CN105921386A - Machining method for negative oxygen ion oil paint wood product - Google Patents
Machining method for negative oxygen ion oil paint wood product Download PDFInfo
- Publication number
- CN105921386A CN105921386A CN201610447933.4A CN201610447933A CN105921386A CN 105921386 A CN105921386 A CN 105921386A CN 201610447933 A CN201610447933 A CN 201610447933A CN 105921386 A CN105921386 A CN 105921386A
- Authority
- CN
- China
- Prior art keywords
- paint
- finished product
- semi
- negative oxygen
- oxygen ion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a machining method for a negative oxygen ion oil paint wood product. The machining method includes the following steps that firstly, wood is selected and machined into a white-embryo semi-finished product, and leveling treatment is conducted on the surface of the white-embryo semi-finished product; secondly, ground color dye is blended according to the color of a ground color plate, the surface of the white-embryo semi-finished product is sprayed with the blended ground color dye, airing is conducted, and the ground color semi-finished product is obtained; thirdly, primer is blended, the surface of the ground color semi-finished product is sprayed with the pre-blended primer, airing is conducted, and the primer semi-finished product is obtained; fourthly, polishing treatment is conducted on the surface of the primer semi-finished product; fifthly, color repairing is conducted on the surface of the primer semi-finished product according to the color of the color plate; sixthly, airing is conducted, the color-repaired semi-finished product is obtained; and seventhly, fine polishing treatment is conducted on the surface of the color-repaired semi-finished product. By the adoption of the machining method for the negative oxygen ion oil paint wood product, the wood product obtained through the machining method can continuously release a great number of negative oxygen ions in air, the air is purified, and the human health can be facilitated as well.
Description
Technical field
The present invention relates to paint technology field, particularly relate to the processing of a kind of negative oxygen ion paint woodwork
Method.
Background technology
In house fitting-up, paint is the link being difficult to avoid that, either chooses solid wood man
Tool or plate fitment, be always difficult to avoid that and varnish furniture.Even if furniture not japanning, metope again may
Can brushing paint.These tastes that may give out difference with material the most constantly being difficult to avoid that, to us
Life bring endless worry.
The solid content of environmental protection paint reaches more than 95%, and during use, the volatilization of organic solvent-free, contained
The whole film-forming of composition, is all minimum to the health hazard of human body and the pollution of environment, is real
Green Product, and the unsaturated polyurethanes paint that we commonly use (PU paint), unsaturated polyester varnish
(PU paint) and nitrate paint (NC paint), have in work progress nearly half solvent (as toluene, two
Toluene, ketone, ester, styrene) and free monomer (such as free toluene diisocyanate TDI) volatilization
In air, pollute environment, the health of the harm mankind.
Summary of the invention
In view of this, the present invention is directed to the deficiency that prior art exists, its main purpose is to provide one
The processing method of negative oxygen ion paint woodwork, the woodwork obtained through this processing method can be in atmosphere
The substantial amounts of negative oxygen ion of sustained release, purifies air, moreover it is possible to promote health.
To achieve these goals, the present invention adopts the following technical scheme that
The processing method of a kind of negative oxygen ion paint woodwork, passes sequentially through following steps and realizes:
(1) choose timber and be processed into white embryo semi-finished product, and the surface of dialogue embryo semi-finished product carries out smooth place
Reason；
(2) according to the mixing color background color dyestuff of background color colour table, using mass ratio is the butyl ester of 100:5
Or acetone, premetallized dye allotment background color dyestuff, and by the background color dye spray that configured in above-mentioned
On the surface of white embryo semi-finished product, through drying, make background color semi-finished product；
(3) use PU polyurethane primer, different hydrohalogenic acid salt, and butyl ester or acetone are in mass ratio
1:0.5:0.8 configures priming paint, sprays pre-configured priming paint on the surface of above-mentioned background color semi-finished product,
Through drying, prepare priming paint semi-finished product；
(4) surface of above-mentioned priming paint semi-finished product is carried out grinding process；
(5) PU polyurethane primer, different hydrohalogenic acid salt, and butyl ester or acetone 1:0.5:1 in mass ratio are used
Allotment colored paint, repaiies color according to the color of colour table to the surface of above-mentioned priming paint semi-finished product and processes；Pass through
Dry, obtain repairing color semi-finished product；
(6) the above-mentioned surface repairing color semi-finished product is carried out fine grinding process；
(7) use PU polyurethane primer, different hydrohalogenic acid salt, and butyl ester or acetone are in mass ratio
1:0.5:0.8 configuration paint intermixture, in deployed paint intermixture add account for paint intermixture total
The negative oxygen ion superfine powder of weight 1-3%, through stirring, filters, makes negative oxygen ion finish paint；
(8) on the surface of above-mentioned priming paint semi-finished product after polishing, above-mentioned negative oxygen ion face is sprayed
Paint, through drying, thus makes negative oxygen ion paint woodwork.
In described step 1, the surface of 180#～240# sand paper dialogue embryo semi-finished product is used to carry out burnishing part
Reason.
In described step 2, every square metre of quantity for spray of background color dyestuff is 90-110 gram, at normal temperatures, dries in the air
The dry time is 10-30 minute.
In described step 3, priming paint is sprayed at above-mentioned background color semi-finished product by " ten " word intersection spraying method
Surface on, spraying number of times be 1-2 time, control priming paint viscosity be the 8-12 second, the spray of every square metre
Painting amount is 190-210 gram, at normal temperatures, and flash-off time at least 4 hours.
In described step 4,400# sand paper is used to carry out smooth, smooth to the surface of priming paint semi-finished product
Polishing.
In described step 5, repairing color and processing is that colored paint is deployed into the solid colour with colour table, and will adjust
The colored paint prepared is sprayed on the surface of above-mentioned priming paint semi-finished product after polishing, controls the viscous of colored paint
Degree is the 8-11 second, and the quantity for spray of every square metre is 140-160 gram, and at normal temperatures, flash-off time is 1-3
Hour.
In described step 6,600# sand paper is used finely to be polished in the above-mentioned surface repairing color semi-finished product.
In described step 7, use blender to be stirred, control the negative oxygen ion finish paint viscosity 9-12 second,
Filter again.
In described step 8, above-mentioned negative oxygen ion finish paint is sprayed at by " ten " word intersection spraying method
Stating on the surface of the priming paint semi-finished product after polishing, spraying number of times is 1-2 time, the spray of every square metre
Painting amount is 170-190 gram, and at normal temperatures, flash-off time is 10-14 hour.
Use technique scheme, the invention have the advantages that
The processing method of the negative oxygen ion paint woodwork of the present invention, by selecting timber through processing system
Becoming white embryo semi-finished product, the surface of dialogue embryo semi-finished product is through smooth process, spraying background color dyestuff, spraying
Priming paint, lacquer painting to priming paint carry out grinding process；Carrying out repairing color through priming paint semi-finished product so that the end
The color on the surface of paint semi-finished product is more uniform, meets demand, more attractive in appearance.Repair after color processes and carry out
Fine polishing, convenient spraying negative oxygen ion finish paint so that finish paint spraying is more firm.Finally passing through
Spray negative oxygen ion finish paint on priming paint semi-finished product after fine polishing and make negative oxygen ion paint woodwork.
Wherein, host, firming agent and diluent is used to carry out configuration paint intermixture, at the paint configured
Adding negative oxygen ion superfine powder configuration negative oxygen ion finish paint in intermixture, negative oxygen ion finish paint can be at air
The substantial amounts of negative oxygen ion of middle sustained release, purifies air, promotes health.
Detailed description of the invention
The present invention is described further with specific embodiment below in conjunction with the accompanying drawings.
As it is shown in figure 1, the processing method of a kind of negative oxygen ion paint woodwork, pass sequentially through following step
Rapid realization:
(1) choose timber and be processed into white embryo semi-finished product, and the surface of dialogue embryo semi-finished product carries out smooth place
Reason；
(2) according to the mixing color background color dyestuff of background color colour table, using mass ratio is the butyl ester of 100:5
Or acetone, premetallized dye allotment background color dyestuff, and by the background color dye spray that configured in above-mentioned
On the surface of white embryo semi-finished product, through drying, make background color semi-finished product；
(3) use PU polyurethane primer, different hydrohalogenic acid salt, and butyl ester or acetone are in mass ratio
1:0.5:0.8 configures priming paint, sprays pre-configured priming paint on the surface of above-mentioned background color semi-finished product,
Through drying, prepare priming paint semi-finished product；
(4) surface of above-mentioned priming paint semi-finished product is carried out grinding process；
(5) PU polyurethane primer, different hydrohalogenic acid salt, and butyl ester or acetone 1:0.5:1 in mass ratio are used
Allotment colored paint, repaiies color according to the color of colour table to the surface of above-mentioned priming paint semi-finished product and processes；Pass through
Dry, obtain repairing color semi-finished product；
(6) the above-mentioned surface repairing color semi-finished product is carried out fine grinding process；
(7) use PU polyurethane primer, different hydrohalogenic acid salt, and butyl ester or acetone are in mass ratio
1:0.5:0.8 configuration paint intermixture, in deployed paint intermixture add account for paint intermixture total
The negative oxygen ion superfine powder of weight 1-3%, through stirring, filters, makes negative oxygen ion finish paint；
(8) on the surface of above-mentioned priming paint semi-finished product after polishing, above-mentioned negative oxygen ion face is sprayed
Paint, through drying, thus makes negative oxygen ion paint woodwork.
In the present embodiment, in described step 1, use the table of 180#～240# sand paper dialogue embryo semi-finished product
Face carries out grinding process.
In the present embodiment, in described step 2, every square metre of quantity for spray of background color dyestuff is 100 grams,
Under room temperature, flash-off time is 20 minutes.Concrete effect is: on the one hand by white embryo surface of semi-finished wood hole
Close.Closing is exactly that conduit to be filled and led up completely, invisible conduit.On the other hand it is at white embryo semi-finished product
Upper spraying background color dyestuff, to obtain required colorful semi-finished product.
In the present embodiment, in described step 3, priming paint is sprayed at by " ten " word intersection spraying method
Stating on the surface of background color semi-finished product, spraying number of times is 1-2 time, and the viscosity controlling priming paint is the 9-11 second,
The quantity for spray of every square metre is 200 grams, and at normal temperatures, flash-off time is more than 4 hours.The most right
" ten " word intersects what spraying method was expanded on further: spray paint in general furniture or finishing, spray
The path being coated with is usually first horizontal spray, sprays perpendicular spray again behind complete face, equal to the path of spray gun at surface of the work
Draw a cross.In like manner, in surface of the work first horizontal spray, spray perpendicular spray again behind complete face, more horizontal spray,
Perpendicular spray again, here it is the spraying of so-called diesis.
In the present embodiment, in described step 4, use 400# sand paper that the surface of priming paint semi-finished product is carried out
Smooth, smooth polishing.
In the present embodiment, in described step 5, repairing color and processing is that colored paint is deployed into the color with colour table
Unanimously, and deployed colored paint is sprayed on the surface of above-mentioned priming paint semi-finished product after polishing,
The viscosity controlling colored paint is 9～10 seconds, and the quantity for spray of every square metre is 150 grams, at normal temperatures, dries in the air
The dry time is 2 hours.Here color process of repairing is that comparison colour table carries out repairing color, repaiies color rear surface and has
Feel full on gloss, sense organ, and close with the depth color of colour table.
In the present embodiment, in described step 6, use 600# sand paper to the above-mentioned surface repairing color semi-finished product
Finely polish.
In the present embodiment, in described step 7, concrete: in deployed paint intermixture, add
Account for the negative oxygen ion superfine powder of paint intermixture gross weight 1%, use blender to be stirred, control negative
Oxonium ion finish paint viscosity 10～11 seconds, filtering.
In the present embodiment, in described step 8, above-mentioned negative oxygen ion finish paint is by the intersection spraying of " ten " word
Mode is sprayed on the surface of above-mentioned priming paint semi-finished product after polishing, and spraying number of times is 1-2 time,
The quantity for spray of every square metre is 180 grams, and at normal temperatures, flash-off time is 12 hours.
It should be noted that in step 7, owing to the proportion of negative oxygen ion superfine powder is than paint weight, make
Industry process easily precipitates, and carries out high-speed stirred uniformly (turning of blender with blender during allotment paint
Speed be 1000-2000 rev/min), must be noted that often to stir in spraying process, it is to avoid bear oxygen from
Sub-powder precipitates, and the product making spray good does not has negative oxygen ion release not reach preferable environment protecting.
Need exist for special instruction: negative oxygen ion painting must every cubic centimetre can discharge
More than 1500 negative oxygen ions, can be only achieved the requirement purifying air.The middle employing of the present invention bear oxygen from
The negative oxygen ion paint woodwork that the processing method of seed oil paint woodwork manufactures, by using air ion
On its wood product surface of measuring instrument, every cubic centimetre of releasing negative oxygen ion number is more than 4140, conforms to
Ask.On negative oxygen ion paint woodwork, the negative oxygen ion of negative oxygen ion paint release can purify air, has
Effect removes PM2.5 particulate matter, negative oxygen ion paint nature sustained release negative oxygen ion more than 20 years, nothing
Any noise, is completely free of electrostatic and pollutes.
Above in conjunction with accompanying drawing, the present invention is described in detail, but embodiments of the present invention are not
Being only limitted to above-mentioned embodiment, the present invention can be made respectively by those skilled in the art according to prior art
Plant deformation, belong to protection scope of the present invention.
Claims (9)
1. the processing method of a negative oxygen ion paint woodwork, it is characterised in that: pass sequentially through following
Step realizes:
(1) choose timber and be processed into white embryo semi-finished product, and the surface of dialogue embryo semi-finished product carries out smooth place
Reason；
(2) according to the mixing color background color dyestuff of background color colour table, using mass ratio is the butyl ester of 100:5
Or acetone, premetallized dye allotment background color dyestuff, and by the background color dye spray that configured in above-mentioned
On the surface of white embryo semi-finished product, through drying, make background color semi-finished product；
(3) use PU polyurethane primer, different hydrohalogenic acid salt, and butyl ester or acetone are in mass ratio
1:0.5:0.8 configures priming paint, sprays pre-configured priming paint on the surface of above-mentioned background color semi-finished product,
Through drying, prepare priming paint semi-finished product；
(4) surface of above-mentioned priming paint semi-finished product is carried out grinding process；
(5) PU polyurethane primer, different hydrohalogenic acid salt, and butyl ester or acetone 1:0.5:1 in mass ratio are used
Allotment colored paint, repaiies color according to the color of colour table to the surface of above-mentioned priming paint semi-finished product and processes；Pass through
Dry, obtain repairing color semi-finished product；
(6) the above-mentioned surface repairing color semi-finished product is carried out fine grinding process；
(7) use PU polyurethane primer, different hydrohalogenic acid salt, and butyl ester or acetone are in mass ratio
1:0.5:0.8 configuration paint intermixture, in deployed paint intermixture add account for paint intermixture total
The negative oxygen ion superfine powder of weight 1-3%, through stirring, filters, makes negative oxygen ion finish paint；
(8) on the surface of above-mentioned priming paint semi-finished product after polishing, above-mentioned negative oxygen ion face is sprayed
Paint, through drying, thus makes negative oxygen ion paint woodwork.
The processing method of a kind of negative oxygen ion the most according to claim 1 paint woodwork, it is special
Levy and be: in described step 1, use the surface of 180#～240# sand paper dialogue embryo semi-finished product to carry out beating
Mill processes.
The processing method of a kind of negative oxygen ion the most according to claim 1 paint woodwork, it is special
Levying and be: in described step 2, every square metre of quantity for spray of background color dyestuff is 90-110 gram, at normal temperatures,
Flash-off time is 10-30 minute.
The processing method of a kind of negative oxygen ion the most according to claim 1 paint woodwork, it is special
Levying and be: in described step 3, priming paint is sprayed at above-mentioned background color half by " ten " word intersection spraying method
On the surface of finished product, spraying number of times is 1-2 time, and the viscosity controlling priming paint is the 8-12 second, every square metre
Quantity for spray be 190-210 gram, at normal temperatures, flash-off time at least 4 hours.
The processing method of a kind of negative oxygen ion the most according to claim 1 paint woodwork, it is special
Levy and be: in described step 4, use 400# sand paper that the surface of priming paint semi-finished product is carried out smooth, light
Sliding polishing.
The processing method of a kind of negative oxygen ion the most according to claim 1 paint woodwork, it is special
Levying and be: in described step 5, repairing color and processing is that colored paint is deployed into the solid colour with colour table, and
Deployed colored paint is sprayed on the surface of above-mentioned priming paint semi-finished product after polishing, controls colored paint
Viscosity be the 8-11 second, the quantity for spray of every square metre is 140-160 gram, at normal temperatures, flash-off time
For 1-3 hour.
The processing method of a kind of negative oxygen ion the most according to claim 1 paint woodwork, it is special
Levy and be: in described step 6, use 600# sand paper that the above-mentioned surface repairing color semi-finished product is carried out finely
Polishing.
The processing method of a kind of negative oxygen ion the most according to claim 1 paint woodwork, it is special
Levy and be: in described step 7, use blender to be stirred, control negative oxygen ion finish paint viscosity 9-12
Second, then filter.
The processing method of a kind of negative oxygen ion the most according to claim 1 paint woodwork, it is special
Levying and be: in described step 8, above-mentioned negative oxygen ion finish paint is by the intersection spraying method spraying of " ten " word
On the surface of above-mentioned priming paint semi-finished product after polishing, spraying number of times is 1-2 time, every square metre
Quantity for spray be 170-190 gram, at normal temperatures, flash-off time is 10-14 hour.