CN106513285A - Paint spraying method for wood product - Google Patents
Paint spraying method for wood product Download PDFInfo
- Publication number
- CN106513285A CN106513285A CN201611001729.6A CN201611001729A CN106513285A CN 106513285 A CN106513285 A CN 106513285A CN 201611001729 A CN201611001729 A CN 201611001729A CN 106513285 A CN106513285 A CN 106513285A
- Authority
- CN
- China
- Prior art keywords
- powder
- parts
- paint spraying
- paint
- standby
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a paint spraying method for a wood product, and belongs to the field of wood processing. The paint spraying method specifically comprises the first step of blank grinding, the second step of ground color making, the third step of primer lacquering, the fourth step of polishing and the fifth step of finish paint lacquering. Through the paint spraying method, the bonding strength between a paint layer and the wood product can be well improved, the probability of micro holes, cracking, bubbles, disengaging and the like happening in the finished product using process is reduced, the oil paint effect is guaranteed, and the using and popularizing value is high.
Description
Technical field
The invention belongs to treating of wood field, and in particular to a kind of method for paint spraying of woodwork.
Background technology
Woodwork mopping is a kind of means for improving product service life and performance, mopping process after woodwork not only with
The quality of paint is relevant, also related to the mode that mopping is processed, if method is incorrect, easily causes pull-away, cracking etc. existing
As occurring, overall use quality is have impact on.
The content of the invention
The present invention is intended to provide a kind of method for paint spraying of woodwork, can preferably lift the effect of spray painting.
The present invention is achieved through the following technical solutions：
A kind of method for paint spraying of woodwork, comprises the steps：
（1）Mill blank：Three time polishings are carried out to wooden base to be processed first, first pass polished with No. 180 sand paper, second time with 240
Number sand paper is polished, and is polished with No. 320 sand paper for the 3rd time, standby after the completion of process；
（2）Do background color：To step（1）After wooden base after process is dried under conditions of being placed in 32 ~ 35 DEG C, then beaten with No. 400 sand paper
Ground smooth, then rubs Ge Lisi, dry for standby under conditions of being placed in 38 ~ 40 DEG C again after the completion of process to which；
（3）Priming：To step（2）Wooden base after process first goes up a PU priming paint, then applies and mends one layer of special putty powder, completes
Go up a PE priming paint afterwards again, finally repaste one layer of special putty powder of benefit standby；
（4）Polishing：First with polisher to step（3）Wooden base after process carries out roughing operations, then turns to manual grinding, sand paper
The order that model is used is No. 220, No. 320, No. 500 and No. 600, standby after finally being polished with sand sponge；
（5）Upper finish paint：By step（4）Wooden base after process is sent in dustless paint spraying booth, carries out finish paint spraying operation, after the completion of will
Which is put into temperature to be dried under conditions of 40 ~ 43 DEG C, and period is aided with the ultrasonic Treatment that frequency is 50 ~ 53kHz, until wood
The overall moisture content of base is not more than 13%.
Further, step（3）The special putty powder is made up of the material of following weight portion：100 ~ 110 parts dispersible
Property latex powder, 5 ~ 8 parts of Polyethylene Glycol, 30 ~ 35 parts of feldspars in powder, 25 ~ 30 parts of Kaolin powder, 6 ~ 10 parts of colliery powders, 25 ~ 30 parts
Sepiolite powder, 5 ~ 10 parts of glass beads, 2 ~ 4 parts of sodium alginates, 3 ~ 5 parts of calcium sulfate；
Its preparation method comprises the steps：
A. feldspar in powder, Kaolin powder, colliery powder and sepiolite powder are mixed jointly, is first put into the chlorination that mass fraction is 4%
40 ~ 45min of immersion treatment in sodium solution, puts it into immersion treatment in the rare earth nitrate solution that mass fraction is 2% again after taking-up
20 ~ 25min, drying for standby after taking-up；Mentioned component is carried out after surface modification treatment, improved its knot with paint film matrix
Intensity is closed, overall corrosion resistant, antiwear characteristic is enhanced；
B. the mixture after the process of step a is ground into into A, B, C three-level by granular size, wherein the granular size of A levels be 200 ~
300 mesh, the granular size of B levels are 500 ~ 600 mesh, and the granular size of C levels is 900 ~ 1000 mesh, then by A, B, C three-level
Grain in mass ratio 15：4：2 mixing, obtain compounded mix standby；Above-mentioned several implants are pressed after gradation proportioning, can be improved and be filled out
The associativity filled and compactness, can be lifted and fill out attached uniformity, it is ensured that the adhesion strength of paint film, enhance it is overall it is water-fast,
Oil resistant characteristic；
C. by the compounded mix obtained by step b with dispersibility latex powder, Polyethylene Glycol, glass bead, sodium alginate, calcium sulfate
It is sufficiently mixed after being uniformly dispersed.
Further, step（4）Described in polisher roughly grind when be defined by not galling PE priming paint.
Further, step（5）Described in drying and processing when relative humidity be controlled to 40 ~ 45%.
The present invention has the advantages that：
The present invention on the basis of bulk trial is optimized to existing mopping technique, wooden base is carried out fine
Mill blank is operated, and enhances its surface uniformity, first goes up PU priming paint, then upper PE priming paint improves the protection effect to wooden base, increases again
The strong tack of finish paint, wherein the special putty powder used when filling up, with dispersion, adhesiveness is good, intensity is high the characteristics of, protect
The associativity between priming paint has been demonstrate,proved, the ultrasonic Treatment applied when being dried after finally going up finish paint, energy is well inside homogenizing paint film
Stress, lifts the adhesion effect between each layer, lifts uniformity, compactness and the glossiness of lacquer painting.Method for paint spraying energy of the present invention
Improve the bond strength of enamelled coating and woodwork well, micropore, cracking occur, bubble, come off when finished product is reduced using process
Deng probability, it is ensured that the effect of paint, application and popularizations value it is higher.
Specific embodiment
Embodiment 1
A kind of method for paint spraying of woodwork, comprises the steps：
（1）Mill blank：Three time polishings are carried out to wooden base to be processed first, first pass polished with No. 180 sand paper, second time with 240
Number sand paper is polished, and is polished with No. 320 sand paper for the 3rd time, standby after the completion of process；
（2）Do background color：To step（1）After wooden base after process is dried under conditions of being placed in 32 DEG C, then with No. 400 sand papering light
It is sliding, then rub Ge Lisi, dry for standby under conditions of 38 DEG C being placed in again after the completion of process to which；
（3）Priming：To step（2）Wooden base after process first goes up a PU priming paint, then applies and mends one layer of special putty powder, completes
Go up a PE priming paint afterwards again, finally repaste one layer of special putty powder of benefit standby；
（4）Polishing：First with polisher to step（3）Wooden base after process carries out roughing operations, then turns to manual grinding, sand paper
The order that model is used is No. 220, No. 320, No. 500 and No. 600, standby after finally being polished with sand sponge；
（5）Upper finish paint：By step（4）Wooden base after process is sent in dustless paint spraying booth, carries out finish paint spraying operation, after the completion of will
Which is put into temperature to be dried under conditions of 40 DEG C, and period is aided with the ultrasonic Treatment that frequency is 50kHz, until wooden base entirety
Moisture content be not more than 13%.
Further, step（3）The special putty powder is made up of the material of following weight portion：100 parts of dispersibility breasts
Rubber powder, 5 parts of Polyethylene Glycol, 30 parts of feldspars in powder, 25 parts of Kaolin powder, 6 parts of colliery powders, 25 parts of sepiolite powders, 5 parts of vitreous are micro-
Pearl, 2 parts of sodium alginates, 3 parts of calcium sulfate；
Its preparation method comprises the steps：
A. feldspar in powder, Kaolin powder, colliery powder and sepiolite powder are mixed jointly, is first put into the chlorination that mass fraction is 4%
Immersion treatment 40min in sodium solution, puts it into immersion treatment in the rare earth nitrate solution that mass fraction is 2% again after taking-up
20min, drying for standby after taking-up；
B. the mixture after the process of step a is ground into into A, B, C three-level by granular size, wherein the granular size of A levels be 200 ~
300 mesh, the granular size of B levels are 500 ~ 600 mesh, and the granular size of C levels is 900 ~ 1000 mesh, then by A, B, C three-level
Grain in mass ratio 15：4：2 mixing, obtain compounded mix standby；
C. by the compounded mix obtained by step b with dispersibility latex powder, Polyethylene Glycol, glass bead, sodium alginate, calcium sulfate
It is sufficiently mixed after being uniformly dispersed.
Further, step（4）Described in polisher roughly grind when be defined by not galling PE priming paint.
Further, step（5）Described in drying and processing when relative humidity be controlled to 40 ~ 45%.
Embodiment 2
A kind of method for paint spraying of woodwork, comprises the steps：
（1）Mill blank：Three time polishings are carried out to wooden base to be processed first, first pass polished with No. 180 sand paper, second time with 240
Number sand paper is polished, and is polished with No. 320 sand paper for the 3rd time, standby after the completion of process；
（2）Do background color：To step（1）After wooden base after process is dried under conditions of being placed in 35 DEG C, then with No. 400 sand papering light
It is sliding, then rub Ge Lisi, dry for standby under conditions of 40 DEG C being placed in again after the completion of process to which；
（3）Priming：To step（2）Wooden base after process first goes up a PU priming paint, then applies and mends one layer of special putty powder, completes
Go up a PE priming paint afterwards again, finally repaste one layer of special putty powder of benefit standby；
（4）Polishing：First with polisher to step（3）Wooden base after process carries out roughing operations, then turns to manual grinding, sand paper
The order that model is used is No. 220, No. 320, No. 500 and No. 600, standby after finally being polished with sand sponge；
（5）Upper finish paint：By step（4）Wooden base after process is sent in dustless paint spraying booth, carries out finish paint spraying operation, after the completion of will
Which is put into temperature to be dried under conditions of 43 DEG C, and period is aided with the ultrasonic Treatment that frequency is 53kHz, until wooden base entirety
Moisture content be not more than 13%.
Further, step（3）The special putty powder is made up of the material of following weight portion：110 parts of dispersibility breasts
Rubber powder, 8 parts of Polyethylene Glycol, 35 parts of feldspars in powder, 30 parts of Kaolin powder, 10 parts of colliery powders, 30 parts of sepiolite powders, 10 parts of vitreous
Microballon, 4 parts of sodium alginates, 5 parts of calcium sulfate；
Its preparation method comprises the steps：
A. feldspar in powder, Kaolin powder, colliery powder and sepiolite powder are mixed jointly, is first put into the chlorination that mass fraction is 4%
Immersion treatment 45min in sodium solution, puts it into immersion treatment in the rare earth nitrate solution that mass fraction is 2% again after taking-up
25min, drying for standby after taking-up；
B. the mixture after the process of step a is ground into into A, B, C three-level by granular size, wherein the granular size of A levels be 200 ~
300 mesh, the granular size of B levels are 500 ~ 600 mesh, and the granular size of C levels is 900 ~ 1000 mesh, then by A, B, C three-level
Grain in mass ratio 15：4：2 mixing, obtain compounded mix standby；
C. by the compounded mix obtained by step b with dispersibility latex powder, Polyethylene Glycol, glass bead, sodium alginate, calcium sulfate
It is sufficiently mixed after being uniformly dispersed.
Further, step（4）Described in polisher roughly grind when be defined by not galling PE priming paint.
Further, step（5）Described in drying and processing when relative humidity be controlled to 40 ~ 45%.
Comparative example 1
This comparative example 1 compared with Example 1, when prepared by special putty powder, the granule of A, B, C three-level is adjusted in mass ratio
Whole is 10：2：1, method and step all same in addition.
Comparative example 2
This comparative example 2 compared with Example 2, is processed in after bake dry run in finish paint, is not aided in applying ultrasonic Treatment, is removed
In addition method and step all same.
Matched group
Existing woodwork spray painting processing method.
In order to contrast effect of the present invention, process behaviour to spray painting being carried out with a collection of tung oil tree timber respectively with above-mentioned six kinds of modes
Make, test experience is then carried out to finished product, specific correction data is as shown in table 1 below：
Table 1
| Salt tolerant duration（h） | Heatproof duration（h） | Finished wood surface condition | |
| Embodiment 1 | 226 | 135 | It is smooth, uniform |
| Embodiment 2 | 234 | 138 | It is smooth, uniform |
| Embodiment 3 | 228 | 136 | It is smooth, uniform |
| Comparative example 1 | 203 | 126 | It is smooth, more uniform |
| Comparative example 2 | 194 | 122 | It is more smooth, more uniform |
| Matched group | 177 | 112 | There are concave point, bubble, it is uneven |
Note：Salt tolerant duration described in upper table 1 is referred to food that the mass fraction that the timber finished product after process is put into 38 DEG C is 1%
Soak in saline, until the salt tolerant immersion duration of obvious bubble, obscission occurs in surface；Described heatproof duration is referred to will be located
It is to toast under conditions of 20% that timber finished product after reason is put into temperature for 60 DEG C, relative humidity, until surface occur obvious bubble,
The heatproof baking duration of obscission.
By upper table 1 as can be seen that method for paint spraying of the present invention can improve well woodwork entirety quality, use value compared with
It is good.
Claims (4)
1. a kind of method for paint spraying of woodwork, it is characterised in that comprise the steps：
（1）Mill blank：Three time polishings are carried out to wooden base to be processed first, first pass polished with No. 180 sand paper, second time with 240
Number sand paper is polished, and is polished with No. 320 sand paper for the 3rd time, standby after the completion of process；
（2）Do background color：To step（1）After wooden base after process is dried under conditions of being placed in 32 ~ 35 DEG C, then beaten with No. 400 sand paper
Ground smooth, then rubs Ge Lisi, dry for standby under conditions of being placed in 38 ~ 40 DEG C again after the completion of process to which；
（3）Priming：To step（2）Wooden base after process first goes up a PU priming paint, then applies and mends one layer of special putty powder, completes
Go up a PE priming paint afterwards again, finally repaste one layer of special putty powder of benefit standby；
（4）Polishing：First with polisher to step（3）Wooden base after process carries out roughing operations, then turns to manual grinding, sand paper
The order that model is used is No. 220, No. 320, No. 500 and No. 600, standby after finally being polished with sand sponge；
（5）Upper finish paint：By step（4）Wooden base after process is sent in dustless paint spraying booth, carries out finish paint spraying operation, after the completion of will
Which is put into temperature to be dried under conditions of 40 ~ 43 DEG C, and period is aided with the ultrasonic Treatment that frequency is 50 ~ 53kHz, until wood
The overall moisture content of base is not more than 13%.
2. a kind of method for paint spraying of woodwork according to claim 1, it is characterised in that step（3）The special putty
Powder is made up of the material of following weight portion：100 ~ 110 parts of dispersibility latex powders, 5 ~ 8 parts of Polyethylene Glycol, 30 ~ 35 parts of potassium feldspars
Powder, 25 ~ 30 parts of Kaolin powder, 6 ~ 10 parts of colliery powders, 25 ~ 30 parts of sepiolite powders, 5 ~ 10 parts of glass beads, 2 ~ 4 parts of alginic acid
Sodium, 3 ~ 5 parts of calcium sulfate；
Its preparation method comprises the steps：
A. feldspar in powder, Kaolin powder, colliery powder and sepiolite powder are mixed jointly, is first put into the chlorination that mass fraction is 4%
40 ~ 45min of immersion treatment in sodium solution, puts it into immersion treatment in the rare earth nitrate solution that mass fraction is 2% again after taking-up
20 ~ 25min, drying for standby after taking-up；
B. the mixture after the process of step a is ground into into A, B, C three-level by granular size, wherein the granular size of A levels be 200 ~
300 mesh, the granular size of B levels are 500 ~ 600 mesh, and the granular size of C levels is 900 ~ 1000 mesh, then by A, B, C three-level
Grain in mass ratio 15：4：2 mixing, obtain compounded mix standby；
C. by the compounded mix obtained by step b with dispersibility latex powder, Polyethylene Glycol, glass bead, sodium alginate, calcium sulfate
It is sufficiently mixed after being uniformly dispersed.
3. a kind of method for paint spraying of woodwork according to claim 1, it is characterised in that step（4）Described in polisher
It is defined by not galling PE priming paint during corase grind.
4. a kind of method for paint spraying of woodwork according to claim 1, it is characterised in that step（5）Described at drying
Relative humidity during reason is controlled to 40 ~ 45%.