CN105966002A - Root resistant waterproof coiled material and preparation method thereof - Google Patents
Root resistant waterproof coiled material and preparation method thereof Download PDFInfo
- Publication number
- CN105966002A CN105966002A CN201610272973.XA CN201610272973A CN105966002A CN 105966002 A CN105966002 A CN 105966002A CN 201610272973 A CN201610272973 A CN 201610272973A CN 105966002 A CN105966002 A CN 105966002A
- Authority
- CN
- China
- Prior art keywords
- root
- resistance agent
- layer
- root resistance
- modified bitumen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a root resistant waterproof coiled material and a preparation method thereof; the waterproof coiled material includes an aluminum sheet blank basis layer, a root retarder modified rubber asphalt layer and a polyethylene film layer; the aluminum blank basis layer is dip-coated with the root retarder modified rubber asphalt layer, and the upper surface of the root retarder modified rubber asphalt layer is covered with the polyethylene film layer; the root retarder modified rubber asphalt layer consists of the following components by the weight percentage: 50-65% of asphalt, 4-10% of polyolefin, 4-6% of SBS, 8-15% of engine oil, 8-16% of a rubber powder, 8-20% of rock flour and 0.1-2% of a chemical root retarder. The preparation method includes the following steps: 1) preparing the root retarder modified rubber asphalt layer; 2) uniformly covering the aluminum sheet blank basis layer with the prepared root retarder modified rubber asphalt layer, then loading the polyethylene film layer on the root retarder modified rubber asphalt layer, and thus obtaining the product. The waterproof coiled material has the advantages of long root retarding acting time and good action effect on thriving plant root systems.
Description
Technical field
The invention belongs to building water-proof coiled material technical field, be specifically related to be that one can effectively stop root system of plant to be worn
Saturating waterproof roll and preparation method thereof.
Background technology
In recent years, along with the continuous expansion of urban construction, people's living standard improves constantly, but the greenery patches in living environment
Area is more and more less.To this end, use roof area to become the field that people try to explore with how rationalizing.Rationally
Change and use roof area to be included on roof the green plants such as structure garden, plantation flowers, vegetable, undershrub, can effectively purify
Air, improve and beautify the environment.Build roof garden firstly the need of solving waterproof problem, currently used more be modified pitch
Waterproof material, but it is the most easily penetrated by the root system of plant, causes roof seepage, and serious even can affect building
Structure.Additionally, in the large-scale highly difficult waterproofing works such as high-speed railway, subway, tunnel, hydraulic engineering, also tend to easily by
Waterproof layer breakage, insufficient strength, bonding security incident and the quality accident such as loosely occur in the puncture of root system of plant.
Existing SBS modified asphalt waterproof material, APP modified asphalt waterproof material the most do not possess anti-plant root puncture merit
Can, and owing to this type of waterproof roll formula is single, the intensity of coiled material is low, cracking resistance and anti ageing property the highest, can be very
Easily penetrated by plant roots.Existing anti-plant root puncture waterproof roll only portion of material has iris action, overall nothing to plant roots
Method forms root resistance structure, it is difficult to eugonic root system of plant is formed permanently effective iris action.
Summary of the invention
, root resistance limited use, short-life technology weak for the existing asphalt waterproofing material root puncture resistant ability of solution are asked
Topic, the present invention proposes a kind of root resistant waterproof roll, this waterproof roll root resistance long action time and grow prosperity root system of plant
Action effect especially good.
The technical scheme is that and be achieved in that:
A kind of root resistant waterproof roll, including aluminium flake tire basic unit, root resistance agent rubber modified bitumen layer and polyethylene film
Layer, described root resistance agent rubber modified bitumen layer dip-coating is on described aluminium flake tire basic unit, and described polyethylene film layer is coated on described
Above root resistance agent rubber modified bitumen layer；Described root resistance agent rubber modified bitumen layer is made up of the component of following percetage by weight:
Colophonium 50-65%, polyolefin 4-10%, SBS 4-6%, machine oil 8-15%, rubber powder 8-16%, stone powder 8-20% and chemistry resistance
Root agent 0.1-2%.
Further, the root resistance agent of described chemistry is root resistance agent-B2.
Further, the thickness of described coiled material is 3-5mm, and width is 1-3 rice.
Further, granularity >=40 mesh of described rubber powder；Granularity >=200 mesh of described stone powder.
It is a further object to provide the preparation method of a kind of root resistant waterproof roll, comprise the following steps:
1) root resistance agent rubber modified bitumen layer is prepared: take asphalt heating to 195 DEG C-205 DEG C, add rubber the most while stirring
Rubber powder, is warming up to 250 DEG C-260 DEG C, and constant temperature stirs 1.5-2.5 hour, is cooled to 185 DEG C-195 DEG C, adds machine oil, stirs 5-
15 minutes, it is subsequently added SBS and polyolefin, stirs under the conditions of 175 DEG C-185 DEG C 0.6-1.6 hour, then grind 1-1.5 little
Time, add stone powder and chemistry root resistance agent, stir 0.5-1.5 hour under the conditions of 175 DEG C-185 DEG C, the root resistance agent that must prepare
Rubber modified bitumen layer；
2) by the above-mentioned root resistance agent rubber modified bitumen layer prepared uniform fold in aluminium flake tire basic unit, then in root resistance agent
Polyethylene film layer on rubber modified bitumen layer,.
Further, granularity >=40 mesh of described rubber powder；Granularity >=200 mesh of described stone powder.
The beneficial effects of the present invention is: the waterproof requirement of building can be ensured well, moreover it is possible to keep out plant roots for a long time
Portion invades coiled material, it is to avoid produces roof and destroys, thus reaches good waterproof effect.
Detailed description of the invention
Embodiment 1
A kind of root resistant waterproof roll, including aluminium flake tire basic unit, root resistance agent rubber modified bitumen layer and polyethylene film
Layer, described root resistance agent rubber modified bitumen layer dip-coating is on described aluminium flake tire basic unit, and described polyethylene film layer is coated on described
Above root resistance agent rubber modified bitumen layer；Described root resistance agent rubber modified bitumen layer is made up of the component of following percetage by weight:
Colophonium 50%, polyolefin 10%, SBS 6%, machine oil 10%, rubber powder 12%, stone powder 10% and root resistance agent-B2 2%.Wherein,
Granularity 50 mesh of rubber powder；Granularity 200 mesh of described stone powder.
The preparation method of root resistant waterproof roll, comprises the following steps:
1) root resistance agent rubber modified bitumen layer is prepared: take asphalt heating to 195 DEG C, add rubber powder the most while stirring,
Being warming up to 250 DEG C, constant temperature stirs 1.5 hours, is cooled to 185 DEG C, adds machine oil, stirs 5 minutes, be subsequently added SBS and polyene
Hydrocarbon, stirs under the conditions of 185 DEG C 0.6 hour, then grinds 1 hour, add stone powder and root resistance agent-B2, under the conditions of 185 DEG C
Stir 1.5 hours, the root resistance agent rubber modified bitumen layer that must prepare；
2) by the above-mentioned root resistance agent rubber modified bitumen layer prepared uniform fold in aluminium flake tire basic unit, then in root resistance agent
Polyethylene film layer on rubber modified bitumen layer,.
Embodiment 2
A kind of root resistant waterproof roll, including aluminium flake tire basic unit, root resistance agent rubber modified bitumen layer and polyethylene film
Layer, described root resistance agent rubber modified bitumen layer dip-coating is on described aluminium flake tire basic unit, and described polyethylene film layer is coated on described
Above root resistance agent rubber modified bitumen layer；Described root resistance agent rubber modified bitumen layer is made up of the component of following percetage by weight:
Colophonium 65%, polyolefin 4%, SBS 4%, machine oil 8%, rubber powder 8%, stone powder 10% and root resistance agent-B2 1%.Wherein, rubber
Granularity 60 mesh of rubber powder；Granularity 240 mesh of described stone powder.
The preparation method of root resistant waterproof roll, comprises the following steps:
1) root resistance agent rubber modified bitumen layer is prepared: take asphalt heating to 205 DEG C, add rubber powder the most while stirring,
Being warming up to 260 DEG C, constant temperature stirs 2.5 hours, is cooled to 195 DEG C, adds machine oil, stirs 10 minutes, be subsequently added SBS and polyene
Hydrocarbon, stirs under the conditions of 185 DEG C 1 hour, then grinds 1.5 hours, add stone powder and root resistance agent-B2, under the conditions of 175 DEG C
Stir 1 hour, the root resistance agent rubber modified bitumen layer that must prepare；
2) by the above-mentioned root resistance agent rubber modified bitumen layer prepared uniform fold in aluminium flake tire basic unit, then in root resistance agent
Polyethylene film layer on rubber modified bitumen layer,.
Embodiment 3
A kind of root resistant waterproof roll, including aluminium flake tire basic unit, root resistance agent rubber modified bitumen layer and polyethylene film
Layer, described root resistance agent rubber modified bitumen layer dip-coating is on described aluminium flake tire basic unit, and described polyethylene film layer is coated on described
Above root resistance agent rubber modified bitumen layer；Described root resistance agent rubber modified bitumen layer is made up of the component of following percetage by weight:
Colophonium 60%, polyolefin 5%, SBS 5%, machine oil 10%, rubber powder 8.9%, stone powder 11% and root resistance agent-B2 0.1%.Its
In, granularity 60 mesh of rubber powder；Granularity 260 mesh of described stone powder.
The preparation method of root resistant waterproof roll, comprises the following steps:
1) root resistance agent rubber modified bitumen layer is prepared: take asphalt heating to 200 DEG C, add rubber powder the most while stirring,
Being warming up to 250 DEG C, constant temperature stirs 2 hours, is cooled to 190 DEG C, adds machine oil, stirs 10 minutes, be subsequently added SBS and polyene
Hydrocarbon, stirs under the conditions of 180 DEG C 0.6 hour, then grinds 1 hour, add stone powder and root resistance agent-B2, under the conditions of 180 DEG C
Stir 0.5 hour, the root resistance agent rubber modified bitumen layer that must prepare；
2) by the above-mentioned root resistance agent rubber modified bitumen layer prepared uniform fold in aluminium flake tire basic unit, then in root resistance agent
Polyethylene film layer on rubber modified bitumen layer,.
Embodiment 4
Root resistant waterproof roll embodiment 1-3 prepared carries out performance detection, the results are shown in Table 1:
Table 1 root resistant waterproof roll performance test results
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all essences in the present invention
Within god and principle, any modification, equivalent substitution and improvement etc. made, should be included within the scope of the present invention.
Claims (6)
1. a root resistant waterproof roll, it is characterised in that include aluminium flake tire basic unit, root resistance agent rubber modified bitumen layer and
Polyethylene film layer, described root resistance agent rubber modified bitumen layer dip-coating on described aluminium flake tire basic unit, described polyethylene film layer bag
Overlay on above described root resistance agent rubber modified bitumen layer；Described root resistance agent rubber modified bitumen layer is by the group of following percetage by weight
Be grouped into: Colophonium 50-65%, polyolefin 4-10%, SBS4-6%, machine oil 8-15%, rubber powder 8-16%, stone powder 8-20% with
Chemistry root resistance agent 0.1-2%.
Root resistant waterproof roll the most according to claim 1, it is characterised in that described chemistry root resistance agent be root resistance agent-
B2。
Root resistant waterproof roll the most according to claim 1, it is characterised in that the thickness of described coiled material is 3-5mm, wide
Degree is 1-3 rice.
Root resistant waterproof roll the most according to claim 1, it is characterised in that granularity >=40 mesh of described rubber powder；
Granularity >=200 mesh of described stone powder.
5. the preparation method of root resistant waterproof roll as claimed in claim 1 or 2, it is characterised in that comprise the following steps:
1) root resistance agent rubber modified bitumen layer is prepared: take asphalt heating to 195 DEG C-205 DEG C, add rubber the most while stirring
Powder, is warming up to 250 DEG C-260 DEG C, and constant temperature stirs 1.5-2.5 hour, is cooled to 185 DEG C-195 DEG C, adds machine oil, stirs 5-15
Minute, it is subsequently added SBS and polyolefin, stirs under the conditions of 175 DEG C-185 DEG C 0.6-1.6 hour, then grind 1-1.5 little
Time, add stone powder and chemistry root resistance agent, stir 0.5-1.5 hour under the conditions of 175 DEG C-185 DEG C, the root resistance agent that must prepare
Rubber modified bitumen layer；
2) by the above-mentioned root resistance agent rubber modified bitumen layer prepared uniform fold in aluminium flake tire basic unit more modified in root resistance agent
Polyethylene film layer on rubber asphalt layer,.
The preparation method of root resistant waterproof roll the most according to claim 5, it is characterised in that the grain of described rubber powder
Degree >=40 mesh；Granularity >=200 mesh of described stone powder.