CN105951265A - Production method for towel untwisted cloth - Google Patents
Production method for towel untwisted cloth Download PDFInfo
- Publication number
- CN105951265A CN105951265A CN201610499536.1A CN201610499536A CN105951265A CN 105951265 A CN105951265 A CN 105951265A CN 201610499536 A CN201610499536 A CN 201610499536A CN 105951265 A CN105951265 A CN 105951265A
- Authority
- CN
- China
- Prior art keywords
- cotton
- towel
- yarn
- molar concentration
- cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production method for towel untwisted cloth. The production method comprises the following steps: reversely winding twisted cotton yarns and vinylon to form cotton-fiber twisted yarns; by taking the cotton-fiber twisted yarns as weft yarns, and taking common cotton yarns as warps, weaving, putting formed blank cloth into water to boil off and untwist, and finally flushing, wherein during weaving, density of weft yarns is 200-230 wefts/10cm, and density of the wraps is 140-230 warps/10cm; during boiling-off, nickel sulfate and propionic acid with molar concentration being 7-9 mmol/L are added, and a molar concentration ratio of the nickel sulfate to the propionic acid is (6-8) to 1. The towel untwisted cloth prepared by the production method is not liable to shrink and deform, and is associated with the molar concentration of nickel sulfate and propionic acid in water during boiling-off; and when the molar concentration ratio of the nickel sulfate to the propionic acid is (6-8) to 1, the prepared towel untwisted cloth has lowest shrinking percentage.
Description
Technical field
The invention belongs to field of textiles, be specifically related to the manufacture method of the non-twist cloth of a kind of towel.
Background technology
In textile industry, the Cotton Gossypii do not twisted spins not resultant yarn, and cloth can not knitted by the yarn do not twisted.Twist yarn can only have been used now to weave.
And Cotton Gossypii maximum feature is fluffy softness, sucting wet air permeability is strong, but, make Cotton Gossypii solid twisting the process spinning and being woven into cloth
Some characteristics have had qualitative change, comfort level to be affected.
In recent years, zero twisted yarn starts to occur, but there are no and directly use zero twisted yarn to weave cotton cloth, this be primarily due to the twist of zero twisted yarn low,
Intensity difference, is unfavorable for manufacturing.And, because there being polyvinyl to be rolled on yarn in zero twisted yarn, being made into cloth or making clothing, soaking
In water or meet uniform temperature will high shrinkage, if clothing will gross distortion shrink.
Summary of the invention
It is an object of the invention to provide the manufacture method of the non-twist cloth of a kind of towel.
The above-mentioned purpose of the present invention is achieved by techniques below scheme:
The manufacture method of the non-twist cloth of a kind of towel, will twist cotton yarn and polyvinyl reverse-winding, form cotton dimension folded yarn, tie up with cotton and close
Weft yarn made by stock yarn, and warp thread made by common cotton yarn, carries out woven, and the grey cloth of formation puts into kiering in water, backtwisting, is finally rinsed；
Wherein, time woven, end count is 200～230/10cm, and filling density is 140～230/10cm；During kiering, interpolation mole in water
Concentration be nickel sulfate and the propanoic acid of 7～9mmol/L, nickel sulfate and propanoic acid molar concentration rate be 6～8:1.
Further, during kiering, water adds nickel sulfate and propanoic acid that molar concentration is 8mmol/L, nickel sulfate and propanoic acid mole
Concentration is than for 7:1.
Further, during kiering, water temperature controls at 70～80 DEG C, and the kiering time is 1～2 hour.
Advantages of the present invention:
The non-twist cloth of towel prepared by the inventive method is difficult to contraction distortion, this and nickel sulfate and propanoic acid molar concentration rate in water during kiering
Relevant, when nickel sulfate and propanoic acid molar concentration rate are 6～8:1, prepared towel non-twist cloth shrinkage factor is minimum.
Detailed description of the invention
Further illustrate the essentiality content of the present invention below in conjunction with embodiment, but do not limit scope with this.To the greatest extent
The present invention is explained in detail by pipe with reference to preferred embodiment, it will be understood by those within the art that, can be to the present invention
Technical scheme modify or equivalent, without deviating from the spirit and scope of technical solution of the present invention.
Embodiment 1: the making of the non-twist cloth of towel
To twist cotton yarn and polyvinyl reverse-winding, and form cotton dimension folded yarn, tie up folded yarn with cotton and make weft yarn, warp thread made by common cotton yarn,
Carrying out woven, the grey cloth of formation puts into kiering in water, backtwisting, is finally rinsed；Wherein, time woven, end count is 215
/ 10cm, filling density is 185/10cm；During kiering, water adds nickel sulfate and propanoic acid that molar concentration is 8mmol/L, sulphuric acid
Nickel and propanoic acid molar concentration rate are 7:1.During kiering, water temperature controls at 75 DEG C, and the kiering time is 1.5 hours.
Embodiment 2: the making of the non-twist cloth of towel
To twist cotton yarn and polyvinyl reverse-winding, and form cotton dimension folded yarn, tie up folded yarn with cotton and make weft yarn, warp thread made by common cotton yarn,
Carrying out woven, the grey cloth of formation puts into kiering in water, backtwisting, is finally rinsed；Wherein, time woven, end count is 200
/ 10cm, filling density is 140/10cm；During kiering, water adds nickel sulfate and propanoic acid that molar concentration is 7mmol/L, sulphuric acid
Nickel and propanoic acid molar concentration rate are 6:1.During kiering, water temperature controls at 70 DEG C, and the kiering time is 2 hours.
Embodiment 3: the making of the non-twist cloth of towel
To twist cotton yarn and polyvinyl reverse-winding, and form cotton dimension folded yarn, tie up folded yarn with cotton and make weft yarn, warp thread made by common cotton yarn,
Carrying out woven, the grey cloth of formation puts into kiering in water, backtwisting, is finally rinsed；Wherein, time woven, end count is 230
/ 10cm, filling density is 230/10cm；During kiering, water adds nickel sulfate and propanoic acid that molar concentration is 9mmol/L, sulphuric acid
Nickel and propanoic acid molar concentration rate are 8:1.During kiering, water temperature controls at 80 DEG C, and the kiering time is 2 hours.
Embodiment 4: the making of the non-twist cloth of towel
To twist cotton yarn and polyvinyl reverse-winding, and form cotton dimension folded yarn, tie up folded yarn with cotton and make weft yarn, warp thread made by common cotton yarn,
Carrying out woven, the grey cloth of formation puts into kiering in water, backtwisting, is finally rinsed；Wherein, time woven, end count is 215
/ 10cm, filling density is 185/10cm；During kiering, water adds nickel sulfate and propanoic acid that molar concentration is 8mmol/L, sulphuric acid
Nickel and propanoic acid molar concentration rate are 6:1.During kiering, water temperature controls at 75 DEG C, and the kiering time is 1.5 hours.
Embodiment 5: the making of the non-twist cloth of towel
To twist cotton yarn and polyvinyl reverse-winding, and form cotton dimension folded yarn, tie up folded yarn with cotton and make weft yarn, warp thread made by common cotton yarn,
Carrying out woven, the grey cloth of formation puts into kiering in water, backtwisting, is finally rinsed；Wherein, time woven, end count is 215
/ 10cm, filling density is 185/10cm；During kiering, water adds nickel sulfate and propanoic acid that molar concentration is 8mmol/L, sulphuric acid
Nickel and propanoic acid molar concentration rate are 8:1.During kiering, water temperature controls at 75 DEG C, and the kiering time is 1.5 hours.
Embodiment 6: comparative example, nickel sulfate and propanoic acid molar concentration rate are 5:1
To twist cotton yarn and polyvinyl reverse-winding, and form cotton dimension folded yarn, tie up folded yarn with cotton and make weft yarn, warp thread made by common cotton yarn,
Carrying out woven, the grey cloth of formation puts into kiering in water, backtwisting, is finally rinsed；Wherein, time woven, end count is 215
/ 10cm, filling density is 185/10cm；During kiering, water adds nickel sulfate and propanoic acid that molar concentration is 8mmol/L, sulphuric acid
Nickel and propanoic acid molar concentration rate are 5:1.During kiering, water temperature controls at 75 DEG C, and the kiering time is 1.5 hours.
Embodiment 7: comparative example, nickel sulfate and propanoic acid molar concentration rate are 9:1
To twist cotton yarn and polyvinyl reverse-winding, and form cotton dimension folded yarn, tie up folded yarn with cotton and make weft yarn, warp thread made by common cotton yarn,
Carrying out woven, the grey cloth of formation puts into kiering in water, backtwisting, is finally rinsed；Wherein, time woven, end count is 215
/ 10cm, filling density is 185/10cm；During kiering, water adds nickel sulfate and propanoic acid that molar concentration is 8mmol/L, sulphuric acid
Nickel and propanoic acid molar concentration rate are 9:1.During kiering, water temperature controls at 75 DEG C, and the kiering time is 1.5 hours.
Embodiment 8: effect example
The shrinkage factor of the non-twist cloth of towel of testing example 1～7 preparation, result such as following table respectively.
| Shrinkage factor (%) | |
| Embodiment 1 | Basic ungauged regions |
| Embodiment 4 | 3% |
| Embodiment 5 | 4% |
| Embodiment 6 | 19% |
| Embodiment 7 | 21% |
Embodiment 2,3 test result is basically identical with embodiment 4,5.
Result shows, the non-twist cloth of towel prepared by the inventive method is difficult to contraction distortion, this and nickel sulfate and propanoic acid in water during kiering
Molar concentration rate is relevant, and when nickel sulfate and propanoic acid molar concentration rate are 6～8:1, prepared towel non-twist cloth shrinkage factor is minimum.
The effect of above-described embodiment indicates that the essentiality content of the present invention, but does not limit protection scope of the present invention with this.
It will be understood by those within the art that, technical scheme can be modified or equivalent, and not take off
Essence and protection domain from technical solution of the present invention.
Claims (3)
1. the manufacture method of the non-twist cloth of towel, it is characterised in that: cotton yarn and polyvinyl reverse-winding will be twisted, form cotton dimension conjunction
Stock yarn, makees weft yarn with cotton dimension folded yarn, and warp thread made by common cotton yarn, carries out woven, and the grey cloth of formation puts into kiering in water, backtwisting,
Finally it is rinsed；Wherein, time woven, end count is 200～230/10cm, and filling density is 140～230/10cm；During kiering,
Adding nickel sulfate and propanoic acid that molar concentration is 7～9mmol/L in water, nickel sulfate and propanoic acid molar concentration rate are 6～8:1.
The manufacture method of the non-twist cloth of towel the most according to claim 1, it is characterised in that: during kiering, interpolation mole in water
Concentration be nickel sulfate and the propanoic acid of 8mmol/L, nickel sulfate and propanoic acid molar concentration rate be 7:1.
The manufacture method of the non-twist cloth of towel the most according to claim 1 and 2, it is characterised in that: during kiering, water temperature controls
At 70～80 DEG C, the kiering time is 1～2 hour.