CN105924049A - 一种干熄焦炉用混凝土 - Google Patents

一种干熄焦炉用混凝土 Download PDF

Info

Publication number
CN105924049A
CN105924049A CN201610314380.5A CN201610314380A CN105924049A CN 105924049 A CN105924049 A CN 105924049A CN 201610314380 A CN201610314380 A CN 201610314380A CN 105924049 A CN105924049 A CN 105924049A
Authority
CN
China
Prior art keywords
parts
concrete
quenching furnace
dry quenching
calcium carbonate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610314380.5A
Other languages
English (en)
Inventor
赵西建
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JURONG LIANZHONG TECHNOLOGY DEVELOPMENT Co Ltd
Original Assignee
JURONG LIANZHONG TECHNOLOGY DEVELOPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JURONG LIANZHONG TECHNOLOGY DEVELOPMENT Co Ltd filed Critical JURONG LIANZHONG TECHNOLOGY DEVELOPMENT Co Ltd
Priority to CN201610314380.5A priority Critical patent/CN105924049A/zh
Publication of CN105924049A publication Critical patent/CN105924049A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种干熄焦炉用混凝土,包括以下重量份数的组分:水泥100~150份,鹅卵石180~240份,河沙80~120份,甘油三酯60~90份,碳酸钙40~50份,二氧化硅30~60份,水120~180份。本发明与传统技术相比,配方科学,原料成本低,适用于干熄焦炉的建设,同时,无污染,对周围环境无害。

Description

一种干熄焦炉用混凝土
技术领域
本发明属于建筑工程材料领域,具体涉及一种干熄焦炉用混凝土。
背景技术
混凝土是当代最主要的土木工程材料之一。它是由胶凝材料,颗粒状集料(也称为骨料),水,以及必要时加入的外加剂和掺合料按一定比例配制,经均匀搅拌,密实成型,养护硬化而成的一种人工石材。混凝土具有原料丰富,价格低廉,生产工艺简单的特点,因而使其用量越来越大。同时混凝土还具有抗压强度高,耐久性好,强度等级范围宽等特点。这些特点使其使用范围十分广泛,不仅在各种土木工程中使用,就是造船业,机械工业,海洋的开发,地热工程等,混凝土也是重要的材料。在实际建筑过程中,根据环境的不同,混凝土的成分以及比例也需要及时调整,以适合不同需求。
发明内容
发明目的:本发明的目的在于针对现有技术的不足,提供一种干熄焦炉用混凝土。
技术方案:为了达到上述发明目的,本发明具体是这样来实现的:一种干熄焦炉用混凝土,包括以下重量份数的组分:水泥100~150份,鹅卵石180~240份,河沙80~120份,甘油三酯60~90份,碳酸钙40~50份,二氧化硅30~60份,水120~180份。
其中,所述河沙含水率小于5%。
其中,所述水泥为硅酸铝水泥。
其中,所述碳酸钙为含水率在5~20%的碳酸钙结晶。
有益效果:本发明与传统技术相比,早期强度较高;凝结硬化速度快,配方科学,原料成本低,适用于干熄焦炉的建设,同时,无污染,对周围环境无害。
具体实施方式
实施例1:
一种干熄焦炉用混凝土,包括以下重量份数的组分:水泥100份,鹅卵石180份,河沙80份,甘油三酯60份,碳酸钙40份,二氧化硅30份,水120份。
实施例2:
一种干熄焦炉用混凝土,包括以下重量份数的组分:水泥110份,鹅卵石190份,河沙90份,甘油三酯70份,碳酸钙50份,二氧化硅40份,水130份。
实施例3:
一种干熄焦炉用混凝土,包括以下重量份数的组分:水泥120份,鹅卵石200份,河沙100份,甘油三酯80份,碳酸钙40份,二氧化硅50份,水140份。
实施例4:
一种干熄焦炉用混凝土,包括以下重量份数的组分:水泥130份,鹅卵石210份,河沙110份,甘油三酯90份,碳酸钙50份,二氧化硅60份,水150份。
实施例5:
一种干熄焦炉用混凝土,包括以下重量份数的组分:水泥140份,鹅卵石220份,河沙120份,甘油三酯75份,碳酸钙40份,二氧化硅45份,水160份。
实施例6:
一种干熄焦炉用混凝土,包括以下重量份数的组分:水泥150份,鹅卵石240份,河沙95份,甘油三酯85份,碳酸钙50份,二氧化硅55份,水180份。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理的前提下,还可以作出若干改进,这些改进也应视为本发明的保护范围。

Claims (4)

1.一种干熄焦炉用混凝土,其特征在于,包括以下重量份数的组分:水泥100~150份,鹅卵石180~240份,河沙80~120份,甘油三酯60~90份,碳酸钙40~50份,二氧化硅30~60份,水120~180份。
2.根据权利要求1所述的干熄焦炉用混凝土,其特征在于,所述河沙含水率小于5%。
3.根据权利要求1或2所述的干熄焦炉用混凝土,其特征在于,所述水泥为硅酸铝水泥。
4.根据权利要求3所述的干熄焦炉用混凝土,其特征在于,所述碳酸钙为含水率在5~20%的碳酸钙结晶。
CN201610314380.5A 2016-05-13 2016-05-13 一种干熄焦炉用混凝土 Pending CN105924049A (zh)