CN105921906A - 高铬铸铁药芯焊丝 - Google Patents

高铬铸铁药芯焊丝 Download PDF

Info

Publication number
CN105921906A
CN105921906A CN201610372491.1A CN201610372491A CN105921906A CN 105921906 A CN105921906 A CN 105921906A CN 201610372491 A CN201610372491 A CN 201610372491A CN 105921906 A CN105921906 A CN 105921906A
Authority
CN
China
Prior art keywords
parts
chromium
cored wire
niobium
iron casting
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610372491.1A
Other languages
English (en)
Inventor
苏红菱
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HAIMEN WEILING WELDING MATERIAL MANUFACTURING CO LTD
Original Assignee
HAIMEN WEILING WELDING MATERIAL MANUFACTURING CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HAIMEN WEILING WELDING MATERIAL MANUFACTURING CO LTD filed Critical HAIMEN WEILING WELDING MATERIAL MANUFACTURING CO LTD
Priority to CN201610372491.1A priority Critical patent/CN105921906A/zh
Publication of CN105921906A publication Critical patent/CN105921906A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高铬铸铁药芯焊丝，包括以下重量份的组分：碳1‑10份、铬5‑45份、钼4‑20份、镍3‑15份、钨3‑15份、钒3‑15份、铌2‑20份，镁5‑10份、铁4‑10份、锰8‑16份，优选的，上述各组分的配备重量份为：碳2‑8份、铬10‑40份、钼8‑16份、镍6‑10份、钨6‑12份、钒6‑12 份、铌8‑16份，镁6‑8份、铁6‑8份、锰10‑14份，本发明中铬的硬度高，耐磨性好，耐腐蚀性强；铌能增加抗氧化性。

Description

高铬铸铁药芯焊丝
技术领域
本发明涉及一种高铬铸铁药芯焊丝。
背景技术
药芯焊丝也称为管状焊丝，可以通过调整药粉的合金成分种类和比例，很方便地设计出各种不同用途的焊接材料，因为它的合金成分可灵活方便的调整，所以药芯焊丝的许多品种是实心焊丝无法冶炼和轧制的。焊丝的材料通常跟工件的材料相同，焊丝焊接时，焊芯金属占整个焊缝金属的一部分，所以焊芯的化学成为，直接影响焊缝的质量。
发明内容
本发明的目的在于提供一种高铬铸铁药芯焊丝。
本发明采用的技术方案是：
高铬铸铁药芯焊丝，包括以下重量份的组分：碳1-10份、铬5-45份、钼4-20份、镍3-15份、钨3-15份、钒3-15份 、铌2-20份、，镁5-10份、铁4-10份、锰8-16份。
优选的，上述各组分的配备重量份为：碳2-8份、铬10-40份、钼8-16份、镍6-10份、钨6-12份、钒6-12 份、铌8-16份、，镁6-8份、铁6-8份、锰10-14份。
本发明的优点：铬的硬度高，耐磨性好，耐腐蚀性强；铌能增加抗氧化性。
具体实施方式
实施例1
高铬铸铁药芯焊丝，包括以下重量份的组分：碳1份、铬5份、钼4份、镍3份、钨3份、钒3份 、铌2份、镁5份、铁4份、锰8份。
本发明中铬的硬度高，耐磨性好，耐腐蚀性强；铌能增加抗氧化性。
实施例2
高铬铸铁药芯焊丝，包括以下重量份的组分：碳10份、铬45份、钼20份、镍15份、钨15份、钒15份 、铌20份、镁10份、铁10份、锰16份。
本发明中铬的硬度高，耐磨性好，耐腐蚀性强；铌能增加抗氧化性。
实施例3
高铬铸铁药芯焊丝，包括以下重量份的组分：碳5.5份、铬25份、钼12份、镍9份、钨9份、钒9份 、铌11份、，镁7.5份、铁7份、锰12份。
本发明中铬的硬度高，耐磨性好，耐腐蚀性强；铌能增加抗氧化性。

Claims (2)

1.高铬铸铁药芯焊丝，其特征在于：包括以下重量份的组分：碳1-10份、铬5-45份、钼4-20份、镍3-15份、钨3-15份、钒3-15份 、铌2-20份、镁5-10份、铁4-10份、锰8-16份。
2.根据权利要求1所述的高铬铸铁药芯焊丝，其特征在于：包括以下重量份的组分：碳2-8份、铬10-40份、钼8-16份、镍6-10份、钨6-12份、钒6-12 份、铌8-16份、，镁6-8份、铁6-8份、锰10-14份。
CN201610372491.1A 2016-05-31 2016-05-31 高铬铸铁药芯焊丝 Pending CN105921906A (zh)