CN103590167A - Left-right-twisted fabric processing and dyeing process - Google Patents
Left-right-twisted fabric processing and dyeing process Download PDFInfo
- Publication number
- CN103590167A CN103590167A CN201310504686.3A CN201310504686A CN103590167A CN 103590167 A CN103590167 A CN 103590167A CN 201310504686 A CN201310504686 A CN 201310504686A CN 103590167 A CN103590167 A CN 103590167A
- Authority
- CN
- China
- Prior art keywords
- yarn
- cloth
- cotton
- fingers
- twisted
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a left-right-twisted fabric processing and dyeing process. The process includes the following steps: (1), reversely winding twisted cotton yarn and vinylon to form cotton-vinylon twisted yarn; (2), taking the cotton-vinylon twisted yarn as weft and common cotton yarn as warp for machine knitting to form blank cloth; (3), placing the blank cloth into water for scouring and untwisting; (4), flushing; (5), washing return size; (6), singeing; (7), performing high-temperature processing and baking; (8), dyeing; (9), shaping a finished product. The fabric formed by the left-right-twisted fabric processing and dyeing process is good in feel and high in wear resistance; the yarn is twisted by a two-for-one twister, so that the fabric is mild in gloss and comparatively steady visually; the yarn after being twisted is far larger than untwisted yarn in strength, and the fabric is far better than untwisted products in wear-resistant performance, and is free of napping and pilling and high in elasticity.
Description
Technical field
The present invention relates to the processing of a kind of cloth and dyeing, relate in particular to that a kind of ABRASION RESISTANCE is good, good springiness, the crease-resistant left and right of anti-folding twist with the fingers the processing of cloth cloth and dyeing.
Background technology
Be no matter that traditional soil spins that soil is knitted or the textile industry of the large production of modernization, the cotton of not twisting is spun not resultant yarn, and the yarn of not twisting can not knitted cloth.Can only adopt now twist yarn weaving.And the maximum characteristic of cotton is fluffy softness, sucting wet air permeability is strong, still, twisting spinning and the process that is woven into cloth just the intrinsic characteristic of cotton had qualitative change, comfort level is affected.
Summary of the invention
For the problems referred to above, main purpose of the present invention is to provide that a kind of ABRASION RESISTANCE is good, good springiness, the crease-resistant left and right of anti-folding are twisted with the fingers the processing of cloth cloth and dyeing.
The present invention solves above-mentioned technical problem by following technical proposals: the processing of cloth cloth and dyeing are twisted with the fingers in a kind of left and right, and described technique comprises the steps:
(1) will twist cotton yarn and dimension wheel reverse-winding, form cotton dimension folded yarn;
(2) above-mentioned cotton dimension folded yarn is made to weft yarn, common cotton yarn is made warp thread, carries out wovenly, forms grey cloth;
Organizine comprises two cocainines, be respectively: T68D/24F FDY+50D/48F POY17T/CM Z twists with the fingers and T68D/24F FDY+50D/48F POY17T/CM S twists with the fingers, tram comprises two cocainines, is respectively: T68D/24F FDY+50D/48F POY17T/CM Z twists with the fingers and T68D/24F FDY+50D/48F POY17T/CM S twists with the fingers;
Machine specification on grey cloth: porter 17.5
#penetrate 4 and enter upper gate width 170cm filling density 36 shuttles;
(3) above-mentioned grey cloth is put into water kiering and backtwisting; During kiering, water temperature is controlled at 60-900C, and the kiering time is 2 hours, and during kiering, the CV value of cotton yarn is less than or equal to 12%;
(4) rinse;
(5) returning pulp-water washes; When returning pulp-water and washing by cloth 0.8-1.4/L return slurry amylase in the 20-40 minute that banks up, temperature is controlled at 60-80 ℃, then with clear water, washs at normal temperatures 5 minutes, bath raio is 1:40;
(6) singe;
(7) high-temperature process and baking and banking up with earth;
(8) dyeing;
(9), finished product is walked type, finished product adopts organizine and tram to make to knit and forms, wherein organizine is processed into polyamide composite filaments bar after adopting nano bamboo-carbon fibre and natural cotton fiber by drafting, rove, spun yarn, winding process, tram adopts spandex fibre and changeable colour sensitization fiber to make spandex chameleon fibre by melt spinning process, and then by scutching cotton, carding step is made.
In a specific embodiment of the present invention: the twist of the twist of twisting cotton yarn during with reverse-winding is identical.
In a specific embodiment of the present invention: twisting cotton yarn adopts 30-150 of the forward twist; Reverse-winding twist during reverse-winding is 30-150.
In a specific embodiment of the present invention: take when woven through close little and institutional framework that filling density is large.
In a specific embodiment of the present invention: during test weaving, through close be 204-220 root/10cm, filling density is 157-220 root/10cm.
Positive progressive effect of the present invention is: the processing of cloth cloth is twisted with the fingers in left and right provided by the invention and dyeing has the following advantages: sense organ is good: yarn is through two-for-one twister twisting, and the gloss of fabric is soft, and visually fabric is more steady.ABRASION RESISTANCE is good: the brute force of the yarn after twisting is far longer than the yarn that there is no twisting, and the anti-wear performance of such fabric is far superior to not have the product of twisting.Reduce pilling: chemical fiber plus material is very serious because the friction of yarn makes the phenomenon of yarn cohesion pilling in wearing process, however yarn by twisting after, increased embracing and degree of fiber in yarn, the phenomenon that reduces pilling occurs; Good springiness: contraction that can be serious in type-approval process through the yarn of twisting is that the door width of fabric significantly reduces, and so just makes the elasticity of fabric fine.Anti-folding is crease-resistant good: the yarn after twisting has good resilience, in the process of making clothing dress, can well avoid wrinkle, even if there is fold also can resilience slowly to restore to the original state.
The specific embodiment
Below in conjunction with specific embodiment, describe technical scheme of the present invention in detail.
Technique of the present invention comprises the steps:
(1), will twist cotton yarn and dimension wheel reverse-winding, the cotton dimension of formation folded yarn;
(2), above-mentioned cotton dimension folded yarn is made to weft yarn, common cotton yarn is made warp thread, carries out wovenly, forms grey cloth;
Organizine comprises two cocainines, be respectively: T68D/24F FDY+50D/48F POY17T/CM Z twists with the fingers and T68D/24F FDY+50D/48F POY17T/CM S twists with the fingers, tram comprises two cocainines, is respectively: T68D/24F FDY+50D/48F POY17T/CM Z twists with the fingers and T68D/24F FDY+50D/48F POY17T/CM S twists with the fingers;
Machine specification on grey cloth: porter 17.5# penetrates 4 and enters upper gate width 170cm filling density 36 shuttles;
(3), above-mentioned grey cloth is put into water kiering, backtwisting;
(4), rinse;
(5), returning pulp-water washes;
(6), singe;
(7), high-temperature process and baking and banking up with earth;
(8) dyeing;
(9), finished product is walked type.
The twist of the twist of twisting cotton yarn during with reverse-winding is identical.In implementation process specifically, twisting cotton yarn adopts the forward twist can elect 30-150 as; Reverse-winding twist during reverse-winding can be elected 30-150 as.
When woven, take through close little, institutional framework that filling density is large, during test weaving, through close be 204-220 root/10cm, filling density is 157-220 root/10cm, during kiering, water temperature is controlled at 60-900C, the kiering time is 2 hours, during kiering, the CV value of cotton yarn is less than or equal to 12%.
When returning pulp-water in described step (5) and washing by cloth 0.8-1.4/L return slurry amylase in the 20-40 minute that banks up, temperature is controlled at 60-80 ℃, then with clear water, washs at normal temperatures 5 minutes, bath raio is 1:40.
Finished product in described step (9) adopts organizine and tram to make to knit and forms, wherein organizine is processed into polyamide composite filaments bar after adopting nano bamboo-carbon fibre and natural cotton fiber by drafting, rove, spun yarn, winding process, tram adopts spandex fibre and changeable colour sensitization fiber to make spandex chameleon fibre by melt spinning process, and then by scutching cotton, carding step is made.
Below specific embodiment:
Embodiment 1:
Technique of the present invention comprises the steps:
(1), will twist cotton yarn and dimension wheel reverse-winding, the cotton dimension of formation folded yarn;
(2), above-mentioned cotton dimension folded yarn is made to weft yarn, common cotton yarn is made warp thread, carries out wovenly, forms grey cloth;
Organizine comprises two cocainines, be respectively: T68D/24F FDY+50D/48F POY17T/CM Z twists with the fingers and T68D/24F FDY+50D/48F POY17T/CM S twists with the fingers, tram comprises two cocainines, is respectively: T68D/24F FDY+50D/48F POY17T/CM Z twists with the fingers and T68D/24F FDY+50D/48F POY17T/CM S twists with the fingers;
Machine specification on grey cloth: porter 17.5# penetrates 4 and enters upper gate width 170cm filling density 36 shuttles;
(3), above-mentioned grey cloth is put into water kiering, backtwisting;
(4), rinse;
(5), returning pulp-water washes;
(6), singe;
(7), high-temperature process and baking and banking up with earth;
(8) dyeing;
(9), finished product is walked type.
The twist of the twist of twisting cotton yarn during with reverse-winding is identical.In implementation process specifically, twisting cotton yarn adopts the forward twist can elect 30 as; Reverse-winding twist during reverse-winding can be elected 30 as.
When woven, take through close little, institutional framework that filling density is large, during test weaving, through close be 204-220 root/10cm, filling density is 157-220 root/10cm, during kiering, water temperature is controlled at 60 ℃, the kiering time is 2 hours, during kiering, the CV value of cotton yarn is less than or equal to 12%.
When returning pulp-water in described step (5) and washing by cloth 0.8-1.4/L return slurry amylase in bank up 20 minutes, temperature is controlled at 60 ℃, then with clear water, washs at normal temperatures 5 minutes, bath raio is 1:40.
Finished product in described step (9) adopts organizine and tram to make to knit and forms, wherein organizine is processed into polyamide composite filaments bar after adopting nano bamboo-carbon fibre and natural cotton fiber by drafting, rove, spun yarn, winding process, tram adopts spandex fibre and changeable colour sensitization fiber to make spandex chameleon fibre by melt spinning process, and then by scutching cotton, carding step is made.
Embodiment 2:
Technique of the present invention comprises the steps:
(1), will twist cotton yarn and dimension wheel reverse-winding, the cotton dimension of formation folded yarn;
(2), above-mentioned cotton dimension folded yarn is made to weft yarn, common cotton yarn is made warp thread, carries out wovenly, forms grey cloth;
Organizine comprises two cocainines, be respectively: T68D/24F FDY+50D/48F POY17T/CM Z twists with the fingers and T68D/24F FDY+50D/48F POY17T/CM S twists with the fingers, tram comprises two cocainines, is respectively: T68D/24F FDY+50D/48F POY17T/CM Z twists with the fingers and T68D/24F FDY+50D/48F POY17T/CM S twists with the fingers;
Machine specification on grey cloth: porter 17.5
#penetrate 4 and enter upper gate width 170cm filling density 36 shuttles;
(3), above-mentioned grey cloth is put into water kiering, backtwisting;
(4), rinse;
(5), returning pulp-water washes;
(6), singe;
(7), high-temperature process and baking and banking up with earth;
(8) dyeing;
(9), finished product is walked type.
The twist of the twist of twisting cotton yarn during with reverse-winding is identical.In implementation process specifically, twisting cotton yarn adopts the forward twist can elect 50 as; Reverse-winding twist during reverse-winding can be elected 50 as.
When woven, take through close little, institutional framework that filling density is large, during test weaving, through close be 204-220 root/10cm, filling density is 157-220 root/10cm, during kiering, water temperature is controlled at 70 ℃, the kiering time is 2 hours, during kiering, the CV value of cotton yarn is less than or equal to 12%.
When returning pulp-water in described step (5) and washing by cloth 0.8-1.4/L return slurry amylase in bank up 30 minutes, temperature is controlled at 60 ℃, then with clear water, washs at normal temperatures 5 minutes, bath raio is 1:40.
Finished product in described step (9) adopts organizine and tram to make to knit and forms, wherein organizine is processed into polyamide composite filaments bar after adopting nano bamboo-carbon fibre and natural cotton fiber by drafting, rove, spun yarn, winding process, tram adopts spandex fibre and changeable colour sensitization fiber to make spandex chameleon fibre by melt spinning process, and then by scutching cotton, carding step is made.
Embodiment 3:
Technique of the present invention comprises the steps:
(1), will twist cotton yarn and dimension wheel reverse-winding, the cotton dimension of formation folded yarn;
(2), above-mentioned cotton dimension folded yarn is made to weft yarn, common cotton yarn is made warp thread, carries out wovenly, forms grey cloth;
Organizine comprises two cocainines, be respectively: T68D/24F FDY+50D/48F POY17T/CM Z twists with the fingers and T68D/24F FDY+50D/48F POY17T/CM S twists with the fingers, tram comprises two cocainines, is respectively: T68D/24F FDY+50D/48F POY17T/CM Z twists with the fingers and T68D/24F FDY+50D/48F POY17T/CM S twists with the fingers;
Machine specification on grey cloth: porter 17.5
#penetrate 4 and enter upper gate width 170cm filling density 36 shuttles;
(3), above-mentioned grey cloth is put into water kiering, backtwisting;
(4), rinse;
(5), returning pulp-water washes;
(6), singe;
(7), high-temperature process and baking and banking up with earth;
(8) dyeing;
(9), finished product is walked type.
The twist of the twist of twisting cotton yarn during with reverse-winding is identical.In implementation process specifically, twisting cotton yarn adopts the forward twist can elect 100 as; Reverse-winding twist during reverse-winding can be elected 100 as.
When woven, take through close little, institutional framework that filling density is large, during test weaving, through close be 204-220 root/10cm, filling density is 157-220 root/10cm, during kiering, water temperature is controlled at 80 ℃, the kiering time is 2 hours, during kiering, the CV value of cotton yarn is less than or equal to 12%.
When returning pulp-water in described step (5) and washing by cloth 0.8-1.4/L return slurry amylase in bank up 40 minutes, temperature is controlled at 70 ℃, then with clear water, washs at normal temperatures 5 minutes, bath raio is 1:40.
Finished product in described step (9) adopts organizine and tram to make to knit and forms, wherein organizine is processed into polyamide composite filaments bar after adopting nano bamboo-carbon fibre and natural cotton fiber by drafting, rove, spun yarn, winding process, tram adopts spandex fibre and changeable colour sensitization fiber to make spandex chameleon fibre by melt spinning process, and then by scutching cotton, carding step is made.
Embodiment 4:
Technique of the present invention comprises the steps:
(1), will twist cotton yarn and dimension wheel reverse-winding, the cotton dimension of formation folded yarn;
(2), above-mentioned cotton dimension folded yarn is made to weft yarn, common cotton yarn is made warp thread, carries out wovenly, forms grey cloth;
Organizine comprises two cocainines, be respectively: T68D/24F FDY+50D/48F POY17T/CM Z twists with the fingers and T68D/24F FDY+50D/48F POY17T/CM S twists with the fingers, tram comprises two cocainines, is respectively: T68D/24F FDY+50D/48F POY17T/CM Z twists with the fingers and T68D/24F FDY+50D/48F POY17T/CM S twists with the fingers;
Machine specification on grey cloth: porter 17.5
#penetrate 4 and enter upper gate width 170cm filling density 36 shuttles;
(3), above-mentioned grey cloth is put into water kiering, backtwisting;
(4), rinse;
(5), returning pulp-water washes;
(6), singe;
(7), high-temperature process and baking and banking up with earth;
(8) dyeing;
(9), finished product is walked type.
The twist of the twist of twisting cotton yarn during with reverse-winding is identical.In implementation process specifically, twisting cotton yarn adopts the forward twist can elect 150 as; It is 150 that reverse-winding twist during reverse-winding can be elected as.
When woven, take through close little, institutional framework that filling density is large, during test weaving, through close be 204-220 root/10cm, filling density is 157-220 root/10cm, during kiering, water temperature is controlled at 90 ℃, the kiering time is 2 hours, during kiering, the CV value of cotton yarn is less than or equal to 12%.
When returning pulp-water in described step (5) and washing by cloth 0.8-1.4/L return slurry amylase in bank up 40 minutes, temperature is controlled at 80 ℃, then with clear water, washs at normal temperatures 5 minutes, bath raio is 1:40.
Finished product in described step (9) adopts organizine and tram to make to knit and forms, wherein organizine is processed into polyamide composite filaments bar after adopting nano bamboo-carbon fibre and natural cotton fiber by drafting, rove, spun yarn, winding process, tram adopts spandex fibre and changeable colour sensitization fiber to make spandex chameleon fibre by melt spinning process, and then by scutching cotton, carding step is made.
Left and right provided by the invention sth. made by twisting cloth cloth processing and dyeing sense organ are good: yarn is through two-for-one twister twisting, and the gloss of fabric is soft, and visually fabric is more steady.ABRASION RESISTANCE is good: the brute force of the yarn after twisting is far longer than the yarn that there is no twisting, and the anti-wear performance of such fabric is far superior to not have the product of twisting.Reduce pilling: chemical fiber plus material is very serious because the friction of yarn makes the phenomenon of yarn cohesion pilling in wearing process, however yarn by twisting after, increased embracing and degree of fiber in yarn, the phenomenon that reduces pilling occurs; Good springiness: contraction that can be serious in type-approval process through the yarn of twisting is that the door width of fabric significantly reduces, and so just makes the elasticity of fabric fine.Anti-folding is crease-resistant good: the yarn after twisting has good resilience, in the process of making clothing dress, can well avoid wrinkle, even if there is fold also can resilience slowly to restore to the original state.
More than show and described basic principle of the present invention and principal character and advantage of the present invention.The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; that in above-described embodiment and description, describes just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications; these changes and improvements all fall in the claimed scope of the invention, and the claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (5)
1. the processing of cloth cloth and a dyeing are twisted with the fingers in left and right, it is characterized in that: described technique comprises the steps:
(1) will twist cotton yarn and dimension wheel reverse-winding, form cotton dimension folded yarn;
(2) above-mentioned cotton dimension folded yarn is made to weft yarn, common cotton yarn is made warp thread, carries out wovenly, forms grey cloth;
Organizine comprises two cocainines, be respectively: T68D/24F FDY+50D/48F POY17T/CM Z twists with the fingers and T68D/24F FDY+50D/48F POY17T/CM S twists with the fingers, tram comprises two cocainines, is respectively: T68D/24F FDY+50D/48F POY17T/CM Z twists with the fingers and T68D/24F FDY+50D/48F POY17T/CM S twists with the fingers;
Machine specification on grey cloth: porter 17.5
#penetrate 4 and enter upper gate width 170cm filling density 36 shuttles;
(3) above-mentioned grey cloth is put into water kiering and backtwisting; During kiering, water temperature is controlled at 60-900C, and the kiering time is 2 hours, and during kiering, the CV value of cotton yarn is less than or equal to 12%;
(4) rinse;
(5) returning pulp-water washes; When returning pulp-water and washing by cloth 0.8-1.4/L return slurry amylase in the 20-40 minute that banks up, temperature is controlled at 60-80 ℃, then with clear water, washs at normal temperatures 5 minutes, bath raio is 1:40;
(6) singe;
(7) high-temperature process and baking and banking up with earth;
(8) dyeing;
(9), finished product is walked type, finished product adopts organizine and tram to make to knit and forms, wherein organizine is processed into polyamide composite filaments bar after adopting nano bamboo-carbon fibre and natural cotton fiber by drafting, rove, spun yarn, winding process, tram adopts spandex fibre and changeable colour sensitization fiber to make spandex chameleon fibre by melt spinning process, and then by scutching cotton, carding step is made.
2. the processing of cloth cloth and dyeing are twisted with the fingers in left and right according to claim 1, it is characterized in that: the twist of the twist of twisting cotton yarn during with reverse-winding is identical.
3. the processing of cloth cloth and dyeing are twisted with the fingers in left and right according to claim 1, it is characterized in that: twisting cotton yarn adopts 30-150 of the forward twist; Reverse-winding twist during reverse-winding is 30-150.
4. the processing of cloth cloth and dyeing are twisted with the fingers in left and right according to claim 1, it is characterized in that: when woven, take through close little and institutional framework that filling density is large.
5. the processing of cloth cloth and dyeing are twisted with the fingers in left and right according to claim 1, it is characterized in that: during test weaving, through close be 204-220 root/10cm, filling density is 157-220 root/10cm.