CN105969486A - Rustproof bearing lubricant additive - Google Patents

Rustproof bearing lubricant additive Download PDF

Info

Publication number
CN105969486A
CN105969486A CN201610375222.0A CN201610375222A CN105969486A CN 105969486 A CN105969486 A CN 105969486A CN 201610375222 A CN201610375222 A CN 201610375222A CN 105969486 A CN105969486 A CN 105969486A
Authority
CN
China
Prior art keywords
parts
zinc
sodium
acid
rustproof
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610375222.0A
Other languages
Chinese (zh)
Inventor
钱宜武
钱宜文
胡森
傅世明
谢传根
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Qianshan Bearing Manufacturing Co Ltd
Original Assignee
Anhui Qianshan Bearing Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Qianshan Bearing Manufacturing Co Ltd filed Critical Anhui Qianshan Bearing Manufacturing Co Ltd
Priority to CN201610375222.0A priority Critical patent/CN105969486A/en
Publication of CN105969486A publication Critical patent/CN105969486A/en
Pending legal-status Critical Current

Abstract

The invention discloses a rustproof bearing lubricant additive. The rustproof bearing lubricant additive is prepared from 2,6-butylated hydroxytoluene, trimethylolpropane, zinc stearate, sodium borate, sodium nitrate, lauryl sodium sulfate, triethanolamine, alkenyl dibutene, pentaerythritol, glycerol, triphenyl phosphorothioate, alkali zinc dialkyl dithiophosphate, para aminobenzoic acid, cocinic glycol amide, laurylene succinic acid, macromolecular polyisobutene oil solution, tricresyl phosphate, long-chain alkyl sodium sulfate, calcium dodecylbenzene sulfonate, dialkyl zinc dithiophosphate, sorbide oleate, castor oil potash soap and a rustproof agent. The rustproof bearing lubricant additive can effectively prevent corrosion and rust and improve viscosity index well, is excellent in hydrophily and lipophilicity, improves rustproof and lubricating effects and prolongs the service life of bearings.

Description

A kind of antirust bearing lubrication oil additive
Technical field
The present invention relates to technical field of bearings, be specifically related to a kind of antirust bearing lubrication oil additive.
Background technology
Bearing oil plays lubrication in using for bearing, cooling, extends bearing life etc. and makees With, some bearings use the most dirt of environment, and common OIL IN LUBRICATING OIL PRODUCTION cost is high, it is impossible at height Good lubricant effect is played under the adverse circumstances such as temperature, heavy load, strong water pouring.Lubricating oil adds Agent is to add one or more compounds in lubricant, so that lubricant obtains the spy that certain is new Property or improve more existing characteristics in lubricant, the additive in market is typically all above each The combination product of single additive, different is exactly the composition difference of single additive and is combined In additive, the ratio of several single additives is different, and the kind of existing additive is numerous Many, it is impossible to the most antiseptic and rustproof, also have can not preferably improve viscosity index (VI).Original axle Hold the coefficient of friction that is used to reduce in power transmission process, if getting rusty or can not get in time Lubrication on the contrary can the resistance of bigger transmission, so lubricating oil is extremely important for bearing, but commonly Lubricating oil be single lubrication and the demand that can not meet market, need in time Renewal.
Summary of the invention
It is desirable to provide a kind of antirust bearing lubrication oil additive.
The present invention provides following technical scheme:
A kind of antirust bearing lubrication oil additive, it is made up of the raw material of following parts by weight: 2,6 ditertiary butyl p cresol 1-4 part, trimethylolpropane 5-8 part, zinc stearate fat 3-4 Part, sodium borate 1-2 part, sodium nitrate 1-2 part, sodium lauryl sulphate 2-3 part, three ethanol Amine 5-9 part, thiazolinyl two butanoic acid 1-5 part, penta tetrol 2-6 part, glycerol 25-34 part, triphen Base thiophosphate 6-9 part, alkali formula sulfur phosphorus double pungent primary alkyl zinc 6-12 part, p-aminophenyl first Acid 6-10 part, coconut oil ethylene glycol amide 8-16 part, benzene succinic acid 3-7 part, height Molecule polyisobutylene oil solution 5-10 part, tricresyl phosphate 5-7 part, chain alkyl sulphuric acid Sodium 3-5 part, alkyl benzene calcium sulfonate 2-9 part, zinc dialkyl dithiophosphate 3-7 part, Pyrusussuriensis Sugar alcohol acid anhydride oleate 5-7 part, Oleum Ricini potash soap 3-6 part, antirust agent 5-10 part.
A kind of antirust bearing lubrication oil additive, it is made up of the raw material of following parts by weight: 2,6 ditertiary butyl p cresol 1 part, trimethylolpropane 5 parts, 3 parts of zinc stearate fat, Sodium borate 1 part, sodium nitrate 1 part, sodium lauryl sulphate 2 parts, triethanolamine 5 parts, alkene Base two butanoic acid 1 part, penta tetrol 2 parts, glycerol 25 parts, triphenylphosphorothionate 6 parts, Alkali formula sulfur phosphorus double 6 parts of pungent primary alkyl zinc, para-amino benzoic acid 6 parts, coconut oil ethylene glycol amide 8 parts, benzene succinic acid 3 parts, polyphosphazene polymer isobutene. oil solution 5 parts, tripotassium phosphate Phenolic ester 5 parts, 3 parts of chain alkyl sodium sulfate, alkyl benzene calcium sulfonate 2 parts, dialkyl dithio Zinc phosphate 3 parts, sorbitol anhydride oleate 5 parts, Oleum Ricini potash soap 3 parts, antirust agent 5 parts.
A kind of antirust bearing lubrication oil additive, it is made up of the raw material of following parts by weight: 2,6 ditertiary butyl p cresol 4 parts, trimethylolpropane 8 parts, 4 parts of zinc stearate fat, Sodium borate 2 parts, sodium nitrate 2 parts, sodium lauryl sulphate 3 parts, triethanolamine 9 parts, alkene Base two butanoic acid 5 parts, penta tetrol 6 parts, glycerol 34 parts, triphenylphosphorothionate 9 parts, Alkali formula sulfur phosphorus double 12 parts of pungent primary alkyl zinc, para-amino benzoic acid 10 parts, coconut oil ethylene glycol acyl Amine 16 parts, benzene succinic acid 7 parts, polyphosphazene polymer isobutene. oil solution 10 parts, phosphoric acid Front three phenolic ester 7 parts, 5 parts of chain alkyl sodium sulfate, alkyl benzene calcium sulfonate 9 parts, dialkyl group two 7 parts of D2EHDTPA zinc, sorbitol anhydride oleate 7 parts, Oleum Ricini potash soap 6 parts, antirust agent 10 parts.
Compared with prior art, the invention has the beneficial effects as follows: the antirust bearing profit of the present invention Oil additive can be the most antiseptic and rustproof, moreover it is possible to preferably improves viscosity index (VI), has excellence Hydrophilic, lipophile, improve antirust, lubrication effect, extend the use longevity of bearing Life.
Detailed description of the invention
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clearly Chu, it is fully described by, it is clear that described embodiment is only a part of embodiment of the present invention, Rather than whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art The every other embodiment obtained under not making creative work premise, broadly falls into this The scope of bright protection.
A kind of antirust bearing lubrication oil additive, it is made up of the raw material of following parts by weight: 2,6 ditertiary butyl p cresol 1-4 part, trimethylolpropane 5-8 part, zinc stearate fat 3-4 Part, sodium borate 1-2 part, sodium nitrate 1-2 part, sodium lauryl sulphate 2-3 part, three ethanol Amine 5-9 part, thiazolinyl two butanoic acid 1-5 part, penta tetrol 2-6 part, glycerol 25-34 part, triphen Base thiophosphate 6-9 part, alkali formula sulfur phosphorus double pungent primary alkyl zinc 6-12 part, p-aminophenyl first Acid 6-10 part, coconut oil ethylene glycol amide 8-16 part, benzene succinic acid 3-7 part, height Molecule polyisobutylene oil solution 5-10 part, tricresyl phosphate 5-7 part, chain alkyl sulphuric acid Sodium 3-5 part, alkyl benzene calcium sulfonate 2-9 part, zinc dialkyl dithiophosphate 3-7 part, Pyrusussuriensis Sugar alcohol acid anhydride oleate 5-7 part, Oleum Ricini potash soap 3-6 part, antirust agent 5-10 part.
A kind of antirust bearing lubrication oil additive, it is made up of the raw material of following parts by weight: 2,6 ditertiary butyl p cresol 1 part, trimethylolpropane 5 parts, 3 parts of zinc stearate fat, Sodium borate 1 part, sodium nitrate 1 part, sodium lauryl sulphate 2 parts, triethanolamine 5 parts, alkene Base two butanoic acid 1 part, penta tetrol 2 parts, glycerol 25 parts, triphenylphosphorothionate 6 parts, Alkali formula sulfur phosphorus double 6 parts of pungent primary alkyl zinc, para-amino benzoic acid 6 parts, coconut oil ethylene glycol amide 8 parts, benzene succinic acid 3 parts, polyphosphazene polymer isobutene. oil solution 5 parts, tripotassium phosphate Phenolic ester 5 parts, 3 parts of chain alkyl sodium sulfate, alkyl benzene calcium sulfonate 2 parts, dialkyl dithio Zinc phosphate 3 parts, sorbitol anhydride oleate 5 parts, Oleum Ricini potash soap 3 parts, antirust agent 5 parts.
A kind of antirust bearing lubrication oil additive, it is made up of the raw material of following parts by weight: 2,6 ditertiary butyl p cresol 4 parts, trimethylolpropane 8 parts, 4 parts of zinc stearate fat, Sodium borate 2 parts, sodium nitrate 2 parts, sodium lauryl sulphate 3 parts, triethanolamine 9 parts, alkene Base two butanoic acid 5 parts, penta tetrol 6 parts, glycerol 34 parts, triphenylphosphorothionate 9 parts, Alkali formula sulfur phosphorus double 12 parts of pungent primary alkyl zinc, para-amino benzoic acid 10 parts, coconut oil ethylene glycol acyl Amine 16 parts, benzene succinic acid 7 parts, polyphosphazene polymer isobutene. oil solution 10 parts, phosphoric acid Front three phenolic ester 7 parts, 5 parts of chain alkyl sodium sulfate, alkyl benzene calcium sulfonate 9 parts, dialkyl group two 7 parts of D2EHDTPA zinc, sorbitol anhydride oleate 7 parts, Oleum Ricini potash soap 6 parts, antirust agent 10 parts.
It is obvious to a person skilled in the art that the invention is not restricted to described one exemplary embodiment Details, and without departing from the spirit or essential characteristics of the present invention, it is possible to it His concrete form realizes the present invention.Therefore, no matter from the point of view of which point, all should be by embodiment Regarding exemplary as, and be nonrestrictive, the scope of the present invention is by claims Rather than described explanation limit, it is intended that by fall claim equivalency implication and In the range of all changes include in the present invention.Although moreover, it will be appreciated that this specification It is been described by according to embodiment, but the most each embodiment only comprises an independent technology Scheme, this narrating mode of description is only for clarity sake, and those skilled in the art should When using description as an entirety, the technical scheme in each embodiment can also be through suitable group Close, form other embodiments that it will be appreciated by those skilled in the art that.

Claims (3)

1. an antirust bearing lubrication oil additive, it is characterised in that it is by following weight The raw material composition of number: 2,6 ditertiary butyl p cresol 1-4 part, trimethylolpropane 5-8 Part, zinc stearate fat 3-4 part, sodium borate 1-2 part, sodium nitrate 1-2 part, dodecyl sulfur Acid sodium 2-3 part, triethanolamine 5-9 part, thiazolinyl two butanoic acid 1-5 part, penta tetrol 2-6 part, Glycerol 25-34 part, triphenylphosphorothionate 6-9 part, the double pungent primary alkyl zinc of alkali formula sulfur phosphorus 6-12 part, para-amino benzoic acid 6-10 part, coconut oil ethylene glycol amide 8-16 part, 12 Alkene succinic acid 3-7 part, polyphosphazene polymer isobutene. oil solution 5-10 part, tricresyl phosphate 5-7 part, chain alkyl sodium sulfate 3-5 part, alkyl benzene calcium sulfonate 2-9 part, dialkyl disulfides For zinc phosphate 3-7 part, sorbitol anhydride oleate 5-7 part, Oleum Ricini potash soap 3-6 part, prevent Rust agent 5-10 part.
One the most according to claim 1 antirust bearing lubrication oil additive, its feature It is: it is made up of the raw material of following parts by weight: 2,6 ditertiary butyl p cresol 1 part, Trimethylolpropane 5 parts, 3 parts of zinc stearate fat, sodium borate 1 part, sodium nitrate 1 part, ten Sodium dialkyl sulfate 2 parts, triethanolamine 5 parts, thiazolinyl two butanoic acid 1 part, penta tetrol 2 parts, Double 6 parts of the pungent primary alkyl zinc of glycerol 25 parts, triphenylphosphorothionate 6 parts, alkali formula sulfur phosphorus, Para-amino benzoic acid 6 parts, coconut oil ethylene glycol amide 8 parts, benzene succinic acid 3 parts, Polyphosphazene polymer isobutene. oil solution 5 parts, tricresyl phosphate 5 parts, chain alkyl sodium sulfate 3 Part, alkyl benzene calcium sulfonate 2 parts, zinc dialkyl dithiophosphate 3 parts, sorbitan oleic acid Ester 5 parts, Oleum Ricini potash soap 3 parts, antirust agent 5 parts.
One the most according to claim 1 antirust bearing lubrication oil additive, its feature It is: it is made up of the raw material of following parts by weight: 2,6 ditertiary butyl p cresol 4 parts, Trimethylolpropane 8 parts, 4 parts of zinc stearate fat, sodium borate 2 parts, sodium nitrate 2 parts, ten Sodium dialkyl sulfate 3 parts, triethanolamine 9 parts, thiazolinyl two butanoic acid 5 parts, penta tetrol 6 parts, Double 12 parts of the pungent primary alkyl zinc of glycerol 34 parts, triphenylphosphorothionate 9 parts, alkali formula sulfur phosphorus, Para-amino benzoic acid 10 parts, coconut oil ethylene glycol amide 16 parts, benzene succinic acid 7 parts, Polyphosphazene polymer isobutene. oil solution 10 parts, tricresyl phosphate 7 parts, chain alkyl sodium sulfate 5 parts, alkyl benzene calcium sulfonate 9 parts, zinc dialkyl dithiophosphate 7 parts, sorbitan oil Acid esters 7 parts, Oleum Ricini potash soap 6 parts, antirust agent 10 parts.
CN201610375222.0A 2016-05-31 2016-05-31 Rustproof bearing lubricant additive Pending CN105969486A (en)