CN105944535A - Air purification spray for formaldehyde removal and preparation method of air purification spray - Google Patents
Air purification spray for formaldehyde removal and preparation method of air purification spray Download PDFInfo
- Publication number
- CN105944535A CN105944535A CN201610309808.7A CN201610309808A CN105944535A CN 105944535 A CN105944535 A CN 105944535A CN 201610309808 A CN201610309808 A CN 201610309808A CN 105944535 A CN105944535 A CN 105944535A
- Authority
- CN
- China
- Prior art keywords
- air cleaning
- cleaning spray
- spray
- weight portions
- formaldehyde air
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an air purification spray for formaldehyde removal. Chitin and nano-silicon powder are taken as effective raw material components ,are proportioned properly and can sufficiently play a synergistic role, the finally prepared air purification spray for formaldehyde removal contains a large quantity of stable and unsaturated positive charge structures and active amino groups, so that on the one hand, the unsaturated positive charge structures are used for adsorbing small-molecular free formaldehyde and other substances, on the other hand, the active amino groups are used for decomposing free formaldehyde, formaldehyde is converted into equimolar water, and a reaction equation is CH2O+H2NR H2CNR+H2O; besides, the spray can produce a strong negative electric field, and the negative electric field can effectively kill harmful microorganisms and bacteria in the air while adsorbing free formaldehyde and VOCs (volatile organic compounds) in the air.
Description
Technical field
The invention belongs to air purification field, be specifically related to a kind of except formaldehyde air cleaning spray and preparation thereof
Method.
Background technology
The interior product category of indoor cart is various, used raw material substantially wood-base fibre and particle panel material, adhesive, skin
Leather, cloth, sponge, wallpaper, stone material, glass, pottery etc..Different qualities is used between various raw materials
Adhesive bonding, and in adhesive, a large amount of formaldehyde of content is as solvent, therefore, with product meeting in indoor cart
Constantly produce the volatile harmful material such as free formaldehyde, VOCs.Free formaldehyde is judged by World Health Organization (WHO)
For one-level carcinogen, the most releasable 15 years of the formaldehyde in wood-base fibre and particle panel material.
Windowing is the better method of volatile harmful material in release indoor cart, but the PM2.5 index of outdoor is remote
Higher than indoor.Window for a long time and can make the amount of dust accumulation superposition of indoor, be a kind of serious air pollution equally.
If haze sky, people dare not window at all, and therefore indoor formaldehyde just cannot eliminate.Night, Ren Menguan
Door is when closing window rest, and the indoor concentration of formaldehyde that dissociates is higher, and hazardness is bigger.
Conventional indoor air purification product has: (1) air purifier, acts primarily as filtration;(2)
Activated carbon, plays adsorption;(3) photocatalyst, with harmful gass such as decomposing formaldehydes, but can need effective light
Source, and preferably ultraviolet light;(4) amino-compound (ammonium chloride, carbamide etc.), reacts with formaldehyde,
But ammonia can be discharged, same contaminated air.
Summary of the invention
In order to solve the problems referred to above that prior art exists, the invention provides that a kind of safety is high, formaldehyde goes
Except rate high except formaldehyde air cleaning spray and preparation method thereof.
The technical solution adopted in the present invention is:
A kind of except formaldehyde air cleaning spray, raw material components includes:
Chitin, 2.5~20 weight portions;
Nano silica fume, 2.5~20 weight portions;
Deionized water, 55~95 weight portions.
The most described raw material components removing formaldehyde air cleaning spray includes:
Chitin, 5~15 weight portions;
Nano silica fume, 5~15 weight portions;
Deionized water, 70~75 weight portions.
The particle diameter of described nano silica fume is 5~100nm.
Described except formaldehyde air cleaning spray raw material components is also added with the auxiliary agent of 0.1~5 weight portions, described
Auxiliary agent is one or more in polyvinyl alcohol, acrylic resin, camphor leaf extract, eucalyptus leaves extract
Mixture with arbitrary proportion composition.
Described camphor leaf extract is adopted and is prepared with the following method:
(S1) Folium cinnamomi camphorae is dried, pulverization process, obtain the Folium cinnamomi camphorae that particle diameter is 80~120 mesh thin
Powder;
(S2) in the Folium cinnamomi camphorae fine powder described in step (S1), add the water of 6~9 times of quality, 0.1~
0.5MPa, carry out water under the conditions of 40~50 DEG C and carry 3~6h, filter, obtain extracting solution;
(S3) extracting solution described in step (S2) is heated at-0.04~-0.07MPa, 40~50 DEG C
Concentrate 2~5h, obtain concentrated solution;
(S4) step (S3) described concentrated solution is spray-dried, obtains camphor leaf extract.
Described eucalyptus leaves extract is adopted and is prepared with the following method:
(S1) eucalyptus leaves is dried, pulverization process, obtain the eucalyptus leaves fine powder that particle diameter is 50~80 mesh;
(S2) in the eucalyptus leaves fine powder described in step (S1), add the water of 6~9 times of quality, 0.1~
0.5MPa, carry out water under the conditions of 30~40 DEG C and carry 2~3h, filter, obtain extracting solution;
(S3) extracting solution described in step (S2) is heated at-0.06~-0.09MPa, 30~40 DEG C
Concentrate 2~3h, obtain concentrated solution;
(S4) step (S3) described concentrated solution is spray-dried, obtains eucalyptus leaves extract.
A kind of prepare described in claim except the method for formaldehyde air cleaning spray, comprise the steps:
(1) weigh described chitin and described nano silica fume respectively, and carry out being sufficiently mixed uniformly, mixed
Compound material;
(2) step (1) described mixed material is added in described deionized water, 180~220r/min
Stir 1~3h under mixing speed, obtain described except formaldehyde air cleaning spray.
The most described except the formaldehyde preparation method of air cleaning spray, comprise the steps:
(1) weigh described auxiliary agent and add in described deionized water, heating under agitation, make described in help
Agent is completely dissolved in water, obtains dispersion liquid;
(2) weigh described chitin and described nano silica fume respectively, and carry out being sufficiently mixed uniformly, mixed
Compound material;
(3) step (2) described mixed material is added in step (1) described dispersion liquid, 180~220r/min
Stir 1~3h under mixing speed, obtain described except formaldehyde air cleaning spray.
In step (1), the temperature carrying out described heating is 80~90 DEG C, and the time carrying out described heating is
0.5-2h。
The invention have the benefit that
Of the present invention except formaldehyde air cleaning spray, use chitin and nano silica fume as the most former
Material component also carries out suitable proportioning, and chitin and two kinds of components of nano silica fume can give full play to synergism,
Ultimately form except in formaldehyde air cleaning spray, do not contain only a large amount of stable unsaturated positive charge structure,
Possibly together with active amino, thus on the one hand utilize unsaturated positive charge structure to things such as the free formaldehydes of little molecule
Matter is adsorbed, and also utilizes active amino to decompose free formaldehyde, and formaldehyde is converted into equimolar water,
Reaction equation is CH2O+H2NR→H2CNR+H2O;Additionally, described spray can produce powerful bearing
Electric field, this negative electric field is while adsorbing the free formaldehyde in air, VOCs, moreover it is possible to effectively kill
Harmful microorganism in evil air and antibacterial.Detect according to QB/T 2761-2006, of the present invention except first
Aldehyde air cleaning spray is more than 95% to the clearance of indoor free formaldehyde.Remove additionally, of the present invention
Formaldehyde is high with air cleaning spray safety, non-stimulated to human body skin, avirulence, does not results in secondary dirty
Dye.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described in detail.
Embodiment 1
The present embodiment provides one except formaldehyde air cleaning spray, and raw material components includes:
Chitin (Taiwan Eastern Zhou Dynasty chemical industry provides), 2.5 weight portions;
Particle diameter is the nano silica fume (healthy family international bio science and technology provides) of 5,20 weight portions;
Deionized water, 55 weight portions.
A kind of described except the method for formaldehyde air cleaning spray, comprise the steps:
(1) weigh described chitin and described nano silica fume respectively, and carry out being sufficiently mixed uniformly, mixed
Compound material;
(2) step (1) described mixed material is added in described deionized water, in 180r/min stirring speed
Stir 3h under degree, obtain described except formaldehyde air cleaning spray.
Embodiment 2
The present embodiment provides one except formaldehyde air cleaning spray, and raw material components includes:
Chitin (Taiwan Eastern Zhou Dynasty chemical industry provides), 20 weight portions;
Particle diameter is the nano silica fume (healthy family international bio science and technology provides) of 100nm, 2.5 weight portions;
Polyvinyl alcohol (silver cyclisation work in Guangzhou provides), 5 weight portions;
Deionized water, 95 weight portions.
A kind of described except the method for formaldehyde air cleaning spray, comprise the steps:
(1) weigh described polyvinyl alcohol and add in described deionized water, under agitation, 80 DEG C carry out
Heating 2h, makes described polyvinyl alcohol be completely dissolved in water, obtains dispersion liquid;
(2) weigh described chitin and described nano silica fume respectively, and carry out being sufficiently mixed uniformly, mixed
Compound material;
(3) step (2) described mixed material is added in step (1) described dispersion liquid, at 220r/min
Stir 1h under mixing speed, obtain described except formaldehyde air cleaning spray.
Embodiment 3
The present embodiment provides one except formaldehyde air cleaning spray, and raw material components includes:
Chitin (Taiwan Eastern Zhou Dynasty chemical industry provides), 5 weight portions;
Particle diameter is the nano silica fume (healthy family international bio science and technology provides) of 40nm, 15 weight portions;
Acrylic resin (Taiwan remembers that making paint industry provides forever), 5 weight portions;
Deionized water, 70 weight portions.
A kind of described except the method for formaldehyde air cleaning spray, comprise the steps:
(1) weigh described polyvinyl alcohol and add in described deionized water, under agitation, 90 DEG C carry out
Heating 0.5h, makes described polyvinyl alcohol be completely dissolved in water, obtains dispersion liquid;
(2) weigh described chitin and described nano silica fume respectively, and carry out being sufficiently mixed uniformly, mixed
Compound material;
(3) step (2) described mixed material is added in step (1) described dispersion liquid, at 200r/min
Stir 2h under mixing speed, obtain described except formaldehyde air cleaning spray.
Embodiment 4
The present embodiment provides one except formaldehyde air cleaning spray, and raw material components includes:
Chitin (Taiwan Eastern Zhou Dynasty chemical industry provides), 15 weight portions;
Particle diameter is the nano silica fume (healthy family international bio science and technology provides) of 40nm, 5 weight portions;
Acrylic resin (Taiwan remembers that making paint industry provides forever), 2.5 weight portions;
Deionized water, 75 weight portions.
A kind of described except the method for formaldehyde air cleaning spray, comprise the steps:
(1) weigh described polyvinyl alcohol and add in described deionized water, under agitation, 90 DEG C carry out
Heating 0.5h, makes described polyvinyl alcohol be completely dissolved in water, obtains dispersion liquid;
(2) weigh described chitin and described nano silica fume respectively, and carry out being sufficiently mixed uniformly, mixed
Compound material;
(3) step (2) described mixed material is added in step (1) described dispersion liquid, at 200r/min
Stir 2h under mixing speed, obtain described except formaldehyde air cleaning spray.
Embodiment 5
The present embodiment provides one except formaldehyde air cleaning spray, and raw material components includes:
Chitin (Taiwan Eastern Zhou Dynasty chemical industry provides), 10 weight portions;
Particle diameter is the nano silica fume (healthy family international bio science and technology provides) of 40nm, 10 weight portions;
Polyvinyl alcohol (silver cyclisation work in Guangzhou provides), 12 weight portions;
Deionized water, 72 weight portions.
A kind of described except the method for formaldehyde air cleaning spray, comprise the steps:
(1) weigh described polyvinyl alcohol and add in described deionized water, under agitation, 85 DEG C carry out
Heating 0.5h, makes described polyvinyl alcohol be completely dissolved in water, obtains dispersion liquid;
(2) weigh described chitin and described nano silica fume respectively, and carry out being sufficiently mixed uniformly, mixed
Compound material;
(3) step (2) described mixed material is added in step (1) described dispersion liquid, at 200r/min
Stir 2h under mixing speed, obtain described except formaldehyde air cleaning spray.
Embodiment 6
Each raw material dosage of the present embodiment and operating condition are the most same as in Example 5, differ only in: use
Polyvinyl alcohol in camphor leaf extract alternate embodiment 5.
Wherein, described camphor leaf extract is adopted and is prepared with the following method:
(S1) Folium cinnamomi camphorae is dried, pulverization process, obtain the Folium cinnamomi camphorae fine powder that particle diameter is 80 mesh;
(S2) in the Folium cinnamomi camphorae fine powder described in step (S1) add 6 times of quality water, 0.1MPa,
Carry out water under the conditions of 40 DEG C and carry 6h, filter, obtain extracting solution;
(S3) extracting solution described in step (S2) is carried out heating at-0.04,40 DEG C and concentrate 5h, obtain dense
Contracting liquid;
(S4) step (S3) described concentrated solution is spray-dried, obtains camphor leaf extract.
Embodiment 7
Each raw material dosage of the present embodiment and operating condition are the most same as in Example 6, differ only in: described
Camphor leaf extract is adopted and is prepared with the following method:
(S1) Folium cinnamomi camphorae is dried, pulverization process, obtain the Folium cinnamomi camphorae fine powder that particle diameter is 120 mesh;
(S2) in the Folium cinnamomi camphorae fine powder described in step (S1) add 9 times of quality water, 0.5MPa,
Carry out water under the conditions of 50 DEG C and carry 3h, filter, obtain extracting solution;
(S3) by the extracting solution described in step (S2)-0.07MPa, 50 DEG C carry out heating concentrate 2h,
To concentrated solution;
(S4) step (S3) described concentrated solution is spray-dried, obtains camphor leaf extract.
Embodiment 8
Each raw material dosage of the present embodiment and operating condition are the most same as in Example 5, differ only in: use
Polyvinyl alcohol in eucalyptus leaves extract alternate embodiment 5.
Wherein, described eucalyptus leaves extract is adopted and is prepared with the following method:
(S1) eucalyptus leaves is dried, pulverization process, obtain the eucalyptus leaves fine powder that particle diameter is 50 mesh;
(S2) in the eucalyptus leaves fine powder described in step (S1) add 6 times of quality water, 0.1MPa,
Carry out water under the conditions of 30 DEG C and carry 3h, filter, obtain extracting solution;
(S3) by the extracting solution described in step (S2)-0.06MPa, 30 DEG C carry out heating concentrate 3h,
To concentrated solution;
(S4) step (S3) described concentrated solution is spray-dried, obtains eucalyptus leaves extract.
Embodiment 9
Each raw material dosage of the present embodiment and operating condition are the most the same as in Example 8, differ only in: described
Eucalyptus leaves extract is adopted and is prepared with the following method:
(S1) eucalyptus leaves is dried, pulverization process, obtain the eucalyptus leaves fine powder that particle diameter is 80 mesh;
(S2) in the eucalyptus leaves fine powder described in step (S1) add 9 times of quality water, 0.5MPa,
Carry out water under the conditions of 40 DEG C and carry 2h, filter, obtain extracting solution;
(S3) by the extracting solution described in step (S2)-0.09MPa, 40 DEG C carry out heating concentrate 2h,
To concentrated solution;
(S4) step (S3) described concentrated solution is spray-dried, obtains eucalyptus leaves extract.
Embodiment 10
Each raw material dosage of the present embodiment and operating condition are the most same as in Example 5, differ only in: use
Polyvinyl alcohol, acrylic resin, camphor leaf extract, eucalyptus leaves extract form according to mass ratio 1:1:1:1
Mixture replacing embodiment 5 in polyvinyl alcohol, described camphor leaf extract uses the side in embodiment 6
Method prepares, and described eucalyptus leaves extract prepares according to the method in embodiment 8.
Experimental example
One, detection project: repeatedly intact skin irritant test
1, material and animal
(1) given the test agent: spray stock solution described in Example 5 is given the test agent.
(2) animal: healthy without dermatosis New Zealand white rabbit 4, regular grade, body weight 2.3-2.5kg, gold
Kind warren, mound provides, animal productiong credit number: SCXK (Soviet Union) 2012-003, and animal feed is originated
And card number: work in coordination with medical bioengineering company limited in Jiangsu Province, and card (2014) 01008 is raised by Soviet Union.
(3) experimental condition: laboratory animal environment uses credit number: SYXK (Soviet Union) 2012-0036;
Ambient temperature: 22 ± 2 DEG C;Relative humidity: 40-70%;Key instrument: pedometer (05-324).
2, method
(1) test basis: Ministry of Public Health (version in 2002) " disinfection technology standard " Part II 2.3.3 skin
Skin stimulates real test.
(2) test method: testing the day before yesterday, cut by family's rabbit back spinal column diamond wool, unhairing scope is respectively
3cm*3cm.During test, take tested material about 0.5ml and spread upon on the skin of unhairing of side, opposite side unhaired hide
Skin, as blank, application area 2.5cm*2.5cm, is smeared 1 time, is smeared 14d continuously every day.Smear
Rear 4h, cleans with warm water, removes residue, and observed result after 24h, according to " disinfection technology standard " (2002
Year version) in table 2-11 scoring, check plot processes as test block.By " disinfection technology is advised at the end of experiment
Model " table 2-12 carries out skin irritation strength grading in (version in 2002).Result such as table 1.
Table 1-spray of the present invention is to rabbit repeatedly intact skin irritation test result
Conclusion: spray sample described in the embodiment of the present invention 5 is equal to rabbit repeatedly intact skin irritant reaction integration
Value is 0, and stimulus intensity is nonirritant.
Two, detection project: acute oral toxicity test
1, material and animal
(1) given the test agent: spray stock solution described in Example 5 is given the test agent.
(2) animal: SPF level health ICR mice 20, body weight 18.2-21.7g, Beijing dimension tonneau China is real
Test zoo technical company limited to provide, male and female half and half, animal productiong credit number: SCXK (capital) 2012-0001
Number, animal feed source and card number: work in coordination with medical bioengineering company limited in Jiangsu Province, card (2014) is raised by Soviet Union
No. 01008.
(3) experimental condition: the barrier environment of laboratory animals uses credit number: SYXK (Soviet Union) 2012-0037
Number;Ambient temperature: 22 ± 2 DEG C;Relative humidity: 40-70%;Key instrument: electronic scale (numbering 05-705),
Electronic balance (numbering 05-314).
2, method
(1) test basis: Ministry of Public Health (version in 2002) " disinfection technology standard " Part II 2.3.1 is anxious
Property Oral toxicity test.
(2) test method: test the most to greatest extent.Design dosage is 5000mg/kg b.wt., weighs and is subject to
Test agent (spray described in the present embodiment 5) 5000mg adds pure water and is made into given the test agent liquid to 20ml.Little
After Mus overnight fasting, gavage of per os gives, and gavage capacity is 5000mg/kg b.wt..After gavage, 4g gives
Food, 1 day observation period.Obvious poisoning manifestations is had no after mouse stomach, without animal dead in the observation period, test
Animal dead the results are shown in Table 2.
Table 2-spray of the present invention is to chmice acute Oral toxicity result of the test
Conclusion: spray sample of the present invention is all higher than 5000mg/kg to male and female chmice acute LD50 of passing through mouth value
B.wt., the nontoxic level in true border.
Three, detection project: formaldehyde clearance
Detect according to QB/T 2761-2006 prescriptive procedure, described in the embodiment of the present invention 5 except formaldehyde air
Purify the spray clearance to indoor free formaldehyde more than 95%.
The present invention is not limited to above-mentioned preferred forms, and anyone can draw it under the enlightenment of the present invention
His various forms of products, no matter but in its shape or structure, make any change, every have and the application
Technical scheme as same or like, within all falling within protection scope of the present invention.
Claims (9)
1. one kind is removed formaldehyde air cleaning spray, it is characterised in that raw material components includes:
Chitin, 2.5~20 weight portions;
Nano silica fume, 2.5~20 weight portions;
Deionized water, 55~95 weight portions.
The most according to claim 1 except formaldehyde air cleaning spray, it is characterised in that raw material group
Divide and include:
Chitin, 5~15 weight portions;
Nano silica fume, 5~15 weight portions;
Deionized water, 70~75 weight portions.
The most according to claim 1 except formaldehyde air cleaning spray, it is characterised in that described in receive
The particle diameter of rice silica flour is 5~100nm.
The most according to claim 1 except formaldehyde air cleaning spray, it is characterised in that raw material group
Being also added with the auxiliary agent of 0.1~5 weight portions in Fen, described auxiliary agent is polyvinyl alcohol, acrylic resin, Folium cinnamomi camphorae
The mixture that one or more in extract, eucalyptus leaves extract form with arbitrary proportion.
The most according to claim 4 except formaldehyde air cleaning spray, it is characterised in that described Camphor tree
Leaf extract is adopted and is prepared with the following method:
(S1) Folium cinnamomi camphorae is dried, pulverization process, obtain the Folium cinnamomi camphorae that particle diameter is 80~120 mesh thin
Powder;
(S2) in the Folium cinnamomi camphorae fine powder described in step (S1), add the water of 6~9 times of quality, 0.1~
0.5MPa, carry out water under the conditions of 40~50 DEG C and carry 3~6h, filter, obtain extracting solution;
(S3) extracting solution described in step (S2) is heated at-0.04~-0.07MPa, 40~50 DEG C
Concentrate 2~5h, obtain concentrated solution;
(S4) step (S3) described concentrated solution is spray-dried, obtains camphor leaf extract.
The most according to claim 4 except formaldehyde air cleaning spray, it is characterised in that described eucalyptus globulus
Leaf extract is adopted and is prepared with the following method:
(S1) eucalyptus leaves is dried, pulverization process, obtain the eucalyptus leaves fine powder that particle diameter is 50~80 mesh;
(S2) in the eucalyptus leaves fine powder described in step (S1), add the water of 6~9 times of quality, 0.1~
0.5MPa, carry out water under the conditions of 30~40 DEG C and carry 2~3h, filter, obtain extracting solution;
(S3) extracting solution described in step (S2) is heated at-0.06~-0.09MPa, 30~40 DEG C
Concentrate 2~3h, obtain concentrated solution;
(S4) step (S3) described concentrated solution is spray-dried, obtains eucalyptus leaves extract.
7. prepare described in any one of claim 1-3 except a method for formaldehyde air cleaning spray, its
It is characterised by, comprises the steps:
(1) weigh described chitin and described nano silica fume respectively, and carry out being sufficiently mixed uniformly, mixed
Compound material;
(2) step (1) described mixed material is added in described deionized water, 180~220r/min
Stir 1~3h under mixing speed, obtain described except formaldehyde air cleaning spray.
8. prepare described in any one of claim 4-6 except a method for formaldehyde air cleaning spray, its
It is characterised by, comprises the steps:
(1) weigh described auxiliary agent and add in described deionized water, heating under agitation, make described in help
Agent is completely dissolved in water, obtains dispersion liquid;
(2) weigh described chitin and described nano silica fume respectively, and carry out being sufficiently mixed uniformly, mixed
Compound material;
(3) step (2) described mixed material is added in step (1) described dispersion liquid, 180~220r/min
Stir 1~3h under mixing speed, obtain described except formaldehyde air cleaning spray.
It is the most according to claim 8 except the preparation method of formaldehyde air cleaning spray, it is characterised in that
In step (1), the temperature carrying out described heating is 80~90 DEG C, and the time carrying out described heating is 0.5-2h.