CN106003926A - 一种体育馆用复合橡胶地板制备方法 - Google Patents

一种体育馆用复合橡胶地板制备方法 Download PDF

Info

Publication number
CN106003926A
CN106003926A CN201610319473.7A CN201610319473A CN106003926A CN 106003926 A CN106003926 A CN 106003926A CN 201610319473 A CN201610319473 A CN 201610319473A CN 106003926 A CN106003926 A CN 106003926A
Authority
CN
China
Prior art keywords
gymnasium
preparation
rubber floor
intermediate layer
composite rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610319473.7A
Other languages
English (en)
Inventor
谢彪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANJIN NOVOTRACK RUBBER PRODUCTS CO Ltd
Original Assignee
TIANJIN NOVOTRACK RUBBER PRODUCTS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANJIN NOVOTRACK RUBBER PRODUCTS CO Ltd filed Critical TIANJIN NOVOTRACK RUBBER PRODUCTS CO Ltd
Priority to CN201610319473.7A priority Critical patent/CN106003926A/zh
Publication of CN106003926A publication Critical patent/CN106003926A/zh
Pending legal-status Critical Current

Abstract

一种体育馆用复合橡胶地板制备方法，它涉及一种体育馆用地板制备方法，具体涉及一种体育馆用复合橡胶地板制备方法。本发明为了解决现有体育场馆用符合橡胶地板制备工艺复杂，制作效率低，生产成本较高的问题。本发明的步骤为：步骤一、压延；步骤二、裁片；步骤三：硫化；步骤四、粘合；步骤五、裁剪。本发明属于体育器材领域。

Description

一种体育馆用复合橡胶地板制备方法
技术领域
本发明涉及一种体育馆用地板制备方法，具体涉及一种体育馆用复合橡胶地板制备方法，属于体育器材领域。
背景技术
橡胶地板是PVC地板的另一种叫法，其主要成分为聚氯乙烯材料，复合式橡胶地板其最上层为纯PVC透明层，下面加上印花层和发泡层，它广泛应用于体育场馆的地面铺设。现有体育场馆用符合橡胶地板制备工艺复杂，制作效率低，生产成本较高。
发明内容
本发明为解决现有体育场馆用符合橡胶地板制备工艺复杂，制作效率低，生产成本较高的问题，进而提出一种体育馆用复合橡胶地板制备方法。
本发明为解决上述问题采取的技术方案是：本发明具体步骤如下：
步骤一、压延：将中间层和底层的胶料用压延机压延出片，再用平板硫化机模压整体硫化出来，面层的胶料也先用压延机压延出片；
步骤二、裁片：按尺寸大小将步骤一中的中间层、底层、面层裁成方片；
步骤三：硫化：对步骤二中裁成的方片用平板硫化机模压分片硫化出来；
步骤四、粘合：中间层、底层、面层的粘合面经表面处理后，涂上胶粘剂等待一段时间，涂刷第二遍，先贴中间层和底层，再贴面层；
步骤五、裁剪：对步骤四中粘合后的产品进行裁剪成为成品。
进一步的，步骤一中硫化条件为硫化温度在140-170℃硫化压力为0.5-3Mpa。
进一步的，步骤三中硫化条件为硫化温度在140-170℃硫化压力为0.5-3Mpa。
进一步的，步骤四中涂上胶粘剂等待5至20分钟。
本发明的有益效果是：本发明所述复合橡胶地板彩色多图案可组合拼装，中间层的吸盘结构使其弹性好，且耐磨、防滑、阻燃、抗静电，所述的制备工艺，工艺简化，能减轻工人劳动强度。
附图说明
图1是本发明的工艺流程图。
具体实施方式
具体实施方式一：结合图1说明本实施方式，本实施方式所述一种体育馆用复合橡胶地板制备方法的具体步骤如下：
步骤一、压延：将中间层和底层的胶料用压延机压延出片，再用平板硫化机模压整体硫化出来，面层的胶料也先用压延机压延出片；
步骤二、裁片：按尺寸大小将步骤一中的中间层、底层、面层裁成方片；
步骤三：硫化：对步骤二中裁成的方片用平板硫化机模压分片硫化出来；
步骤四、粘合：中间层、底层、面层的粘合面经表面处理后，涂上胶粘剂等待一段时间，涂刷第二遍，先贴中间层和底层，再贴面层；
步骤五、裁剪：对步骤四中粘合后的产品进行裁剪成为成品。
具体实施方式二：结合图1说明本实施方式，本实施方式所述一种体育馆用复合橡胶地板制备方法的步骤一中硫化条件为硫化温度在140-170℃硫化压力为0.5-3Mpa。其它组成及连接关系与具体实施方式一相同。
具体实施方式三：结合图1说明本实施方式，本实施方式所述一种体育馆用复合橡胶地板制备方法的步骤三中硫化条件为硫化温度在140-170℃硫化压力为0.5-3Mpa。其它组成及连接关系与具体实施方式一相同。
具体实施方式四：结合图1说明本实施方式，本实施方式所述一种体育馆用复合橡胶地板制备方法的步骤四中涂上胶粘剂等待5至20分钟。其它组成及连接关系与具体实施方式一相同。
以上所述，仅是本发明的较佳实施例而已，并非对本发明作任何形式上的限制，虽然本发明已以较佳实施例揭露如上，然而并非用以限定本发明，任何熟悉本专业的技术人员，在不脱离本发明技术方案范围内，当可利用上述揭示的技术内容做出些许更动或修饰为等同变化的等效实施例，但凡是未脱离本发明技术方案内容，依据本发明的技术实质，在本发明的精神和原则之内，对以上实施例所作的任何简单的修改、等同替换与改进等，均仍属于本发明技术方案的保护范围之内。

Claims (4)

1.一种体育馆用复合橡胶地板制备方法，其特征在于：所述一种体育馆用复合橡胶地板制备方法的具体步骤如下：
步骤一、压延：将中间层和底层的胶料用压延机压延出片，再用平板硫化机模压整体硫化出来，面层的胶料也先用压延机压延出片；
步骤二、裁片：按尺寸大小将步骤一中的中间层、底层、面层裁成方片；
步骤三：硫化：对步骤二中裁成的方片用平板硫化机模压分片硫化出来；
步骤四、粘合：中间层、底层、面层的粘合面经表面处理后，涂上胶粘剂等待一段时间，涂刷第二遍，先贴中间层和底层，再贴面层；
步骤五、裁剪：对步骤四中粘合后的产品进行裁剪成为成品。
2.根据权利要求1所述一种体育馆用复合橡胶地板制备方法，其特征在于：步骤一中硫化条件为硫化温度在140-170℃硫化压力为0.5-3Mpa。
3.根据权利要求1所述一种体育馆用复合橡胶地板制备方法，其特征在于：步骤三中硫化条件为硫化温度在140-170℃硫化压力为0.5-3Mpa。
4.根据权利要求1所述一种体育馆用复合橡胶地板制备方法，其特征在于：步骤四中涂上胶粘剂等待5至20分钟。
CN201610319473.7A 2016-05-16 2016-05-16 一种体育馆用复合橡胶地板制备方法 Pending CN106003926A (zh)