CN106009136A - Preparation method of wood toy - Google Patents
Preparation method of wood toy Download PDFInfo
- Publication number
- CN106009136A CN106009136A CN201610493532.2A CN201610493532A CN106009136A CN 106009136 A CN106009136 A CN 106009136A CN 201610493532 A CN201610493532 A CN 201610493532A CN 106009136 A CN106009136 A CN 106009136A
- Authority
- CN
- China
- Prior art keywords
- preparation
- parts
- rubber
- surface layer
- transition surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a preparation method of a wood toy. The preparation method at least comprises the following steps: body preparation, primer painting, ash supplementing, finish paint spraying, and inspection and packaging. The preparation method also comprises the step of transition surface layer preparation. The transition surface layer is formed on the surface layer of the body obtained in the body preparation process, and the primer is painted on the transition surface layer. The transition surface layer is prepared from the following raw materials in parts by weight: 100-120 parts of rubber, 50-80 parts of high-dispersity white carbon black, 10-20 parts of coupling agent, 5-8 parts of stearic acid, 5-8 parts of activator, 1-3 parts of microcrystalline wax and 1-3 parts of polyethyleneglycol. The preparation method has the advantages of simple technique, high product structure stability and firm painting interlayer combination, effectively enhances the quality and corrosion resistance of the wood toy, and prolongs the service life of the wood toy.
Description
Technical field
The present invention relates to the preparation method of a kind of toy, the preparation method of a kind of wooden toy.
Background technology
The wooden toy in ancient times generation, is single wooden toy, modern wooden toy practical unlike material work the most in various degree
The contact of skill and process, reach the variation of play function, multifunction.
One main kind of in toy classification of wooden toy, history is of long standing and well established, and wooden toy is sent out in the history of European and American developed countries
Each each stage of exhibition, at unique culture and realization configuration of being had of America and Europe, respective country in history, the wooden toy of Germany
It is the most also to be most notable.In the ancient times of Germany, just having the appearance of belt driven lathe, wooden toy is exactly belt driven lathe processing,
Polishing the most by hand, the size of this kind of wooden toy has to the biggest toy from the least several feet, and this type toy most has
The works entering the coffin-die Asia Noah's ark represented.
Have a people being A Erbai in U.S. Philadelphia, he is German, within 1872, migrates the U.S. arrived, and he starts as circus troupe's system
Making wooden horse toy, his made wooden saddlery has nimbly and freely, lifelike feature, and by locality, a lot of circus troupe adopts
With, the most still can see its trace, be the most popular wooden horse.Later, circus troupe is mounted with four wheels at wooden horse,
Reform into the blank of carriage in ancient times.
Because the inspiration of wooden horse, during wooden toy afterwards manufactures, wooden train, wooden vehicle, wooden steamer, wooden
Tractors etc. occur in succession, by now till, wooden aircraft has become favorite in children's toy, from this point can be seen that,
The existing long history of wooden toy and cultural connotation, have the breath in imparting epoch.
In other wooden toy, stilt and gyro are also the toys that children are delithted with, and stilt are the simplest wooden toies,
Teaching through lively activities, gyro is the practical simplest wooden toy of processing technology, but in the middle of child, application is at most, as a child at ice
Above make gyro, when gyro rotates when, therefrom acquire the knowledge such as mechanics principle, acceleration, it may be said that wooden toy pair
People's intellectual development is performed meritorious deeds never to be obliterated.
In China, wooden toy history is the longest, famous ' Huarongdao ' in ancient times, the most always plays, understands everyone
The effect of thing, power and the skill mutually fought are all critically important, afterwards, occur in that again wooden toy building blocks, long-pending building
During wood, having understood the reason of building, put up and would not fall, the not science built is fallen down exactly, and perhaps this develop
A lot of building designers, thus, toy is the intelligence teacher that the mankind impart rudimentary knowledge to beginners, and the good children's intelligence of object for appreciation will be the most outstanding,
This also gives the glorious responsibility of toy manufacturing enterprise.
Wooden toy the most morphologically have nature, abstract, artistic form point.The naturally essence of morphologic appearance toy,
To the comfort of people's soul, the mental factor of abstract morphologic appearance toy, to the unlimited reverie of people.The morphologic appearance toy of art
Appreciation factor, to the sensation that people is beautiful.When people is mood is gloomy when, if he is appreciating a toy the most stupid very greatly, that
He is more painful, at this time, he appreciate one in bright gay color, profile is graceful, it appears that the most happy toy, mood meeting
Different.
Wooden toy is not only to have unique charm in intellectual development, has good feature, practical safety the most in other respects
It is first, owing to wooden toy is all processed with timber, nonpoisonous and tasteless, helpful to the physical and mental health of child, then have
Being exactly to fall not bad, wear-resisting, the resistance to advantage such as beat, this is also the factor abroad hankering after buying Chinese wooden.
Although existing wooden toy has aforesaid advantage, but it is as natural organic, is difficult to without doubt avoid
To make moist, to go mouldy, corruption, the problem of the aspect such as deformation, bring difficulty for life-time service, cause the highest popularization should
Use cost.
Summary of the invention
For solving the problems referred to above, the invention discloses the preparation method of a kind of wooden toy, technique is simple, and cost controllability is good,
Product structure good stability, brushing interlayer is firmly combined with, and is effectively improved quality and the antiseptic property of wooden toy, extends it
Service life.
The preparation method of wooden toy disclosed by the invention, at least include body preparation, transition surface layer prepare, prime, benefit
The spraying of ash, finish paint forms top coat layer and test package, and transition surface layer is formed on the base substrate top layer that body preparation obtains, priming paint
Being formed on transition surface layer by prime, transition surface layer includes according to the raw material of weight portion: rubber 100-120 part, high score
Dissipate white carbon 50-80 part, coupling agent 10-20 part, stearic acid 5-8 part, activating agent 5-8 part, microwax 1-3 part, poly-second
Glycol 1-3 part.Coupling agent (such as silane coupler etc.), activating agent etc. are the material that this area is commonly commonly used, and to the present invention
Scheme has universal adaptability.The transition surface layer arranged by employing in this programme, forms transitionality by it in billet surface
Structure, the binding ability of wooden structures Yu skin of paint to strengthen base substrate, to reduce in the base substrate renovation process of toy right simultaneously
Mend the dependency of ash technique, reduce benefit mortar and have influence on the associativity of skin of paint on surface or the larger amount of use of local
Can, thus improve overall structure performance and the quality stability of toy.
A kind of improvement of the preparation method of wooden toy disclosed by the invention, rubber be natural rubber, butadiene-styrene rubber, isoprene rubber,
Butyl rubber, butadiene rubber, polyurethane, SIS, SB, polyacrylic acid
One or more in ester, ethene-vinyl acetate copolymer.When rubber is the above-mentioned multiple mixture enumerated, then it is any matter
Amount ratio.
A kind of improvement of the preparation method of wooden toy disclosed by the invention, after benefit ash is for being prepared as slurry by ash material, is coated on work
On part, through polishing.
A kind of improvement of the preparation method of wooden toy disclosed by the invention, ash material includes the raw material of following weight portion: common silicic acid
Salt cement 30～60 parts, Gypsum Fibrosum 10～30 parts, penetrant crystalline material 1～4 parts, rubber powder 1～4 parts, water-retaining agent 0～0.3 part
With fiber 0.1～0.3 part.By using special ash material to form in this programme, form, at surface of the work, the structure sheaf that hardness is higher,
Be beneficial to processing and post-processing operation, simultaneously by simple grinding process after, its add fiber can by polish strength control
Its prominent surface is formed and is similar to the structure of " burr " and controls this structure highlight the length on surface, thus shape in subsequent treatment
Become interlaminar improvement attachment structure, thus strengthen the fastness of Coating combination so that the surface structure of toy is more stable firmly, adds
Work is more preferable, and abrasion resistance is higher.
A kind of improvement of the preparation method of wooden toy disclosed by the invention, penetrant crystalline material is activated silica penetrant crystalline masterbatch.
A kind of improvement of the preparation method of wooden toy disclosed by the invention, rubber powder is the Redispersable latex good with the cement compatibility
Powder.
A kind of improvement of the preparation method of wooden toy disclosed by the invention, redispersable latex powder selected from ethylene-vinyl acetate,
One or more in acrylate and styrene-acrylate.
A kind of improvement of the preparation method of wooden toy disclosed by the invention, finish paint outer layer is also formed with glass sedimentary, and glass sinks
Lamination is formed on finish paint outer layer.This glass sedimentary is that sodium silicate alkaline aqueous solution brushing to dried coat of paint surface obtains,
It is 0.5-0.8 micron that glass sedimentary forms thickness.By the glass sedimentary formed in the technical program, with the outermost of toy
Rotating fields is formed with one layer of comparatively dense glass structure layer, thus play effective oxygen barrier, water proof rises the most to a certain extent
To the effect of fire protection flame retarding, (other parts of wooden toy are respectively provided with combustibility, and this glass sedimentary then serves certain slow
Solution effect, and be difficult to simply be lighted), simultaneously facilitate and surface is polished or frosted, improve the outward appearance of product, have
Good case hardness and wearability.
Toy disclosed by the invention, has good surface texture, has good Surface Machining performance and serviceability, and
Technique is simple, and cost controllability is good, product structure good stability, and brushing interlayer is firmly combined with, and is effectively improved wooden toy
Quality and antiseptic property, extend its service life, and there is good safety in utilization.
Detailed description of the invention
Below in conjunction with detailed description of the invention, it is further elucidated with the present invention, it should be understood that following detailed description of the invention is merely to illustrate this
Bright rather than limit the scope of the present invention.
Embodiment 1
The preparation method of the present embodiment toy, at least includes that prepared by body preparation, transition surface layer, prime, benefit are grey, finish paint
Spraying forms top coat layer and test package, and transition surface layer is formed on the base substrate top layer that body preparation obtains, and priming paint passes through priming paint
Brushing be formed on transition surface layer, transition surface layer includes according to the raw material of weight portion: rubber 100 parts, high-dispersion white carbon black 70 parts,
Coupling agent 20 parts, stearic acid 6.4 parts, activating agent 5.8 parts, microwax 1.6 parts, Polyethylene Glycol 2.3 parts.
Embodiment 2
The preparation method of the present embodiment toy, at least includes that prepared by body preparation, transition surface layer, prime, benefit are grey, finish paint
Spraying forms top coat layer and test package, and transition surface layer is formed on the base substrate top layer that body preparation obtains, and priming paint passes through priming paint
Brushing be formed on transition surface layer, transition surface layer includes according to the raw material of weight portion: rubber 103 parts, high-dispersion white carbon black 73 parts,
Coupling agent 10 parts, stearic acid 7.2 parts, activating agent 8 parts, microwax 2.7 parts, Polyethylene Glycol 3 parts.
Embodiment 3
The preparation method of the present embodiment toy, at least includes that prepared by body preparation, transition surface layer, prime, benefit are grey, finish paint
Spraying forms top coat layer and test package, and transition surface layer is formed on the base substrate top layer that body preparation obtains, and priming paint passes through priming paint
Brushing be formed on transition surface layer, transition surface layer includes according to the raw material of weight portion: rubber 109 parts, high-dispersion white carbon black 50 parts,
Coupling agent 15 parts, stearic acid 5.5 parts, activating agent 5 parts, microwax 2 parts, Polyethylene Glycol 1 part.
Embodiment 4
The preparation method of the present embodiment toy, at least includes that prepared by body preparation, transition surface layer, prime, benefit are grey, finish paint
Spraying forms top coat layer and test package, and transition surface layer is formed on the base substrate top layer that body preparation obtains, and priming paint passes through priming paint
Brushing be formed on transition surface layer, transition surface layer includes according to the raw material of weight portion: rubber 110 parts, high-dispersion white carbon black 80 parts,
Coupling agent 12 parts, stearic acid 8 parts, activating agent 6.2 parts, microwax 3 parts, Polyethylene Glycol 1.8 parts.
Embodiment 5
The preparation method of the present embodiment toy, at least includes that prepared by body preparation, transition surface layer, prime, benefit are grey, finish paint
Spraying forms top coat layer and test package, and transition surface layer is formed on the base substrate top layer that body preparation obtains, and priming paint passes through priming paint
Brushing be formed on transition surface layer, transition surface layer includes according to the raw material of weight portion: rubber 113 parts, high-dispersion white carbon black 60 parts,
Coupling agent 17 parts, stearic acid 7 parts, activating agent 7 parts, microwax 1 part, Polyethylene Glycol 2 parts.
Embodiment 6
The preparation method of the present embodiment toy, at least includes that prepared by body preparation, transition surface layer, prime, benefit are grey, finish paint
Spraying forms top coat layer and test package, and transition surface layer is formed on the base substrate top layer that body preparation obtains, and priming paint passes through priming paint
Brushing be formed on transition surface layer, transition surface layer includes according to the raw material of weight portion: rubber 116 parts, high-dispersion white carbon black 70 parts,
Coupling agent 16 parts, stearic acid 6 parts, activating agent 6 parts, microwax 2.4 parts, Polyethylene Glycol 1.2 parts.
Embodiment 7
The preparation method of the present embodiment toy, at least includes that prepared by body preparation, transition surface layer, prime, benefit are grey, finish paint
Spraying forms top coat layer and test package, and transition surface layer is formed on the base substrate top layer that body preparation obtains, and priming paint passes through priming paint
Brushing be formed on transition surface layer, transition surface layer includes according to the raw material of weight portion: rubber 120 parts, high-dispersion white carbon black 56 parts,
Coupling agent 13 parts, stearic acid 5 parts, activating agent 7.8 parts, microwax 1.3 parts, Polyethylene Glycol 2.6 parts.
Distinguish with above-described embodiment, the scheme of rubber be include, without being limited to following arbitrary: rubber is natural rubber；
Butadiene-styrene rubber；Isoprene rubber；Butyl rubber；Butadiene rubber；Polyurethane；SIS；Styrene-fourth
Diene copolymers；Polyacrylate；Ethene-vinyl acetate copolymer；It is natural rubber, butadiene-styrene rubber, isoamyl rubber including rubber
Glue, butyl rubber, butadiene rubber, polyurethane, SIS, SB, poly-third
Any two kinds in olefin(e) acid ester, ethene-vinyl acetate copolymer (if rubber is natural rubber, any quality of two kinds of butadiene-styrene rubber
Than composition, remaining scheme does not enumerates, and can be obtained by simple permutation and combination)；It is natural rubber including rubber
Glue, butadiene-styrene rubber, isoprene rubber, butyl rubber, butadiene rubber, polyurethane, SIS, styrene
Any three kinds in-butadiene copolymer, polyacrylate, ethene-vinyl acetate copolymer (if rubber is natural rubber, fourth
Benzene rubber, any mass ratio composition of butadiene rubber three kinds, remaining scheme does not enumerates, can be by simple row
Row combination obtains)；Including rubber be natural rubber, butadiene-styrene rubber, isoprene rubber, butyl rubber, butadiene rubber, polyurethane,
Appointing in SIS, SB, polyacrylate, ethene-vinyl acetate copolymer
Anticipate four kinds (if rubber is polyacrylate, ethene-vinyl acetate copolymer, isoprene rubber, any quality of butadiene rubber four kinds
Than composition, remaining scheme does not enumerates, and can be obtained by simple permutation and combination)；And other include five kinds,
Six kinds of grades are in interior whole schemes.This place as space is limited with the factor of the arrangement aspect such as probability, with regard to feasible program is not carried out by
One enumerates, and only illustrates with preceding sections, and not as the restriction of claimed range.
Distinguish with above-described embodiment, mend ash for ash material is prepared as slurry after, be coated on workpiece, through polishing.
Distinguishing with above-described embodiment, the composition of ash material is illustrated by following PART, and not as requiring model
The restriction enclosed, and all can be suitable in the present invention program:
The composition embodiment 1 of ash material
In this enforcement, ash material includes the raw material of following weight portion: Portland cement 30 parts, 12 parts of Gypsum Fibrosum, penetrant crystalline material
Expect 3 parts, rubber powder 3.3 parts and fiber 0.22 part.
The composition embodiment 2 of ash material
In this enforcement, ash material includes the raw material of following weight portion: Portland cement 40 parts, 30 parts of Gypsum Fibrosum, penetrant crystalline material
Expect 1 part, rubber powder 2.5 parts, water-retaining agent 0.3 part and fiber 0.2 part.
The composition embodiment 3 of ash material
In this enforcement, ash material includes the raw material of following weight portion: Portland cement 50 parts, 26 parts of Gypsum Fibrosum, penetrant crystalline material
Expect 2 parts, rubber powder 3 parts, water-retaining agent 0.1 part and fiber 0.3 part.
The composition embodiment 4 of ash material
In this enforcement, ash material includes the raw material of following weight portion: Portland cement 60 parts, 20 parts of Gypsum Fibrosum, penetrant crystalline material
Expect 4 parts, rubber powder 2 parts, water-retaining agent 0.2 part and fiber 0.1 part.
The composition embodiment 5 of ash material
In this enforcement, ash material includes the raw material of following weight portion: Portland cement 38 parts, 17 parts of Gypsum Fibrosum, penetrant crystalline material
Expect 1.8 parts, rubber powder 4 parts, water-retaining agent 0.15 part and fiber 0.28 part.
The composition embodiment 6 of ash material
In this enforcement, ash material includes the raw material of following weight portion: Portland cement 52 parts, 10 parts of Gypsum Fibrosum, penetrant crystalline material
Expect 3.2 parts, rubber powder 1 part, water-retaining agent 0.23 part and fiber 0.13 part.
Distinguishing with above-described embodiment, penetrant crystalline material is activated silica penetrant crystalline masterbatch.
Distinguishing with above-described embodiment, rubber powder is the redispersable latex powder good with the cement compatibility.
Distinguishing with above-described embodiment, redispersable latex powder is to include, without being limited to the one in following scheme: ethyl vinyl acetate
Vinyl acetate；Acrylate；Styrene-acrylate；Ethylene-vinyl acetate, acrylate；Ethylene-vinyl acetate, benzene
Ethylene-acrylate；Acrylate, styrene-acrylate and；Ethylene-vinyl acetate, acrylate, styrene-acrylonitrile copolymer
Acid esters.When redispersable latex powder has plurality of raw materials, combine for any mass ratio.
Include, without being limited in embodiments above, the toy product obtained, through different batches sampling 10, carry out water soaking,
Oil immersion bubble, 1m height concrete floor base plate drop 3 times, the solid desktop 100 inferior tests that rub continuously all damage without obvious.
Distinguishing with above-described embodiment, finish paint outer layer is also formed with glass sedimentary, glass sedimentary is formed on finish paint outer layer.
Distinguishing with above-described embodiment, glass sedimentary is that sodium silicate alkaline aqueous solution brushing to dried coat of paint surface obtains
Arrive, glass sedimentary formed thickness be 0.5 micron (glass sedimentary forms thickness can also be arbitrary for including, without being limited to:
0.54 micron, 0.6 micron, 0.62 micron, 0.7 micron, 0.78 micron, 0.8 micron and 0.5-0.8 micron).
Including, without being limited in embodiments above, the toy product with glass sedimentary obtained, through different batches sampling
10, carry out water soaking, oil immersion bubble, 1m height concrete floor base plate drop 3 times, the solid desktop 100 inferior tests that rub continuously equal
Without substantially damage, and under conventional chambers environment, with general flame calcination 3min without substantially peeling off and combustion phenomena.
This place embodiment is to right in place of the claimed non-limit of technical scope midrange and in embodiment technical scheme
Single or multiple technical characteristic replace the new technical scheme formed on an equal basis, the most all in the scope of protection of present invention
In；Simultaneously in all embodiments enumerated or do not enumerate of the present invention program, parameters in the same embodiment is merely representative of
One example (i.e. a kind of feasible scheme) of its technical scheme, and between parameters, there is not strict cooperation and restriction
Relation, the most each parameter can mutually be replaced, except special declaration when stating ask without prejudice to axiom and the present invention.
Technological means disclosed in the present invention program is not limited only to the technological means disclosed in above-mentioned technological means, also include by more than
The technical scheme that technical characteristic combination in any is formed.The above is the detailed description of the invention of the present invention, it is noted that for
For those skilled in the art, under the premise without departing from the principles of the invention, it is also possible to make some improvement and profit
Decorations, these improvements and modifications are also considered as protection scope of the present invention.
Claims (7)
1. a preparation method for wooden toy, at least includes body preparation, prime, benefit ash, finish paint spraying and inspection bag
Dress, it is characterised in that: described preparation method also includes prepared by transition surface layer, and described transition surface layer is formed at body preparation and obtains
To base substrate top layer on, described priming paint is formed on transition surface layer by prime, and described transition surface layer is according to weight portion
Raw material include: rubber 100-120 part, high-dispersion white carbon black 50-80 part, coupling agent 10-20 part, stearic acid 5-8
Part, activating agent 5-8 part, microwax 1-3 part, Polyethylene Glycol 1-3 part.
The preparation method of wooden toy the most according to claim 1, it is characterised in that: described rubber is natural rubber, butylbenzene
Rubber, isoprene rubber, butyl rubber, butadiene rubber, polyurethane, SIS, styrene-fourth
One or more in diene copolymers, polyacrylate, ethene-vinyl acetate copolymer.
The preparation method of wooden toy the most according to claim 1, it is characterised in that: described ash of mending is for prepare pulping by ash material
After material, it is coated on workpiece, through polishing.
The preparation method of wooden toy the most according to claim 1, it is characterised in that: described ash material includes following weight portion
Raw material: Portland cement 30～60 parts, Gypsum Fibrosum 10～30 parts, penetrant crystalline material 1～4 parts, rubber powder 1～4
Part, water-retaining agent 0～0.3 part and fiber 0.1～0.3 part.
The preparation method of wooden toy the most according to claim 4, it is characterised in that: described penetrant crystalline material is activated silica
Penetrant crystalline masterbatch.
The preparation method of wooden toy the most according to claim 4, it is characterised in that: described rubber powder is good with the cement compatibility
Redispersable latex powder.
The preparation method of wooden toy the most according to claim 6, it is characterised in that: described redispersable latex powder is selected from second
One or more in alkene-vinylacetate, acrylate and styrene-acrylate.