CN108929744A - A kind of bearing oil specialist additive - Google Patents

A kind of bearing oil specialist additive Download PDF

Info

Publication number
CN108929744A
CN108929744A CN201810686964.4A CN201810686964A CN108929744A CN 108929744 A CN108929744 A CN 108929744A CN 201810686964 A CN201810686964 A CN 201810686964A CN 108929744 A CN108929744 A CN 108929744A
Authority
CN
China
Prior art keywords
parts
succinic acid
acid
bearing oil
boratex
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810686964.4A
Other languages
Chinese (zh)
Inventor
龚双林
龚大浪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anqing Yinyi Bearings Co Ltd
Original Assignee
Anqing Yinyi Bearings Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anqing Yinyi Bearings Co Ltd filed Critical Anqing Yinyi Bearings Co Ltd
Priority to CN201810686964.4A priority Critical patent/CN108929744A/en
Publication of CN108929744A publication Critical patent/CN108929744A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of bearing oil specialist additives, the bearing oil specialist additive is to be prepared from the following raw materials in parts by weight: 8-16 parts of cocoanut fatty acid diethanolamide, 5-9 parts of neopelex, 3-7 parts of sorbitol anhydride oleate, 3-6 parts of Boratex, 6-12 parts of triphenylphosphorothionate, 4-8 parts of alkadienes succinic acid, 2-5 parts of glycerol, 3-7 parts of octyl phenol, 1-5 parts of alkyl calcium salicylate, 2-6 parts of benzoic acid, 3-6 parts of perfluoro octyl sulfonic acid sodium, 1-5 parts of boronation polyisobutylene succinamide, 6-13 parts of benzene succinic acid, it is aluminium triphosphate 3-9 parts modified, 5-10 parts of polyvinyl n-butyl ether, 2-6 parts of polymethacrylates, 2-5 parts of oxidation and corrosion inhibitor, 3-6 parts of antiwear additive.Bearing oil specialist additive in the present invention can greatly improve antirust, lubricant effect.

Description

A kind of bearing oil specialist additive
Technical field
The present invention relates to technical field of lubricating oil, and in particular to a kind of bearing oil specialist additive.
Background technique
Lube oil additive concept is that one or more of lubricant compound is added, so that lubricant obtains certain newly Characteristic or improve lubricant in existing some characteristics.Additive mainly has antioxidant, antiwear additive, friction to change by function point Kind agent (also known as oiliness improver), EP agent, dispersing agent, foam in hibitors, corrosion prevention rust preventer, flow point improver, glue detersive Spend the types such as index improver.The additive sold in market is typically all the combination product of above each single additive, and institute is not Same is exactly the ratio difference of several single additives inside the ingredient difference and compound additive of single additive.But It is that the synergistic effect after additive addition is poor, while improving a certain performance, will cause the reduction of another performance, It causes certain performance of lubricating oil to be short of, influences normal use.
Summary of the invention
The purpose of the present invention is to provide a kind of bearing oil specialist additives, which can Effectively to solve the technical issues of being previously mentioned in background technique.
To achieve the above object, the invention provides the following technical scheme:
A kind of bearing oil specialist additive is made of the component of following parts by weight: coco-nut oil fatty acid diethanol 8-16 parts of amide, 5-9 parts of neopelex, 3-7 parts of sorbitol anhydride oleate, 3-6 parts of Boratex, triphenyl is thio 6-12 parts of phosphate, 4-8 parts of alkadienes succinic acid, 2-5 parts of glycerol, 3-7 parts of octyl phenol, 1-5 parts of alkyl calcium salicylate, benzoic acid 2-6 parts, 3-6 parts of perfluoro octyl sulfonic acid sodium, 1-5 parts of boronation polyisobutylene succinamide, 6-13 parts of benzene succinic acid, It is aluminium triphosphate 3-9 parts modified, 5-10 parts of polyvinyl n-butyl ether, 2-6 parts of polymethacrylates, oxidation and corrosion inhibitor 2-5 Part, 3-6 parts of antiwear additive.
Preferably, the bearing oil specialist additive is made of the component of following parts by weight: coconut oil fat 10 parts of sour diglycollic amide, 6 parts of neopelex, 5 parts of sorbitol anhydride oleate, 5 parts of Boratex, triphenyl is thio 8 parts of phosphate, 5 parts of alkadienes succinic acid, 3 parts of glycerol, 5 parts of octyl phenol, 2 parts of alkyl calcium salicylate, 3 parts of benzoic acid, perfluor is pungent 5 parts of base sodium sulfonate, 2 parts of boronation polyisobutylene succinamide, 11 parts of benzene succinic acid, modified 6 parts of aluminium triphosphate, 6 parts of polyvinyl n-butyl ether, 3 parts of polymethacrylates, 2 parts of oxidation and corrosion inhibitor, 5 parts of antiwear additive.
Preferably, the bearing oil specialist additive is made of the component of following parts by weight: coconut oil fat 16 parts of sour diglycollic amide, 5 parts of neopelex, 4 parts of sorbitol anhydride oleate, 4 parts of Boratex, triphenyl is thio 7 parts of phosphate, 5 parts of alkadienes succinic acid, 5 parts of glycerol, 6 parts of octyl phenol, 1 part of alkyl calcium salicylate, 3 parts of benzoic acid, perfluor is pungent 5 parts of base sodium sulfonate, 3 parts of boronation polyisobutylene succinamide, 11 parts of benzene succinic acid, modified 7 parts of aluminium triphosphate, 6 parts of polyvinyl n-butyl ether, 3 parts of polymethacrylates, 3 parts of oxidation and corrosion inhibitor, 5 parts of antiwear additive.
Preferably, the bearing oil specialist additive is made of the component of following parts by weight: coconut oil fat 9 parts of sour diglycollic amide, 6 parts of neopelex, 4 parts of sorbitol anhydride oleate, 4 parts of Boratex, triphenyl is thio 8 parts of phosphate, 6 parts of alkadienes succinic acid, 3 parts of glycerol, 5 parts of octyl phenol, 3 parts of alkyl calcium salicylate, 3 parts of benzoic acid, perfluor is pungent 5 parts of base sodium sulfonate, 2 parts of boronation polyisobutylene succinamide, 7 parts of benzene succinic acid, modified 5 parts of aluminium triphosphate, 5 parts of polyvinyl n-butyl ether, 5 parts of polymethacrylates, 3 parts of oxidation and corrosion inhibitor, 3 parts of antiwear additive.
Preferably, the bearing oil specialist additive is made of the component of following parts by weight: coconut oil fat 13 parts of sour diglycollic amide, 6 parts of neopelex, 5 parts of sorbitol anhydride oleate, 4 parts of Boratex, triphenyl is thio 10 parts of phosphate, 8 parts of alkadienes succinic acid, 5 parts of glycerol, 3 parts of octyl phenol, 4 parts of alkyl calcium salicylate, 3 parts of benzoic acid, perfluor is pungent 4 parts of base sodium sulfonate, 2 parts of boronation polyisobutylene succinamide, 12 parts of benzene succinic acid, modified 5 parts of aluminium triphosphate, 6 parts of polyvinyl n-butyl ether, 3 parts of polymethacrylates, 3 parts of oxidation and corrosion inhibitor, 5 parts of antiwear additive.
Preferably, the bearing oil specialist additive is made of the component of following parts by weight: coconut oil fat 8 parts of sour diglycollic amide, 5 parts of neopelex, 6 parts of sorbitol anhydride oleate, 6 parts of Boratex, triphenyl is thio 10 parts of phosphate, 6 parts of alkadienes succinic acid, 3 parts of glycerol, 4 parts of octyl phenol, 2 parts of alkyl calcium salicylate, 3 parts of benzoic acid, perfluor is pungent 5 parts of base sodium sulfonate, 2 parts of boronation polyisobutylene succinamide, 9 parts of benzene succinic acid, modified 9 parts of aluminium triphosphate, 8 parts of polyvinyl n-butyl ether, 4 parts of polymethacrylates, 3 parts of oxidation and corrosion inhibitor, 5 parts of antiwear additive.
Compared with prior art, the beneficial effects of the present invention are:
Bearing oil specialist additive in the present invention has been especially added with cocoanut fatty acid diethanolamide, dodecane Base benzene sulfonic acid sodium salt, sorbitol anhydride oleate, Boratex, octyl phenol, alkyl calcium salicylate, perfluoro octyl sulfonic acid sodium, modified three The raw materials such as poly aluminium phosphate, oxidation and corrosion inhibitor and antiwear additive pass through the reasonably combined bearing oil that makes between each raw material component Antirust, lubricant effect greatly promote.
Specific embodiment
Below with reference to the embodiment technical solution that the present invention will be described in detail, but protection scope is not limited thereto.
Embodiment one:
A kind of bearing oil specialist additive is made of the component of following parts by weight: coco-nut oil fatty acid diethanol 8 parts of amide, 5 parts of neopelex, 3 parts of sorbitol anhydride oleate, 3 parts of Boratex, triphenylphosphorothionate 6 Part, 4 parts of alkadienes succinic acid, 2 parts of glycerol, 3 parts of octyl phenol, 1 part of alkyl calcium salicylate, 2 parts of benzoic acid, perfluoro octyl sulfonic acid sodium 3 parts, 1 part of boronation polyisobutylene succinamide, 6 parts of benzene succinic acid, modified 3 parts of aluminium triphosphate, polyvinyl 5 parts of n-butyl ether, 2 parts of polymethacrylates, 2 parts of oxidation and corrosion inhibitor, 3 parts of antiwear additive.
Embodiment two:
A kind of bearing oil specialist additive is made of the component of following parts by weight: coco-nut oil fatty acid diethanol 16 parts of amide, 9 parts of neopelex, 7 parts of sorbitol anhydride oleate, 6 parts of Boratex, triphenylphosphorothionate 12 Part, 8 parts of alkadienes succinic acid, 5 parts of glycerol, 7 parts of octyl phenol, 5 parts of alkyl calcium salicylate, 6 parts of benzoic acid, perfluoro octyl sulfonic acid sodium 6 parts, 5 parts of boronation polyisobutylene succinamide, 13 parts of benzene succinic acid, modified 9 parts of aluminium triphosphate, polyvinyl 10 parts of n-butyl ether, 6 parts of polymethacrylates, 5 parts of oxidation and corrosion inhibitor, 6 parts of antiwear additive.
Embodiment three:
A kind of bearing oil specialist additive is made of the component of following parts by weight: coco-nut oil fatty acid diethanol 10 parts of amide, 6 parts of neopelex, 5 parts of sorbitol anhydride oleate, 5 parts of Boratex, triphenylphosphorothionate 8 Part, 5 parts of alkadienes succinic acid, 3 parts of glycerol, 5 parts of octyl phenol, 2 parts of alkyl calcium salicylate, 3 parts of benzoic acid, perfluoro octyl sulfonic acid sodium 5 parts, 2 parts of boronation polyisobutylene succinamide, 11 parts of benzene succinic acid, modified 6 parts of aluminium triphosphate, polyvinyl 6 parts of n-butyl ether, 3 parts of polymethacrylates, 2 parts of oxidation and corrosion inhibitor, 5 parts of antiwear additive.
Example IV:
A kind of bearing oil specialist additive is made of the component of following parts by weight: coco-nut oil fatty acid diethanol 16 parts of amide, 5 parts of neopelex, 4 parts of sorbitol anhydride oleate, 4 parts of Boratex, triphenylphosphorothionate 7 Part, 5 parts of alkadienes succinic acid, 5 parts of glycerol, 6 parts of octyl phenol, 1 part of alkyl calcium salicylate, 3 parts of benzoic acid, perfluoro octyl sulfonic acid sodium 5 parts, 3 parts of boronation polyisobutylene succinamide, 11 parts of benzene succinic acid, modified 7 parts of aluminium triphosphate, polyvinyl 6 parts of n-butyl ether, 3 parts of polymethacrylates, 3 parts of oxidation and corrosion inhibitor, 5 parts of antiwear additive.
Embodiment five:
A kind of bearing oil specialist additive is made of the component of following parts by weight: coco-nut oil fatty acid diethanol 9 parts of amide, 6 parts of neopelex, 4 parts of sorbitol anhydride oleate, 4 parts of Boratex, triphenylphosphorothionate 8 Part, 6 parts of alkadienes succinic acid, 3 parts of glycerol, 5 parts of octyl phenol, 3 parts of alkyl calcium salicylate, 3 parts of benzoic acid, perfluoro octyl sulfonic acid sodium 5 parts, 2 parts of boronation polyisobutylene succinamide, 7 parts of benzene succinic acid, modified 5 parts of aluminium triphosphate, polyvinyl 5 parts of n-butyl ether, 5 parts of polymethacrylates, 3 parts of oxidation and corrosion inhibitor, 3 parts of antiwear additive.
Embodiment six:
A kind of bearing oil specialist additive is made of the component of following parts by weight: coco-nut oil fatty acid diethanol 13 parts of amide, 6 parts of neopelex, 5 parts of sorbitol anhydride oleate, 4 parts of Boratex, triphenylphosphorothionate 10 Part, 8 parts of alkadienes succinic acid, 5 parts of glycerol, 3 parts of octyl phenol, 4 parts of alkyl calcium salicylate, 3 parts of benzoic acid, perfluoro octyl sulfonic acid sodium 4 parts, 2 parts of boronation polyisobutylene succinamide, 12 parts of benzene succinic acid, modified 5 parts of aluminium triphosphate, polyvinyl 6 parts of n-butyl ether, 3 parts of polymethacrylates, 3 parts of oxidation and corrosion inhibitor, 5 parts of antiwear additive.
Embodiment seven:
A kind of bearing oil specialist additive is made of the component of following parts by weight: coco-nut oil fatty acid diethanol 8 parts of amide, 5 parts of neopelex, 6 parts of sorbitol anhydride oleate, 6 parts of Boratex, triphenylphosphorothionate 10 Part, 6 parts of alkadienes succinic acid, 3 parts of glycerol, 4 parts of octyl phenol, 2 parts of alkyl calcium salicylate, 3 parts of benzoic acid, perfluoro octyl sulfonic acid sodium 5 parts, 2 parts of boronation polyisobutylene succinamide, 9 parts of benzene succinic acid, modified 9 parts of aluminium triphosphate, polyvinyl 8 parts of n-butyl ether, 4 parts of polymethacrylates, 3 parts of oxidation and corrosion inhibitor, 5 parts of antiwear additive.
Finally, it is stated that the above examples are only used to illustrate the technical scheme of the present invention and are not limiting, although referring to compared with Good embodiment describes the invention in detail, those skilled in the art should understand that, it can be to skill of the invention Art scheme is modified or replaced equivalently, and without departing from the objective and range of the technical program, should all be covered in the present invention Scope of the claims in.

Claims (6)

1. a kind of bearing oil specialist additive, which is characterized in that it is to be prepared from the following raw materials in parts by weight: coconut oil 8-16 parts of fatty diglycollic amide, 5-9 parts of neopelex, 3-7 parts of sorbitol anhydride oleate, Boratex 3-6 Part, 6-12 parts of triphenylphosphorothionate, 4-8 parts of alkadienes succinic acid, 2-5 parts of glycerol, 3-7 parts of octyl phenol, alkyl salicylate 1-5 parts of calcium, 2-6 parts of benzoic acid, 3-6 parts of perfluoro octyl sulfonic acid sodium, 1-5 parts of boronation polyisobutylene succinamide, laurylene It is 6-13 parts of hydrocarbon succinic acid, aluminium triphosphate 3-9 parts modified, 5-10 parts of polyvinyl n-butyl ether, polymethacrylates 2-6 Part, 2-5 parts of oxidation and corrosion inhibitor, 3-6 parts of antiwear additive.
2. a kind of bearing oil specialist additive according to claim 1, which is characterized in that it is by following parts by weight Several raw materials are made: 10 parts of cocoanut fatty acid diethanolamide, 6 parts of neopelex, and sorbitol anhydride oleate 5 Part, 5 parts of Boratex, 8 parts of triphenylphosphorothionate, 5 parts of alkadienes succinic acid, 3 parts of glycerol, 5 parts of octyl phenol, alkyl salicylate 2 parts of calcium, 3 parts of benzoic acid, 5 parts of perfluoro octyl sulfonic acid sodium, 2 parts of boronation polyisobutylene succinamide, benzene succinic acid 11 parts, modified 6 parts of aluminium triphosphate, 3 parts of polymethacrylates, 2 parts of oxidation and corrosion inhibitor, resists by 6 parts of polyvinyl n-butyl ether 5 parts of grinding agent.
3. a kind of bearing oil specialist additive according to claim 1, which is characterized in that it is by following parts by weight Several raw materials are made: 16 parts of cocoanut fatty acid diethanolamide, 5 parts of neopelex, and sorbitol anhydride oleate 4 Part, 4 parts of Boratex, 7 parts of triphenylphosphorothionate, 5 parts of alkadienes succinic acid, 5 parts of glycerol, 6 parts of octyl phenol, alkyl salicylate 1 part of calcium, 3 parts of benzoic acid, 5 parts of perfluoro octyl sulfonic acid sodium, 3 parts of boronation polyisobutylene succinamide, benzene succinic acid 11 parts, modified 7 parts of aluminium triphosphate, 3 parts of polymethacrylates, 3 parts of oxidation and corrosion inhibitor, resists by 6 parts of polyvinyl n-butyl ether 5 parts of grinding agent.
4. a kind of bearing oil specialist additive according to claim 1, which is characterized in that it is by following parts by weight Several raw materials are made: 9 parts of cocoanut fatty acid diethanolamide, 6 parts of neopelex, and sorbitol anhydride oleate 4 Part, 4 parts of Boratex, 8 parts of triphenylphosphorothionate, 6 parts of alkadienes succinic acid, 3 parts of glycerol, 5 parts of octyl phenol, alkyl salicylate 3 parts of calcium, 3 parts of benzoic acid, 5 parts of perfluoro octyl sulfonic acid sodium, 2 parts of boronation polyisobutylene succinamide, benzene succinic acid 7 Part, modified 5 parts of aluminium triphosphate is 5 parts of polyvinyl n-butyl ether, 5 parts of polymethacrylates, 3 parts of oxidation and corrosion inhibitor, wear-resistant 3 parts of agent.
5. a kind of bearing oil specialist additive according to claim 1, which is characterized in that it is by following parts by weight Several raw materials are made: 13 parts of cocoanut fatty acid diethanolamide, 6 parts of neopelex, and sorbitol anhydride oleate 5 Part, 4 parts of Boratex, 10 parts of triphenylphosphorothionate, 8 parts of alkadienes succinic acid, 5 parts of glycerol, 3 parts of octyl phenol, alkylated salicylamide 4 parts of sour calcium, 3 parts of benzoic acid, 4 parts of perfluoro octyl sulfonic acid sodium, 2 parts of boronation polyisobutylene succinamide, benzene fourth two 12 parts of acid, modified 5 parts of aluminium triphosphate, 6 parts of polyvinyl n-butyl ether, 3 parts of polymethacrylates, 3 parts of oxidation and corrosion inhibitor, 5 parts of antiwear additive.
6. a kind of bearing oil specialist additive according to claim 1, which is characterized in that it is by following parts by weight Several raw materials are made: 8 parts of cocoanut fatty acid diethanolamide, 5 parts of neopelex, and sorbitol anhydride oleate 6 Part, 6 parts of Boratex, 10 parts of triphenylphosphorothionate, 6 parts of alkadienes succinic acid, 3 parts of glycerol, 4 parts of octyl phenol, alkylated salicylamide 2 parts of sour calcium, 3 parts of benzoic acid, 5 parts of perfluoro octyl sulfonic acid sodium, 2 parts of boronation polyisobutylene succinamide, benzene fourth two 9 parts of acid, modified 9 parts of aluminium triphosphate, 8 parts of polyvinyl n-butyl ether, 4 parts of polymethacrylates, 3 parts of oxidation and corrosion inhibitor, 5 parts of antiwear additive.
CN201810686964.4A 2018-06-28 2018-06-28 A kind of bearing oil specialist additive Pending CN108929744A (en)