment.
Embodiment one: a kind of modified polyvinyl alcohol clothes wrapping material, its composition is polyvinyl alcohol, nano-calcium carbonate, 18 triglyceride.Among these three kinds of components, the weight percentage of nano-calcium carbonate is 10%, and the weight percentage of polyvinyl alcohol is 89.8%, and the weight percentage of 18 triglyceride is 0.2%.The polymerization degree of polyvinyl alcohol is 1000, and alcoholysis degree is 98%.
The production method of the foregoing description is: with the polymerization degree be 1000, alcoholysis degree be 98% polyvinyl alcohol resin add mediate in the still after, adding an amount of water stirs, then add nano-calcium carbonate and stirring, add 18 triglyceride again, make mixture after the mixing, by hydrostomia method or blown film method this mixture is processed into the clothes packaging film again.
Embodiment two: a kind of modified polyvinyl alcohol clothes wrapping material, its composition is polyvinyl alcohol, nano-calcium carbonate, glycerine.Among these three kinds of components, the weight percentage of nano-calcium carbonate is 60%, and the weight percentage of polyvinyl alcohol is 39.8%, and the weight percentage of glycerine is 0.2%.The polymerization degree of polyvinyl alcohol is 2000, and alcoholysis degree is 99%.
The production method of the foregoing description is: with the polymerization degree be 2000, alcoholysis degree be 99% polyvinyl alcohol resin add mediate in the still after, adding an amount of water stirs, then add nano-calcium carbonate and stirring, add glycerine again, make mixture after the mixing, by hydrostomia method or blown film method this mixture is processed into the clothes packaging film again.
Embodiment three: a kind of modified polyvinyl alcohol clothes wrapping material, its composition is polyvinyl alcohol, nano-calcium carbonate, glycerine, 18 triglyceride, among these four kinds of components, the weight percentage of nano-calcium carbonate is 5%, the weight percentage of polyvinyl alcohol is 94.6%, the weight percentage of glycerine is 0.2%, and the weight percentage of 18 triglyceride is 0.2%.The polymerization degree of polyvinyl alcohol is 1700, and alcoholysis degree is 99.98%.
The production method of the foregoing description is: with the polymerization degree be 1700, alcoholysis degree be 99.98% polyvinyl alcohol resin add mediate in the still after, adding an amount of water stirs, then add nano-calcium carbonate and stirring, add glycerine, 18 triglyceride again, make mixture after the mixing, by hydrostomia method or blown film method this mixture is processed into the clothes packaging film again.
Claims (4)
1, a kind of nano modified poly ethylene alcohol clothes wrapping material, the composition that it is characterized in that it is polyvinyl alcohol, nano-calcium carbonate, processing aid 18 triglyceride or glycerine, the total weight percentage of these three kinds of components is 100%, wherein the weight percentage of nano-calcium carbonate is 3%-80%, and the weight percentage of polyvinyl alcohol is 20%-97%.
2, nano modified poly ethylene alcohol clothes wrapping material according to claim 1, the weight percentage that it is characterized in that processing aid 18 triglyceride or glycerine is 0.1%-0.3%.
3, nano modified poly ethylene alcohol clothes wrapping material according to claim 1, the polymerization degree that it is characterized in that polyvinyl alcohol is 500-2200, alcoholysis degree is 97-99.99%.
4, the nano modified poly ethylene alcohol clothes according to claim 1 production method of wrapping material, its production stage is: after adding polyvinyl alcohol resin in the kneading still, adding an amount of water stirs, then add nano-calcium carbonate and stirring, add processing aid 18 triglyceride or glycerine again, make mixture after the mixing, by hydrostomia method or blown film method this mixture is processed into the clothes packaging film again.