CN105969121A - Flat paint for furniture and preparation method thereof - Google Patents
Flat paint for furniture and preparation method thereof Download PDFInfo
- Publication number
- CN105969121A CN105969121A CN201610187081.XA CN201610187081A CN105969121A CN 105969121 A CN105969121 A CN 105969121A CN 201610187081 A CN201610187081 A CN 201610187081A CN 105969121 A CN105969121 A CN 105969121A
- Authority
- CN
- China
- Prior art keywords
- parts
- mentioned
- add
- minute
- tetraethyl orthosilicate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a flat paint for furniture. The flat paint is composed of the following raw materials (by weight): 1.4-3 parts of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, 0.7-2 parts of PTMEG, 0.8-2 parts of p-toluenesulfonamide, 10-12 parts of tung oil, 0.06-0.07 part of sodium hydroxide, 3-4 parts of methanol, 0.1-0.2 part of perfluorosulfonate resin, 6-8 parts of acetic acid, 10-15 parts of 26-30% hydrogen peroxide, 10-17 parts of tetraethyl orthosilicate, 0.1-0.2 part of Y-chloropropyltrimethoxysilane, 70-80 parts of unsaturated polyester resin, 0.6-1 part of methylethyl ketone peroxide, 15-20 parts of barite powder, 1-2 parts of naphthenic soap, 0.8-2.2 parts of lauryl alcohol phosphoric acid ester potassium, 1-2 parts of phenylimidazoline, 0.8-1 part of calcium alginate, 3-5 parts of titanium dioxide and 0.2-0.4 part of polyoxyethylene octylphenol ether. By adding titanium dioxide and barite powder into the paint, effective effects can be achieved, and decorative performance of a film is enhanced.
Description
Technical field
The present invention relates to coatings for furniture technical field, particularly relate to a kind of furniture antiglossing pigment and preparation method thereof.
Background technology
Saturated polyester resin is to prepare one of conventional film-forming resin of coating, but use unsaturated polyester resins for general purpose to there is the shortcomings such as resistance to water, solvent resistance, thermostability and poor mechanical property when preparing coating, need unsaturated polyester resin is modified to improve its combination property and currently mainly utilize polyurethane or base polyurethane prepolymer for use as, acrylic resin, epoxy resin, organosilicon, nano material and vegetable oil etc. unsaturated polyester resin to be modified to improving performance when it prepares coating.Wherein, plant oil modified unsaturated polyester vinegar resin is increasingly paid attention to by people.Vegetable oil is incorporated in unsaturated polyester resin by chemical reaction, easily cause the polyreaction of vegetable oil self, make the limited vegetable oil of modified effect also due to both poor compatibility, modification can be caused by the method modified unsaturated polyester resin being blended to fall flat.Therefore, after vegetable oil derivatization, improve the compatibility of vegetable oil and unsaturated polyester resin, be the important channel of plant oil modified unsaturated polyester resin.
In crude vegetal, Oleum Verniciae fordii is more special, and its main component is eleostearic acid glyceride, has conjugated triene structures, can be used alone in oil-based paint, it is also possible to neutralize other semi-drying oils at synthetic resin coating, non-drying oil is used in mixed way.Oleum Verniciae fordii also has good water proofing property, is widely used in building, paints, prints aspects such as (ink).
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of furniture antiglossing pigment and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of furniture antiglossing pigment, it is made up of the raw material of following weight parts:
Lauryl Alcohol ester 1.4-3, PTMG 0.7-2, para toluene sulfonamide 0.8-2, Oleum Verniciae fordii 10-12, sodium hydroxide 0.06-0.07, methanol 3-4, perfluorinated sulfonic resin 0.1-0.2, acetic acid 6-8, the hydrogen peroxide 10-15 of 26-30%, tetraethyl orthosilicate 10-17, Y-r-chloropropyl trimethoxyl silane 0.1-0.2, unsaturated polyester resin 70-80, methyl ethyl ketone peroxide 0.6-1, blanc fixe 15-20, naphthenic soap 1-2, Monododecylphosphate potassium 0.8-2, 2-benzylimidazoline 1-2, calcium alginate 0.8-1, titanium dioxide 3-5, OPEO 0.2-0.4.
The preparation method of a kind of described furniture antiglossing pigment, comprises the following steps:
(1) joining in Oleum Verniciae fordii by above-mentioned methanol, add sodium hydroxide, react 70-80 minute at 37-40 DEG C under stirring condition, distill methanol removal, stratification, the supernatant liquid of collection first with sulfuric acid scrubbing, the washing of reusable heat water, distillation dehydration, obtains methyl eleostearate;
(2) 50-60% of above-mentioned methyl eleostearate with perfluorinated sulfonic resin, above-mentioned acetic acid weight is mixed, rise high-temperature and be 60-68 DEG C, the hydrogen peroxide of above-mentioned 26-30% is dripped under stirring condition, insulation reaction 3-4 hour after dropping, filter, filtrate is neutralized with alkali, washing, it is vacuum dried 3-4 hour at 50-60 DEG C, obtains epoxidation methyl eleostearate;
(3) by above-mentioned Monododecylphosphate potassium, calcium alginate mixing, join in the deionized water of compound weight 40-50 times, add para toluene sulfonamide, stir, for amine emulsion;
(4) being joined in its weight 3-5 times dehydrated alcohol by above-mentioned 2-benzylimidazoline, stir, add PTMG, insulated and stirred 10-15 minute at 70-80 DEG C, for alcoholic solution;
(5) by above-mentioned Lauryl Alcohol ester, naphthenic soap mixing, stir, add tetraethyl orthosilicate, preheat 10-16 minute at 70-80 DEG C, obtain modified tetraethyl orthosilicate;
(6) by above-mentioned modified tetraethyl orthosilicate, the mixing of epoxidation methyl eleostearate, warming temperature is 36-40 DEG C, add remaining acetic acid, insulated and stirred 10-20 minute, drip above-mentioned amine emulsion, add Y-r-chloropropyl trimethoxyl silane after dropping, at 76-80 DEG C, be incubated 6-7 hour, obtain silica sol modified epoxidation methyl eleostearate;
(7) above-mentioned silica sol modified epoxidation methyl eleostearate is joined in above-mentioned alcoholic solution, stir, add OPEO, 100-200 rev/min is stirred 30-40 minute, mix with remaining each raw material, melt extruded by extruder, after then tabletting is broken, again through pulverizing, sieving, to obtain final product.
The invention have the advantage that
The epoxidation methyl eleostearate molecular structure of the present invention contains epoxy bond and double bond simultaneously, with the carboxyl in unsaturated polyester resin, hydroxyl and double bond, oxidation cross-linked reaction can occur, improve the crosslink density of film, improve filming performance, thus improve the hot strength of film, also improve hardness and the shock resistance of film to a certain extent simultaneously;
Containing hydrophobic fatty acid Long carbon chain in the epoxidation methyl eleostearate of the present invention, when Oleum Verniciae fordii derivant is dispersed in film forming in unsaturated polyester resin, these hydrophobic aliphatic hydrocarbyl groups are at film surface enrichment, film is made to be in a kind of low-surface-energy state, reduce the combination energy on surface and hydrone, thus reduce the water absorption rate of unsaturated polyester resin film, improve unsaturated polyester resin water resistance;
The epoxidation methyl eleostearate of the present invention contains conjugated double bond, and conjugated double bond, in the film forming later stage, occurs oxidation cross-linked, forming network polymers, so that it is tightr to be combined with each other between molecule, the density of film increases, solvent molecule slows down at the permeating speed of film coated surface, thus solvent resistance strengthens;
The epoxidation methyl eleostearate of the present invention has aliphatic long-chain hydrocarbon, and long chain hydrocarbon can play the effect of plasticising in resin, it is possible to strengthen the flexility of unsaturated polyester resin;
The coating of the present invention adds titanium dioxide, blanc fixe, the effect that can effectively have effect, and strengthens the dicoration of film.
Detailed description of the invention
A kind of furniture antiglossing pigment, it is made up of the raw material of following weight parts:
Lauryl Alcohol ester 1.4, PTMG 0.7, para toluene sulfonamide 0.8, Oleum Verniciae fordii 10, sodium hydroxide 0.06, methanol 3, perfluorinated sulfonic resin 0.1, the hydrogen peroxide 10 of acetic acid 6,26%, tetraethyl orthosilicate 10, Y r-chloropropyl trimethoxyl silane 0.1, unsaturated polyester resin 70, methyl ethyl ketone peroxide 0.6, blanc fixe 15, naphthenic soap 1, Monododecylphosphate potassium 0.8,2 benzylimidazoline 1, calcium alginate 0.8, titanium dioxide 3, OPEO 0.2.
The preparation method of a kind of described furniture antiglossing pigment, comprises the following steps:
(1) joining in Oleum Verniciae fordii by above-mentioned methanol, add sodium hydroxide, react 70 minutes at 37 DEG C under stirring condition, distill methanol removal, stratification, the supernatant liquid of collection first with sulfuric acid scrubbing, the washing of reusable heat water, distillation dehydration, obtains methyl eleostearate;
(2) by above-mentioned methyl eleostearate and perfluorinated sulfonic resin, the 50% of above-mentioned acetic acid weight mix, rising high-temperature is 60 DEG C, the hydrogen peroxide of above-mentioned 26% is dripped under stirring condition, insulation reaction 3 hours after dropping, filter, filtrate is neutralized with alkali, washing, it is vacuum dried 3 hours at 50 DEG C, obtains epoxidation methyl eleostearate;
(3) by above-mentioned Monododecylphosphate potassium, calcium alginate mixing, join in the deionized water of compound weight 40 times, add para toluene sulfonamide, stir, for amine emulsion;
(4) being joined in 3 times of dehydrated alcohol of its weight by above-mentioned 2 benzylimidazolines, stir, add PTMG, insulated and stirred 10 minutes at 70 DEG C, for alcoholic solution;
(5) by above-mentioned Lauryl Alcohol ester, naphthenic soap mixing, stir, add tetraethyl orthosilicate, preheat 10 minutes at 70 DEG C, obtain modified tetraethyl orthosilicate;
(6) by above-mentioned modified tetraethyl orthosilicate, the mixing of epoxidation methyl eleostearate, warming temperature is 36 DEG C, add remaining acetic acid, insulated and stirred 10 minutes, drip above-mentioned amine emulsion, add Y r-chloropropyl trimethoxyl silane after dropping, at 76 DEG C, be incubated 6 hours, obtain silica sol modified epoxidation methyl eleostearate;
(7) above-mentioned silica sol modified epoxidation methyl eleostearate is joined in above-mentioned alcoholic solution, stir, add OPEO, 100 revs/min are stirred 30 minutes, mix with remaining each raw material, are melt extruded by extruder, then after tabletting is broken, then through pulverizing, sieving, to obtain final product.
Performance test:
Impact resistance: >=50kg/cm;
Hardness: 2H.
Claims (2)
1. a furniture antiglossing pigment, it is characterised in that it is made up of the raw material of following weight parts:
Lauryl Alcohol ester 1.4-3, PTMG 0.7-2, para toluene sulfonamide 0.8-2, Oleum Verniciae fordii 10-12, sodium hydroxide 0.06-0.07, methanol 3-4, perfluorinated sulfonic resin 0.1-0.2, acetic acid 6-8, the hydrogen peroxide 10-15 of 26-30%, tetraethyl orthosilicate 10-17, Y-r-chloropropyl trimethoxyl silane 0.1-0.2, unsaturated polyester resin 70-80, methyl ethyl ketone peroxide 0.6-1, blanc fixe 15-20, naphthenic soap 1-2, Monododecylphosphate potassium 0.8-2, 2-benzylimidazoline 1-2, calcium alginate 0.8-1, titanium dioxide 3-5, OPEO 0.2-0.4.
2. the preparation method of a furniture antiglossing pigment as claimed in claim 1, it is characterised in that comprise the following steps:
(1) joining in Oleum Verniciae fordii by above-mentioned methanol, add sodium hydroxide, react 70-80 minute at 37-40 DEG C under stirring condition, distill methanol removal, stratification, the supernatant liquid of collection first with sulfuric acid scrubbing, the washing of reusable heat water, distillation dehydration, obtains methyl eleostearate;
(2) 50-60% of above-mentioned methyl eleostearate with perfluorinated sulfonic resin, above-mentioned acetic acid weight is mixed, rise high-temperature and be 60-68 DEG C, the hydrogen peroxide of above-mentioned 26-30% is dripped under stirring condition, insulation reaction 3-4 hour after dropping, filter, filtrate is neutralized with alkali, washing, it is vacuum dried 3-4 hour at 50-60 DEG C, obtains epoxidation methyl eleostearate;
(3) by above-mentioned Monododecylphosphate potassium, calcium alginate mixing, join in the deionized water of compound weight 40-50 times, add para toluene sulfonamide, stir, for amine emulsion;
(4) being joined in its weight 3-5 times dehydrated alcohol by above-mentioned 2-benzylimidazoline, stir, add PTMG, insulated and stirred 10-15 minute at 70-80 DEG C, for alcoholic solution;
(5) by above-mentioned Lauryl Alcohol ester, naphthenic soap mixing, stir, add tetraethyl orthosilicate, preheat 10-16 minute at 70-80 DEG C, obtain modified tetraethyl orthosilicate;
(6) by above-mentioned modified tetraethyl orthosilicate, the mixing of epoxidation methyl eleostearate, warming temperature is 36-40 DEG C, add remaining acetic acid, insulated and stirred 10-20 minute, drip above-mentioned amine emulsion, add Y-r-chloropropyl trimethoxyl silane after dropping, at 76-80 DEG C, be incubated 6-7 hour, obtain silica sol modified epoxidation methyl eleostearate;
(7) above-mentioned silica sol modified epoxidation methyl eleostearate is joined in above-mentioned alcoholic solution, stir, add OPEO, 100-200 rev/min is stirred 30-40 minute, mix with remaining each raw material, melt extruded by extruder, after then tabletting is broken, again through pulverizing, sieving, to obtain final product.