CN105985568A - 一种抗老化抗紫外电缆料 - Google Patents
一种抗老化抗紫外电缆料 Download PDFInfo
- Publication number
- CN105985568A CN105985568A CN201510092541.6A CN201510092541A CN105985568A CN 105985568 A CN105985568 A CN 105985568A CN 201510092541 A CN201510092541 A CN 201510092541A CN 105985568 A CN105985568 A CN 105985568A
- Authority
- CN
- China
- Prior art keywords
- parts
- cable materials
- aging resistance
- antioxidant
- absorbent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种抗老化抗紫外电缆料，其特征在于，由下列重量份的原料组分制备而成：线性聚乙烯125-135份、高密度聚乙烯15-25份、光稳定剂3-4份、抗氧化剂4-7份、紫外线吸收剂2-3份、防老剂4-9份、氧化铈4-8份、氧化钕2-4份、氧化镧1-2份和色母料5-10份，不仅具有优秀的耐寒性、耐热性、耐化学性和耐磨性，同时具有很好的抗氧化性能，延长了电缆料的使用寿命，使用色母料为电缆料着色，方便分辨，而且混入了少量氧化铈、氧化钕和氧化镧，提高了本配方各原料之间的结合性。
Description
技术领域
本发明涉及无机填料领域，具体是涉及一种抗老化抗紫外电缆料。
背景技术
电缆料是电线电缆绝缘及护套用塑料的俗称，其材质包括了橡胶、塑料、尼龙等多种，其中尤以聚乙烯为材质居多，以卧式角向挤出法经混合、挤出、造粒等工序制造。电缆料被应用于电线电缆绝缘及护套，多被设置于室外，受天气、温度、紫外线等因素影响，往往会导致电缆料制成的电缆绝缘护套发生龟裂、断裂。
发明内容
针对上述问题，本发明提供了一种抗老化抗紫外电缆料。
为解决以上技术问题，本发明提供的技术方案是:
一种抗老化抗紫外电缆料，其特征在于，由下列重量份的原料组分制备而成：
线性聚乙烯 125-135份
高密度聚乙烯 15-25份
光稳定剂 3-4份
抗氧化剂 4-7份
紫外线吸收剂 2-3份
防老剂 4-9份
氧化铈 4-8份
氧化钕 2-4份
氧化镧 1-2份
色母料 5-10份。
上述的一种抗老化抗紫外电缆料，其中，线性聚乙烯与高密度聚乙烯的份数混合比例为1：0.1-0.2。
上述的一种抗老化抗紫外电缆料，其中，所述光稳定剂为紫外光屏蔽剂和紫外光吸收剂以1:0.5的比例混合而成。
上述的一种抗老化抗紫外电缆料，其中，所述抗氧化剂为抗氧剂1010和抗氧剂168以1：1的比例混合而成。
上述的一种抗老化抗紫外电缆料，其中，所述紫外线吸收剂为紫外线吸收剂uv531。
上述的一种抗老化抗紫外电缆料，其中，氧化铈、氧化钕和氧化镧的份数混合比例为1：0.5：0.25。
一种抗老化抗紫外电缆料，其中，优选的，所述电缆料的组成成分按重量份数计如下：
线性聚乙烯 130份
高密度聚乙烯 20份
光稳定剂 4份
抗氧化剂 7份
紫外线吸收剂 3份
防老剂 6份
氧化铈 8份
氧化钕 4份
氧化镧 2份
色母料 7份。
本发明的有益效果为：
本发明提供的一种抗老化抗紫外电缆料，不仅具有优秀的耐寒性、耐热性、耐化学性和耐磨性，同时具有很好的抗氧化性能，延长了电缆料的使用寿命，使用色母料为电缆料着色，方便分辨，而且混入了少量氧化铈、氧化钕和氧化镧，提高了本配方各原料之间的结合性，同时加入了紫外线吸收剂、光稳定剂和抗氧化剂，极大的提升了电缆料的紫外线吸收能力，强化了电缆料的抗紫外线能力，并大幅度提升了电缆料的抗老化性能，降低了电缆料手天气、温度、紫外线等因素而发生龟裂和断裂的可能性。
具体实施方式
实例一
一种抗老化抗紫外电缆料，其特征在于，所述电缆料的组成成分按重量份数计如下：
线性聚乙烯 130份
高密度聚乙烯 20份
光稳定剂 4份
抗氧化剂 7份
紫外线吸收剂 3份
防老剂 6份
氧化铈 8份
氧化钕 4份
氧化镧 2份
色母料 7份。
其中，线性聚乙烯与高密度聚乙烯的份数混合比例为1：0.15，所述光稳定剂为紫外光屏蔽剂和紫外光吸收剂以1:0.5的比例混合而成，所述抗氧化剂为抗氧剂1010和抗氧剂168以1：1的比例混合而成，所述紫外线吸收剂为紫外线吸收剂uv531，氧化铈、氧化钕和氧化镧的份数混合比例为1：0.5：0.25。
实例二
一种抗老化抗紫外电缆料，其特征在于，所述电缆料的组成成分按重量份数计如下：
线性聚乙烯 125份
高密度聚乙烯 25份
光稳定剂 3份
抗氧化剂 5份
紫外线吸收剂 5份
防老剂 8份
氧化铈 8份
氧化钕 4份
氧化镧 2份
色母料 8份。
其中，线性聚乙烯与高密度聚乙烯的份数混合比例为1：0.2，所述光稳定剂为紫外光屏蔽剂和紫外光吸收剂以1:0.5的比例混合而成，所述抗氧化剂为抗氧剂1010和抗氧剂168以1：1的比例混合而成，所述紫外线吸收剂为紫外线吸收剂uv531，氧化铈、氧化钕和氧化镧的份数混合比例为1：0.5：0.25。
实例三
一种抗老化抗紫外电缆料，其特征在于，所述电缆料的组成成分按重量份数计如下：
线性聚乙烯 135份
高密度聚乙烯 25份
光稳定剂 3份
抗氧化剂 5份
紫外线吸收剂 5份
防老剂 8份
氧化铈 4份
氧化钕 2份
氧化镧 1份
色母料 7份。
其中，线性聚乙烯与高密度聚乙烯的份数混合比例为1：0.18，所述光稳定剂为紫外光屏蔽剂和紫外光吸收剂以1:0.5的比例混合而成，所述抗氧化剂为抗氧剂1010和抗氧剂168以1：1的比例混合而成，所述紫外线吸收剂为紫外线吸收剂uv531，氧化铈、氧化钕和氧化镧的份数混合比例为1：0.5：0.25。
一种抗老化抗紫外电缆料，不仅具有优秀的耐寒性、耐热性、耐化学性和耐磨性，同时具有很好的抗氧化性能，延长了电缆料的使用寿命，使用色母料为电缆料着色，方便分辨，而且混入了少量氧化铈、氧化钕和氧化镧，提高了本配方各原料之间的结合性，同时加入了紫外线吸收剂、光稳定剂和抗氧化剂，极大的提升了电缆料的紫外线吸收能力，强化了电缆料的抗紫外线能力，并大幅度提升了电缆料的抗老化性能，降低了电缆料手天气、温度、紫外线等因素而发生龟裂和断裂的可能性。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，可轻易想到的变化或替换，都应涵盖在本发明的保护范围内。因此，本发明的保护范围应该以权利要求书的保护范围为准。
Claims (7)
1.一种抗老化抗紫外电缆料，其特征在于，由下列重量份的原料组分制备而成：
线性聚乙烯
125-135份
高密度聚乙烯
15-25份
光稳定剂
3-4份
抗氧化剂
4-7份
紫外线吸收剂
2-3份
防老剂
4-9份
氧化铈
4-8份
氧化钕
2-4份
氧化镧
1-2份
色母料
5-10份。
2.如权利要求1所述的一种抗老化抗紫外电缆料，其特征在于，优选的，所述电缆料的组成成分按重量份数计如下;
线性聚乙烯
130份
高密度聚乙烯
20份
光稳定剂
4份
抗氧化剂
7份
紫外线吸收剂
3份
防老剂
6份
氧化铈
8份
氧化钕
4份
氧化镧
2份
色母料
7份。
3.如权利要求1所述的一种抗老化抗紫外电缆料，其特征在于，线性聚乙烯与高密度聚乙烯的份数混合比例为1：0.1-0.2。
4.如权利要求1所述的一种抗老化抗紫外电缆料，其特征在于，所述光稳定剂为紫外光屏蔽剂和紫外光吸收剂以1:0.5的比例混合而成。
5.如权利要求1所述的一种抗老化抗紫外电缆料，其特征在于，所述抗氧化剂为抗氧剂1010和抗氧剂168以1：1的比例混合而成。
6.如权利要求1所述的一种抗老化抗紫外电缆料，其特征在于，所述紫外线吸收剂为紫外线吸收剂uv531。
7.如权利要求1所述的一种抗老化抗紫外电缆料，其特征在于，氧化铈、氧化钕和氧化镧的份数混合比例为1：0.5：0.25。