CN105969127A - Gas-permeable furniture coating and preparation method thereof - Google Patents
Gas-permeable furniture coating and preparation method thereof Download PDFInfo
- Publication number
- CN105969127A CN105969127A CN201610187091.3A CN201610187091A CN105969127A CN 105969127 A CN105969127 A CN 105969127A CN 201610187091 A CN201610187091 A CN 201610187091A CN 105969127 A CN105969127 A CN 105969127A
- Authority
- CN
- China
- Prior art keywords
- mentioned
- parts
- weight
- add
- minute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a gas-permeable furniture coating, which is composed of the following raw materials (by weight): 1-2 parts of nickel aminosulfonate, 16-20 parts of scolecite, 0.3-1 part of benzoin, 1-2 parts of tetrabromobisphenol-A polycarbonate, 10-12 parts of tung oil, 0.06-0.07 part of sodium hydroxide, 3-4 parts of methanol, 0.1-0.2 part of perfluorosulfonate resin, 6-8 parts of acetic acid, 10-15 parts of 26-30% hydrogen peroxide, 10-17 parts of tetraethyl orthosilicate, 0.1-0.2 part of Y-chloropropyltrimethoxysilane, 70-80 parts of unsaturated polyester resin, 0.6-1 part of methylethyl ketone peroxide, 0.2-0.3 part of p-tert-amylphenol, 1-2 parts of stearic acid, 0.7-1 part of oleic diethanolamide, 1-2 parts of zinc acetylacetonate, 0.7-2 parts of sodium lauryl sulfate and 0.1-0.3 part of epoxy chloropropane. By adding scolecite and benzoin, etc., gas permeability of film surface can be effectively raised.
Description
Technical field
The present invention relates to coatings for furniture technical field, particularly relate to a kind of vapor-permeable type coatings for furniture and preparation method thereof.
Background technology
Saturated polyester resin is to prepare one of conventional film-forming resin of coating, but use unsaturated polyester resins for general purpose to there is the shortcomings such as resistance to water, solvent resistance, thermostability and poor mechanical property when preparing coating, need unsaturated polyester resin is modified to improve its combination property and currently mainly utilize polyurethane or base polyurethane prepolymer for use as, acrylic resin, epoxy resin, organosilicon, nano material and vegetable oil etc. unsaturated polyester resin to be modified to improving performance when it prepares coating.Wherein, plant oil modified unsaturated polyester vinegar resin is increasingly paid attention to by people.Vegetable oil is incorporated in unsaturated polyester resin by chemical reaction, easily cause the polyreaction of vegetable oil self, make the limited vegetable oil of modified effect also due to both poor compatibility, modification can be caused by the method modified unsaturated polyester resin being blended to fall flat.Therefore, after vegetable oil derivatization, improve the compatibility of vegetable oil and unsaturated polyester resin, be the important channel of plant oil modified unsaturated polyester resin.
In crude vegetal, Oleum Verniciae fordii is more special, and its main component is eleostearic acid glyceride, has conjugated triene structures, can be used alone in oil-based paint, it is also possible to neutralize other semi-drying oils at synthetic resin coating, non-drying oil is used in mixed way.Oleum Verniciae fordii also has good water proofing property, is widely used in building, paints, prints aspects such as (ink).
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of vapor-permeable type coatings for furniture and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of vapor-permeable type coatings for furniture, it is made up of the raw material of following weight parts:
Nickel sulfamic acid 1-2, scolecite 16-20, Benzoinum 0.3-1, tetrabromobisphenol a polycarbonate 1-2, Oleum Verniciae fordii 10-12, sodium hydroxide 0.06-0.07, methanol 3-4, perfluorinated sulfonic resin 0.1-0.2, acetic acid 6-8, the hydrogen peroxide 10-15 of 26-30%, tetraethyl orthosilicate 10-17, Y-r-chloropropyl trimethoxyl silane 0.1-0.2, unsaturated polyester resin 70-80, methyl ethyl ketone peroxide 0.6-1, p-tert-amylphenol 0.2-0.3, stearic acid 1-2, oleic acid diethyl amide 0.7-1, zinc acetylacetonate 1-2, sodium lauryl sulphate 0.7-2, epoxychloropropane 0.1-0.3.
The preparation method of a kind of described vapor-permeable type coatings for furniture, comprises the following steps:
(1) joining in Oleum Verniciae fordii by above-mentioned methanol, add sodium hydroxide, react 70-80 minute at 37-40 DEG C under stirring condition, distill methanol removal, stratification, the supernatant liquid of collection first with sulfuric acid scrubbing, the washing of reusable heat water, distillation dehydration, obtains methyl eleostearate;
(2) 50-60% of above-mentioned methyl eleostearate, perfluorinated sulfonic resin, above-mentioned acetic acid weight is mixed, rise high-temperature and be 60-68 DEG C, the hydrogen peroxide of above-mentioned 26-30% is dripped under stirring condition, insulation reaction 3-4 hour after dropping, filter, filtrate is neutralized with alkali, washing, it is vacuum dried 3-4 hour at 50-60 DEG C, obtains epoxidation methyl eleostearate;
(3) being joined by above-mentioned p-tert-amylphenol in the dehydrated alcohol of its weight 40-50 times, warming temperature is 70-80 DEG C, adds zinc acetylacetonate, insulated and stirred 3-5 minute, adds above-mentioned Y-r-chloropropyl trimethoxyl silane, and stirring, to room temperature, obtains silanol liquid;
(4) above-mentioned sodium lauryl sulphate is joined in the deionized water of its weight 30-40 times, add nickel sulfamic acid, stir, obtain saline solution;
(5) by above-mentioned tetraethyl orthosilicate, the mixing of epoxidation methyl eleostearate, warming temperature is 36-40 DEG C, add remaining acetic acid, insulated and stirred 10-20 minute, drip the deionized water of above-mentioned mixed system weight 60-70%, add saline solution, silanol liquid after dropping, at 76-80 DEG C, be incubated 6-7 hour, obtain silica sol modified epoxidation methyl eleostearate;
(6) by above-mentioned silica sol modified epoxidation methyl eleostearate, oleic acid diethyl amide mixing, join the dehydrated alcohol of compound weight 40-50%, stir, add above-mentioned tetrabromobisphenol a polycarbonate, send in the water-bath of 80-90 DEG C, insulated and stirred 10-13 minute, discharging cools down, adding epoxychloropropane, 300-400 rev/min is stirred 20-30 minute, must premix ester material;
(7) above-mentioned premix ester material is mixed with remaining each raw material, melt extruded by extruder, after then tabletting is broken, then through pulverizing, sieving, to obtain final product.
The invention have the advantage that in the epoxidation methyl eleostearate molecular structure of the present invention and contain epoxy bond and double bond simultaneously, with the carboxyl in unsaturated polyester resin, hydroxyl and double bond, oxidation cross-linked reaction can occur, improve the crosslink density of film, improve filming performance, thus improve the hot strength of film, also improve hardness and the shock resistance of film to a certain extent simultaneously;
Containing hydrophobic fatty acid Long carbon chain in the epoxidation methyl eleostearate of the present invention, when Oleum Verniciae fordii derivant is dispersed in film forming in unsaturated polyester resin, these hydrophobic aliphatic hydrocarbyl groups are at film surface enrichment, film is made to be in a kind of low-surface-energy state, reduce the combination energy on surface and hydrone, thus reduce the water absorption rate of unsaturated polyester resin film, improve unsaturated polyester resin water resistance;
The epoxidation methyl eleostearate of the present invention contains conjugated double bond, and conjugated double bond, in the film forming later stage, occurs oxidation cross-linked, forming network polymers, so that it is tightr to be combined with each other between molecule, the density of film increases, solvent molecule slows down at the permeating speed of film coated surface, thus solvent resistance strengthens;
The epoxidation methyl eleostearate of the present invention has aliphatic long-chain hydrocarbon, and long chain hydrocarbon can play the effect of plasticising in resin, it is possible to strengthen the flexility of unsaturated polyester resin.
The scolecite of present invention addition, Benzoinum etc. can effectively improve the breathability of film coated surface.
Detailed description of the invention
A kind of vapor-permeable type coatings for furniture, it is made up of the raw material of following weight parts:
Nickel sulfamic acid 1, scolecite 16, Benzoinum 0.3, tetrabromobisphenol a polycarbonate 1, Oleum Verniciae fordii 10, sodium hydroxide 0.06, methanol 3, perfluorinated sulfonic resin 0.1, the hydrogen peroxide 10 of acetic acid 6,26%, tetraethyl orthosilicate 10, Y r-chloropropyl trimethoxyl silane 0.1, unsaturated polyester resin 70, methyl ethyl ketone peroxide 0.6, p-tert-amylphenol 0.2, stearic acid 1, oleic acid diethyl amide 0.7, zinc acetylacetonate 1, sodium lauryl sulphate 0.7, epoxychloropropane 0.1.
The preparation method of a kind of described vapor-permeable type coatings for furniture, comprises the following steps:
(1) joining in Oleum Verniciae fordii by above-mentioned methanol, add sodium hydroxide, react 70 minutes at 37 DEG C under stirring condition, distill methanol removal, stratification, the supernatant liquid of collection first with sulfuric acid scrubbing, the washing of reusable heat water, distillation dehydration, obtains methyl eleostearate;
(2) by above-mentioned methyl eleostearate, perfluorinated sulfonic resin, 50% mixing of above-mentioned acetic acid weight, rising high-temperature is 60 DEG C, the hydrogen peroxide of above-mentioned 26% is dripped under stirring condition, insulation reaction 3 hours after dropping, filter, filtrate is neutralized with alkali, washing, it is vacuum dried 3 hours at 50 DEG C, obtains epoxidation methyl eleostearate;
(3) being joined by above-mentioned p-tert-amylphenol in the dehydrated alcohol of its weight 40 times, warming temperature is 70 DEG C, adds zinc acetylacetonate, insulated and stirred 3 minutes, adds above-mentioned Y r-chloropropyl trimethoxyl silane, and stirring, to room temperature, obtains silanol liquid;
(4) above-mentioned sodium lauryl sulphate is joined in the deionized water of its weight 30 times, add nickel sulfamic acid, stir, obtain saline solution;
(5) by above-mentioned tetraethyl orthosilicate, the mixing of epoxidation methyl eleostearate, warming temperature is 36 DEG C, add remaining acetic acid, insulated and stirred 10 minutes, drip the deionized water of above-mentioned mixed system weight 60%, add saline solution, silanol liquid after dropping, at 76 DEG C, be incubated 6 hours, obtain silica sol modified epoxidation methyl eleostearate;
(6) by above-mentioned silica sol modified epoxidation methyl eleostearate, oleic acid diethyl amide mixing, join the dehydrated alcohol of compound weight 40%, stir, add above-mentioned tetrabromobisphenol a polycarbonate, send in the water-bath of 80 DEG C, insulated and stirred 10 minutes, discharging cools down, adding epoxychloropropane, 300 revs/min are stirred 20 minutes, must premix ester material;
(7) above-mentioned premix ester material is mixed with remaining each raw material, melt extruded by extruder, after then tabletting is broken, then through pulverizing, sieving, to obtain final product.
Performance test:
Impact resistance: >=50kg/cm;
Hardness: 2H.
Claims (2)
1. a vapor-permeable type coatings for furniture, it is characterised in that it is made up of the raw material of following weight parts:
Nickel sulfamic acid 1-2, scolecite 16-20, Benzoinum 0.3-1, tetrabromobisphenol a polycarbonate 1-2, Oleum Verniciae fordii 10-12, sodium hydroxide 0.06-0.07, methanol 3-4, perfluorinated sulfonic resin 0.1-0.2, acetic acid 6-8, the hydrogen peroxide 10-15 of 26-30%, tetraethyl orthosilicate 10-17, Y-r-chloropropyl trimethoxyl silane 0.1-0.2, unsaturated polyester resin 70-80, methyl ethyl ketone peroxide 0.6-1, p-tert-amylphenol 0.2-0.3, stearic acid 1-2, oleic acid diethyl amide 0.7-1, zinc acetylacetonate 1-2, sodium lauryl sulphate 0.7-2, epoxychloropropane 0.1-0.3.
2. the preparation method of a vapor-permeable type coatings for furniture as claimed in claim 1, it is characterised in that comprise the following steps:
(1) joining in Oleum Verniciae fordii by above-mentioned methanol, add sodium hydroxide, react 70-80 minute at 37-40 DEG C under stirring condition, distill methanol removal, stratification, the supernatant liquid of collection first with sulfuric acid scrubbing, the washing of reusable heat water, distillation dehydration, obtains methyl eleostearate;
(2) 50-60% of above-mentioned methyl eleostearate, perfluorinated sulfonic resin, above-mentioned acetic acid weight is mixed, rise high-temperature and be 60-68 DEG C, the hydrogen peroxide of above-mentioned 26-30% is dripped under stirring condition, insulation reaction 3-4 hour after dropping, filter, filtrate is neutralized with alkali, washing, it is vacuum dried 3-4 hour at 50-60 DEG C, obtains epoxidation methyl eleostearate;
(3) being joined by above-mentioned p-tert-amylphenol in the dehydrated alcohol of its weight 40-50 times, warming temperature is 70-80 DEG C, adds zinc acetylacetonate, insulated and stirred 3-5 minute, adds above-mentioned Y-r-chloropropyl trimethoxyl silane, and stirring, to room temperature, obtains silanol liquid;
(4) above-mentioned sodium lauryl sulphate is joined in the deionized water of its weight 30-40 times, add nickel sulfamic acid, stir, obtain saline solution;
(5) by above-mentioned tetraethyl orthosilicate, the mixing of epoxidation methyl eleostearate, warming temperature is 36-40 DEG C, add remaining acetic acid, insulated and stirred 10-20 minute, drip the deionized water of above-mentioned mixed system weight 60-70%, add saline solution, silanol liquid after dropping, at 76-80 DEG C, be incubated 6-7 hour, obtain silica sol modified epoxidation methyl eleostearate;
(6) by above-mentioned silica sol modified epoxidation methyl eleostearate, oleic acid diethyl amide mixing, join the dehydrated alcohol of compound weight 40-50%, stir, add above-mentioned tetrabromobisphenol a polycarbonate, send in the water-bath of 80-90 DEG C, insulated and stirred 10-13 minute, discharging cools down, adding epoxychloropropane, 300-400 rev/min is stirred 20-30 minute, must premix ester material;
(7) above-mentioned premix ester material is mixed with remaining each raw material, melt extruded by extruder, after then tabletting is broken, then through pulverizing, sieving, to obtain final product.