CN105968634A - Waterproof heat-resistant cable sheath material with excellent tenacity - Google Patents
Waterproof heat-resistant cable sheath material with excellent tenacity Download PDFInfo
- Publication number
- CN105968634A CN105968634A CN201610369474.2A CN201610369474A CN105968634A CN 105968634 A CN105968634 A CN 105968634A CN 201610369474 A CN201610369474 A CN 201610369474A CN 105968634 A CN105968634 A CN 105968634A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterproof heat
- heat resistant
- excellent toughness
- complex sol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a waterproof heat-resistant cable sheath material with excellent tenacity. The cable sheath material is prepared from, by weight, 15-30 parts of ethylene-vinyl acetate copolymer, 10-20 parts of high-density polyethylene, 20-35 parts of polyvinyl chloride, 0.5-1 part of disproportionated rosin, 0.5-1.2 parts of microcrystalline wax, 1-2 parts of zinc oxide, 10-25 parts of modified composite sol, 1-2 parts of magnesium stearate, 1-2 parts of zinc stearate, 0.8-1.6 parts of tetramethylthiuram disulfide, 0.4-0.9 part of dibutyltin dilaurate, 0.8-1.4 parts of peroxide tert-butyl acetate, 10-30 parts of calcined kaolin, 30-50 parts of nano silica, 5-15 parts of light calcium carbonate and 1-3 parts of antiager. The waterproof heat-resistant cable sheath material is flame retardant, waterproof and high in heat stability and tenacity.
Description
Technical field
The present invention relates to CABLE MATERIALS technical field, particularly relate to a kind of waterproof heat resistant and there is the electricity of excellent toughness
Cable protective cover material
Background technology
Along with rapid development of economy, the demand of cable sheath material is increasing, it is desirable to more and more higher,
Traditional cable material is faced with huge challenge, and electric wire transmits body as electric energy and information, is handing over
Logical transport, the every field of the industry life such as mine, electrical communications can see cable miscellaneous, with
Cable increase of status in life, its sheath quality is the most increasingly subject to people's attention, China only by
The fire damage that cable causes, annual up to tens yuans, the fire-retardant problem of electric wire and cable jacket material
Increasingly causing the concern of people, in protection fire, the person and property safety are the major issues that people are concerned about, especially
Being fire-retardant, waterproof, Heat stability is good, the research and development of the cable jacket material of good toughness are by each field professional person
Highest attention.
Summary of the invention
The present invention proposes a kind of waterproof heat resistant and has the cable jacket material of excellent toughness, fire-retardant, waterproof,
Heat stability is good, good toughness.
A kind of waterproof heat resistant that the present invention proposes and have the cable jacket material of excellent toughness, its raw material is by weight
Part includes: ethylene-vinyl acetate copolymer 15-30 part, high density polyethylene (HDPE) 10-20 part, polrvinyl chloride
20-35 part, disproportionated rosin 0.5-1 part, microcrystalline wax 0.5-1.2 part, zinc oxide 1-2 part is modified compound
Colloidal sol 10-25 part, magnesium stearate 1-2 part, zinc stearate 1-2 part, tetramethylthiuram disulfide 0.8-1.6
Part, dibutyl tin laurate 0.4-0.9 part, peroxidating tert-butyl acetate 0.8-1.4 part, calcine kaolinite
Soil 10-30 part, nano silicon 30-50 part, precipitated calcium carbonate 5-15 part, age resistor 1-3 part.
Preferably, modified complex sol uses following technique to prepare: by weight by 20-40 part glycerol,
30-50 part water mix and blend 40-80min, obtains the first prefabricated material;By 5-10 part soybean meal, 40-80
Part water, 0.4-0.8 part sodium sulfite mix and blend 20-50min, regulation system pH value is 8.5-9.5, stirs
Mixing 40-80min, whipping temp is 45-55 DEG C, centrifugation, adds 20-40 in the solids obtained
Part water, 0.1-0.4 silver nitrate, 10-20 part sericine, 0.2-0.6 part sodium sulfite, 1-2 part ten
Dialkyl sulfonates, 0.2-0.8 part sodium carboxymethyl cellulose mixed at room temperature stirring 4-8min, is warming up to
65-75 DEG C, under stirring, drip the first prefabricated material, drip complete follow-up continuous stirring 20-40min, regulation
System pH is 7.5-8, continues stirring 1-2h, and whipping temp is 55-65 DEG C, cooling, obtains modified multiple
Close colloidal sol.
Preferably, ethylene-vinyl acetate copolymer, high density polyethylene (HDPE), the weight ratio of polrvinyl chloride are
20-26:14-18:26-30.
Preferably, disproportionated rosin, microcrystalline wax, zinc oxide, the weight ratio of modified complex sol are 0.6-0.8:
0.8-1.1:1.4-1.8:20-23.
Preferably, modified complex sol, tetramethylthiuram disulfide, dibutyl tin laurate, peroxide
The weight ratio changing tert-butyl acetate is 20-23:1.2-1.4:0.5-0.7:0.9-1.2.
Preferably, modified complex sol, calcined kaolin, nano silicon, the weight of precipitated calcium carbonate
Ratio is 20-23:20-24:40-46:10-13.
Preferably, ethylene-vinyl acetate copolymer, high density polyethylene (HDPE), polrvinyl chloride, modification are combined molten
The weight ratio of glue is 20-26:14-18:26-30:20-23.
Preferably, described waterproof heat resistant and have the cable jacket material of excellent toughness, its raw material is by weight
Including: ethylene-vinyl acetate copolymer 20-26 part, high density polyethylene (HDPE) 14-18 part, polrvinyl chloride 26-30
Part, disproportionated rosin 0.6-0.8 part, microcrystalline wax 0.8-1.1 part, zinc oxide 1.4-1.8 part, modified multiple
Close colloidal sol 20-23 part, magnesium stearate 1.4-1.9 part, zinc stearate 1.2-1.5 part, tetramethyl
Thiuram 1.2-1.4 part, dibutyl tin laurate 0.5-0.7 part, peroxidating tert-butyl acetate 0.9-1.2
Part, calcined kaolin 20-24 part, nano silicon 40-46 part, precipitated calcium carbonate 10-13 part is anti-
Old agent 1.5-2 part.
In the present invention, soybean meal is through pretreatment, by the sky of its internal soybean protein molecule of Reasonable adjustment
Between structure, and sericine mating reaction, and use the blended cross linking of sodium carboxymethyl cellulose, and can having
Effect avoids Proteolytic enzyme to run off, and goods toughness is high, and discarded degradable, the glycerol that it is possible to additionally incorporate can be by nitric acid
Silver is reduced to silver oxide, and sericin and pretreated soybean meal utilize its curling backbone to ensure
Nano oxidized Argent grain is not reunited, goods and polrvinyl chloride, ethylene-vinyl acetate copolymer, highly dense
Degree polyethylene and zinc oxide, peroxidating tert-butyl acetate, tetramethylthiuram disulfide, tin dilaurate two fourth
The good dispersion property of Ji Xi sulfuration, modified complex sol, zinc oxide, peroxidating tert-butyl acetate, two sulfur
Change tetra methylthiuram, dibutyl tin laurate is worked in coordination with and is vulcanized major ingredient, and mutual adhesion is the most extremely strong,
And crosslink density is uniform, good toughness, Heat stability is good, and the magnesium stearate added, zinc stearate, crystallite
Paraffin, disproportionated rosin and modified complex sol synergism, on the basis of ensureing the tear-resistant performance of goods,
Can promote that toughness is equilibrium with hardness, modified complex sol and precipitated calcium carbonate, calcined kaolin, nanometer two
Silicon oxide effect, mutual degree of aggregation is low, each other card and make good use of and adhesion is strong, goods heat stability
Extremely strong with hydrophobic performance.
Detailed description of the invention
Embodiment 1
A kind of waterproof heat resistant and there is the cable jacket material of excellent toughness, its raw material includes by weight: ethylene-
Vinyl acetate co-polymer 30 parts, high density polyethylene (HDPE) 10 parts, polrvinyl chloride 35 parts, disproportionated rosin 0.5
Part, microcrystalline wax 1.2 parts, zinc oxide 1 part, modified complex sol 25 parts, magnesium stearate 1 part, stearic
2 parts of zinc of acid, tetramethylthiuram disulfide 0.8 part, dibutyl tin laurate 0.9 part, peroxidating vinegar
Tert-butyl acrylate 0.8 part, calcined kaolin 30 parts, nano silicon 30 parts, precipitated calcium carbonate 15 parts,
1 part of age resistor.
Embodiment 2
A kind of waterproof heat resistant and there is the cable jacket material of excellent toughness, its raw material includes by weight: ethylene-
Vinyl acetate co-polymer 15 parts, high density polyethylene (HDPE) 20 parts, polrvinyl chloride 20 parts, disproportionated rosin 1 part,
Microcrystalline wax 0.5 part, zinc oxide 2 parts, modified complex sol 10 parts, magnesium stearate 2 parts, zinc stearate
1 part, tetramethylthiuram disulfide 1.6 parts, dibutyl tin laurate 0.4 part, the tertiary fourth of peroxidating acetic acid
Ester 1.4 parts, calcined kaolin 10 parts, nano silicon 50 parts, precipitated calcium carbonate 5 parts, age resistor 3
Part.
Embodiment 3
A kind of waterproof heat resistant and there is the cable jacket material of excellent toughness, its raw material includes by weight: ethylene-
Vinyl acetate co-polymer 26 parts, high density polyethylene (HDPE) 14 parts, polrvinyl chloride 30 parts, disproportionated rosin 0.6
Part, microcrystalline wax 1.1 parts, zinc oxide 1.4 parts, modified complex sol 23 parts, magnesium stearate 1.4 parts,
Zinc stearate 1.5 parts, tetramethylthiuram disulfide 1.2 parts, dibutyl tin laurate 0.7 part, mistake
Oxidation tert-butyl acetate 0.9 part, calcined kaolin 24 parts, nano silicon 40 parts, precipitated calcium carbonate
13 parts, 1.5 parts of age resistor.
Modified complex sol uses following technique to prepare: 40 parts of glycerol, 30 parts of water mixing are stirred by weight
Mix 80min, obtain the first prefabricated material;5 parts of soybean meals, 80 parts of water, 0.4 part of sodium sulfite mixing are stirred
Mixing 50min, regulation system pH value is 8.5, stirs 80min, and whipping temp is 45 DEG C, centrifugation,
40 parts of water, 0.1 silver nitrate, 20 parts of sericines, 0.2 part of sulfurous acid are added in the solids obtained
Sodium, 2 parts of dodecyl sodium sulfates, 0.2 part of sodium carboxymethyl cellulose mixed at room temperature stirring 8min, be warming up to
65 DEG C, under stirring, drip the first prefabricated material, drip complete follow-up continuous stirring 40min, regulation system
PH value is 7.5, continues stirring 2h, and whipping temp is 55 DEG C, cooling, obtains modified complex sol.
Embodiment 4
A kind of waterproof heat resistant and there is the cable jacket material of excellent toughness, its raw material includes by weight: ethylene-
Vinyl acetate co-polymer 20 parts, high density polyethylene (HDPE) 18 parts, polrvinyl chloride 26 parts, disproportionated rosin 0.8
Part, microcrystalline wax 0.8 part, zinc oxide 1.8 parts, modified complex sol 20 parts, magnesium stearate 1.9 parts,
Zinc stearate 1.2 parts, tetramethylthiuram disulfide 1.4 parts, dibutyl tin laurate 0.5 part, mistake
Oxidation tert-butyl acetate 1.2 parts, calcined kaolin 20 parts, nano silicon 46 parts, precipitated calcium carbonate
10 parts, 2 parts of age resistor.
Modified complex sol uses following technique to prepare: 20 parts of glycerol, 50 parts of water mixing are stirred by weight
Mix 40min, obtain the first prefabricated material;By 10 parts of soybean meals, 40 parts of water, 0.8 part of sodium sulfite mixing
Stirring 20min, regulation system pH value is 9.5, stirs 40min, and whipping temp is 55 DEG C, centrifugation,
20 parts of water, 0.4 silver nitrate, 10 parts of sericines, 0.6 part of sulfurous acid are added in the solids obtained
Sodium, 1 part of dodecyl sodium sulfate, 0.8 part of sodium carboxymethyl cellulose mixed at room temperature stirring 4min, be warming up to
75 DEG C, under stirring, drip the first prefabricated material, drip complete follow-up continuous stirring 20min, regulation system
PH value is 8, continues stirring 1h, and whipping temp is 65 DEG C, cooling, obtains modified complex sol.
Embodiment 5
A kind of waterproof heat resistant and there is the cable jacket material of excellent toughness, its raw material includes by weight: ethylene-
Vinyl acetate co-polymer 23 parts, high density polyethylene (HDPE) 16 parts, polrvinyl chloride 28 parts, disproportionated rosin 0.75
Part, microcrystalline wax 0.95 part, zinc oxide 1.6 parts, modified complex sol 22 parts, magnesium stearate 1.6 parts,
Zinc stearate 1.35 parts, tetramethylthiuram disulfide 1.3 parts, dibutyl tin laurate 0.6 part, mistake
Oxidation tert-butyl acetate 1.05 parts, calcined kaolin 22 parts, nano silicon 43 parts, precipitated calcium carbonate
12 parts, 1.8 parts of age resistor.
Modified complex sol uses following technique to prepare: 25 parts of glycerol, 40 parts of water mixing are stirred by weight
Mix 60min, obtain the first prefabricated material;8 parts of soybean meals, 60 parts of water, 0.6 part of sodium sulfite mixing are stirred
Mixing 30min, regulation system pH value is 9.2, stirs 60min, and whipping temp is 52 DEG C, centrifugation,
32 parts of water, 0.24 silver nitrate, 14 parts of sericines, 0.4 part of sulfurous acid are added in the solids obtained
Sodium, 1.5 parts of dodecyl sodium sulfates, 0.6 part of sodium carboxymethyl cellulose mixed at room temperature stirring 6min, be warming up to
72 DEG C, under stirring, drip the first prefabricated material, drip complete follow-up continuous stirring 30min, regulation system
PH value is 7.8, continues stirring 1.5h, and whipping temp is 62 DEG C, cooling, obtains modified complex sol.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention not office
Being limited to this, any those familiar with the art is in the technical scope that the invention discloses, according to this
The technical scheme of invention and inventive concept thereof in addition equivalent or change, all should contain the protection in the present invention
Within the scope of.
Claims (8)
1. a waterproof heat resistant and there is the cable jacket material of excellent toughness, it is characterised in that its raw material is by weight
Amount part includes: ethylene-vinyl acetate copolymer 15-30 part, high density polyethylene (HDPE) 10-20 part, polychlorostyrene second
Alkene 20-35 part, disproportionated rosin 0.5-1 part, microcrystalline wax 0.5-1.2 part, zinc oxide 1-2 part is modified
Complex sol 10-25 part, magnesium stearate 1-2 part, zinc stearate 1-2 part, tetramethylthiuram disulfide
0.8-1.6 part, dibutyl tin laurate 0.4-0.9 part, peroxidating tert-butyl acetate 0.8-1.4 part,
Calcined kaolin 10-30 part, nano silicon 30-50 part, precipitated calcium carbonate 5-15 part, age resistor
1-3 part.
Waterproof heat resistant the most according to claim 1 and there is the cable jacket material of excellent toughness, its feature
Being, modified complex sol uses following technique to prepare: by weight by 20-40 part glycerol, 30-50
Part water mix and blend 40-80min, obtains the first prefabricated material;By 5-10 part soybean meal, 40-80 part water,
0.4-0.8 part sodium sulfite mix and blend 20-50min, regulation system pH value is 8.5-9.5, stirring
40-80min, whipping temp is 45-55 DEG C, centrifugation, adds 20-40 part in the solids obtained
Water, 0.1-0.4 silver nitrate, 10-20 part sericine, 0.2-0.6 part sodium sulfite, 1-2 part 12
Sodium alkyl sulfonate, 0.2-0.8 part sodium carboxymethyl cellulose mixed at room temperature stirring 4-8min, is warming up to 65-75 DEG C,
Under stirring, drip the first prefabricated material, drip complete follow-up continuous stirring 20-40min, regulation system pH
Value is 7.5-8, continues stirring 1-2h, and whipping temp is 55-65 DEG C, cooling, obtains modified complex sol.
Waterproof heat resistant the most according to claim 1 and 2 and there is the cable jacket material of excellent toughness, its
Being characterised by, ethylene-vinyl acetate copolymer, high density polyethylene (HDPE), the weight ratio of polrvinyl chloride are 20-26:
14-18:26-30.
4. according to the waterproof heat resistant described in any one of claim 1-3 and the cable cover(ing) with excellent toughness
Material, it is characterised in that disproportionated rosin, microcrystalline wax, zinc oxide, the weight ratio of modified complex sol are
0.6-0.8:0.8-1.1:1.4-1.8:20-23.
5. according to the waterproof heat resistant described in any one of claim 1-4 and the cable cover(ing) with excellent toughness
Material, it is characterised in that modified complex sol, tetramethylthiuram disulfide, dibutyl tin laurate,
The weight ratio of peroxidating tert-butyl acetate is 20-23:1.2-1.4:0.5-0.7:0.9-1.2.
6. according to the waterproof heat resistant described in any one of claim 1-5 and the cable cover(ing) with excellent toughness
Material, it is characterised in that modified complex sol, calcined kaolin, nano silicon, precipitated calcium carbonate
Weight ratio is 20-23:20-24:40-46:10-13.
7. according to the waterproof heat resistant described in any one of claim 1-6 and the cable cover(ing) with excellent toughness
Material, it is characterised in that ethylene-vinyl acetate copolymer, high density polyethylene (HDPE), polrvinyl chloride, modification are again
The weight ratio closing colloidal sol is 20-26:14-18:26-30:20-23.
8. according to the waterproof heat resistant described in any one of claim 1-7 and the cable cover(ing) with excellent toughness
Material, it is characterised in that its raw material includes by weight: ethylene-vinyl acetate copolymer 20-26 part is high
Density polyethylene 14-18 part, polrvinyl chloride 26-30 part, disproportionated rosin 0.6-0.8 part, microcrystalline wax
0.8-1.1 part, zinc oxide 1.4-1.8 part, modified complex sol 20-23 part, magnesium stearate 1.4-1.9
Part, zinc stearate 1.2-1.5 part, tetramethylthiuram disulfide 1.2-1.4 part, di lauric dibutyl
Stannum 0.5-0.7 part, peroxidating tert-butyl acetate 0.9-1.2 part, calcined kaolin 20-24 part, nanometer two
Silicon oxide 40-46 part, precipitated calcium carbonate 10-13 part, age resistor 1.5-2 part.